We have investigated the correlation between the microwave loss and patterning method for coplanar waveguide titanium nitride resonators fabricated on silicon wafers. Three different methods were investigated: fluorine- and chlorine-based reactive ion etches and an argon-ion mill. At high microwave probe powers, the reactive etched resonators showed low internal loss, whereas the ion-milled samples showed dramatically higher loss. At single-photon powers, we found that the fluorine-etched resonators exhibited substantially lower loss than the chlorine-etched ones. We interpret the results by use of numerically calculated filling factors and find that the silicon surface exhibits a higher loss when chlorine-etched than when fluorine-etched. We also find from microscopy that re-deposition of silicon onto the photoresist and side walls is the probable cause for the high loss observed for the ion-milled resonators.
We report on the fabrication and characterization of superconducting coplanar waveguide (CPW) resonators based on titanium nitride (TiN) thin films deposited on 200\,mm diameter high-resistivity Si(100) substrates. We systematically investigate how deposition conditions, dry-etch power and in-situ resist strip temperature affect morphology, superconducting properties and dielectric losses. By tuning reactive sputtering conditions, three distinct preferred out-of-plane crystal orientations - (111), (200), and a mix of both are achieved. Our results demonstrate that all films exhibit similar minimal two-level system (TLS) losses, with TiN111 exhibiting the lowest median TLS losses
δ~TLS, and greater robustness against reoxidation. The applied structuring process, in contrast, has a far greater influence on the TLS loss than the crystal orientation of the TiN film and, consequently, the intrinsic material properties of the superconducting layer. The lowest TLS losses for all TiN depositions were achieved with a low power etch and low temperature resist strip. An additional buffered oxide etch (BOE) treatment could remove high-loss interfacial oxides at the metal-air (MA) and substrate-air (SA) interface and recover the etch-induced TLS losses. Consequently, TiN resonators exhibiting
δ~TLS values as low as
9.67×10−7 were realized. The corresponding median low-power loss,
δ~LP, amounts to
11.04×10−7, which translates to an internal quality factor approaching one million. These findings highlight the critical role of process induced oxide formation at the MA and SA interfaces in limiting the performance of TiN resonators and provide a scalable, low-loss process compatible with industry-grade 200\,mm CMOS qubit fabrication workflows.