arXiv:2603.00441 · Applied Physics Reviews

Optimizing CMOS-compatible, superconducting titanium nitride resonators: Deposition conditions and structuring processes

Simon J. K. Lang, Alexandra Schewski, Ignaz Eisele, Johannes Weber, Carla Moran-Guizan, Zhen Lou, Moritz Singer, Benedikt Schoof, Marc Tornow, Thomas Mayer, Daniela Zahn, Rui N. Pereira, Christoph Kutter

quant-phSubmitted Feb 28, 2026• Announced Mar 3, 2026• 0 citations• Revised Jul 16, 2026 (v2)
v1 · Feb 28, 2026v2 · Jul 16, 2026
arXivHTMLPDF

Abstract

We report on the fabrication and characterization of superconducting coplanar waveguide (CPW) resonators based on titanium nitride (TiN) thin films deposited on 200\,mm diameter high-resistivity Si(100) substrates. We systematically investigate how deposition conditions, dry-etch power and in-situ resist strip temperature affect morphology, superconducting properties and dielectric losses. By tuning reactive sputtering conditions, three distinct preferred out-of-plane crystal orientations - (111), (200), and a mix of both are achieved. Our results demonstrate that all films exhibit similar minimal two-level system (TLS) losses, with TiN111 exhibiting the lowest median TLS losses $\tildeδ_\mathrm{TLS}$, and greater robustness against reoxidation. The applied structuring process, in contrast, has a far greater influence on the TLS loss than the crystal orientation of the TiN film and, consequently, the intrinsic material properties of the superconducting layer. The lowest TLS losses for all TiN depositions were achieved with a low power etch and low temperature resist strip. An additional buffered oxide etch (BOE) treatment could remove high-loss interfacial oxides at the metal-air (MA) and substrate-air (SA) interface and recover the etch-induced TLS losses. Consequently, TiN resonators exhibiting $\tildeδ_\mathrm{TLS}$ values as low as $9.67 \times 10^{-7}$ were realized. The corresponding median low-power loss, $\tildeδ_\mathrm{LP}$, amounts to $11.04 \times 10^{-7}$, which translates to an internal quality factor approaching one million. These findings highlight the critical role of process induced oxide formation at the MA and SA interfaces in limiting the performance of TiN resonators and provide a scalable, low-loss process compatible with industry-grade 200\,mm CMOS qubit fabrication workflows.

Journal reference
Appl. Phys. Rev. 13, 031403, 2026
DOI
10.1063/5.0331943
Comments
10 pages, 10 figures

Related papers

Reducing TLS loss in tantalum CPW resonators using titanium sacrificial layers

Zachary Degnan, Chun-Ching Chiu, Yi-Hsun Chen +5 more

We demonstrate a substantial reduction in two-level system loss in tantalum coplanar waveguide resonators fabricated on high-resistivity silicon substrates through the use of an ultrathin titanium sacrificial layer. A 0.2nm titanium film, deposited atop pre-sputtered α-tantalum, acts as a solid-state oxygen getter that chemically modifies the native Ta oxide at the metal-air interface. After device fabrication, the titanium layer is removed using buffered oxide etchant, leaving behind a chemically reduced Ta oxide surface. Subsequent high-vacuum annealing further suppresses two-level system loss. Resonators treated with this process exhibit internal quality factors Qi exceeding an average of 1.5 million in the single-photon regime across ten devices, over three times higher than otherwise identical devices lacking the titanium layer. These results highlight the critical role of interfacial oxide chemistry in superconducting loss and reinforce atomic-scale surface engineering as an effective approach to improving coherence in tantalum-based quantum circuits. The method is compatible with existing fabrication workflows applicable to tantalum films, offering a practical route to further extending T1 lifetimes in superconducting qubits.

quant-pharXiv:2601.16369•Applied Physics Reviews•Jan 26, 2026•0 citations

Dielectric Loss in Superconducting NbN (200) CPW Resonator Developed on Si Substrate

Wei Qiu, Kazumasa Makise, Hirotaka Terai

In current superconducting qubit circuit development, coherence time is limited by low-frequency flux noise introduced from localized two-level systems (TLSs) in the fabricated superconducting circuit, including superconducting materials, the interface between thin films, and the substrate. As a part of the effect to tackle this issue from a substrate standpoint, we succeed in fabricating NbN (200) oriented coplanar waveguide resonator (CPWR) on a thin titanium nitride (TiN) (200) buffered Si (100) substrate. The internal loss is close to 3 × 10-5nearphoton> ~1, improved from ~2 × 10-4in NbN (200) CPWR fabricated on MgO (100). For NbN (200) resonators grown on Si (100), the internal loss shows microwave energy independent. To further clarity if this energy independence is due to the change of substrate material, we also fabricated TiN (200) CPWR on Si (100). In contrast to NbN (200) CPWR, the loss of TiN (200) resonator shows a strong microwave dependent, an indication of TLSs originated from the interface and the surface. We suggest TLSs in NbN (200) CPWR are dominated from different mechanism other than arising from the interface and surface.

IEEE Transactions on Applied Superconductivity•Jan 9, 2017•5 citations

Low loss superconducting titanium nitride coplanar waveguide resonators

Michael R. Vissers, J. Gao, David Wisbey +5 more

Thin films of TiN were sputter-deposited onto Si and sapphire wafers with and without SiN buffer layers. The films were fabricated into rf coplanar waveguide resonators, and internal quality factor measurements were taken at millikelvin temperatures in both the many photon and single photon limits, i.e., high and low electric field regimes, respectively. At high field, we found the highest internal quality factors (∼107) were measured for TiN with predominantly a (200)-TiN orientation. The (200)-TiN is favored for growth at high temperature on either bare Si or SiN buffer layers. However, growth on bare sapphire or Si(100) at low temperature resulted in primarily a (111)-TiN orientation. Ellipsometry and Auger measurements indicate that the (200)-TiN growth on the bare Si substrates is correlated with the formation of a thin, ≈2 nm, layer of SiN during the predeposition procedure. On these surfaces we found a significant increase of Qi for both high and low electric field regimes.

arXiv:1007.5096•Applied Physics Letters•Dec 6, 2010•189 citations

Tantalum Thin Films Sputtered on Silicon and on Different Seed Layers: Material Characterization and Coplanar Waveguide Resonator Performance

Moritz Singer, Benedikt Schoof, H. M. Gupta +3 more

Superconducting qubits are a promising platform for large-scale quantum computing. Besides the Josephson junction, most parts of a superconducting qubit are made of a planar, patterned superconducting thin films. In the past, most qubit architectures have relied on niobium (Nb) as the material of choice for the superconducting layer. However, there is also a variety of alternative materials with potentially less losses, which may thereby result in increased qubit performance. One such material is tantalum (Ta), for which high-performance qubit components have already been demonstrated. In this study, we report the sputter-deposition of Ta thin films directly on heated and unheated silicon (Si) substrates as well as onto different, nanometer-thin seed layers from tantalum nitride (TaN), titanium nitride (TiN) or aluminum nitride (AIN) that were deposited first. The thin films are characterized in terms of surface morphology, crystal structure, phase composition, critical temperature, residual resistance ratio (RRR) and RF-performance. We obtain thin films indicative of pure alpha-Ta for high temperature (600°C) sputtering directly on silicon and for Ta deposited on TaN or TiN seed layers. Coplanar waveguide (CPW) resonator measurements show that the Ta deposited directly on the heated silicon substrate performs best with internal quality factors Qi reaching 1xl06in the single-photon regime, measured at T=100 mK.

arXiv:2409.06041•IEEE International Conference on Quantum Computing and Engineering (QCE)•Sep 15, 2024•3 citations

Comparison of dielectric loss in titanium nitride and aluminum superconducting resonators

Alexander J. Melville, Greg Calusine, Wayne H. Woods +8 more

Lossy dielectrics are a significant source of decoherence in superconducting quantum circuits. In this report, we model and compare the dielectric loss in bulk and interfacial dielectrics in titanium nitride (TiN) and aluminum (Al) superconducting coplanar waveguide resonators. We fabricate isotropically trenched resonators to produce a series of device geometries that accentuate a specific dielectric region's contribution to the resonator quality factor. While each dielectric region contributes significantly to loss in TiN devices, the metal–air interface dominates the loss in the Al devices. Furthermore, we evaluate the quality factor of each TiN resonator geometry with and without a post-process hydrofluoric etch and find that it reduced losses from the substrate–air interface, thereby improving the quality factor.

arXiv:2007.07338•Applied Physics Letters•Sep 21, 2020•69 citations

High-Q superconducting microwave resonators using MBE titanium nitride

Anand Ithepalli, Hüseyin Ozan Ҫirkinoğlu, Eegene Clara Chung +9 more

Using molecular beam epitaxy, we have realized thin films of titanium nitride (TiN) on c-plane sapphire that exhibit the lowest observed full-width at half maximum X-ray rocking curve width of 18 arcsec. Though the (111) oriented TiN exhibits an abrupt and crystalline interface with sapphire, for the first time we observe sub-surface defects in the sapphire substrate, which nucleate structural defects in the epitaxial TiN layer. Using quarter-wavelength coplanar waveguide (CPW) resonators in a 3 \textmu m/6 \textmu m/3 \textmu m gap/strip/gap lines in a hanger geometry, we find the internal quality factor of the TiN resonators to be $>10^{6}$ in the single-photon $\langle n \rangle \sim 1$ limit at 5.8 GHz and 10 mK, rising to $>20 \times 10^{6}$ at $\langle n \rangle \sim 10^{6}$. The results are of high interest for applications of superconducting TiN in several areas, and provide a path towards epitaxial Josephson junctions with crystalline barriers in the future for high coherence qubits.

arXiv:2607.15230•Jul 16, 2026•0 citations
We report on the fabrication and characterization of superconducting coplanar waveguide (CPW) resonators based on titanium nitride (TiN) thin films deposited on 200,mm diameter high-resistivity Si(100) substrates. We systematically investigate how deposition conditions, dry-etch power and in-situ resist strip temperature affect morphology, superconducting properties and dielectric losses. By tuning reactive sputtering conditions, three distinct preferred out-of-plane crystal orientations - (111), (200), and a mix of both are achieved. Our results demonstrate that all films exhibit similar minimal two-level system (TLS) losses, with TiN111 exhibiting the lowest median TLS losses δ~TLS\tildeδ_\mathrm{TLS}δ~TLS​, and greater robustness against reoxidation. The applied structuring process, in contrast, has a far greater influence on the TLS loss than the crystal orientation of the TiN film and, consequently, the intrinsic material properties of the superconducting layer. The lowest TLS losses for all TiN depositions were achieved with a low power etch and low temperature resist strip. An additional buffered oxide etch (BOE) treatment could remove high-loss interfacial oxides at the metal-air (MA) and substrate-air (SA) interface and recover the etch-induced TLS losses. Consequently, TiN resonators exhibiting δ~TLS\tildeδ_\mathrm{TLS}δ~TLS​ values as low as 9.67×10−79.67 \times 10^{-7}9.67×10−7 were realized. The corresponding median low-power loss, δ~LP\tildeδ_\mathrm{LP}δ~LP​, amounts to 11.04×10−711.04 \times 10^{-7}11.04×10−7, which translates to an internal quality factor approaching one million. These findings highlight the critical role of process induced oxide formation at the MA and SA interfaces in limiting the performance of TiN resonators and provide a scalable, low-loss process compatible with industry-grade 200,mm CMOS qubit fabrication workflows.
We demonstrate a substantial reduction in two-level system loss in tantalum coplanar waveguide resonators fabricated on high-resistivity silicon substrates through the use of an ultrathin titanium sacrificial layer. A 0.2nm titanium film, deposited atop pre-sputtered α-tantalum, acts as a solid-state oxygen getter that chemically modifies the native Ta oxide at the metal-air interface. After device fabrication, the titanium layer is removed using buffered oxide etchant, leaving behind a chemically reduced Ta oxide surface. Subsequent high-vacuum annealing further suppresses two-level system loss. Resonators treated with this process exhibit internal quality factors Qi exceeding an average of 1.5 million in the single-photon regime across ten devices, over three times higher than otherwise identical devices lacking the titanium layer. These results highlight the critical role of interfacial oxide chemistry in superconducting loss and reinforce atomic-scale surface engineering as an effective approach to improving coherence in tantalum-based quantum circuits. The method is compatible with existing fabrication workflows applicable to tantalum films, offering a practical route to further extending T1 lifetimes in superconducting qubits.
In current superconducting qubit circuit development, coherence time is limited by low-frequency flux noise introduced from localized two-level systems (TLSs) in the fabricated superconducting circuit, including superconducting materials, the interface between thin films, and the substrate. As a part of the effect to tackle this issue from a substrate standpoint, we succeed in fabricating NbN (200) oriented coplanar waveguide resonator (CPWR) on a thin titanium nitride (TiN) (200) buffered Si (100) substrate. The internal loss is close to 3 × 10-5nearphoton> ~1, improved from ~2 × 10-4in NbN (200) CPWR fabricated on MgO (100). For NbN (200) resonators grown on Si (100), the internal loss shows microwave energy independent. To further clarity if this energy independence is due to the change of substrate material, we also fabricated TiN (200) CPWR on Si (100). In contrast to NbN (200) CPWR, the loss of TiN (200) resonator shows a strong microwave dependent, an indication of TLSs originated from the interface and the surface. We suggest TLSs in NbN (200) CPWR are dominated from different mechanism other than arising from the interface and surface.
Thin films of TiN were sputter-deposited onto Si and sapphire wafers with and without SiN buffer layers. The films were fabricated into rf coplanar waveguide resonators, and internal quality factor measurements were taken at millikelvin temperatures in both the many photon and single photon limits, i.e., high and low electric field regimes, respectively. At high field, we found the highest internal quality factors (∼107) were measured for TiN with predominantly a (200)-TiN orientation. The (200)-TiN is favored for growth at high temperature on either bare Si or SiN buffer layers. However, growth on bare sapphire or Si(100) at low temperature resulted in primarily a (111)-TiN orientation. Ellipsometry and Auger measurements indicate that the (200)-TiN growth on the bare Si substrates is correlated with the formation of a thin, ≈2 nm, layer of SiN during the predeposition procedure. On these surfaces we found a significant increase of Qi for both high and low electric field regimes.
Superconducting qubits are a promising platform for large-scale quantum computing. Besides the Josephson junction, most parts of a superconducting qubit are made of a planar, patterned superconducting thin films. In the past, most qubit architectures have relied on niobium (Nb) as the material of choice for the superconducting layer. However, there is also a variety of alternative materials with potentially less losses, which may thereby result in increased qubit performance. One such material is tantalum (Ta), for which high-performance qubit components have already been demonstrated. In this study, we report the sputter-deposition of Ta thin films directly on heated and unheated silicon (Si) substrates as well as onto different, nanometer-thin seed layers from tantalum nitride (TaN), titanium nitride (TiN) or aluminum nitride (AIN) that were deposited first. The thin films are characterized in terms of surface morphology, crystal structure, phase composition, critical temperature, residual resistance ratio (RRR) and RF-performance. We obtain thin films indicative of pure alpha-Ta for high temperature (600°C) sputtering directly on silicon and for Ta deposited on TaN or TiN seed layers. Coplanar waveguide (CPW) resonator measurements show that the Ta deposited directly on the heated silicon substrate performs best with internal quality factors Qi reaching 1xl06in the single-photon regime, measured at T=100 mK.
Lossy dielectrics are a significant source of decoherence in superconducting quantum circuits. In this report, we model and compare the dielectric loss in bulk and interfacial dielectrics in titanium nitride (TiN) and aluminum (Al) superconducting coplanar waveguide resonators. We fabricate isotropically trenched resonators to produce a series of device geometries that accentuate a specific dielectric region's contribution to the resonator quality factor. While each dielectric region contributes significantly to loss in TiN devices, the metal–air interface dominates the loss in the Al devices. Furthermore, we evaluate the quality factor of each TiN resonator geometry with and without a post-process hydrofluoric etch and find that it reduced losses from the substrate–air interface, thereby improving the quality factor.
Using molecular beam epitaxy, we have realized thin films of titanium nitride (TiN) on c-plane sapphire that exhibit the lowest observed full-width at half maximum X-ray rocking curve width of 18 arcsec. Though the (111) oriented TiN exhibits an abrupt and crystalline interface with sapphire, for the first time we observe sub-surface defects in the sapphire substrate, which nucleate structural defects in the epitaxial TiN layer. Using quarter-wavelength coplanar waveguide (CPW) resonators in a 3 \textmu m/6 \textmu m/3 \textmu m gap/strip/gap lines in a hanger geometry, we find the internal quality factor of the TiN resonators to be >106>10^{6}>106 in the single-photon ⟨n⟩∼1\langle n \rangle \sim 1⟨n⟩∼1 limit at 5.8 GHz and 10 mK, rising to >20×106>20 \times 10^{6}>20×106 at ⟨n⟩∼106\langle n \rangle \sim 10^{6}⟨n⟩∼106. The results are of high interest for applications of superconducting TiN in several areas, and provide a path towards epitaxial Josephson junctions with crystalline barriers in the future for high coherence qubits.