Abstract Dielectric losses are one of the key factors limiting the coherence of superconducting qubits. The impact of materials and fabrication steps on dielectric losses can be evaluated using coplanar waveguide (CPW) microwave resonators. Here, we report on superconducting CPW microwave resonators with internal quality factors systematically exceeding 5 × 106 at high powers and 2 × 106 (with the best value of 4.4 × 106) at low power. Such performance is demonstrated for 100-nm-thick aluminum resonators with 7–10.5 um center trace on high-resistivity silicon substrates commonly used in Josephson-junction based quantum circuit. We investigate internal quality factors of the resonators with both dry and wet aluminum etching, as well as deep and isotropic reactive ion etching of silicon substrate. Josephson junction compatible CPW resonators fabrication process with both airbridges and silicon substrate etching is proposed. Finally, we demonstrate the effect of airbridges’ positions and extra process steps on the overall dielectric losses. The best quality factors are obtained for the wet etched aluminum resonators and isotropically removed substrate with the proposed ultrasonic metal edge microcutting.
Material losses in superconducting circuits fundamentally limit qubit coherence times and resonator quality factors. Most research efforts focus on mitigating losses at circuit interfaces, including metal--substrate, substrate--air, and metal--air interfaces. However, the correlation between TLS and non-TLS losses with the intrinsic properties of the superconducting metal and the dielectric edge smoothness is not well studied. In this work, we link the aluminum film grain size to non-TLS losses and the dielectric trimming profile and roughness to TLS loss; both loss mechanisms are subsequently mitigated. To reduce metal-related losses, we engineer the aluminum microstructure by heating during deposition, increasing grain size and reducing grain boundary density. Beyond mitigating metal losses, we introduce a two-step etching technique, Tropic etching, to suppress dielectric TLS loss by producing an ultra-smooth silicon surface with minimal defects and redeposition. These results lay out the fabrication pathway for aluminum resonators with lower loss, demonstrating two-orders-of-magnitude improvement in quality factor from
6×104 to
2.3×106. Since aluminum is the basis for most high-coherence Josephson junctions and dielectric edges are inherent to all common device geometries, the improvements in aluminum microstructure and edge profiling, presented here, can enhance the performance of superconducting quantum devices.
Abstract Quantum bits (qubits) with long coherence times are an important element for the implementation of medium- and large-scale quantum computers. In the case of superconducting planar qubits, understanding and improving qubits’ quality can be achieved by studying superconducting planar resonators. In this paper, we fabricate and characterize coplanar waveguide resonators made from aluminum thin films deposited on silicon substrates. We perform three different substrate surface treatments prior to aluminum deposition: one chemical treatment based on a hydrofluoric acid clean; one physical treatment consisting of a thermal annealing at 880 °C in high vacuum; and one combined treatment comprising both the chemical and the physical treatments. The aim of these treatments is to remove the two-level state (TLS) defects hosted by the native oxides residing at the various samples’ interfaces. We first characterize the fabricated samples through cross-sectional tunneling electron microscopy, acquiring electron energy loss spectroscopy maps of the samples’ cross sections. These measurements show that both the chemical and the physical treatments almost entirely remove native silicon oxide from the substrate surface and that their combination results in the cleanest interface. Additionally, we analyze the effects of the various substrate treatments on the roughness of the silicon surface by means of atomic force microscopy surface morphology mapping. We then study the quality of the resonators by means of microwave measurements in the ‘quantum regime’, i.e., at a temperature T ∼ 10 mK and at a mean microwave photon number 〈 n ph 〉 ∼ 1 . In this regime, we find that both surface treatments independently improve the resonator’s intrinsic quality factor by ≈172%. The highest quality factor is obtained for the combined treatment, Q i ≈ 0.82 million, corresponding to an improvement by ≈256%. Finally, we find that the TLS quality factor averaged over a time period of 3 h is ∼3 million at 〈 n ph 〉 ∼ 10 , indicating that substrate surface engineering can potentially reduce the TLS loss below other losses such as quasiparticle loss and flux noise.