We have developed a combined photolithography and electron-beam lithography fabrication process for sub-\mum to \mum-size Nb/Al-AlOx/Nb Josephson junctions. In order to define the junction size and protect its top electrode during anodic oxidation, we developed and used the new concept of an aluminum hard mask. Josephson junctions of sizes down to 0.5 \mum2 have been fabricated and thoroughly characterized. We found that they have a very high quality, which is witnessed by the IV curves with quality parameters Vm > 50 mV and Vgap = 2.8 mV at 4.2 K, as well as IcRN products of 1.75-1.93 mV obtained at lower temperatures. In order to test the usability of our fabrication process for superconducting quantum bits, we have also designed, fabricated and experimentally investigated phase qubits made of these junctions. We found a relaxation time of T1 = 26 ns and a dephasing time of T2 = 21 ns.
We have developed a combined photolithography and electron-beam lithography fabrication process for sub-\mum to \mum-size Nb/Al-AlOx/Nb Josephson junctions. In order to define the junction size and protect its top electrode during anodic oxidation, we developed and used the new concept of an aluminum hard mask. Josephson junctions of sizes down to 0.5 \mum2 have been fabricated and thoroughly characterized. We found that they have a very high quality, which is witnessed by the IV curves with quality parameters Vm > 50 mV and Vgap = 2.8 mV at 4.2 K, as well as IcRN products of 1.75-1.93 mV obtained at lower temperatures. In order to test the usability of our fabrication process for superconducting quantum bits, we have also designed, fabricated and experimentally investigated phase qubits made of these junctions. We found a relaxation time of T1 = 26 ns and a dephasing time of T2 = 21 ns.
Nb/Al–AlO x /Nb tunnel junctions are often used in the studies of macroscopic quantum phenomena and superconducting qubit applications of the Josephson devices. In this work, we describe a convenient and reliable process using electron beam lithography for the fabrication of high-quality, submicron-sized Nb/Al–AlO x /Nb Josephson junctions. The technique follows the well-known selective Nb etching process and produces high-quality junctions with V m = 100 mV at 2.3 K for the typical critical current density of 2.2 kA/cm 2 , which can be adjusted by controlling the oxygen pressure and oxidation time during the formation of the tunnelling barrier. We present the results of the temperature dependence of the sub-gap current and in-plane magnetic-field dependence of the critical current, and compare them with the theoretical predictions.
Fabrication of sub-micron Josephson junctions is demonstrated using standard processing techniques for high-coherence, superconducting qubits. These junctions are made in two separate lithography steps with normal-angle evaporation. Most significantly, this work demonstrates that it is possible to achieve high coherence with junctions formed on aluminum surfaces cleaned in situ with Ar milling before the junction oxidation. This method eliminates the angle-dependent shadow masks typically used for small junctions. Therefore, this is conducive to the implementation of typical methods for improving margins and yield using conventional CMOS processing. The current method uses electron-beam lithography and an additive process to define the top and bottom electrodes. Extension of this work to optical lithography and subtractive processes is discussed.
For enhancing operating speed of a superconducting integrated circuit (IC), the device size must be reduced into the submicron level. For this purpose, we have introduced electron beam (EB) direct writing technique into the fabrication process of a Nb/AlOx/Nb Josephson IC. A two-layer (PMMA/(alpha) M-CMS) resist method called the portable conformable mask (PCM) method was utilized for having a high aspect ratio. The electron cyclotron resonance (ECR) plasma etching technique was utilized. We have fabricated micron or submicron-size Nb/AlOx/Nb Josephson junctions, where the size of the junction was varied from 2 micrometer to 0.5 micrometer at 0.1 micrometer intervals. These junctions were designed for evaluating the spread of the junction critical current. We achieved minimum-to-maximum Ic spread of plus or minus 13% for 0.81-micrometer-square (plus or minus 16% for 0.67-micrometer-square) 100 junctions spreading in 130- micrometer-square area. The size deviation of 0.05 micrometer was estimated from the spread values. We have successfully demonstrated a small-scale logic IC with 0.9-micrometer-square junctions having a 50 4JL OR-gate chain, where 4JL means four junctions logic family. The circuit was designed for measuring the gate delay. We obtained a preliminary result of the OR- gate logic delay, where the minimum delay was 8.6 ps/gate.
Fabrication And Characterization Of High-Quality Nb/Al-AlOx/Nb Cross-Type Josephson Tunnel Junctions Utilising CMP-based Planarisation Techniques
Josephson tunnel junctions (JJs) are the fundamental building blocks of today's most advanced superconducting electronic components, such as qubits and superconducting quantum interference devices (SQUIDs). Given the ongoing demand for scalability of these devices on the wafer-scale, it is crucial to control the fabrication process as precisely as possible to ensure uniform quality and reproducibility. Today, window-type JJs are often used in the production of DC SQUIDs and while they are reliable and reproducible, they suffer from alignment inaccuracies caused by photolithography and unavoidable parasitic capacitances, thus limiting the energy sensitivity of DC SQUIDs. These problems can be circumvented by producing JJs with cross-type geometry, which allows for smaller junction areas and eliminates parasitic capacitances. Here we discuss the fabrication of Nb/Al-AlOx/Nb-based cross-type JJs, where the trilayer is embedded in sputter-deposited SiO2 to allow for planarisation of the structures and to ensure the reliable insulation of the sidewalls of the bottom electrode. Instead of lift-off processes that require a lot of time and potentially leave unwanted wings along the edges of microstructures behind that might compromise subsequent layers, we use chemical-mechanical polishing (CMP) for the removal of excess SiO2. This is not only much faster, but produces smooth and uniform surfaces, which in turn effectively improves the reliability of our JJ production process resulting in a high yield of over 90% on wafer-scale. In addition, we discuss the influence of fabrication details on the quality and electrical properties of our JJs with different junction areas down to 1μm×1μm distributed across the wafer and extract the junction specific quality parameters from their IV-characteristics and their Fraunhofer patterns.
As one of the candidates for realizing quantum bits, superconducting quantum bits, based on Josephson junction, have the advantages of easy integrating, coupling with the outside environment and so on. Double-layer photoresist was used to prepare suspended shadow mask by deep ultra-violet (DUV) lithography. We fabricated the sample of superconducting flux quantum bits by electron beam evaporation and static oxidization with aluminum as superconducting material. According to the dependence of the flatness on the thickness of aluminum film, we select 60 nm as the thickness of the bottom electrode of tunnel junction. By increasing the distance between the evaporation source and the substrate, we have improved the smoothness of film and thus reduced the leakage current of tunnel junction. The tri-layer structure of aluminum tunnel junction was observed by transmission electron microscopy (TEM), and the relationship between the thickness of barrier layer and the oxidation pressure was obtained.
Sub-μm Josephson Junctions for Superconducting Quantum Devices
For high-performance superconducting quantum devices based on Josephson junctions (JJs), decreasing lateral sizes is of great importance. Fabrication of sub-μm JJs is challenging, due to nonflat surfaces with step heights of up to several 100 nm generated during the fabrication process. We have refined a fabrication process with significantly decreased film thicknesses, resulting in almost flat surfaces at intermediate steps during the JJ definition. In combination with a mix-and-match process, combining electron-beam lithography and conventional photolithography, we can fabricate JJs with lateral dimensions down to 0.023 μm2. We propose this refined process as an alternative to the commonly used chemical-mechanical polishing procedure. Transport measurements of JJs, having critical-current densities ranging from 50 to 104A/cm2, are presented at 4.2 K. Our JJ process yields excellent quality parameters, Rsg/RNup to ~ 50, Vmfrom 15 to 80 mV and Vgapup to 2.81 mV, and also allows the fabrication of high-quality, sub-μm wide, long JJs (LJJs) for the study of Josephson vortex behavior. The developed technique can also be used for similar multilayer processes and is very promising for fabricating sub- μm JJs for quantum devices such as SQUIDs, qubits, and SIS mixers.