times 2 to 5 times longer than baseline niobium qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 200 microseconds. Our comparative structural and chemical analysis suggests that amorphous niobium oxides may induce higher losses compared to other amorphous oxides. These results are in line with high-accuracy measurements of the niobium oxide loss tangent obtained with ultra-high Q superconducting radiofrequency (SRF) cavities. This new surface encapsulation strategy enables even further reduction of dielectric losses via passivation with ambient-stable materials, while preserving fabrication and scalable manufacturability thanks to the compatibility with silicon processes.
times 2 to 5 times longer than baseline niobium qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 200 microseconds. Our comparative structural and chemical analysis suggests that amorphous niobium oxides may induce higher losses compared to other amorphous oxides. These results are in line with high-accuracy measurements of the niobium oxide loss tangent obtained with ultra-high Q superconducting radiofrequency (SRF) cavities. This new surface encapsulation strategy enables even further reduction of dielectric losses via passivation with ambient-stable materials, while preserving fabrication and scalable manufacturability thanks to the compatibility with silicon processes.
times 2 to 5 times longer than baseline niobium qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 200 microseconds. Our comparative structural and chemical analysis suggests that amorphous niobium oxides may induce higher losses compared to other amorphous oxides. These results are in line with high-accuracy measurements of the niobium oxide loss tangent obtained with ultra-high Q superconducting radiofrequency (SRF) cavities. This new surface encapsulation strategy enables even further reduction of dielectric losses via passivation with ambient-stable materials, while preserving fabrication and scalable manufacturability thanks to the compatibility with silicon processes.
Superconducting coplanar waveguide resonators are essential components in quantum processors, where their internal quality factor (Qi) constrains qubit coherence and readout fidelity. In niobium devices, microwave losses at millikelvin temperatures are strongly influenced by two-level systems (TLS) associated with the complex NbOx surface oxide. To mitigate these losses, we investigate a surface-engineering approach in which Nb films are capped in situ with a thin tantalum layer to suppress Nb2O5 formation and replace the native NbOx interface with a Ta-based oxide.
We fabricate Nb/Ta bilayer and reference Nb resonators on high-resistivity silicon using identical DC sputtering and wet etching conditions, and characterize their performance at millikelvin temperatures. Fresh Ta-encapsulated devices exhibit internal quality factors up to 2.4 x 10^6 in the near-single-photon regime, with power dependence consistent with reduced TLS-related loss at the metal-air interface. A control Nb device fabricated under the same process shows comparatively lower Q_TLS, consistent with the beneficial effect of the Ta capping layer. Furthermore, ageing tests performed on Nb/Ta resonators after six months reveal a moderate reduction in Q_TLS relative to their initial values, yet the performance remains superior to newly fabricated Nb-only devices. These results suggest that thin Ta encapsulation enhances interface quality and contributes to improved temporal stability while remaining compatible with Nb-based fabrication workflows.
Abstract We present a transmon qubit fabrication technique that yields systematic improvements in T 1 relaxation times. We encapsulate the surface of niobium and prevent the formation of its lossy surface oxide. By maintaining the same superconducting metal and only varying the surface, this comparative investigation examining different capping materials, such as tantalum, aluminum, titanium nitride, and gold, as well as substrates across different qubit foundries demonstrates the detrimental impact that niobium oxides have on coherence times of superconducting qubits, compared to native oxides of tantalum, aluminum or titanium nitride. Our surface-encapsulated niobium qubit devices exhibit T 1 relaxation times 2–5 times longer than baseline qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 300 μs, with maximum values up to 600 μs. Our comparative structural and chemical analysis provides insight into why amorphous niobium oxides may induce higher losses compared to other amorphous oxides.
Improving qubit lifetime is essential for fault-tolerant quantum computing. It is widely acknowledged that intricate processing techniques introduce defects at the interfaces and surfaces of superconducting quantum circuits, which can create sources of decoherence. Therefore, a precise understanding of how a material's structure contributes to decoherence is critical for enhancing the performance of superconducting qubits. This talk highlights our recent advancements in understanding surface oxides in resonators and ultrathin aluminum oxide barriers in Josephson junctions (JJs) using transmission electron microscopy and spectroscopy techniques [1-4]. The Superconducting Quantum Materials & Systems Center (SQMS) demonstrated that encapsulating niobium surfaces with a ∼10nm tantalum layer results in 2-5x longer T1 than bare niobium [2]. Our collaborative investigation shows that this improvement is attributed to tantalum's less lossy surface oxide, which contains fewer sub-oxides than niobium oxide. Moreover, the amorphous Ta2O5 shows a bonding nature closer to crystalline form than amorphous Nb2O5, potentially reducing hydrogen diffusion toward the oxide/metal interface [1, 2]. Moreover, we will briefly discuss our preliminary study of the thin film structure under cryogenic conditions down to 20K, conducted using a liquid helium TEM holder in a Thermo Cs-corrected Titan. We also explored the effect of aluminum deposition rates on aluminum oxide microstructure and qubit lifetime. Although increasing the deposition rate from 0.5 Å/s to 5 Å/s significantly improved oxide layer roughness and thickness variation, the qubits’ coherence remained unchanged. This is likely due to Cooper pairs only tunneling through the thinnest parts of the barrier, making them less affected by the grain boundaries in the thin aluminum films. Additionally, we uncovered a stress-induced grain boundary sliding mechanism, which contributes to short-circuit failures in JJs [4]. Our discovery provides vital insight into oxide microstructure and superconducting qubits’ functionality [5].
The presence of amorphous oxide layers can significantly affect the coherent time of superconducting qubits due to their high dielectric loss. Typically, the surface oxides of superconductor films exhibit lossy and unstable behavior when exposed to air. To increase the coherence time, it is essential for qubits to have stable and low dielectric loss oxides, either as barrier or passivation layers. In this study, we highlight the robust and stable nature of an amorphous tantalum oxide layer formed on α-Ta (110) film by employing chemical and structural analyses. Such kind of oxide layer forms in a self-limiting process on the surface of α-Ta (110) film in piranha solution, yielding stable thickness and steady chemical composition. Quarter-wavelength coplanar waveguide resonators are made to study the loss of this oxide. One resonator has a Qi of 3.0 × 106 in the single photon region. The Qi of most devices are higher than 2.0 × 106. Moreover, most of them are still over 1 × 106 even after exposed to air for months. Based on these findings, we propose an all-tantalum superconducting qubit utilizing such oxide as passivation layers, which possess low dielectric loss and improved stability.
The lifetime of superconducting qubits is limited by dielectric loss, and a major source of dielectric loss is the native oxide present at the surface of the superconducting metal. Specifically, tantalum-based superconducting qubits have been demonstrated with record lifetimes, but a major source of loss is the presence of two-level systems in the surface tantalum oxide. Here, we demonstrate a strategy for avoiding oxide formation by encapsulating the tantalum with noble metals that do not form native oxide. By depositing a few nanometers of Au or AuPd alloy before breaking vacuum, we completely suppress tantalum oxide formation. Microwave loss measurements of superconducting resonators reveal that the noble metal is proximitized, with a superconducting gap over 80% of the bare tantalum at thicknesses where the oxide is fully suppressed. Our findings suggest that losses in resonators fabricated by subtractive etching are dominated by oxides on the sidewalls, pointing to total surface encapsulation by additive fabrication as a promising strategy for eliminating surface oxide two-level system loss in superconducting qubits.