Applied Physics Letters

Tantalum microwave resonators with ultra-high intrinsic quality factors

Lili Shi, Tingting Guo, Runfeng Su, Tianyuan Chi, Yifan Sheng, Junliang Jiang, Chunhai Cao, Jingbo Wu, Xuecou Tu, Guozhu Sun, Jian Chen, Peiheng Wu

Published Dec 12, 2022• 25 citations
Publisher

Abstract

We acquire tantalum thin film in its α phase (α-Ta) using direct-current magnetron sputtering. According to x-ray diffraction results, 110-Ta is dominant. Quarter-wavelength coplanar waveguide resonators are fabricated with the α-Ta film and characterized at millikelvin in a dilution refrigerator. In the single photon regime, an intrinsic quality factor (Qi) up to 3×106 is obtained in these resonators. At high power, Qi rises to 6×106. Moreover, we also fabricate an array with 7 × 7 lumped element resonators using the α-Ta film. The array shows excellent uniformity. At high power, Qis of all pixels exceed 1×106. In the single photon regime, Qis of over 90% pixels exceed 1×106. Superconducting quantum computing and ultrasensitive electromagnetic wave detectors will benefit a lot from devices based on the α-Ta film.

DOI
10.1063/5.0124821

Related papers

Investigation of the deposition of α-tantalum (110) films on a-plane sapphire substrate by molecular beam epitaxy for superconducting circuit

Haolin Jia, Boyi Zhou, Tao Wang +7 more

Polycrystalline α-tantalum (110) films deposited on the c-plane sapphire substrate by sputtering are used in superconducting qubits nowadays. However, these films always occasionally form other structures, such as α-tantalum (111) grains and β-tantalum grains. To improve the film quality, we investigate the growth of α-tantalum (110) films on the a-plane sapphire substrate under varying conditions by molecular beam epitaxy technology. The optimized α-tantalum (110) film is a single crystal, with a smooth surface and atomically flat metal–substrate interface. The film with thickness of 30 nm shows a Tc of 4.12 K and a high residual resistance ratio of 9.53. The quarter wavelength coplanar waveguide resonators fabricated with the 150 nm optimized α-tantalum (110) film exhibit intrinsic quality factor of over one million under single photon excitation at millikelvin temperature.

arXiv:2306.09566•Journal of Vacuum Science & Technology B Nanotechnology and Microelectronics Materials Processing Measurement and Phenomena•Sep 1, 2023•14 citations

Tantalum Thin Films Sputtered on Silicon and on Different Seed Layers: Material Characterization and Coplanar Waveguide Resonator Performance

Moritz Singer, Benedikt Schoof, H. M. Gupta +3 more

Superconducting qubits are a promising platform for large-scale quantum computing. Besides the Josephson junction, most parts of a superconducting qubit are made of a planar, patterned superconducting thin films. In the past, most qubit architectures have relied on niobium (Nb) as the material of choice for the superconducting layer. However, there is also a variety of alternative materials with potentially less losses, which may thereby result in increased qubit performance. One such material is tantalum (Ta), for which high-performance qubit components have already been demonstrated. In this study, we report the sputter-deposition of Ta thin films directly on heated and unheated silicon (Si) substrates as well as onto different, nanometer-thin seed layers from tantalum nitride (TaN), titanium nitride (TiN) or aluminum nitride (AIN) that were deposited first. The thin films are characterized in terms of surface morphology, crystal structure, phase composition, critical temperature, residual resistance ratio (RRR) and RF-performance. We obtain thin films indicative of pure alpha-Ta for high temperature (600°C) sputtering directly on silicon and for Ta deposited on TaN or TiN seed layers. Coplanar waveguide (CPW) resonator measurements show that the Ta deposited directly on the heated silicon substrate performs best with internal quality factors Qi reaching 1xl06in the single-photon regime, measured at T=100 mK.

arXiv:2409.06041•IEEE International Conference on Quantum Computing and Engineering (QCE)•Sep 15, 2024•3 citations

Tantalum-Encapsulated Niobium Superconducting Resonators: High Internal Quality Factor and Improved Temporal Stability via Surface Passivation

Anas Alkhazaleh, Juan Villegas, Florent Ravaux +1 more

Superconducting coplanar waveguide resonators are essential components in quantum processors, where their internal quality factor (Qi) constrains qubit coherence and readout fidelity. In niobium devices, microwave losses at millikelvin temperatures are strongly influenced by two-level systems (TLS) associated with the complex NbOx surface oxide. To mitigate these losses, we investigate a surface-engineering approach in which Nb films are capped in situ with a thin tantalum layer to suppress Nb2O5 formation and replace the native NbOx interface with a Ta-based oxide. We fabricate Nb/Ta bilayer and reference Nb resonators on high-resistivity silicon using identical DC sputtering and wet etching conditions, and characterize their performance at millikelvin temperatures. Fresh Ta-encapsulated devices exhibit internal quality factors up to 2.4 x 10^6 in the near-single-photon regime, with power dependence consistent with reduced TLS-related loss at the metal-air interface. A control Nb device fabricated under the same process shows comparatively lower Q_TLS, consistent with the beneficial effect of the Ta capping layer. Furthermore, ageing tests performed on Nb/Ta resonators after six months reveal a moderate reduction in Q_TLS relative to their initial values, yet the performance remains superior to newly fabricated Nb-only devices. These results suggest that thin Ta encapsulation enhances interface quality and contributes to improved temporal stability while remaining compatible with Nb-based fabrication workflows.

quant-pharXiv:2604.09050•Apr 13, 2026•0 citations

Engineering high-Q superconducting tantalum microwave coplanar waveguide resonators for compact coherent quantum circuits

Shima Poorgholam-Khanjari, Valentino Seferai, Paniz Foshat +5 more

Tantalum (Ta) has recently received considerable attention in manufacturing robust superconducting quantum circuits. Ta offers low microwave loss, high kinetic inductance compared to aluminium (Al) and niobium (Nb), and good compatibility with complementary metal-oxide-semiconductor (CMOS) technology, which is essential for quantum computing applications. Here, we demonstrate the fabrication engineering of thickness-dependent high quality factor (high-Q_i) Ta superconducting microwave coplanar waveguide resonators. All films are deposited on high-resistivity silicon substrates at room temperature without additional substrate heating. Before Ta deposition, a niobium (Nb) seed layer is used to ensure a body-centred cubic lattice (α-Ta) formation. We further engineer the kinetic inductance (L_K) resonators by varying Ta film thicknesses. High L_K is a key advantage for applications because it facilitates the realisation of high-impedance, compact quantum circuits with enhanced coupling to qubits. The maximum internal quality factor Q_i of ~ 3.6 * 10^6 is achieved at the high power regime for 100 nm Ta, while the highest kinetic inductance is obtained to be 0.6 pH/sq for the thinnest film, which is 40 nm. This combination of high Q_i and high L_K highlights the potential of Ta microwave circuits for high-fidelity operations of compact quantum circuits.

arXiv:2412.16099•Dec 20, 2024•0 citations

Krypton-sputtered tantalum films for scalable high-performance quantum devices

Maciej W. Olszewski

Superconducting qubits and microwave resonators based on tantalum thin films have recently demonstrated large increases in performance. This makes Ta an at- tractive material for superconducting quantum computing applications, but, so far, direct deposition has largely relied on high substrate temperatures exceeding 400 ◦C to achieve the cubic (BCC) phase of tantalum. Here, we show that changing the sputter gas from argon to krypton promotes synthesis of very high crystallinity BCC tantalum films on silicon at temperatures as low as 200 ◦C. This provides a wide process window compatible with back-end-of-the-line fabrication standards. The microwave performance of coplanar waveguide resonators fabricated from krypton-sputtered films shows a tight performance distribution at the state of the art. Higher temperature-grown films exhibit higher losses, in correlation with the degree of tantalum/silicon intermixing. Finally, with these films, we demonstrate transmon qubits with a relatively compact, 20 μm capacitor gap, achieving a time-averaged quality factor up to 16.9 million.

•Nov 19, 2025•1 citation

Microwave characterization of tantalum superconducting resonators on silicon substrate with niobium buffer layer

Yoshiro Urade, Kay Yakushiji, Manabu Tsujimoto +4 more

Tantalum thin films sputtered on unheated silicon substrates are characterized with microwaves at around 10 GHz in a 10 mK environment. We show that the phase of tantalum with a body-centered cubic lattice (α-Ta) can be grown selectively by depositing a niobium buffer layer prior to a tantalum film. The physical properties of the films, such as superconducting transition temperature and crystallinity, change markedly with the addition of the buffer layer. Coplanar waveguide resonators based on the composite film exhibit significantly enhanced internal quality factors compared with a film without the buffer layer. The internal quality factor approaches 2 × 107 at a large-photon-number limit. While the quality factor decreases at the single-photon level owing to two-level system (TLS) loss, we have deduced that one of the causes of TLS loss is the amorphous silicon layer at the film–substrate interface, which originates from the substrate cleaning before the film deposition rather than the film itself. The temperature dependence of the internal quality factors shows a marked rise below 200 mK, suggesting the presence of TLS–TLS interactions. The present low-loss tantalum films can be deposited without substrate heating and thus have various potential applications in superconducting quantum electronics.

arXiv:2306.15258•APL Materials•Feb 1, 2024•20 citations
We acquire tantalum thin film in its α phase (α-Ta) using direct-current magnetron sputtering. According to x-ray diffraction results, 110-Ta is dominant. Quarter-wavelength coplanar waveguide resonators are fabricated with the α-Ta film and characterized at millikelvin in a dilution refrigerator. In the single photon regime, an intrinsic quality factor (Qi) up to 3×106 is obtained in these resonators. At high power, Qi rises to 6×106. Moreover, we also fabricate an array with 7 × 7 lumped element resonators using the α-Ta film. The array shows excellent uniformity. At high power, Qis of all pixels exceed 1×106. In the single photon regime, Qis of over 90% pixels exceed 1×106. Superconducting quantum computing and ultrasensitive electromagnetic wave detectors will benefit a lot from devices based on the α-Ta film.
Polycrystalline α-tantalum (110) films deposited on the c-plane sapphire substrate by sputtering are used in superconducting qubits nowadays. However, these films always occasionally form other structures, such as α-tantalum (111) grains and β-tantalum grains. To improve the film quality, we investigate the growth of α-tantalum (110) films on the a-plane sapphire substrate under varying conditions by molecular beam epitaxy technology. The optimized α-tantalum (110) film is a single crystal, with a smooth surface and atomically flat metal–substrate interface. The film with thickness of 30 nm shows a Tc of 4.12 K and a high residual resistance ratio of 9.53. The quarter wavelength coplanar waveguide resonators fabricated with the 150 nm optimized α-tantalum (110) film exhibit intrinsic quality factor of over one million under single photon excitation at millikelvin temperature.
Superconducting qubits are a promising platform for large-scale quantum computing. Besides the Josephson junction, most parts of a superconducting qubit are made of a planar, patterned superconducting thin films. In the past, most qubit architectures have relied on niobium (Nb) as the material of choice for the superconducting layer. However, there is also a variety of alternative materials with potentially less losses, which may thereby result in increased qubit performance. One such material is tantalum (Ta), for which high-performance qubit components have already been demonstrated. In this study, we report the sputter-deposition of Ta thin films directly on heated and unheated silicon (Si) substrates as well as onto different, nanometer-thin seed layers from tantalum nitride (TaN), titanium nitride (TiN) or aluminum nitride (AIN) that were deposited first. The thin films are characterized in terms of surface morphology, crystal structure, phase composition, critical temperature, residual resistance ratio (RRR) and RF-performance. We obtain thin films indicative of pure alpha-Ta for high temperature (600°C) sputtering directly on silicon and for Ta deposited on TaN or TiN seed layers. Coplanar waveguide (CPW) resonator measurements show that the Ta deposited directly on the heated silicon substrate performs best with internal quality factors Qi reaching 1xl06in the single-photon regime, measured at T=100 mK.
Superconducting coplanar waveguide resonators are essential components in quantum processors, where their internal quality factor (Qi) constrains qubit coherence and readout fidelity. In niobium devices, microwave losses at millikelvin temperatures are strongly influenced by two-level systems (TLS) associated with the complex NbOx surface oxide. To mitigate these losses, we investigate a surface-engineering approach in which Nb films are capped in situ with a thin tantalum layer to suppress Nb2O5 formation and replace the native NbOx interface with a Ta-based oxide. We fabricate Nb/Ta bilayer and reference Nb resonators on high-resistivity silicon using identical DC sputtering and wet etching conditions, and characterize their performance at millikelvin temperatures. Fresh Ta-encapsulated devices exhibit internal quality factors up to 2.4 x 10^6 in the near-single-photon regime, with power dependence consistent with reduced TLS-related loss at the metal-air interface. A control Nb device fabricated under the same process shows comparatively lower Q_TLS, consistent with the beneficial effect of the Ta capping layer. Furthermore, ageing tests performed on Nb/Ta resonators after six months reveal a moderate reduction in Q_TLS relative to their initial values, yet the performance remains superior to newly fabricated Nb-only devices. These results suggest that thin Ta encapsulation enhances interface quality and contributes to improved temporal stability while remaining compatible with Nb-based fabrication workflows.
Tantalum (Ta) has recently received considerable attention in manufacturing robust superconducting quantum circuits. Ta offers low microwave loss, high kinetic inductance compared to aluminium (Al) and niobium (Nb), and good compatibility with complementary metal-oxide-semiconductor (CMOS) technology, which is essential for quantum computing applications. Here, we demonstrate the fabrication engineering of thickness-dependent high quality factor (high-Q_i) Ta superconducting microwave coplanar waveguide resonators. All films are deposited on high-resistivity silicon substrates at room temperature without additional substrate heating. Before Ta deposition, a niobium (Nb) seed layer is used to ensure a body-centred cubic lattice (α-Ta) formation. We further engineer the kinetic inductance (L_K) resonators by varying Ta film thicknesses. High L_K is a key advantage for applications because it facilitates the realisation of high-impedance, compact quantum circuits with enhanced coupling to qubits. The maximum internal quality factor Q_i of ~ 3.6 * 10^6 is achieved at the high power regime for 100 nm Ta, while the highest kinetic inductance is obtained to be 0.6 pH/sq for the thinnest film, which is 40 nm. This combination of high Q_i and high L_K highlights the potential of Ta microwave circuits for high-fidelity operations of compact quantum circuits.
Superconducting qubits and microwave resonators based on tantalum thin films have recently demonstrated large increases in performance. This makes Ta an at- tractive material for superconducting quantum computing applications, but, so far, direct deposition has largely relied on high substrate temperatures exceeding 400 ◦C to achieve the cubic (BCC) phase of tantalum. Here, we show that changing the sputter gas from argon to krypton promotes synthesis of very high crystallinity BCC tantalum films on silicon at temperatures as low as 200 ◦C. This provides a wide process window compatible with back-end-of-the-line fabrication standards. The microwave performance of coplanar waveguide resonators fabricated from krypton-sputtered films shows a tight performance distribution at the state of the art. Higher temperature-grown films exhibit higher losses, in correlation with the degree of tantalum/silicon intermixing. Finally, with these films, we demonstrate transmon qubits with a relatively compact, 20 μm capacitor gap, achieving a time-averaged quality factor up to 16.9 million.
Tantalum thin films sputtered on unheated silicon substrates are characterized with microwaves at around 10 GHz in a 10 mK environment. We show that the phase of tantalum with a body-centered cubic lattice (α-Ta) can be grown selectively by depositing a niobium buffer layer prior to a tantalum film. The physical properties of the films, such as superconducting transition temperature and crystallinity, change markedly with the addition of the buffer layer. Coplanar waveguide resonators based on the composite film exhibit significantly enhanced internal quality factors compared with a film without the buffer layer. The internal quality factor approaches 2 × 107 at a large-photon-number limit. While the quality factor decreases at the single-photon level owing to two-level system (TLS) loss, we have deduced that one of the causes of TLS loss is the amorphous silicon layer at the film–substrate interface, which originates from the substrate cleaning before the film deposition rather than the film itself. The temperature dependence of the internal quality factors shows a marked rise below 200 mK, suggesting the presence of TLS–TLS interactions. The present low-loss tantalum films can be deposited without substrate heating and thus have various potential applications in superconducting quantum electronics.