Bright Telecom Spin-Photon Interface in Silicon Photonics

Carolina Crosta, Amirehsan Alizadehherfati, Purbita Purkayastha, Kyu-Young Kim, Jasvith Raj Basani, Chang-Min Lee, Fabio Pezzoli, Edo Waks

quant-phphysics.opticsSubmitted Jul 20, 2026• Announced Jul 22, 2026• Revised Jul 27, 2026 (v2)
v1 · Jul 20, 2026v2 · Jul 27, 2026
arXivHTMLPDF

Abstract

Silicon is an attractive host for scalable quantum photonics, but the absence of bright telecom-band emitters with optically addressable spin states has limited its use for spin-photon interfaces. Here we demonstrate the Al1-center, an aluminum--carbon defect in silicon, as a bright waveguide-integrated single-photon emitter with a ground-state spin. Using isotopically purified silicon-on-insulator nanophotonic devices, we isolate individual Al1-centers and observe high-purity single-photon emission with $g^{(2)}(0)=0.04$ without background subtraction. Time-resolved photoluminescence spectroscopy reveals a fast excited-state lifetime of 135 ns, nearly an order of magnitude shorter than the benchmark provided by the well-studied T-center. Resonant photoluminescence excitation measurements further resolve the zero-phonon transition and reveal a narrow homogeneous linewidth reaching 47 MHz, threefold narrower than the T-center under comparable temperature. Through magneto-optical spectroscopy, we resolve the spin-dependent transitions of the bound-exciton manifold and achieve spin-selective optical pumping, fulfilling the prerequisite for quantum state initialization and readout. These results establish the Al1-center as a bright telecom-band spin-photon interface in silicon photonics and introduce a promising platform for integrated quantum networks.

Related papers

Optical spin readout of a silicon color center in the telecom L-band

Shuyu Wen, Gregor Pieplow, Junchun Yang +6 more

Silicon-based quantum technologies have gained increasing attention due to their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While several optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band-a key wavelength range for low-loss fiber-based communication-has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance, enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.

arXiv:2502.07632•Feb 11, 2025•2 citations

L-band single-photon generation from a cavity-coupled silicon C-center

Carolina Crosta, Kyu-Young Kim, Purbita Purkayastha +7 more

Monolithic integration of single-photon sources into silicon photonics offers a compelling solution for realizing scalable quantum telecommunication architectures. Among the candidate silicon color centers, the C-center features a zero-phonon emission in the telecom L-band, corresponding to the spectral window of minimum transmission loss in optical fibers. Despite this advantage, isolating single C-centers has remained an unrealized challenge in solid-state quantum optics. In this work, we report the isolation of a single silicon C-center. We enhance the spontaneous emission rate of the zero-phonon line by coupling the single emitter to a nanophotonic crystal cavity, observing a fivefold reduction in the excited-state lifetime compared to bulk conditions, which corresponds to a Purcell factor lower bound of 33. Second-order autocorrelation measurements confirm single-photon emission from the investigated defect, obtaining an optical purity of $g^{(2)}(0) = 0.23$ without background correction. Our results establish a native telecom L-band quantum light source in silicon, laying the foundation for ultra-low-loss and long-distance quantum applications.

quant-pharXiv:2609.37244•Sep 30, 2026•0 citations

Optical spin readout of a silicon color center in the telecom L-band

Yonder Berencén, Shuyu Wen, Gregor Pieplow +6 more

Abstract Optically active spin systems in silicon are attracting growing interest for quantum technologies, driven by their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces, which allow coupling between spin degrees of freedom and photons are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While a variety of optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band (1565–1625 nm)—a key wavelength range for low-loss fiber-based communication—has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance (ODMR), enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.

•Mar 31, 2025•0 citations

Inverse-Designed Nanobeam Cavities for High-Cooperativity Spin-Photon Interfaces in Silicon

Nail Letty, Md Sakibul Islam, Wayesh Qarony

Telecom-band spin defects in silicon offer a compelling platform for integrated quantum networks by combining scalable silicon photonics with spin-based quantum memories and multiqubit registers. The T center and recently demonstrated Al1 center are particularly promising, but their limited coherent zero-phonon emission requires strong cavity enhancement for efficient spin-photon interfaces. Here, we inverse-design silicon nanobeam cavities for both centers using a unified adjoint-optimization framework targeting Purcell enhancement, resonance alignment, and photon extraction. For each emitter, symmetric cavities maximize Purcell enhancement, while asymmetric cavities provide directional coupling to an integrated waveguide. Three-dimensional finite-difference time-domain simulations yield loaded quality factors up to 3.25 x 10^6, Purcell factors up to 1.43 x 10^5, and cooperativities of approximately 280-5000, corresponding to cavity-coupled emission fractions exceeding 99.6%. The asymmetric cavities direct approximately 90% of emitted power into a single on-chip waveguide while maintaining cooperativity above 280. Under nanometer-scale fabrication perturbations, all four designs remain within the high-cooperativity regime, and high cooperativity persists when the cavity quality factor is constrained to a realistic absorption-limited value of 10^5. This unified, fabrication-compatible framework establishes a scalable cavity-design route for silicon telecom spin-photon interfaces and, to our knowledge, the first cavity designs for the Al1 center.

quant-pharXiv:2609.32205•Sep 29, 2026

Optically Resolved Excited State Hyperfine Structure of a Silicon Colour Centre in the Telecom Bands

Austin Woolverton, Nicholas Brunelle, Mehdi Keshavarz +8 more

Nuclear spin qubits in silicon offer exceptionally coherent quantum memory, and optically-interfaced spins are a promising platform for both quantum networking and distributed quantum computing. It has been proposed that emitters with diamagnetic ground states may permit an optical interface to nuclear spin memories via metastable, hyperfine-coupled excited states while suppressing key sources of decoherence. Until now, direct optical observation of suitable transitions in silicon colour centres has remained elusive. Here we characterize the singly-ionized interstitial aluminum donor (Al$_\mathrm{i}^+$) in isotopically purified $^{28}$Si and find several novel features of this little-studied defect. We measure bright emission and strong optical transitions and, in contrast to previous studies of this centre, attribute its emission to an exchange-split spin triplet and singlet level of the lowest-energy 1s:T$_2$ excited state. We measure the excited-state lifetimes and, as a consequence of its narrow emission linewidth, observe the fine and hyperfine structure of the long-lived triplet state. This constitutes the first measurement of an optically-resolved hyperfine structure in the excited state of a telecommunications-band silicon colour centre.

quant-pharXiv:2607.28943•Aug 3, 2026

Epitaxial single T centres in silicon-on-insulator

Christian H. Christiansen, Kasper H. Nielsen, Alisha Nanwani +26 more

Spin-photon interfaces based on silicon quantum emitters offer a scalable platform for quantum computing and networking. However, achieving coherent photon emission remains a primary challenge due to stringent material quality requirements. To overcome this, we utilise high-purity molecular-beam epitaxy (MBE) to epitaxially incorporate single T centres in silicon-on-insulator (SOI) wafers. We demonstrate single T-centre emission coupled to a nanophotonic waveguide and observe significant suppression of homogeneous broadening, yielding optical linewidths as narrow as 30 MHz using natural silicon for crystal growth. These results establish epitaxial T centres as a robust foundation for coherent spin-photon interfaces in silicon quantum photonics.

quant-pharXiv:2607.06272•Jul 8, 2026
Silicon is an attractive host for scalable quantum photonics, but the absence of bright telecom-band emitters with optically addressable spin states has limited its use for spin-photon interfaces. Here we demonstrate the Al1-center, an aluminum--carbon defect in silicon, as a bright waveguide-integrated single-photon emitter with a ground-state spin. Using isotopically purified silicon-on-insulator nanophotonic devices, we isolate individual Al1-centers and observe high-purity single-photon emission with g(2)(0)=0.04g^{(2)}(0)=0.04g(2)(0)=0.04 without background subtraction. Time-resolved photoluminescence spectroscopy reveals a fast excited-state lifetime of 135 ns, nearly an order of magnitude shorter than the benchmark provided by the well-studied T-center. Resonant photoluminescence excitation measurements further resolve the zero-phonon transition and reveal a narrow homogeneous linewidth reaching 47 MHz, threefold narrower than the T-center under comparable temperature. Through magneto-optical spectroscopy, we resolve the spin-dependent transitions of the bound-exciton manifold and achieve spin-selective optical pumping, fulfilling the prerequisite for quantum state initialization and readout. These results establish the Al1-center as a bright telecom-band spin-photon interface in silicon photonics and introduce a promising platform for integrated quantum networks.
Silicon-based quantum technologies have gained increasing attention due to their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While several optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band-a key wavelength range for low-loss fiber-based communication-has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance, enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Monolithic integration of single-photon sources into silicon photonics offers a compelling solution for realizing scalable quantum telecommunication architectures. Among the candidate silicon color centers, the C-center features a zero-phonon emission in the telecom L-band, corresponding to the spectral window of minimum transmission loss in optical fibers. Despite this advantage, isolating single C-centers has remained an unrealized challenge in solid-state quantum optics. In this work, we report the isolation of a single silicon C-center. We enhance the spontaneous emission rate of the zero-phonon line by coupling the single emitter to a nanophotonic crystal cavity, observing a fivefold reduction in the excited-state lifetime compared to bulk conditions, which corresponds to a Purcell factor lower bound of 33. Second-order autocorrelation measurements confirm single-photon emission from the investigated defect, obtaining an optical purity of g(2)(0)=0.23g^{(2)}(0) = 0.23g(2)(0)=0.23 without background correction. Our results establish a native telecom L-band quantum light source in silicon, laying the foundation for ultra-low-loss and long-distance quantum applications.
Abstract Optically active spin systems in silicon are attracting growing interest for quantum technologies, driven by their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces, which allow coupling between spin degrees of freedom and photons are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While a variety of optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band (1565–1625 nm)—a key wavelength range for low-loss fiber-based communication—has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance (ODMR), enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Telecom-band spin defects in silicon offer a compelling platform for integrated quantum networks by combining scalable silicon photonics with spin-based quantum memories and multiqubit registers. The T center and recently demonstrated Al1 center are particularly promising, but their limited coherent zero-phonon emission requires strong cavity enhancement for efficient spin-photon interfaces. Here, we inverse-design silicon nanobeam cavities for both centers using a unified adjoint-optimization framework targeting Purcell enhancement, resonance alignment, and photon extraction. For each emitter, symmetric cavities maximize Purcell enhancement, while asymmetric cavities provide directional coupling to an integrated waveguide. Three-dimensional finite-difference time-domain simulations yield loaded quality factors up to 3.25 x 10^6, Purcell factors up to 1.43 x 10^5, and cooperativities of approximately 280-5000, corresponding to cavity-coupled emission fractions exceeding 99.6%. The asymmetric cavities direct approximately 90% of emitted power into a single on-chip waveguide while maintaining cooperativity above 280. Under nanometer-scale fabrication perturbations, all four designs remain within the high-cooperativity regime, and high cooperativity persists when the cavity quality factor is constrained to a realistic absorption-limited value of 10^5. This unified, fabrication-compatible framework establishes a scalable cavity-design route for silicon telecom spin-photon interfaces and, to our knowledge, the first cavity designs for the Al1 center.
Nuclear spin qubits in silicon offer exceptionally coherent quantum memory, and optically-interfaced spins are a promising platform for both quantum networking and distributed quantum computing. It has been proposed that emitters with diamagnetic ground states may permit an optical interface to nuclear spin memories via metastable, hyperfine-coupled excited states while suppressing key sources of decoherence. Until now, direct optical observation of suitable transitions in silicon colour centres has remained elusive. Here we characterize the singly-ionized interstitial aluminum donor (Ali+_\mathrm{i}^+i+​) in isotopically purified 28^{28}28Si and find several novel features of this little-studied defect. We measure bright emission and strong optical transitions and, in contrast to previous studies of this centre, attribute its emission to an exchange-split spin triplet and singlet level of the lowest-energy 1s:T2_22​ excited state. We measure the excited-state lifetimes and, as a consequence of its narrow emission linewidth, observe the fine and hyperfine structure of the long-lived triplet state. This constitutes the first measurement of an optically-resolved hyperfine structure in the excited state of a telecommunications-band silicon colour centre.
Spin-photon interfaces based on silicon quantum emitters offer a scalable platform for quantum computing and networking. However, achieving coherent photon emission remains a primary challenge due to stringent material quality requirements. To overcome this, we utilise high-purity molecular-beam epitaxy (MBE) to epitaxially incorporate single T centres in silicon-on-insulator (SOI) wafers. We demonstrate single T-centre emission coupled to a nanophotonic waveguide and observe significant suppression of homogeneous broadening, yielding optical linewidths as narrow as 30 MHz using natural silicon for crystal growth. These results establish epitaxial T centres as a robust foundation for coherent spin-photon interfaces in silicon quantum photonics.