Silicon-based quantum technologies have gained increasing attention due to their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While several optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band-a key wavelength range for low-loss fiber-based communication-has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance, enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Silicon-based quantum technologies have gained increasing attention due to their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While several optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band-a key wavelength range for low-loss fiber-based communication-has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance, enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Abstract Optically active spin systems in silicon are attracting growing interest for quantum technologies, driven by their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces, which allow coupling between spin degrees of freedom and photons are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While a variety of optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band (1565–1625 nm)—a key wavelength range for low-loss fiber-based communication—has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance (ODMR), enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Realization of quantum memory with a photonic interface in the telecommunication bands in a wafer-scalable platform is a central requirement for long-distance quantum networks. Silicon carbide (SiC) provides a technologically mature host for integrated quantum photonics, yet only a limited number of defects combine spin functionality with telecom emission. Here we report on chlorine-based defects in 4H-SiC as a platform for telecom-band quantum memory. The emission of these defects spans the entire telecommunication range with zero-phonon lines in the O- and C-bands and a Debye-Waller factor of up to 39%. Time-resolved photoluminescence measurements reveal a short excited-state lifetime in the sub-nanosecond range. We demonstrate that these defects are spin-active even at room temperature, exhibiting optically detected magnetic resonances (ODMR) in the sub-GHz frequency range. Using ODMR spectroscopy and Ramsey interferometry, we resolve the hyperfine structure arising from the interaction with 35Cl nuclear spins. The ODMR spectra exhibit complex behaviour in an external magnetic field due to mixing of electron-nuclear spin states, which is well reproduced by our simulations. The spin relaxation and coherence times are in the sub-microsecond range, limited by rapid quenching of the ODMR contrast and attributed to charge-state metastability. The combination of telecom-band emission, coherent spin control and compatibility with wafer-scale fabrication positions Cl-related defects in SiC as a promising platform for chip-scale quantum memories with spin-photon interfaces operating in the fiber-optic telecommunication windows.
Silicon is an attractive host for scalable quantum photonics, but the absence of bright telecom-band emitters with optically addressable spin states has limited its use for spin-photon interfaces. Here we demonstrate the Al1-center, an aluminum--carbon defect in silicon, as a bright waveguide-integrated single-photon emitter with a ground-state spin. Using isotopically purified silicon-on-insulator nanophotonic devices, we isolate individual Al1-centers and observe high-purity single-photon emission with g(2)(0)=0.04 without background subtraction. Time-resolved photoluminescence spectroscopy reveals a fast excited-state lifetime of 135 ns, nearly an order of magnitude shorter than the benchmark provided by the well-studied T-center. Resonant photoluminescence excitation measurements further resolve the zero-phonon transition and reveal a narrow homogeneous linewidth reaching 47 MHz, threefold narrower than the T-center under comparable temperature. Through magneto-optical spectroscopy, we resolve the spin-dependent transitions of the bound-exciton manifold and achieve spin-selective optical pumping, fulfilling the prerequisite for quantum state initialization and readout. These results establish the Al1-center as a bright telecom-band spin-photon interface in silicon photonics and introduce a promising platform for integrated quantum networks.
Solid-state quantum light sources offer a scalable pathway for interfacing stationary spin qubits with flying photonic qubits, forming the backbone of future quantum networks. Telecom-band spin-photonic qubits, operating in the 1260-1675 nm wavelength range, are particularly well-suited for long-distance quantum communication due to minimal loss in standard optical fibers. Achieving scalability, however, hinges on fulfilling several stringent criteria: coherent spin-state control, deterministic and indistinguishable single-photon emission, and integration with nanophotonic structures that enhance radiative properties, such as lifetime, coherence, and photon indistinguishability. This study explores the state-of-the-art spin-photonic qubits across solid-state platforms, including diamond color centers, silicon carbide defect centers, quantum dots, and two-dimensional materials. Special attention is given to silicon-based emitters, particularly G, T, C- and Ci-centers, which promise monolithic integration with complementary metal-oxide-semiconductor (CMOS) technology and telecom-band operation. We classify these systems based on spin-photon interface availability, CMOS process compatibility, and emitter scalability. We also discuss recent advances in cavity quantum electrodynamics (cQED), including Purcell enhancement and quality factor engineering in integrated photonic (circuits) environments. The work highlights emerging demonstrations of quantum networking over metropolitan scales and outlines the trajectory toward chip-scale quantum photonic integrated circuits (QPICs). It combines deterministic emitter creation, coherent spin manipulation, and quantum information processing. These developments pave the way for global quantum networks, enabling secure communication, distributed quantum computing, and quantum-enhanced sensing.
Abstract Realization of quantum memory with a photonic interface in the telecommunication bands in a wafer-scalable platform is a central requirement for long-distance quantum networks. Silicon carbide (SiC) provides a technologically mature host for integrated quantum photonics, yet only a limited number of defects combine spin functionality with telecom emission. Here we report on chlorine-based defects in 4H-SiC as a platform for telecom-band quantum memory. The emission of these defects spans the entire telecommunication range with zero-phonon lines in the O- and C-bands and a Debye-Waller factor of up to 39 %. Time-resolved photoluminescence measurements reveal a short excited-state lifetime in the sub-nanosecond range. We demonstrate that these defects are spin-active even at room temperature, exhibiting optically detected magnetic resonances (ODMR) in the sub-GHz frequency range. Using ODMR spectroscopy and Ramsey interferometry, we resolve the hyperfine structure arising from the interaction with Cl-35 nuclear spins. The ODMR spectra exhibit complex behaviour in an external magnetic field due to mixing of electron-nuclear spin states, which is well reproduced by our simulations. The spin relaxation and coherence times are in the sub microsecond range, limited by rapid quenching of the ODMR contrast and attributed to charge-state metastability. The combination of telecom-band emission, coherent spin control and compatibility with wafer-scale fabrication positions Cl-related defects in SiC as a promising platform for chip-scale quantum memories with spin-photon interfaces operating in the fiber-optic telecommunication windows.
Color centers in silicon are emerging as promising platforms for quantum technologies. Among them, the G center has attracted considerable interest owing to its bright telecom O-band single-photon emission and its optically addressable metastable electron-spin triplet state. Here we investigate the spin properties of ensembles of G centers under above-band-gap excitation. We elucidate the spin photo-dynamics giving rise to the optical detected magnetic resonance (ODMR) response of G centers. The optimal pulsed sequence for measuring the ODMR spectrum of the G defects is identified, along with the temperature and optical-power regimes maximizing the spin readout contrast. Through magneto-optical measurements, we detect a level-anticrossing of the G center electron spin states. At last, we demonstrate coherent spin control of the defects, and characterize their spin-coherence properties. Unveiling the spin degree of freedom of the G center opens new avenues for the realization of quantum memories and quantum registers based on silicon color centers.