Abstract Superconducting resonators integrated with germanium (Ge) quantum wells (QWs) offer a promising platform for hybrid quantum devices. Yet, in the most common heterostructure architectures, they have so far been limited by sizable photon losses. Here, we report the fabrication and characterization of microwave resonators patterned in the aluminum (Al) thin film of an in-situ grown superconductor/semiconductor hybrid heterostructure (HS). The semiconductor part of this hybrid HS is grown on a commercial Ge substrate. We consistently achieve internal quality factors Q i > 1000, surpassing previous results on Ge QW heterostructures grown using the concept of a virtual Ge substrate on silicon (Si) substrates. We reach Q i ≈ 49,000 at single-photon occupation and a plateau of Q i ≈ 20,000 at sub-one photon, an order of magnitude larger than any previously reported value of resonators on Ge QW structures at low power. We further characterize the thin Al film forming the resonator, extracting its kinetic inductance and superconducting gap, and studying its magnetic field dependence. Notably, the resonance remains well-defined up to in-plane magnetic fields of 850 mT. A hysteresis emerges in the out-of-plane magnetic field dependence, for both the resonance frequency and the quality factor, indicating an interesting interplay between vortex-and quasiparticle loss mechanisms.
Abstract Superconducting resonators integrated with germanium (Ge) quantum wells (QWs) offer a promising platform for hybrid quantum devices. Yet, in the most common heterostructure architectures, they have so far been limited by sizable photon losses. Here, we report the fabrication and characterization of microwave resonators patterned in the aluminum (Al) thin film of an in-situ grown superconductor/semiconductor hybrid heterostructure (HS). The semiconductor part of this hybrid HS is grown on a commercial Ge substrate. We consistently achieve internal quality factors Q i > 1000, surpassing previous results on Ge QW heterostructures grown using the concept of a virtual Ge substrate on silicon (Si) substrates. We reach Q i ≈ 49,000 at single-photon occupation and a plateau of Q i ≈ 20,000 at sub-one photon, an order of magnitude larger than any previously reported value of resonators on Ge QW structures at low power. We further characterize the thin Al film forming the resonator, extracting its kinetic inductance and superconducting gap, and studying its magnetic field dependence. Notably, the resonance remains well-defined up to in-plane magnetic fields of 850 mT. A hysteresis emerges in the out-of-plane magnetic field dependence, for both the resonance frequency and the quality factor, indicating an interesting interplay between vortex-and quasiparticle loss mechanisms.
Ge/SiGe heterostructures represent a promising platform for hosting various quantum devices such as hole spin qubits and Andreev spin qubits. However, the compatibility of such heterostructures with high-quality-factor microwave superconducting cavities remains a challenge due to defects in the material stack. In this work, we present an approach to enhance the coherence of cavity modes on a reverse-graded Ge/SiGe heterostructure, which consists of etching the full ∼1.6μm-thick Ge/SiGe stack down to its starting high-resistivity Si substrate, in order to pattern superconducting cavities directly on it. We engineer the mesa step to be tapered, so that it can be easily climbed by the superconducting cavities to reach the quantum devices potentially hosted in the Ge quantum well. Using this approach, we observe internal quality factors of Qi≈10000−20000 for high-impedance frequency-tunable Josephson junction array resonators, limited by the junctions' fabrication, and Qi≈100000 for 50Ω coplanar waveguide Nb lift-off resonators. These Qi are preserved despite the overlap with the mesa structure in the climbing region, and are comparable to the ones obtained for identical resonators fabricated on a high-resistivity Si wafer reference. Thereby, this work paves a practical path toward superconductor-semiconductor hybrid devices, immediately applicable to emerging technologies on planar Ge.
We present a flip-chip-based sensing scheme to measure effective microwave losses associated with target materials for quantum technologies, without requiring any device fabrication on the material under test. Using this approach, we quantify the microwave losses of a strain-engineered Ge/SiGe quantum well heterostructure and investigate losses arising from its Ge substrate and intermediate layers. The quality factors of the fabricated microwave resonators agree with the losses of dielectric materials independently extracted from flip-chip sensing measurements. We further study the superconductor platinum silicon germanide (PtSiGe) prepared by thermal reaction with a deposited Pt film, finding high microwave losses that limit the suitability of the films studied here as the sole superconductor for high-quality resonator applications. By coating Pt with Nb prior to the reaction, we observe a substantial reduction in microwave loss and a nearly three-fold enhancement of the transport critical temperature. The temperature dependence of the microwave loss is consistent with gap inhomogeneity in both superconducting films. These results identify constraints on material choices, provide design guidance for microwave circuits on planar Ge heterostructures, and demonstrate a fast-turnaround testing method for new materials for superconducting quantum circuits.
Superconducting high kinetic inductance elements constitute a valuable resource for quantum circuit design and millimeter-wave detection. Granular aluminum (grAl) in the superconducting regime is a particularly interesting material since it has already shown a kinetic inductance in the range of nH/□ and its deposition is compatible with conventional Al/AlOx/Al Josephson junction fabrication. We characterize microwave resonators fabricated from grAl with a room temperature resistivity of 4×10^{3} μΩ cm, which is a factor of 3 below the superconductor to insulator transition, showing a kinetic inductance fraction close to unity. The measured internal quality factors are on the order of Q_{i}=10^{5} in the single photon regime, and we demonstrate that nonequilibrium quasiparticles (QPs) constitute the dominant loss mechanism. We extract QP relaxation times in the range of 1 s and we observe QP bursts every ∼20 s. The current level of coherence of grAl resonators makes them attractive for integration in quantum devices, while it also evidences the need to reduce the density of nonequilibrium QPs.
Abstract We systematically study the performance of compact lumped element planar microwave Nb70Ti30N (NbTiN) resonators operating at 5 GHz in external in-plane magnetic fields up to 440 mT, a broad temperature regime from 2.2 K up to 13 K, as well as mK temperatures. For comparison, the resonators have been fabricated on thermally oxidized and pristine, (001) oriented silicon substrates. When operating the resonators in the multi-photon regime at T = 2.2 K, we find internal quality factors Q int ≃ 2 × 105 for NbTiN resonators grown on pristine Si substrates. In addition, we investigate the Q-factors of the resonators on pristine Si substrates at millikelvin temperatures to assess their applicability for quantum applications. We find Q int ≃ 2 × 105 in the single photon regime and Q int ≃ 5 × 105 in the high power regime at T = 7 mK. From the excellent performance of our resonators over a broad temperature and magnetic field range, we conclude that NbTiN deposited on Si (100) substrates, where the surface oxide has been removed, constitutes a promising material platform for electron spin resonance and ferromagnetic resonance experiments using superconducting planar microwave resonators.
We have characterized the microwave loss of high-Q parallel plate capacitors fabricated from thin-film Al/Al2O3/Re heterostructures on (0001) Al2O3 substrates. The superconductor-insulator-superconductor trilayers were grown in situ in a hybrid deposition system: the epitaxial Re base and polycrystalline Al counterelectrode layers were grown by sputtering, while the epitaxial Al2O3 layer was grown by pulsed laser deposition. Structural analysis indicates a highly crystalline epitaxial Al2O3 layer and sharp interfaces. The measured intrinsic (low-power, low-temperature) quality factor of the resonators is as high as 3 × 104. These results indicate that low-loss grown Al2O3 is an attractive candidate dielectric for high-fidelity superconducting qubit circuits.
The performance and coherence of superconducting quantum systems are fundamentally tied to the quality of the materials from which they are built. In superconducting transmon qubits, many loss mechanisms and sources of decoherence originate from material imperfections or unwanted oxide formation. Likewise, semiconductor–superconductor hybrid systems depend on high-quality interfaces to ensure strong coupling between electronic states in the two materials. In such hybrid devices, the accessible operating regime is often dictated by the intrinsic material properties of either the semiconductor or the superconductor. Advancing quantum device performance therefore requires exploring new material systems and optimizing their physical characteristics. In this thesis, we present the development of several superconducting material platforms for quantum technologies, including superconducting qubits, single-photon detectors, and semiconductor superconductor hybrid devices. We focus on the growth and characterization of superconducting films and heterostructures, and we establish clear connections between their material properties and the resulting device performance. First, we will present a novel semiconductor-superconductor hybrid material based on in-situ deposited epitaxial layers of Nb and Al on a shallow InAs quantum well. In this structure, the Al interlayer provides an epitaxial connection between an in-situ magnetron sputtered Nb or NbTi thin film and a shallow InAs two dimensional electron gas. This metal-to-metal epitaxy is achieved by optimization of the material stack and results in an induced superconducting gap of approximately 1 meV, determined from transport measurements of superconductor semiconductor Josephson junctions. This induced gap is approximately five times larger than the values reported for Al-based hybrid materials and indicates the formation of highly-transparent interfaces that are required in high-quality hybrid material platforms. Then, we discuss a different approach in the next chapter where we develop a hybrid material based on a molecular beam epitaxy grown InAsSb surface quantum well with an in-situ deposited Nb layer directly on top of the quantum well. Relative to conventional Al-InAs based systems, the InAsSb surface quantum well offers a lower effective mass and stronger spin-orbit interaction, while the Nb layer has a higher critical temperature and a larger critical magnetic field. The in-situ deposition of the Nb layer directly on top of the quantum well results in a high-quality interface that enables strong coupling to the InAsSb quantum well. Transport measurements on Josephson junctions reveal an induced superconducting gap of 1.3 meV and a critical current density of 3.75 × 10³A/cm². Furthermore, a planar asymmetric SQUID is realized, exhibiting gate-tunable superimposed oscillations originating from both the individual Josephson junction and the full SQUID loop. The large induced superconducting gap combined with strong spin-orbit interaction position this material as an attractive platform for experiments exploring gate-tunable superconductivity and topological superconducting devices. In the next chapter, we will focus on establishing a link between Nb film crystal properties and their performance in superconducting circuits. In this study, we investigate the microwave properties of niobium resonators with different crystalline properties and related surface topographies. We analyze a series of magnetron sputtered films in which the Nb crystal orientation and surface topography are changed by varying the substrate temperatures between room temperature and 975 K. The lowest-loss resonators that we measure have quality factors of over 10⁶ at single-photon powers, among the best ever recorded using the Nb on sapphire platform. We observe the highest quality factors in films grown at an intermediate temperature regime of the growth series (550 K) where the films display both preferential ordering of the crystal domains and low surface roughness. Furthermore, we analyze the temperature-dependent behavior of our resonators to learn about how the quasi-particle density in the Nb film is affected by the niobium crystal structure and the presence of grain boundaries. Then, we explore yet a different material platform by attempting to realize onchip NbTiN single photon detectors on LiNbO₃, an emerging photonic platform with high potential for scalable quantum information processing. We use DC reactive magnetron sputtering to grow high-quality NbTiN thin films and investigate the impact of substrate temperature during NbTiN growth. We achieve four nm thick superconducting films with a critical temperature (𝑇𝑐) of 12.3 K grown at a substrate temperature of 825 K. We demonstrate that the increased substrate temperature reduces the oxygen concentration in our films and improves the overall stoichiometry. In addition, we integrate these films with the LiNbO3 platform and investigate the obtained interface quality. Finally, we fabricate superconducting nanowire single photon detectors from the NbTiN film on LiNbO₃ and characterize the detector performance. Lastly, we report a gate-tunable Josephson diode effect in hybrid nanowire junctions consisting of a spin-orbit-coupled semiconductor core coated with epitaxial ferromagnetic insulator and superconductor shells. The wires display a hysteretic superconducting window as a function of axial magnetic field. In the superconducting regime, the devices exhibit nonreciprocal current transport, with the diode efficiency showing a strong dependence on back-gate voltage. The effect persists in a remanent magnetization state following a controlled demagnetization procedure, establishing zero-field operation. The combination of results presented in this thesis stress the importance of a material-focused approach in advancing the performance of quantum hardware. The novel hybrid material platforms developed in this thesis expand the operating regime of devices, which could enable future experiments involving gate-tunable superconductivity or topological properties. Similarly, we demonstrate that optimizing superconductor crystal structure benefits quantum devices, such as single-photon detectors and superconducting resonators.