Spectral Hole-Burning and Related Spectroscopies: Science and Applications

Room-Temperature Persistent Spectral Hole Burning in Sm2+:SrFCl0.5Br0.5

Raivo Jaaniso, Hans Bill

Published Jan 1, 1991• 0 citations
Publisher

Abstract

We report the first observation of spectral hole burning in the spectra of impurity centers at room temperature. The persistent holes are burned in the 5D17F0 (632 nm) and 5D0-7F0 (690 nm) transitions of Sm2+ ions in the title compound.
DOI
10.1364/pshb.1991.fa4

Related papers

Room-Temperature Persistent Spectral Hole-Burning in Sm2+-Doped Glass

Atusi Kurita, T. Kushida, TETSURO IZUMITANI +1 more

We report the first observation of room-temperature persistent spectral hole-burning in glass. The holes were burned in the 7F0→5D0 line of Sm2+ ions in fluorohafnate glass.

Spectral Hole-Burning and Related Spectroscopies: Science and Applications•Jan 1, 1992•0 citations

Spectral Hole-Burning Between 2 K and Room Temperature in Sm2+ Doped Substitutionally Disordered Microcrystals

Keith Holliday, Changjiang Wei, Mauro Croci +1 more

Photon gated spectral hole-burning was first observed in a samarium doped crystal, BaFCl:Sm2+ [1]. This material was of interest to the developement of optical memories as the holes were found to be stable to room temperature thermal cycling. Holes could be burnt at liquid helium temperatures but as the temperature was raised the line quickly became homogeneously broadened. The addition of bromine to the melt succeeded in broadening the inhomogeneous linewidths to about 2 nm through substitutional disorder [2] and persistent holes were observed at 77 K [3]. Subsequently, a study of the parameters for spectral hole-burning in a BaFCl0.5Br0.5:Sm2+ crystalline powder was performed [4] and the highest temperature for which persistent hole-burning had been observed was raised to 133 K. Here we report spectral hole-burning at room temperature (figure 1) in a related compound, Sr0.5Mg0.5FCl0.5Br0.5:Sm2+.

Spectral Hole-Burning and Related Spectroscopies: Science and Applications•Jan 1, 1991•0 citations

Room-temperature persistent spectral hole burning in SrFCl:Sm2+ films: Temporal and spatial response

Marc Schnieper, F. Trotta, S. Bersier +1 more

Persistent spectral hole burning was performed on the 7F0–5D1 transition of Sm2+ in thin films of SrFCl. Depending on the substrate and the growth conditions, a total hole depth between 47% and 70% was reached. The holes were Lorentzians of width 4(±0.3) cm−1. The time evolution of the hole depth was studied. It is described by two exponentials: a short time decay (t1=0.37 days) and a long time decay (t2=20.4 days) with a 20% infinite time limit. One- and two-photon burning mechanisms act.

Applied Physics Letters•Jul 5, 1999•10 citations

Electron transition process of 5D2→7F0 of Sm2+ in spectral hole-burning

Hongwei Song, Jiahua Zhang, Shihua Huang +1 more

Materials of MyM’1-yFClxBr1-x:Sm2+ have been widely applied in spectral hole-burning since the first observation of persistent spectral hole-burning in BaFCl:Sm2+ at 2K was reported by A. Winnaker, etc. in 1985[1]. From then on, hole-burning in BaFCl0.5Br0.5:Sm2+ at 77K[2] in SrFCl and Mg0.5Sr0.5FCl0.5Br0.5:Sm2+ at room temperature[3, 4] were reported. Room temperature hole-buring of Sm2+ in fluorohafnate glasses[5,6] were reported in recent years also. These materials are of potential use in high temperature hole- burning. But comparing to organic materials, they have lower hole- burning efficiency and narrower inhomogenous line width. In order to apply spetral hole- buring in frequency domain optical storage, it is important to improve these materials.

Spectral Hole-Burning and Related Spectroscopies: Science and Applications•Jan 1, 1994•0 citations

Persistent spectral hole burning and optical properties of Sm2+doped into Mg0.5Sr0.5FCl0.5Br0.5mixed crystal

Kiwan Jang, Il-Gon Kim, Hyo-Jin Seo +3 more

We measured the temperature dependence of the fluorescence of Sm 2+ ions doped into a Mg 0.5 Sr 0.5 FCl 0.5 Br 0.5 mixed crystal and observed the persistent spectral hole burning at 90 K and 300 K. The electrons appearing at the 5 D 0 → 7 F 0 transition mostly come via the 4f5d→ 5 D 1 → 5 D 0 → 7 F 0 route but some of the electrons come directly from the 4f5d band. At 90 K, persistent spectral hole burning was achieved much more efficiently by the photon-gated spectral hole-burning process than by the one-photon hole-burning process, while the one-photon hole-burning process is much more efficient at 300 K.

Journal of Physics Condensed Matter•Mar 15, 2001•0 citations

Room-temperature persistent spectral hole burning in Sm-doped KLaF4 crystals

Nobuhiro Kodama, Tomoko Takahashi, Kazuyuki Hirao

Persistent spectral hole burning is observed at room temperature in the excitation spectrum for the F07→D05 transition of Sm2+ in KLaF4 single crystals. The hole width and depth are about 10 cm−1 and 18% of the total intensity, respectively. It is concluded that the dominant burning mechanism in this crystal is a photoionization of electron trapping at a site other than Sm3+ ions because of the absence of an antihole around the burned hole.

Applied Physics Letters•Mar 30, 1998•7 citations
Photon gated spectral hole-burning was first observed in a samarium doped crystal, BaFCl:Sm2+ [1]. This material was of interest to the developement of optical memories as the holes were found to be stable to room temperature thermal cycling. Holes could be burnt at liquid helium temperatures but as the temperature was raised the line quickly became homogeneously broadened. The addition of bromine to the melt succeeded in broadening the inhomogeneous linewidths to about 2 nm through substitutional disorder [2] and persistent holes were observed at 77 K [3]. Subsequently, a study of the parameters for spectral hole-burning in a BaFCl0.5Br0.5:Sm2+ crystalline powder was performed [4] and the highest temperature for which persistent hole-burning had been observed was raised to 133 K. Here we report spectral hole-burning at room temperature (figure 1) in a related compound, Sr0.5Mg0.5FCl0.5Br0.5:Sm2+.
Materials of MyM’1-yFClxBr1-x:Sm2+ have been widely applied in spectral hole-burning since the first observation of persistent spectral hole-burning in BaFCl:Sm2+ at 2K was reported by A. Winnaker, etc. in 1985[1]. From then on, hole-burning in BaFCl0.5Br0.5:Sm2+ at 77K[2] in SrFCl and Mg0.5Sr0.5FCl0.5Br0.5:Sm2+ at room temperature[3, 4] were reported. Room temperature hole-buring of Sm2+ in fluorohafnate glasses[5,6] were reported in recent years also. These materials are of potential use in high temperature hole- burning. But comparing to organic materials, they have lower hole- burning efficiency and narrower inhomogenous line width. In order to apply spetral hole- buring in frequency domain optical storage, it is important to improve these materials.
We measured the temperature dependence of the fluorescence of Sm 2+ ions doped into a Mg 0.5 Sr 0.5 FCl 0.5 Br 0.5 mixed crystal and observed the persistent spectral hole burning at 90 K and 300 K. The electrons appearing at the 5 D 0 → 7 F 0 transition mostly come via the 4f5d→ 5 D 1 → 5 D 0 → 7 F 0 route but some of the electrons come directly from the 4f5d band. At 90 K, persistent spectral hole burning was achieved much more efficiently by the photon-gated spectral hole-burning process than by the one-photon hole-burning process, while the one-photon hole-burning process is much more efficient at 300 K.