Abstract Here we report a breakthrough in the fabrication of a long lifetime transmon qubit. We use tantalum films as the base superconductor. By using a dry etching process, we obtained transmon qubits with a best T1 lifetime of 503 μs. As a comparison, we also fabricated transmon qubits with other popular materials, including niobium and aluminum, under the same design and fabrication processes. After characterizing their coherence properties, we found that qubits prepared with tantalum films have the best performance. Since the dry etching process is stable and highly anisotropic, it is much more suitable for fabricating complex scalable quantum circuits, when compared to wet etching. As a result, the current breakthrough indicates that the dry etching process of tantalum film is a promising approach to fabricate medium- or large-scale superconducting quantum circuits with a much longer lifetime, meeting the requirements for building practical quantum computers.
Abstract Here we report a breakthrough in the fabrication of a long lifetime transmon qubit. We use tantalum films as the base superconductor. By using a dry etching process, we obtained transmon qubits with a best T1 lifetime of 503 μs. As a comparison, we also fabricated transmon qubits with other popular materials, including niobium and aluminum, under the same design and fabrication processes. After characterizing their coherence properties, we found that qubits prepared with tantalum films have the best performance. Since the dry etching process is stable and highly anisotropic, it is much more suitable for fabricating complex scalable quantum circuits, when compared to wet etching. As a result, the current breakthrough indicates that the dry etching process of tantalum film is a promising approach to fabricate medium- or large-scale superconducting quantum circuits with a much longer lifetime, meeting the requirements for building practical quantum computers.
By using the dry etching process of tantalum (Ta) film, we had obtained transmon qubit with the best lifetime (T1) 503 us, suggesting that the dry etching process can be adopted in the following multi-qubit fabrication with Ta film. We also compared the relaxation and coherence times of transmons made with different materials (Ta, Nb and Al) with the same design and fabrication processes of Josephson junction, we found that samples prepared with Ta film had the best performance, followed by those with Al film and Nb film. We inferred that the reason for this difference was due to the different loss of oxide materials located at the metal-air interface.
The superconducting transmon qubit is a leading platform for quantum computing and quantum science. Building large, useful quantum systems based on transmon qubits will require significant improvements in qubit relaxation and coherence times, which are orders of magnitude shorter than limits imposed by bulk properties of the constituent materials. This indicates that relaxation likely originates from uncontrolled surfaces, interfaces, and contaminants. Previous efforts to improve qubit lifetimes have focused primarily on designs that minimize contributions from surfaces. However, significant improvements in the lifetime of two-dimensional transmon qubits have remained elusive for several years. Here, we fabricate two-dimensional transmon qubits that have both lifetimes and coherence times with dynamical decoupling exceeding 0.3 milliseconds by replacing niobium with tantalum in the device. We have observed increased lifetimes for seventeen devices, indicating that these material improvements are robust, paving the way for higher gate fidelities in multi-qubit processors.
Tantalum-based transmon qubits are a promising platform for building large-scale quantum processors. So far, these qubits have been made from tantalum films grown exclusively in the alpha phase (α-Ta). The beta phase of tantalum (\{beta}-Ta) readily nucleates at room temperature, making it attractive for scalable qubit fabrication. However, \{beta}-Ta is widely believed to be detrimental to qubit performance because it has a lower superconducting critical temperature than α-Ta. We challenge this prevailing belief by fabricating low-loss transmon qubits from \{beta}-Ta films on sapphire. Across 11 qubits, the mean time-averaged quality factor is (5.6 +/- 2.3) x 10^6, with the best qubit recording a time-averaged quality factor of (10.1 +/- 1.3) x 10^6. Resonator studies demonstrate that the dominant microwave loss channel is surface two-level systems, with the surface loss contribution for \{beta}-Ta being about twice that of α-Ta. \{beta}-Ta films exhibit significant kinetic inductance, consistent with an estimated magnetic penetration depth of (1.78 +/- 0.02) μm. This work establishes \{beta}-Ta on sapphire as a material platform for realizing low-loss transmon qubits and other superconducting devices such as compact resonators, kinetic inductance detectors, and quasiparticle traps.
Abstract We present a transmon qubit fabrication technique that yields systematic improvements in T 1 relaxation times. We encapsulate the surface of niobium and prevent the formation of its lossy surface oxide. By maintaining the same superconducting metal and only varying the surface, this comparative investigation examining different capping materials, such as tantalum, aluminum, titanium nitride, and gold, as well as substrates across different qubit foundries demonstrates the detrimental impact that niobium oxides have on coherence times of superconducting qubits, compared to native oxides of tantalum, aluminum or titanium nitride. Our surface-encapsulated niobium qubit devices exhibit T 1 relaxation times 2–5 times longer than baseline qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 300 μs, with maximum values up to 600 μs. Our comparative structural and chemical analysis provides insight into why amorphous niobium oxides may induce higher losses compared to other amorphous oxides.
The performance of superconducting integrated circuits for quantum applications is fundamentally limited by material-related losses. Tantalum, as an emerging material for next-generation quantum circuits, has attracted considerable attention in recent years after demonstrating breakthrough performance in both superconducting microwave resonators and qubits. Concurrently, a growing body of work is devoted to the operation of tantalum-based circuits and related fabrication techniques. This interest is further stimulated by tantalum thin films polymorphism resulting in a variety of its crystalline structure, superconducting properties, coherence, etc. Furthermore, tantalum circuits exhibit distinctive features in cryogenic experiments, which have not been observed in aluminum- or niobium-based ones. In this review, we summarize the recent research of tantalum thin films growth and phase selection mechanisms on various substrates, key aspects of fabrication and performance of superconducting circuit, including a material first-principles theoretical study. In conclusion, we address a number of open issues, including the role of \b{eta}-phase impurities, the effect of hydrofluoric acid solutions on chain characteristics, and the anomalous behavior of α-tantalum chains at cryogenic temperatures.
Abstract Tantalum (Ta) is a promising material for superconducting qubits due to its stable chemical properties, formation of a single oxide, and resistance to reaction with other substances. However, achieving the desired α -Ta typically requires high-temperature substrate heating, leading to a time-consuming process and stringent requirements for the film deposition system. Here we demonstrate the deposition of high-quality α -Ta at room temperature using a niobium (Nb) film as a buffer layer. The buffered films are characterized using x-ray diffraction, transmission electron microscopy, and scanning electron microscopy. Transmons with capacitors, transmission lines, and readout resonators fabricated with such Nb-buffered Ta exhibit excellent performance. We observed an “inflection point” in the dependence of the Q i of the resonators on the input microwave photons, which can be fitted well with an expression for the superposition of the buffered resonators. These experimental results show that the buffered films deposited at room temperature have promising applications in superconducting devices.