Diamond optical emitters have been explored extensively in recent years for applications to quantum information and processing. Recently they have also been considered for quantum sensing, especially as nanocrystals in biological systems. However, for most of these applications, the performance of the diamond optical emitters is sensitive to the quality of the material. However, there are still important problems that still must be solved in order to realize the full potential of diamond. For example, existing growth and processing techniques (including ion implantation) are fundamentally probabilistic in nature and so cannot easily produce scalable quantum systems. To overcome these problems, we show a molecule-seeded growth technique that decouples the doping and growth processes. The result is near-deterministic creation of specific color centers in chemically pure, low-strain diamond.
I discuss new ways to grow diamond that promise near-deterministic design of fluorescent color-centers, optimized for quantum sensing and metrology applications. The key is to grow diamond from organic molecules at a low enough temperature such that only some of the molecules decompose. This approach gives unprecedented control over the properties of diamond color centers by decoupling diamond-growth from color-center creation. In addition, low growth temperature produces high quality diamonds and allows a wider choice of growth pressures than is currently believed possible.
Progress in controlling diamond synthesis has made it possible to produce very pure crystals and to incorporate and control atomic impurities and carbon vacancies in the crystal lattice. The appropriate impurity-vacancy combinations can give rise to special defects known as color centers, such as the nitrogen-vacancy (NV) or the silicon-vacancy (SiV), which exhibit exceptional quantum properties with spins that are optically addressable. The use of diamond containing color centers has paved the way for the development of innovative quantum technologies, such as very high-resolution magnetometry and quantum information processing. Nevertheless, the development of quantum sensors at the nanometric scale remains one of the most interesting challenges. In this context, the development of a reliable nanoparticle synthesis technique that allows the desired defects to be incorporated and their quantum optical properties to be modulated is crucial. In this seminar, an efficient and recent method to produce diamond nanoparticles containing NV, SiV and germanium-vacancy (GeV) centers is proposed through direct plasma assisted chemical vapour deposition (CVD) growth. This technique allows good control of both nanoparticle growth processes and color centers formation. The optimization of the CVD nanodiamond growth process is presented, showing the impact of different plasma parameters and gas phasecomposition on nanoparticle crystallinity, size and shape. Morphological characterizations reveal the production of small (around 100 nm) and well faceted nanodiamond particles. In addition, the SiV and GeV color centers incorporation can be tuned within this material by varying the gas phase composition which emphasizes the high flexibility of the CVD growth technique. Finally, the quantum properties of the incorporated color centers have been successfully investigated under extreme pressure conditions (up to ~ 180 GPa) showing a monotonic blue shift of their optical zero-phonon line. Since their luminescence remains stable, SiV and GeV centers emerge as high-pressure nanosensors.
New color centers are being discovered in diamond every year. For the most part these are guided by the desire to replace the silicon-vacancy (SiV) by emitters with higher quantum efficiency and longer storage times. I will discuss color centers produced by some of the most recently implanted elements into diamond including Ge, Sn, Pb, Mg. I will also discuss the rationale for elements to be implanted soon. Finally I will also discuss new options for the future, including designer color centers made possible by novel diamond growth techniques.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.
I discuss new ways to grow diamond that promise near-deterministic design of fluorescent color-centers, optimized for quantum sensing applications. Briefly diamonds are grown around diamond-like organic seed molecules that have the dopant atoms needed for specific color centers, located in the correct approximate locations. It can be seen that this approach can give unprecedented control over the number and placement of color centers. Complete quantum registers might also be fabricated, for example a nitrogen-vacancy and at 13C atom with a well-defined separation surrounded by only 12C diamond. In this talk I will discuss our first key success, which is growing diamonds under conditions where the seed molecules are stable, as well as current experiments.