Trapped ions in Paul traps (radio frequency ion traps) are a promising candidate for the realization of a quantum computer. To date, experimental demonstrations of quantum computing and information processing with trapped ions have been limited to small numbers of quantum bits (qubits). The most prominent challenge to realise ion-trap quantum computation is to scale the system and control a large number of trapped ions coherently. Surface-electrode ion trap designs which are amenable to various microfabrication techniques offer a path to achieve this. In this work, design, fabrication and key operations of two types of surface-electrode ion traps, i.e. a Y-junction trap and a two-dimensional (2D) hexagonal lattice trap developed towards scaling ion-trap architectures, are presented. The steps involved in the fabrication of the ion-trap devices included photolithography, wet etch (hydrofluoric acid etch) and dry etch (deep reactive ion and inductively coupled plasma etching), and metal evaporation. The devices were fabricated on SOI substrates with different buried oxide thicknesses (i.e. 5 µm and 10 µm) and different metals for the trap electrodes (i.e. gold and aluminium). An extremely high-breakdown voltage up to 1 kV was measured in vacuum for the SOI-built test devices with a 10 µm-thick buried oxide formed by oxide film-to-oxide film bonding process. This is attributed to the deep V-shaped undercut profile of the buried oxide layer which resulted in a large breakdown path length, and so mitigating surface breakdown effects. Owing to the V-shaped undercut profile, the surface breakdown voltage was improved by 15% for the devices fabricated on SOI substrates with a 10 µm-thick buried oxide. In the first experiment, the demonstration of ytterbium (174Yb+) ion trapping in the 2D hexagonal lattice trap is achieved with a relatively long lifetime of a laser-cooled ion up to 90 minutes and ≤ 5 minutes without cooling in ultra-high vacuum system. The 2D lattice trap design allows for reliable trapping of 2D ion lattices, rudimentary shuttling between lattice sites and deterministic introducing of defects into the ion lattice. Based on all these abilities, such a 2D lattice trap with the predicted reduction of lattice spacing down to 32 µm can be configured as a versatile architecture for 2D quantum simulations with trapped ions. In the second experiment, microparticle trapping in the 2D lattice trap, performed in air, is achieved with the longest trapping lifetime of 60 minutes. Both gold and aluminium-coated electrodes also lead to comparable trapping performances. Furthermore, the in situ levitation of microparticles is successfully demonstrated at the maximum levitation height of 30 µm. This ability provides additional control on the trapping height which increases the overall functionality of the 2D lattice trap.
Trapped ions in Paul traps (radio frequency ion traps) are a promising candidate for the realization of a quantum computer. To date, experimental demonstrations of quantum computing and information processing with trapped ions have been limited to small numbers of quantum bits (qubits). The most prominent challenge to realise ion-trap quantum computation is to scale the system and control a large number of trapped ions coherently. Surface-electrode ion trap designs which are amenable to various microfabrication techniques offer a path to achieve this. In this work, design, fabrication and key operations of two types of surface-electrode ion traps, i.e. a Y-junction trap and a two-dimensional (2D) hexagonal lattice trap developed towards scaling ion-trap architectures, are presented. The steps involved in the fabrication of the ion-trap devices included photolithography, wet etch (hydrofluoric acid etch) and dry etch (deep reactive ion and inductively coupled plasma etching), and metal evaporation. The devices were fabricated on SOI substrates with different buried oxide thicknesses (i.e. 5 µm and 10 µm) and different metals for the trap electrodes (i.e. gold and aluminium). An extremely high-breakdown voltage up to 1 kV was measured in vacuum for the SOI-built test devices with a 10 µm-thick buried oxide formed by oxide film-to-oxide film bonding process. This is attributed to the deep V-shaped undercut profile of the buried oxide layer which resulted in a large breakdown path length, and so mitigating surface breakdown effects. Owing to the V-shaped undercut profile, the surface breakdown voltage was improved by 15% for the devices fabricated on SOI substrates with a 10 µm-thick buried oxide. In the first experiment, the demonstration of ytterbium (174Yb+) ion trapping in the 2D hexagonal lattice trap is achieved with a relatively long lifetime of a laser-cooled ion up to 90 minutes and ≤ 5 minutes without cooling in ultra-high vacuum system. The 2D lattice trap design allows for reliable trapping of 2D ion lattices, rudimentary shuttling between lattice sites and deterministic introducing of defects into the ion lattice. Based on all these abilities, such a 2D lattice trap with the predicted reduction of lattice spacing down to 32 µm can be configured as a versatile architecture for 2D quantum simulations with trapped ions. In the second experiment, microparticle trapping in the 2D lattice trap, performed in air, is achieved with the longest trapping lifetime of 60 minutes. Both gold and aluminium-coated electrodes also lead to comparable trapping performances. Furthermore, the in situ levitation of microparticles is successfully demonstrated at the maximum levitation height of 30 µm. This ability provides additional control on the trapping height which increases the overall functionality of the 2D lattice trap.
Trapped ions within Paul traps have shown to be a promising architecture in the realisation of a quantum information processor together with the ability of providing quantum simulations. Linear Paul traps have demonstrated long coherence times with ions being well isolated from the environment, single and multi-qubit gates and the high fidelity detection of states. The scalability to large number of qubits, incorporating all the previous achievements requires an array of linear ion traps. Microfabrication techniques allow for fabrication and micron level accuracy of the trap electrode dimensions through photolithography techniques. The first part of this thesis presents the experiential setup and trapping of Yb+ ions needed to test large ion trap arrays. This include vacuum systems that can host advanced symmetric and asymmetric ion traps with up to 90 static voltage control electrodes. Demonstration of a single trapped Yb+ ion within a two-layer macroscopic ion trap is presented. with an ion-electrode distance of 310(10) µm. The anomalous heating rate and spectral noise density of the trap was measured, a main form of decoherence within ion traps. The second half of this thesis presents the design and fabrication of multi-layer asymmetric ion traps. This allows for isolated electrodes that cannot be accessed via surface pathways, allowing for higher density of electrodes as well as creating novel trap designs that allow for the potential of quantum simulations to be demonstrated. These include two-dimensional lattices and ring trap designs in which the isolated electrodes provide more control in the ion position. For the microfabrication of these traps I present a novel high-aspect ratio electroplated electrode design that provides shielding of the dielectric layer. This provides a means to mitigate stray electric field due to charge build up on the dielectric surfaces. Electrical testing of the trap structures was performed to test bulk breakdown and surface flashover of the ion trap architectures. Results showed sufficient isolation between electrodes for both radio frequency and static breakdown. Surface flashover voltage measurements over the dielectric layer showed an improvement of more than double over previous results using a new fabrication technique. This will allow for more powerful ion trap chips needed for the next generation of microfabricated ion trap arrays for scalable quantum technologies.
We present the design, fabrication and experimental result of a two-dimensional (2D) hexagonal lattice trap capable of trapping a lattice of charged particles. The microtrap consists of 29-hexagonal lattice sites each capable of trapping an ion. Each trapped ion has up to six neighbors with an ion-ion separation of 270.5 μm. A SOI-based structure was optimized to improve the trap performance substantially increasing the breakdown voltage (>1 kV) previously reported. Ytterbium (174Yb002B;) ions were successfully confined in an ultra-high vacuum (UHV) system by applying a radio frequency (RF) voltage of 455 V at a drive frequency Ω/2π = 32.2 MHz. In addition, our design is suitable to control the trapping height in situ by applying a secondary rf potentials. Numerical simulations of the 2D lattice trap demonstrated a large operating range by trapping ions as well as micro-particles with charge to mass ratio in order of 10-4to 105Kg/C at a frequency range of a few kilohertz to megahertz.
Over the past 15 years ion traps have demonstrated all the building blocks required of a quantum computer. Despite this success, trapping ions remains a challenging task, with the requirement for extensive laser systems and vacuum systems to perform operations on only a handful of qubits. To scale these proof of principle experiments into something that can outperform a classical computer requires an advancement in the trap technologies that will allow multiple trapping zones, junctions and utilize scalable fabrication technologies. I will discuss the construction of an ion trapping experiment, focussing on my work towards the laser stabilization and ion trap design but also covering the experimental setup as a whole. The vacuum system that I designed allows the mounting and testing of a variety of ion trap chips, with versatile optical access and a fast turn around time. I will also present the design and fabrication of a microfabricated Y junction and a 2- dimensional ion trap lattice. I achieve a suppression of barrier height and small variation of secular frequency through the Y junction, aiding to the junctions applicability to adiabatic shuttling operations. I also report the design and fabrication of a 2-D ion trap lattice. Such structures have been proposed as a means to implement quantum simulators and to my knowledge is the first microfabricated lattice trap. Electrical testing of the trap structures was undertaken to investigate the breakdown voltage of microfabricated structures with both static and radio frequency voltages. The results from these tests negate the concern over reduced rf voltage breakdown and in fact demonstrates breakdown voltages significantly above that typically required for ion trapping. This may allow ion traps to be designed to operate with higher voltages and greater ion-electrode separations, reducing anomalous heating. Lastly I present my work towards the implementation of magnetic fields gradients and microwaves on chip. This may allow coupling of the ions internal state to its motion using microwaves, thus reducing the requirements for the use of laser systems.
Among the various physical systems for quantum bit (qubit) implementation, trapped ion has drawn significant attention due to its long coherence time (in the second range) and high gate fidelity (>99.99% for single qubit gate). After years of careful development, the ion trap, from mechanically assembled linear trap to lithography-defined surface electrode ion trap, is compatible with CMOS fabrication, which opens the door for the high-resolution, high-repeatability and large-scale ion trap manufacturing. To date, the number of fully connected ion qubits in state-of-the-art ion trapping devices is ~10. However, to scale close to or even beyond the noisy intermediate-scale quantum regime (NISQ, ~100 ions), some challenges remain. One such challenge is to maintain the delicate control of multiple components over individual ion with increasing ion number. In such context, this thesis is committed to boost the scalability of ion trap by integrating advanced 3D interconnects (e.g., through silicon via) and other functional modules (e.g., silicon photonics and multilayer metallization). 3D interconnects are integrated in the half space underneath surface electrode, to replace conventional wire bonding that extends out of the surface. Silicon photonics (grating coupler and waveguide) in place of bulk optics and lenses are used for on-chip light routing and emission. Multilayer metallization is used to maintain the overall RF performance and enable high-density interconnection where necessary. Firstly, surface electrode ion traps on different substrates (namely high resistivity silicon, silicon with grounding plane and glass) are designed and fabricated. Standard CMOS back-end-of-line fabrication process on 12-inch wafer platform is employed. The electrical performances of different traps are compared in terms of leakage current (I-V), parasitic capacitance (C-V), on-chip RF loss (S-parameter) and post-packaging resonance. Though the leakage (at the order of 10-8 A) between neighboring electrodes is relatively high, ion trap on glass substrate demonstrates extremely small capacitance (<1 pF) and low RF loss (insertion loss of <0.05 dB at RF frequency of 50 MHz), as compared to the silicon counterparts. This is mainly due to excellent insulation property of glass. Following that, ion trapping test is performed on the glass trap and ions are successfully confined with an averaged lifetime of ~30 minutes (compatible with the 10-11 mbar vacuum level (10-13 Pa)). To simultaneously leverage the dielectric property of glass and the microfabrication compatibility of silicon, the integration of silicon ion trap and glass interposer is performed, between which TSV is used to build the vertical interconnection. Due to the incorporation of TSV, the original wire bonding pads as well as the connection circuits on the surface electrodes can be eliminated. As a result, the form factor of TSV integrated trap is reduced by ~10 times. Correspondingly, the parasitic capacitance between neighboring electrodes is reduced from >24 pF to 3 pF. Similarly, the insertion loss of TSV integrated trap drops to 0.11 dB, in sharp comparison to the previous traps on silicon substrates (up to 2.4 dB). Analytical models are built to respectively characterize the electrode capacitance and overall power loss, and a good agreement is achieved between the model and the measurement result. In addition, since TSV is located in the half space underneath the surface electrodes, the electrodes geometry design is enabled with high flexibility. Meanwhile, the laser obstruction issue due to the stick-out bonding wires has been resolved. In terms of the ion trapping performance, both the heating rate (17 quanta/ms for an axial frequency of 300 kHz) and the lifetime (~30 minutes) of TSV trap are comparable with non-cryogenic traps of similar dimensions. Moreover, a customized CPGA with patterned redistribution layer is used to locate TSV integrated trap directly in the absence of glass interposer, facilitating high-efficiency thermal management and upgrading the packaging flexibility. At the next stage, the co-integration of other functional modules such as silicon photonics and multilayer metallization with TSV trap is investigated. In silicon photonics module, waveguide and grating coupler are on-chip introduced in place of bulk optics to achieve localized light routing and emission. In multilayer metallization module, as a first step, a grounding plane is incorporated into TSV trap to shield the silicon substrate from RF signal, in which specific windows are patterned onto the plane to accommodate TSV and allow the transmission of lights. The compatibility between TSV/multilayer metallization and waveguide/grating coupler for electrical and optical (E/O) signal routing is demonstrated. The preliminary test result based on wafer frontside shows that a ~40% capacitance reduction is achieved, and the insertion loss further drops to 0.06 dB, close to the performance of glass trap. In addition, the simulation results on photonics components indicate that an overall coupling efficiency of <30 dB is obtained from the input fiber to the ion through the photonics circuit. However, the measured power loss for light with wavelength of 1092 nm is as high as 50 dB. The deviation between the simulation and measurement is largely due to the fabrication imperfection and the resultant sloped grating coupler profile. This thesis focuses on the scalability enhancement of ion trap by integrating TSV, silicon photonics and multilayer metallization into conventional ion trap. The results are promising and pave the way for the future large scale quantum computing based on trapped ion.
Microfabricated ion traps are an important tool in the development of scalable quantum systems. Tremendous advancements towards an ion quantum computer were made in the past decade and most requirements for a quantum computer have been fulfilled in individual experiments. Incorporating all essential capabilities in a fully scalable system will require the further advancement of established quantum information technologies and development of new trap fabrication techniques. In my thesis I will discuss the theoretical background and experimental setup required for the operation of ion traps. Measurement of the important ion trap heating rate was performed in the setup and I will discuss the results in more detail. I will give a review of microfabrication processes used for the fabrication of traps, outlining advantages, disadvantages and issues inherent to the processes. Following the review I will present my work on a concept for a scalable ion trap quantum system based on microwave quantum gates and shuttling through X-junctions. Many of the required building blocks, including ion trap structures with current-carrying wires intended to create strong magnetic field gradients for microwave gates were investigated further. A novel fabrication process was developed to combine current-carrying wires with advanced multilayered ion trap structures. Several trap designs intended for proof of principle experiments of high fidelity microwave gates, advanced detection techniques and shuttling between electrically disconnected ion traps will be presented. Also the electrode geometry of an optimized X-junction design with strongly suppressed rf barrier height will be presented. Further, I developed several modifications for the experimental setup to extend the existing capabilities. A plasma source capable of performing in-situ cleans of the trap electrode surfaces, which has been demonstrated to dramatically reduce the heating rate in ion traps, was incorporated. I will also present a vacuum system modification designed to cool ion traps with current-carrying wires and transport the generated heat out of the vacuum system. In addition a novel low-noise, high-speed, multichannel voltage control system was developed by me. The device can be used in future experiments to precisely shuttle ions from one trapping zone to another and also to shuttle ions through ion trap junctions. Lastly I will outline the process optimization and microfabrication of my ion trap designs. A novel fabrication process which makes use of the extremely high thermal conductivity of diamond substrates and combines it with thick copper tracks embedded in the substrate was developed. Large currents will be passed through the wires creating a strong and controllable magnetic field gradient. Ion trap designs with isolated electrodes connected via buried wires can be placed on top of the current-carrying wires, allowing the most advanced electrode designs to be fabricated with current-carrying wires.
Ions trapped in a quadrupole Paul trap have been considered one of the strong physical candidates to implement quantum information processing. This is due to their long coherence time and their capability to manipulate and detect individual quantum bits (qubits). In more recent years, microfabricated surface ion traps have received more attention for large-scale integrated qubit platforms. This paper presents a microfabrication methodology for ion traps using micro-electro-mechanical system (MEMS) technology, including the fabrication method for a 14 µm-thick dielectric layer and metal overhang structures atop the dielectric layer. In addition, an experimental procedure for trapping ytterbium (Yb) ions of isotope 174 (174Yb+) using 369.5 nm, 399 nm, and 935 nm diode lasers is described. These methodologies and procedures involve many scientific and engineering disciplines, and this paper first presents the detailed experimental procedures. The methods discussed in this paper can easily be extended to the trapping of Yb ions of isotope 171 (171Yb+) and to the manipulation of qubits.