Proper grounding between different ground planes in coplanar superconducting qubit circuits is important to avoid spurious resonances which increase decoherence. Here, the authors present a possible solution to suppress such undesired modes using superconducting aluminum air-bridges which have been fabricated on top of aluminum coplanar waveguide transmission lines. 3D electromagnetic simulations were done to guide the design of the air-bridges such that the input reflection (S11) of the bridges was kept at a minimum level. A fabrication method based on optical lithography techniques was developed and it resulted in air-bridges with a height of approximately 10 μm and lengths of up to 500 μm. The method can be generalized to arbitrary length air-bridge with heights even exceeding 15 μm.
Proper grounding between different ground planes in coplanar superconducting qubit circuits is important to avoid spurious resonances which increase decoherence. Here, the authors present a possible solution to suppress such undesired modes using superconducting aluminum air-bridges which have been fabricated on top of aluminum coplanar waveguide transmission lines. 3D electromagnetic simulations were done to guide the design of the air-bridges such that the input reflection (S11) of the bridges was kept at a minimum level. A fabrication method based on optical lithography techniques was developed and it resulted in air-bridges with a height of approximately 10 μm and lengths of up to 500 μm. The method can be generalized to arbitrary length air-bridge with heights even exceeding 15 μm.
Superconducting quantum electrical circuit based on Co-planar waveguide technology is considered one of the most promising candidates for practical realization of a\nquantum computer in future. For purpose of designing a multi-qubit quantum processor which is the heart of a quantum computer, it is required to couple qubits to a large number of superconducting transmission lines and resonators. Placing all these transmission lines and\nresonators in a practical design unavoidably creates bending and discontinuities in the ground\nplanes which have higher order parasitic modes that can be excited. These undesired parasitic\nmodes are detrimental for quantum measurement, for example during readout of a qubit.\nUnwanted modes can easily interfere with a resonator frequency when coupling to the qubit.\nThese parasitic modes can propagate throughout CPW structure and make unequal ground\npotential at the corresponding ground planes. The easiest way to suppress these parasitic\nmodes is to connect two unequal ground potential with superconducting air-bridges in order\nto bring them under equal potential in superconducting state. However, connecting airbridges on top of CPW adds shunt capacitor which may cause undesired reflection in the\nCPW.\nIn this thesis work, we designed superconducting air-bridges on top of\nsuperconducting CPW transmission line which is a subsystem of large quantum electrical\ncircuit. Our focus was to reduce added shunt capacitance by choosing the right height of these\nair-bridges. To keep the reflection coming from the air-bridge at minimum level, an airbridge\nheight of 8.5μm~15μm was chosen. The performance was verified by EM simulation\nand these heights were selected for device fabrication. We developed a new fabrication\nmethod for processing 8.5μm~15μm high aluminum air-bridges for quantum electrical\ncircuits. The method is compatible with the quantum circuit and easily reproducible. Finally,\ninput reflection measurement (S11) at cryogenic temperature was performed for 8.5μm high,\n300μm long aluminum air-bridges with aluminum CPW transmission line. Negligible amount\nof input reflection (S11) was observed from these measurements which is consistent with the\nresult of EM simulation.
Superconducting coplanar waveguide (CPW) can be widely used as two-dimensional (2D) resonator, transmission line or feedline, providing an important component for superconducting quantum circuit which is a promising candidate for quantum information processing. Due to the discontinuities and asymmetries in the ground planes, CPW usually exhibits the spurious resonance, which is a common source of decoherence in circuit quantum electrodynamics experiments. To mitigate the spurious resonance, we fabricated superconducting aluminum air-bridges on Nb CPW. The fabricated air-bridges are approximately 3 μm high and up to 120 μm long. Compared with other methods, the fabrication procedures of our air-bridges are simpler, and the air-bridge can withstand strong ultrasound.
Extraneous high frequency chip modes parasitic to superconducting quantum circuits can result in decoherence when these modes are excited. To suppress these modes, superconducting air bridges (AB) are commonly used to electrically connect ground planes together when interrupted by transmission lines. Here, we demonstrate the use of two-photon photolithography to build a supporting 3D resist structure in conjunction with a liftoff process to create AB. The resulting aluminum AB have a superconducting transition temperature of Tc=1.08 K and exhibit good mechanical strength up to lengths of 100 μm. A measurable amount of microwave loss is observed when 35 AB were placed over a high-Q Ta quarter-wave coplanar waveguide resonator.
In superconducting quantum devices, air bridges enable increased circuit complexity and density, and mitigate the risk of microwave loss arising from mode mixing. We implement aluminum air bridges using a simple process based on single-step electron-beam gradient exposure. The resulting bridges have sizes ranging from 20 µm to 100 µm, with a yield exceeding 99% for lengths up to 36 µm. When used to connect ground planes in coplanar waveguide resonators, the induced loss contributed to the system is negligible, corresponding to a loss per bridge less than 1.0×10−8. The bridge process is compatible with Josephson junctions and allows for the simultaneous creation of low loss bandages between superconducting layers.
In the upcoming decades quantum technologies, especially quantum computation, will have a strong influence on industrial, technological, economic, and social progress and are, therefore, considered to be one of the key technologies. The fundamental building blocks for quantum computation are quantum bits (qubits). The superconducting platform offers one of the most promising implementations due to its monolithic character and potential for scalability. Present research around the world primarily focusses on scaling up the number of qubits, so reliable wafer-scale fabrication technologies are mandatory. In this paper, we present our recent developments on wafer-scale fabrication of superconducting quantum circuits including Josephson junctions by the Manhattan-type technology. We discuss fabrication parameters as well as electrical characterization. For arrays out of 50 Josephson junctions with structure dimensions of 200 nm × 200 nm, we achieve a critical current standard deviation of approx. 3% on-chip and 7% on-wafer. We also show first measurement results of so fabricated transmon-type qubits with relaxation and decoherence times ofT1= 12.5 µs andT2= 15.0 µs, respectively. With an increasing number of superconducting qubits and, thus, their input and read-out lines, new challenges arise: Crosstalk between qubits, unwanted modes in the qubit environment, and required interconnections. One way to counteract is the implementation of low inductance connections across coplanar waveguides. This can be realized by aluminum air bridges. In this paper we discuss the air bridges’ fabrication parameters and the impact on the integrated circuits’ elements, e.g., Josephson junctions. We show electrical and superconducting measurements with critical temperatures and critical currents ofTc> 1.0 K andIc> 0.6 mA, respectively.
Scaling up superconducting quantum processors necessitates the use of a high routing density for readout and control lines, relying on low-loss interconnects to maintain design flexibility and device performance. We propose and demonstrate a universal subtractive fabrication process for air bridges based on an aluminum hard mask and niobium as the superconducting film. Using this technology, we fabricate superconducting coplanar waveguide resonators incorporating several niobium air bridges in and across their center conductors. Through rigorous cleaning methods, we achieve mean internal quality factors in the single-photon limit exceeding Q int = 8.2 × 10 6 . Notably, the loss per air bridge remains below the detection threshold of the resonators. Due to the larger superconducting energy gap of niobium, compared with conventional aluminum air bridges, our approach enables stable performance at elevated temperatures and magnetic fields, which we experimentally confirm in temperatures up to 3.9 K and in a magnetic field of up to 1.60 T. Additionally, we utilize air bridges to realize low-loss vacuum-gap capacitors and demonstrate their successful integration in transmon qubits by achieving median qubit lifetimes of T 1 = 51.6 μ s .