GAIN BANDWIDTH OF PHONON-COOLED HEB MIXER MADE OF NBN THIN FILM WITH MgO BUFFER LAYER ON Si.

Yu. B. Vachtomin, Matvey I. Finkel, Sergey V. Antipov, Boris M. Voronov, K. V. Sminov, N. Kaurova, Vladimir Drakinski, Alex Goltsman

Published Mar 1, 2002• 11 citations
OpenAlex

Abstract

We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate. Introduction. In the last years, the development of HEB mixers has reached such a high level that these devices can be successfully utilized in heterodyne receivers of THz frequency range. Their high sensitivity and low LO power make them suitable for radioastronomic observations on space- and airbom platforms. An NbN HEB mixer seems to be a

Related papers

NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers

Gregory N Gol'tsman, Yu. B. Vachtomin, Sergey V. Antipov +8 more

We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.

Proceedings of SPIE, the International Society for Optical Engineering/Proceedings of SPIE•Mar 25, 2005•11 citations

Gain bandwidth of NbN HEB mixers on GaN buffer layer operating at 2 THz local oscillator frequency

Sergey V. Antipov, Andrey Trifonov, Sascha Krause +4 more

In this paper, we present IF bandwidth measurement results of NbN HEB mixers, which are employing NbN thin films grown on a GaN buffer-layer. The HEB mixers were operated in the heterodyne regime at a bath temperature of approximately 4.5 K and with a local oscillator operating at a frequency of 2 THz. A quantum cascade laser served as the local oscillator and a reference synthesizer based on a BWO generator (130-160 GHz) and a semiconductor superlattice (SSL) frequency multiplier was used as a signal source. By changing the LO frequency it was possible to record the IF response or gain bandwidth of the HEB with a spectrum analyzer at the operation point, which yielded lowest noise temperature. The gain bandwidth that was recorded in the heterodyne regime at 2 THz amounts to approximately 5 GHz and coincides well with a measurement that has been performed at elevated bath temperatures and lower LO frequency of 140 GHz. These findings strongly support that by using a GaN buffer-layer the phonon escape time of NbN HEBs can be significantly lower as compared to e.g. Si substrate, thus, providing higher gain bandwidth.

•Jan 1, 2017•0 citations

Noise performance of quasioptical ultrathin NbN hot-electron bolometer mixer at 2.5 and 3.8 THz

Sergey V. Antipov, Yu.B. Vachtornin, S. N. Maslennikov +5 more

To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.

International Kharkiv Symposium on Physics and Engineering of Microwaves, Millimeter and Submillimeter Waves•Oct 26, 2004•0 citations

IF bandwidth and noise temperature measurements of NbN HEB mixers on MgO substrates

Shigehito Miki, Yoshinori Uzawa, Akira Kawakami +1 more

We report the fabrication and testing of hot electron bolometric mixers with an ultrathin NbN film as heterodyne receivers operating at terahertz frequencies. We found that the quality of the NbN strip is usually degraded by damage resulting from the fabrication process, and we developed a process for reducing such damage. We also fabricated HEB mixers with a new structure in order to study the IF bandwidth determined by the original quality of the NbN thin films. Investigations at 100 GHz revealed that the widest IF bandwidth of 2.0 GHz was obtained by a mixer based on a 2.8 nm-thick NbN film. An HEB mixer based on the 2.8 nm-thick NbN film was also fabricated and evaluated. The receiver noise temperature at 900 GHz was 780 K, the absorbed LO power was about 400 nW, and the conversion gain was -13 dB.

IEEE Transactions on Applied Superconductivity•Mar 1, 2001•20 citations

Study of the IF bandwidth of NbN HEB mixers based on crystalline quartz substrate with an MgO buffer layer

Denis Meledin, Edward Tong, R. Blundell +4 more

In this paper, we present the results of IF bandwidth measurements on 3-4 nm thick NbN hot electron bolometer waveguide mixers, which have been fabricated on a 200-nm thick MgO buffer layer deposited on a crystalline quartz substrate. The 3-dB IF bandwidth, measured at an LO frequency of 0.81 THz, is 3.7 GHz at the optimal bias point for low noise receiver operation. We have also made measurements of the IF dynamic impedance, which allow us to evaluate the intrinsic electron temperature relaxation time and self-heating parameters at different bias conditions.

IEEE Transactions on Applied Superconductivity•Jun 1, 2003•29 citations

NbN FILM DEVELOPMENT FOR PHONON-COOLED HEB DEVICES

Eyal Gerecht, Ashok K. Bhupathiraju, Erich N. Grossman +4 more

Superconducting Hot-electron Bolometric (HE.B) mixers employing thin films ofNbN have become the devices of choice for heterodyne detection at tera,hertz frequen- cies. HEB mixers are inherently insensitive to the bandgap frequency of the superconducting material used in the device, in contrast to SIS mixers,. We have developed a fabrication pro- cess for thin NbN films at the National Institute of Standards and Technology in Boulder, CO. A two-fold approach can be taken. The first is to maximize the critical temperature of the superconducting device by growing thicker films at the expense of IF bandwidth, whereas the second approach focuses on maximizing the IF bandwidth at the expense of the critical tem- perature. So far, we have developed a film-deposition process utilizing our DC reactive mag- netron sputtering chamber. By current-biasing the RF plasma in a mixture of Ar and N2, while using a Nb target, we can control the film stoichiometry and produce films with thicknesses of 5 nm. The films are deposited on MgO substrates that are heated to about 800 °C during depo- sition. A typical critical temperature (TO is about 10 K and the transition width is very small (0.5 K). The films are evaluated by measuring their superconducting characteristics as well as their thickness and surface roughness by means of AFM analysis. Phonon-cooled HEB devices are fabricated from the films to study their performance as HEB mixers. The device fabrication process at UMass/Amherst involves lift-off lithography of the antenna (gold), and Reactive ion etching (R1E) or wet etching of the NbN. The I-V char- acteristics and noise temperatures of the devices were measured in order to determine their quality for PHEB applications.

•Mar 1, 2002•1 citation
We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate. Introduction. In the last years, the development of HEB mixers has reached such a high level that these devices can be successfully utilized in heterodyne receivers of THz frequency range. Their high sensitivity and low LO power make them suitable for radioastronomic observations on space- and airbom platforms. An NbN HEB mixer seems to be a
We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
In this paper, we present IF bandwidth measurement results of NbN HEB mixers, which are employing NbN thin films grown on a GaN buffer-layer. The HEB mixers were operated in the heterodyne regime at a bath temperature of approximately 4.5 K and with a local oscillator operating at a frequency of 2 THz. A quantum cascade laser served as the local oscillator and a reference synthesizer based on a BWO generator (130-160 GHz) and a semiconductor superlattice (SSL) frequency multiplier was used as a signal source. By changing the LO frequency it was possible to record the IF response or gain bandwidth of the HEB with a spectrum analyzer at the operation point, which yielded lowest noise temperature. The gain bandwidth that was recorded in the heterodyne regime at 2 THz amounts to approximately 5 GHz and coincides well with a measurement that has been performed at elevated bath temperatures and lower LO frequency of 140 GHz. These findings strongly support that by using a GaN buffer-layer the phonon escape time of NbN HEBs can be significantly lower as compared to e.g. Si substrate, thus, providing higher gain bandwidth.
To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.
We report the fabrication and testing of hot electron bolometric mixers with an ultrathin NbN film as heterodyne receivers operating at terahertz frequencies. We found that the quality of the NbN strip is usually degraded by damage resulting from the fabrication process, and we developed a process for reducing such damage. We also fabricated HEB mixers with a new structure in order to study the IF bandwidth determined by the original quality of the NbN thin films. Investigations at 100 GHz revealed that the widest IF bandwidth of 2.0 GHz was obtained by a mixer based on a 2.8 nm-thick NbN film. An HEB mixer based on the 2.8 nm-thick NbN film was also fabricated and evaluated. The receiver noise temperature at 900 GHz was 780 K, the absorbed LO power was about 400 nW, and the conversion gain was -13 dB.
In this paper, we present the results of IF bandwidth measurements on 3-4 nm thick NbN hot electron bolometer waveguide mixers, which have been fabricated on a 200-nm thick MgO buffer layer deposited on a crystalline quartz substrate. The 3-dB IF bandwidth, measured at an LO frequency of 0.81 THz, is 3.7 GHz at the optimal bias point for low noise receiver operation. We have also made measurements of the IF dynamic impedance, which allow us to evaluate the intrinsic electron temperature relaxation time and self-heating parameters at different bias conditions.
Superconducting Hot-electron Bolometric (HE.B) mixers employing thin films ofNbN have become the devices of choice for heterodyne detection at tera,hertz frequen- cies. HEB mixers are inherently insensitive to the bandgap frequency of the superconducting material used in the device, in contrast to SIS mixers,. We have developed a fabrication pro- cess for thin NbN films at the National Institute of Standards and Technology in Boulder, CO. A two-fold approach can be taken. The first is to maximize the critical temperature of the superconducting device by growing thicker films at the expense of IF bandwidth, whereas the second approach focuses on maximizing the IF bandwidth at the expense of the critical tem- perature. So far, we have developed a film-deposition process utilizing our DC reactive mag- netron sputtering chamber. By current-biasing the RF plasma in a mixture of Ar and N2, while using a Nb target, we can control the film stoichiometry and produce films with thicknesses of 5 nm. The films are deposited on MgO substrates that are heated to about 800 °C during depo- sition. A typical critical temperature (TO is about 10 K and the transition width is very small (0.5 K). The films are evaluated by measuring their superconducting characteristics as well as their thickness and surface roughness by means of AFM analysis. Phonon-cooled HEB devices are fabricated from the films to study their performance as HEB mixers. The device fabrication process at UMass/Amherst involves lift-off lithography of the antenna (gold), and Reactive ion etching (R1E) or wet etching of the NbN. The I-V char- acteristics and noise temperatures of the devices were measured in order to determine their quality for PHEB applications.