A photoluminescence (PL) and magnetic resonance investigation of a defect in chlorine-implanted 4H-SiC is presented. This Cl-related center emits light at telecom wavelengths with zero-phonon lines in the range 1350-1540 nm. Its four configurations exhibit stable PL spectra characterized by narrow zero-phonon lines. For the two configurations that emit light at the C-band, a Debye-Waller factor in the range 22-25% is estimated. Optically detected magnetic resonance confirms that the Cl-related center is spin active and stable at room temperature with the zero-field splitting in the range of 1.0-1.4 GHz. The combined optical and spin properties suggest this center to be a highly promising candidate for scalable quantum networks.
A photoluminescence (PL) and magnetic resonance investigation of a defect in chlorine-implanted 4H-SiC is presented. This Cl-related center emits light at telecom wavelengths with zero-phonon lines in the range 1350-1540 nm. Its four configurations exhibit stable PL spectra characterized by narrow zero-phonon lines. For the two configurations that emit light at the C-band, a Debye-Waller factor in the range 22-25% is estimated. Optically detected magnetic resonance confirms that the Cl-related center is spin active and stable at room temperature with the zero-field splitting in the range of 1.0-1.4 GHz. The combined optical and spin properties suggest this center to be a highly promising candidate for scalable quantum networks.
Realization of quantum memory with a photonic interface in the telecommunication bands in a wafer-scalable platform is a central requirement for long-distance quantum networks. Silicon carbide (SiC) provides a technologically mature host for integrated quantum photonics, yet only a limited number of defects combine spin functionality with telecom emission. Here we report on chlorine-based defects in 4H-SiC as a platform for telecom-band quantum memory. The emission of these defects spans the entire telecommunication range with zero-phonon lines in the O- and C-bands and a Debye-Waller factor of up to 39%. Time-resolved photoluminescence measurements reveal a short excited-state lifetime in the sub-nanosecond range. We demonstrate that these defects are spin-active even at room temperature, exhibiting optically detected magnetic resonances (ODMR) in the sub-GHz frequency range. Using ODMR spectroscopy and Ramsey interferometry, we resolve the hyperfine structure arising from the interaction with 35Cl nuclear spins. The ODMR spectra exhibit complex behaviour in an external magnetic field due to mixing of electron-nuclear spin states, which is well reproduced by our simulations. The spin relaxation and coherence times are in the sub-microsecond range, limited by rapid quenching of the ODMR contrast and attributed to charge-state metastability. The combination of telecom-band emission, coherent spin control and compatibility with wafer-scale fabrication positions Cl-related defects in SiC as a promising platform for chip-scale quantum memories with spin-photon interfaces operating in the fiber-optic telecommunication windows.
Abstract Realization of quantum memory with a photonic interface in the telecommunication bands in a wafer-scalable platform is a central requirement for long-distance quantum networks. Silicon carbide (SiC) provides a technologically mature host for integrated quantum photonics, yet only a limited number of defects combine spin functionality with telecom emission. Here we report on chlorine-based defects in 4H-SiC as a platform for telecom-band quantum memory. The emission of these defects spans the entire telecommunication range with zero-phonon lines in the O- and C-bands and a Debye-Waller factor of up to 39 %. Time-resolved photoluminescence measurements reveal a short excited-state lifetime in the sub-nanosecond range. We demonstrate that these defects are spin-active even at room temperature, exhibiting optically detected magnetic resonances (ODMR) in the sub-GHz frequency range. Using ODMR spectroscopy and Ramsey interferometry, we resolve the hyperfine structure arising from the interaction with Cl-35 nuclear spins. The ODMR spectra exhibit complex behaviour in an external magnetic field due to mixing of electron-nuclear spin states, which is well reproduced by our simulations. The spin relaxation and coherence times are in the sub microsecond range, limited by rapid quenching of the ODMR contrast and attributed to charge-state metastability. The combination of telecom-band emission, coherent spin control and compatibility with wafer-scale fabrication positions Cl-related defects in SiC as a promising platform for chip-scale quantum memories with spin-photon interfaces operating in the fiber-optic telecommunication windows.
Abstract Optically active spin systems in silicon are attracting growing interest for quantum technologies, driven by their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces, which allow coupling between spin degrees of freedom and photons are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While a variety of optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band (1565–1625 nm)—a key wavelength range for low-loss fiber-based communication—has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance (ODMR), enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Vanadium color centers in silicon carbide (SiC) offer telecom O-band emission, sub-microsecond optical lifetimes, and second-scale spin relaxation times, rendering them promising candidates for quantum network nodes. However, efficient photon extraction from the high-refractive-index SiC host remains challenging. Here, we introduce a silicon-on-SiC heterogeneous photonic platform in which silicon nanocavities evanescently couple to shallow vanadium dopants in commercial 4H-SiC, enabling efficient zero-phonon line (ZPL) collection under resonant excitation. In as-grown ensembles, we observe Purcell-enhanced photoluminescence with transient spectral hole burning linewidths of 50 MHz on microsecond timescales. In dilute implanted samples, we isolate individual vanadium centers with high-purity single photon emission and a Purcell-enhanced lifetime of 109 ns. The entire optical interface operates through a single lensed fiber, including a 905 nm repump laser that recovers the vanadium charge state with 95% efficiency. These results establish Si-on-SiC as a scalable, foundry-compatible platform for telecom-wavelength spin-photon interfaces.
Silicon-based quantum technologies have gained increasing attention due to their potential for large-scale photonic integration, long spin coherence times, and compatibility with CMOS fabrication. Efficient spin-photon interfaces are crucial for quantum networks, enabling entanglement distribution and information transfer over long distances. While several optically active quantum emitters in silicon have been investigated, no spin-active defect with optical transitions in the telecom L-band-a key wavelength range for low-loss fiber-based communication-has been experimentally demonstrated. Here, we demonstrate the optical detection of spin states in the C center, a carbon-oxygen defect in silicon that exhibits a zero-phonon line at 1571 nm. By combining optical excitation with microwave driving, we achieve optically detected magnetic resonance, enabling spin-state readout via telecom-band optical transitions. These findings provide experimental validation of recent theoretical predictions and mark a significant step toward integrating spin-based quantum functionalities into silicon photonic platforms, paving the way for scalable quantum communication and memory applications in the telecom L-band.
Silicon is an attractive host for scalable quantum photonics, but the absence of bright telecom-band emitters with optically addressable spin states has limited its use for spin-photon interfaces. Here we demonstrate the Al1-center, an aluminum--carbon defect in silicon, as a bright waveguide-integrated single-photon emitter with a ground-state spin. Using isotopically purified silicon-on-insulator nanophotonic devices, we isolate individual Al1-centers and observe high-purity single-photon emission with g(2)(0)=0.04 without background subtraction. Time-resolved photoluminescence spectroscopy reveals a fast excited-state lifetime of 135 ns, nearly an order of magnitude shorter than the benchmark provided by the well-studied T-center. Resonant photoluminescence excitation measurements further resolve the zero-phonon transition and reveal a narrow homogeneous linewidth reaching 47 MHz, threefold narrower than the T-center under comparable temperature. Through magneto-optical spectroscopy, we resolve the spin-dependent transitions of the bound-exciton manifold and achieve spin-selective optical pumping, fulfilling the prerequisite for quantum state initialization and readout. These results establish the Al1-center as a bright telecom-band spin-photon interface in silicon photonics and introduce a promising platform for integrated quantum networks.