Terahertz near-field imaging of sidewall-induced losses in superconducting qubits
Richard H. J. Kim, Samuel Haeuser, J.-M. Park, Randall K. Chan, Jin‐Su Oh, Thomas Koschny, Lin Zhou, Matthew Joseph Kramer, Akshay A. Murthy, Mustafa Bal, Francesco Crisa, Sabrina Garattoni, Shaojiang Zhu, Andrei Lunin, David I. Olaya, P. F. Hopkins, Alexander Romanenko, Anna Grassellino, Jigang Wang
Correlating superconducting qubit performance with advanced materials analysis is a key strategy for improving coherence. Existing diagnostics for key properties, such as dielectric loss, structural discontinuity, and interface heterogeneity, often rely on destructive electron microscopy or low-throughput millikelvin measurements. Here, we demonstrate noninvasive terahertz (THz) nano-imaging/spectroscopy of encapsulated niobium transmon qubits as a high-throughput proxy for performance evaluation. We identify large variations in sidewall near-field signals, implicating sidewall loss and discontinuity as major coherence limiters, and also use THz hyperspectral line scans to probe dielectric responses and field participation at Al junction interfaces.
Correlating superconducting qubit performance with advanced materials analysis is a key strategy for improving coherence. Existing diagnostics for key properties, such as dielectric loss, structural discontinuity, and interface heterogeneity, often rely on destructive electron microscopy or low-throughput millikelvin measurements. Here, we demonstrate noninvasive terahertz (THz) nano-imaging/spectroscopy of encapsulated niobium transmon qubits as a high-throughput proxy for performance evaluation. We identify large variations in sidewall near-field signals, implicating sidewall loss and discontinuity as major coherence limiters, and also use THz hyperspectral line scans to probe dielectric responses and field participation at Al junction interfaces.
Abstract The fundamental challenge underlying superconducting quantum computing is to characterize heterogeneity and disorder that lead to local electric field concentration, charge scattering, dissipation and ultimately decoherence. It is particularly challenging to probe deep sub-wavelength electric field distribution under electromagnetic wave coupling at individual nano-junctions and correlate them with structural imperfections from interface and boundary, ubiquitous in Josephson junctions used in transmon qubits. A major obstacle lies in the fact that conventional microscopy tools are incapable of measuring {\em simultaneous} at nanometer and terahertz, ``nano-THz” scales, which often associate with frequency-dependent charge scattering in nano-junctions. Here we directly visualize interface nano-dipole near-field distribution of individual Al/AlOx/Al junctions used in transmon qubits. Our THz nanoscope images show a remarkable asymmetry across the junction in electromagnetic wave-junction coupling response that manifests as ``hot" vs ``cold" cusp spatial electrical field structures and correlates with defected boundaries from the multi-angle deposition processes in JJ fabrication inside qubit devices. The asymmetric nano-dipole electric field contrast also correlates with distinguishing, ``overshoot" frequency dependence that characterizes the charge scattering and dissipation at nanoscale, hidden in responses from topographic, structural imaging and spatially-averaged techniques. The scheme can be extended to guide qubit nano-fabrication for ultimately optimizing qubit coherence times.
In superconducting transmon qubits, macroscopic characterization is the primary method for probing performance metrics, such as relaxation T1 and dephasing T2 times, resonance frequency, and quality factor. While these measurements can aid our understanding of the dielectric loss of a transmon, they do not allow us to characterize the structural and chemical inhomogeneity of the interfaces which directly impacts this energy loss. These fundamental materials problems must be studied using transmission electron microscopy (TEM) to provide insight into these defects across different qubit interfaces at an atomic scale. In this contribution, we will examine qubits, such as those shown in Figure 1, fabricated at Fermi National Accelerator Laboratory (SQMS Center) [1]. The qubit devices consist of superconducting metal base layers, typically sputter deposited Nb or Ta, and Al/AlOx/Al junctions, where the AlOx barrier is roughly 3nm in thickness and prepared through in-situ oxidation [2]. Characterizing this system prior to its integration within a superconducting radio frequency cavity establishes a baseline for the system, allowing us to isolate fabrication-induced defects before they manifest in performance degradation during quantum measurements. With the samples and fabrication process well known on a macroscopic scale, we study the atomic structure and chemistry of different heterointerfaces within the Josephson junction (JJ) of the transmon qubit and between the sapphire substrate and Nb resonator pads to identify potential defects contributing to the decoherence for qubits constructed with particular geometries. To resolve these defects, atomic-resolution imaging, energy-dispersive X-ray spectroscopy (EDS), and electron-energy loss spectroscopy (EELS) are performed using the JEOL-ARM200CF, an aberration-corrected scanning transmission electron microscope (STEM). Figure 2 provides a clear image of the stacked layers formed as the JJ, but with the addition of a platinum and carbon protective coating added during the focus ion beam (FIB) milling process to preserve pristine Al/AlOx/Al interfaces. 4D-STEM approaches, such as ptychography, orientation mapping and nanoscale diffraction will be employed to further study the layered interfaces and defects in real space and reciprocal space. These techniques can also provide insight into any damage that incurs during lamella preparation using the FIB [3]. Magnetic field-free atomic resolution imaging, differential phase contrast mapping, and monochromated EELS can be achieved using the new MARS-MONO STEM (JEM-Z200MF) without inducing current fluctuations or magnetic field related distortions [4]. By integrating this work across the functional interfaces of the transmon qubits and their different geometries, we will identify possible structural and chemical defects which limit device performance using our multi-modal approach [5]. SQMS fabricated transmon qubits fabricated on HEMEX sapphire substrate imaged via a) ZEISS optical microscope, b) SEM and c) EDS. TEM image of Josephson Junction layered interface at on JEOL-ARM200CF on the ClearView camera with a 200kV accelerating voltage.
times 2 to 5 times longer than baseline niobium qubit devices with native niobium oxides. When capping niobium with tantalum, we obtain median qubit lifetimes above 200 microseconds. Our comparative structural and chemical analysis suggests that amorphous niobium oxides may induce higher losses compared to other amorphous oxides. These results are in line with high-accuracy measurements of the niobium oxide loss tangent obtained with ultra-high Q superconducting radiofrequency (SRF) cavities. This new surface encapsulation strategy enables even further reduction of dielectric losses via passivation with ambient-stable materials, while preserving fabrication and scalable manufacturability thanks to the compatibility with silicon processes.
Superconducting qubit technology is among the most promising hardware platform for quantum computing due to its fast gate operation, manufacturing scalability, and architectural flexibility [1]. A key figure of merit that dictates quantum computing functionality is the qubit’s coherence time, which needs to be maximized in order to bring quantum computing to the practical and scalable realm [2]. In particular, the T1 relaxation time—now on the order of milliseconds—can be enhanced with materials engineering, as amorphous dielectrics and crystallographic defects, among other factors, are known to induce decoherence [3-7]. Current state-of-the-art superconducting qubit devices use amorphous AlOx sandwiched between two superconducting Al electrodes as the Josephson junction (JJ), a key element in the transmon qubit, but amorphous dielectrics introduce two-level system (TLS) loss that underlie decoherence [8]. For this reason, numerous efforts have explored crystalline dielectrics as a replacement for amorphous AlOx, since single-crystal materials do not suffer from the lack of long-range order and sub-stoichiometry that comprise TLS defects [9-12]. However, none of these alternative materials choices have been able to surpass, let alone replicate, the performance of Al-AlOx-Al JJs. In this work, we fabricate superconducting quantum devices using a novel heteroepitaxial TiN/γ-Al2O3/TiN tri-layer stack grown on sapphire (Fig. 1a) and find that the measured microwave loss of the single-crystal γ-Al2O3 dielectric is lower than that of amorphous AlOx by two orders of magnitude. For qubits made with this tri-layer to transcend the coherence of incumbent Al-AlOx-Al, the structural, chemical, and electronic defects that induce TLS loss in these materials need to be well understood. Towards this end, we combine scanning transmission electron microscopy (STEM) and scanning electron microscopy (SEM) methods to highlight structural and interfacial complexity across length scales, ultimately identifying loss sources in the TiN/γ-Al2O3/TiN heteroepitaxial tri-layer. With atomic-resolution imaging and four-dimensional (4D-)STEM nanobeam electron diffraction (NBED), we find that the dielectric γ-Al2O3 layer, though single-crystalline (Fig. 1b), suffers from the formation of antiphase boundaries (Fig. 1c), which can host strong local electric fields and enhance lossy dielectric response [13]. Correlated with these nanoscale planar defects is uniformly distributed elastic strain, on the order of 6%, between the lattice-mismatched γ-Al2O3 and TiN (Fig. 1d). In other words, the dielectric layer is fully strained to match the underlying metal layer; such high strain can distort local bonding environments and thus create new TLSs or shift existing TLSs into resonance. Beyond imperfections within the bulk of the dielectric layer, there are noteworthy interfacial defects: roughening of both TiN/γ-Al2O3 interfaces deviate from atomically flat boundaries (Fig. 1c), while anion interdiffusion across both interfaces, as evident from core-loss electron energy-loss spectral (EELS) maps (Fig. 1e), leave behind vacancies and undercoordinated metal atoms, thereby creating 1.5 – 2 nm nonstoichiometric diffuse interfacial layers, both of which can cause TLS loss. In the superconducting TiN layers, we again use NBED to identify 180°-reflected specular twinned domains, indicating distinct heteroepitaxial relationships of [111]TiN//[0006]Al2O3 and [002¯]TiN//[22¯02¯]Al2O3 (Fig. 2a) [14]. Crystal twinning of the TiN epilayer is not only spatially distributed at the nanoscale, as shown using virtual dark-field (VDF) images (Fig. 2b), but is also widespread at the microscale, as shown using SEM electron backscatter diffraction (EBSD) (Fig. 2c). While microwave performance is not limited by a single factor, it is clear that defective quantum microstructure across length scales collectively contribute to dielectric loss, and in turn, TLS-related decoherence. By correlating nanoscale crystallographic and spectroscopic information with microscale diffraction measurements, our work can guide interface engineering during material growth, paving the way towards further improvements in quantum device performance. Cross-sectional samples were prepared by subsequent 30 kV, 8 kV and 5 kV Xe+ plasma focused ion beam (FIB) using the Thermo Scientific Helios 5 Hydra CX DualBeam Plasma FIB/SEM. Samples were then plasma cleaned using South Bay Technology PC-2000 Plasma Cleaner with a 3:1 mixture of Ar:O2 gas at 20∼40 W RF power for 15 s at 150 mTorr. High-angle annular dark-field (HAADF-) and annular bright-field (ABF-) STEM images were collected on a probe-corrected JEOL JEM-ARM200CF S/TEM operating at 200 kV using JEOL detectors. The STEM convergence angle, HAADF collection angle, and ABF collection angle were 27 mrad, 90 – 370 mrad, and 23 mrad, respectively. EELS data were collected on a JEOL JEM-ARM300F GrandARM S/TEM operating at 300 kV using the Gatan GIF Continuum K3 IS system. The data were collected using a 2.5 mm aperture and a 750 eV wide energy slit at a dispersion of 0.18 eV/Ch and a camera length of 2 cm. 4D-STEM data were collected on the same microscope and detector system using a 0.5 – 1.5 mrad convergence angle and a 20 eV wide energy slit at a camera length of 4 cm. All STEM data processing was performed using the Gatan Microscopy Suite software. Top-down EBSD measurements were performed in the Thermo Scientific Helios 5 CX DualBeam FIB/SEM at 25 kV using the Oxford Symmetry S3 detector. EBSD data processing was performed using the Oxford AZtecCrystal software [15]. Defects in γ-Al2O3. a) HAADF-STEM image of a TiN/γ-Al2O3/TiN tri-layer stack on a α-Al2O3 (0001) substrate. The thickness of γ-Al2O3 is approximately 13.5 nm. b) 4D-STEM NBED pattern of the γ-Al2O3 layer, confirming the {111} out-of-plane orientation. c) Fourier-filtered atomic-resolution ABF-STEM image of the γ-Al2O3 dielectric layer, taken from the cyan-colored square region in a), emphasizing the planar defects along both TiN/γ-Al2O3 interfaces and within the γ-Al2O3 layer itself–interfacial roughness (yellow lines) and antiphase boundaries (colored parallelograms), respectively. The scale bar is 2 nm. d) In-plane and out-of-plane strain maps of the heteroepitaxial tri-layer stack, with approximately 6.5∼6.8% strain in both directions. The units of the intensity bar are such that 100% strain would be equivalent to 1.0. e) STEM-EELS maps of Ti-L2,3, N-K, and O-K edges, along with a superimposed image of the three, taken from the same region as c). The scale bars are all 5 nm. Defects in TiN. a) 4D-STEM NBED patterns and b) VDF images of nanoscale TiN {111} and {002} twins. c) SEM EBSD pole figures in the three face-centered cubic crystallographic directions, revealing that the 60° rotation twinning behavior (with the [111] twin axis) is spread across the microscale.
Superconducting quantum circuits are one of the leading quantum computing platforms. To advance superconducting quantum computing to a point of practical importance, it is critical to identify and address material imperfections that lead to decoherence. Here, we use terahertz scanning near-field optical microscopy to probe the local dielectric properties and carrier concentrations of wet-etched aluminum resonators on silicon, one of the most characteristic components of the superconducting quantum processors. Using a recently developed vector calibration technique, we extract the THz permittivity from spectroscopy in proximity to the microwave feedline. Fitting the extracted permittivity to the Drude model, we find that silicon in the etched channel has a carrier concentration greater than buffer oxide etched silicon and we explore post-processing methods to reduce the carrier concentrations. Our results show that near-field THz investigations can be used to quantitatively evaluate and identify inhomogeneities in quantum devices.
While significant strides have been made to increase the coherence time of superconducting qubits, further advancements are essential for realizing scalable quantum computing. Decoherence is often a result of loss and noise stemming from two-level systems and excess quasiparticles, arising due to material defects, fabrication processes, and ambient exposure, particularly at surfaces and interfaces. Our recent efforts to mitigate these decoherence mechanisms have employed a variety of strategies, including low-loss surface encapsulation materials, advanced substrate preparation techniques, modifications to metal film growth, and the development of novel fabrication processes. The structural and chemical properties of materials, surfaces, and interfaces are studied using scanning probe microscopy, electron microscopy, photoelectron spectroscopy, mass spectrometry, and X-ray diffraction, which is correlated to device performance metrics, including superconducting resonator internal quality factor and qubit T1 time. This information is used to identify and understand material sources of loss and their origins in the device fabrication process. Through multi-institution efforts within SQMS we have identified the loss mechanism of interstitial hydrogen in niobium-based devices and shown how standard fabrication processes introduce these hydrides, developing strategies to mitigate their formation.1 Furthermore, we have characterized the metal-substrate interface, including the loss of niobium-silicides formed at that interface, and developed silicon surface treatments that reduce atomic scale roughness and oxygen content at the metal-substrate and Josephson junction interfaces.2-4 By developing the connection between materials properties and the overall performance of superconducting quantum circuitry, we can develop fabrication strategies to mitigate material losses, thus supporting the ongoing efforts to enhance coherence time in superconducting quantum devices. 1. Torres-Castanedo, C. G.*, Goronzy, D. P.*, et al., Adv. Funct. Mater., 2401365 (2024) 2. Lu, X., et al., Phys. Rev. Materials 6, 064402 (2022) 3. Berti, G., Appl. Phys. Lett. 122, 192605 (2023) 4. Kopas, C. J., Goronzy, D. P., et al., arXiv:2408.02863 (2024)