Low-loss superconducting rf devices are required when used for quantum computation. Here, we present a series of measurements and simulations showing that conducting losses in the packaging of our superconducting resonator devices affect the maximum achievable internal quality factors (Qi) for a series of thin-film Al quarter-wave resonators with fundamental resonant frequencies varying between 4.9 and 5.8 GHz. By utilizing resonators with different widths and gaps, different volumes of the stored electromagnetic energy were sampled, thus affecting Qi. When the backside of the sapphire substrate of the resonator device is adhered to a Cu package with a conducting silver glue, a monotonic decrease in the maximum achievable Qi is found as the electromagnetic sampling volume is increased. This is a result of induced currents in large surface resistance regions and dissipation underneath the substrate. By placing a hole underneath the substrate and using superconducting material for the package, we decrease the Ohmic losses and increase the maximum Qi for the larger size resonators.
Low-loss superconducting rf devices are required when used for quantum computation. Here, we present a series of measurements and simulations showing that conducting losses in the packaging of our superconducting resonator devices affect the maximum achievable internal quality factors (Qi) for a series of thin-film Al quarter-wave resonators with fundamental resonant frequencies varying between 4.9 and 5.8 GHz. By utilizing resonators with different widths and gaps, different volumes of the stored electromagnetic energy were sampled, thus affecting Qi. When the backside of the sapphire substrate of the resonator device is adhered to a Cu package with a conducting silver glue, a monotonic decrease in the maximum achievable Qi is found as the electromagnetic sampling volume is increased. This is a result of induced currents in large surface resistance regions and dissipation underneath the substrate. By placing a hole underneath the substrate and using superconducting material for the package, we decrease the Ohmic losses and increase the maximum Qi for the larger size resonators.
We present a systematic analysis of the internal losses of superconducting coplanar waveguide microwave resonators based on niobium thin films on silicon substrates. In particular, we investigate losses introduced by Nb/Al interfaces in the center conductor, which is important for experiments where Al based Josephson junctions are integrated into Nb based circuits. We find that these interfaces can be a strong source for two-level state (TLS) losses, when the interfaces are not positioned at current nodes of the resonator. In addition to TLS losses, for resonators including Al, quasiparticle losses become relevant above 200 mK. Finally, we investigate how losses generated by eddy currents in conductive material on the backside of the substrate can be minimized by using thick enough substrates or metals with high conductivity on the substrate backside.
The loss in superconducting microwave resonators at low-photon numbers and low temperatures is not well understood but has implications for achievable coherence times in superconducting qubits. We have fabricated single-layer resonators with a high quality factor by patterning a superconducting aluminum film on a sapphire substrate. Four resonator geometries were studied with resonant frequencies ranging from 5 to 7 GHz: a quasi-lumped element resonator, a coplanar strip waveguide resonator, and two hybrid designs that contain both a coplanar strip and a quasi-lumped element. Transmitted power measurements were taken at 30 mK as a function of frequency and probe power. We find that the resonator loss, expressed as the inverse of the internal quality factor, decreases slowly over four decades of photon number in a manner not merely explained by loss from a conventional uniform spatial distribution of two-level systems in an oxide layer on the superconducting surfaces of the resonator.
The performance of superconducting microwave circuits is strongly influenced by the material properties of the superconducting film and substrate. While progress has been made in understanding the importance of surface preparation and the effect of surface oxides, the complex effect of superconductor film structure on microwave losses is not yet fully understood. In this study, we investigate the microwave properties of niobium resonators with different crystalline properties and related surface topographies. We analyze a series of magnetron sputtered films in which the Nb crystal orientation and surface topography are changed by varying the substrate temperatures between room temperature and 975 K. The lowest-loss resonators that we measure have quality factors of over one million at single-photon powers, among the best ever recorded using the Nb on sapphire platform. We observe the highest quality factors in films grown at an intermediate temperature regime of the growth series (550 K) where the films display both preferential ordering of the crystal domains and low surface roughness. Furthermore, we analyze the temperature-dependent behavior of our resonators to learn about how the quasiparticle density in the Nb film is affected by the niobium crystal structure and the presence of grain boundaries. Our results stress the connection between the crystal structure of superconducting films and the loss mechanisms suffered by the resonators and demonstrate that even a moderate change in temperature during thin film deposition can significantly affect the resulting quality factors.
Superconducting quantum computing systems, including coplanar waveguide (CPW) resonators and qubits, are highly susceptible to energy dissipation from two-level systems (TLS) within bulk and interfacial dielectrics. CPW resonators serve as an ideal platform for characterizing these material losses at the single-photon excitation level. Building on recent experimental evidence that interface engineering can mitigate TLS losses, this study employs simulations to evaluate resonator quality factors across various interface modifications. Our results demonstrate that reducing losses at the substrate–air (SA) interface can increase the internal quality factor Qi by up to three orders of magnitude. While etching the SA interface also enhances Qi, material loss remains the dominant dissipation mechanism. Furthermore, we find that other lossy interfaces have a significantly smaller impact on the quality factor compared to the SA interface. These simulation results align with established experimental findings, providing a robust framework for refining resonator design. This work offers precise guidelines for TLS mitigation, essential for enhancing coherence times and developing more reliable superconducting quantum processors.
The performance of superconducting microwave circuits is strongly influenced by the material properties of the superconducting film and substrate. While progress has been made in understanding the importance of surface preparation and the effect of surface oxides, the complex effect of superconductor film structure on microwave losses is not yet fully understood. In this study, we investigate the microwave properties of niobium resonators with different crystalline properties and related surface topographies. We analyze a series of magnetron sputtered films in which the Nb crystal orientation and surface topography are changed by varying the substrate temperatures between room temperature and 975K. The lowest-loss resonators that we measure have quality factors of over 106 at single-photon powers, among the best ever recorded using the Nb on sapphire platform. We observe the highest quality factors in films grown at an intermediate temperature regime of the growth series (550K) where the films display both preferential ordering of the crystal domains and low surface roughness. Furthermore, we analyze the temperature-dependent behavior of our resonators to learn about how the quasiparticle density in the Nb film is affected by the niobium crystal structure and the presence of grain boundaries. Our results stress the connection between the crystal structure of superconducting films and the loss mechanisms suffered by the resonators and indicate that even a moderate change in temperature during thin film deposition can significantly affect the resulting quality factors.
In this master's thesis, I present the design, fabrication, and characterisation of superconducting microwave resonators. These resonators are quarter-wavelength coplanar waveguide resonators, operating at resonance frequencies between 4 GHz and 8 GHz. This kind of resonator is a key component in several applications, ranging from quantum computation devices to parametric amplifiers. Minimising the losses (achieving high internal quality factors) in these resonators is important to maximise performance of the applications they are used for. During the thesis work, we have studied several possible changes to improve the resonator quality.\n\nFabrication of the resonators was done in the Nanofabrication Laboratory at Chalmers University of Technology, and consist of the following steps: cleaning a sapphire or silicon wafer, depositing a layer of superconducting niobium, photolithography, and etching the waveguide. We then measured the resonators in a cryogen-free dilution refrigerator, at a temperature of 10 mK. The measurements consisted of a power sweep, in order to quantify the quality factor at high and low excitation powers. As an example, the first resonator we fabricated had a quality factor of 4.3 x 10^4 at high power (about 10^5 photons in the resonator), and quality factor of 3.7 x 10^4 at the single-photon level.\n\nWe then investigated different loss mechanisms that we expect to negatively affect the quality factor, and how to reduce this loss. Firstly, to reduce radiation losses and magnetic vortex losses, we reduced the lateral dimensions of the resonator. Secondly, as two-level system (TLS) losses are believed to mainly reside at the surfaces of the materials and interfaces between them, we etched into the substrate to selectively move a part of the TLS away from the resonator. We also studied the effect of the meandering of the resonator on the quality factor, as well as using two different etching gasses.\n\nBy gathering all this data, we were then able to compare the different combinations to see the effect of the changing parameters. In conclusion, the reduced lateral dimensions and the removal of part of the substrate indeed reduce the losses, as expected from the theory. We also found interesting behaviour with regards to the meandering, namely that having a meandered structure negatively affects the quality factor.\n\nCombining all results, we can give a guideline for the fabrication of resonators in the future, which gave us a quality factor up to 4.9 x 10^5 at high excitation power, and 3.0 x 10^5 at the single photon level.