The current generation of quantum sensing technologies using color centers in diamond crystals is primarily based on the principle that the resonant microwave frequency of the luminescence between quantum levels of the nitrogen-vacancy (NV) center varies with temperature and electric and magnetic fields. This principle enables us to measure, for instance, magnetic and electric fields, as well as local temperature with nanometer resolution in conjunction with a scanning probe microscope (SPM). However, the time resolution of conventional quantum sensing technologies has been limited to microseconds due to the limited luminescence lifetime. Here, we investigate ultrafast opto-magnetic effects in diamond crystals containing NV centers to improve the time resolution of quantum sensing to sub-picosecond time scales. The spin ensemble from diamond NV centers induces an inverse Cotton–Mouton effect (ICME) in the form of a sub-picosecond optical response in a femtosecond pump–probe measurement. The helicity and quadratic power dependence of the ICME can be interpreted as a second-order opto-magnetic effect in which ensembles of NV electron spins act as a source for the ICME. The results provide fundamental guidelines for enabling high-resolution spatial-time quantum sensing technologies when combined with SPM techniques.
The current generation of quantum sensing technologies using color centers in diamond crystals is primarily based on the principle that the resonant microwave frequency of the luminescence between quantum levels of the nitrogen-vacancy (NV) center varies with temperature and electric and magnetic fields. This principle enables us to measure, for instance, magnetic and electric fields, as well as local temperature with nanometer resolution in conjunction with a scanning probe microscope (SPM). However, the time resolution of conventional quantum sensing technologies has been limited to microseconds due to the limited luminescence lifetime. Here, we investigate ultrafast opto-magnetic effects in diamond crystals containing NV centers to improve the time resolution of quantum sensing to sub-picosecond time scales. The spin ensemble from diamond NV centers induces an inverse Cotton–Mouton effect (ICME) in the form of a sub-picosecond optical response in a femtosecond pump–probe measurement. The helicity and quadratic power dependence of the ICME can be interpreted as a second-order opto-magnetic effect in which ensembles of NV electron spins act as a source for the ICME. The results provide fundamental guidelines for enabling high-resolution spatial-time quantum sensing technologies when combined with SPM techniques.
In modern-day quantum metrology, quantum sensors are widely employed to detect weak magnetic fields or nanoscale signals. Quantum devices, exploiting quantum coherence, are inevitably connected to physical constants and can achieve accuracy, repeatability, and precision approaching fundamental limits. As a result, these sensors have shown utility in a wide range of research domains spanning both science and technology. A rapidly emerging quantum sensing platform employs atomic-scale defects in crystals. In particular, magnetometry using nitrogen-vacancy (NV) color centers in diamond has garnered increasing interest. NV systems possess a combination of remarkable properties, optical addressability, long coherence times, and biocompatibility. Sensors based on NV centers excel in spatial resolution and magnetic sensitivity. These diamond-based sensors promise comparable combination of high spatial resolution and magnetic sensitivity without cryogenic operation. The above properties of NV magnetometers promise increasingly integrated quantum measurement technology, as a result, they have been extensively developed with various protocols and find use in numerous applications spanning materials characterization, nuclear magnetic resonance (NMR), condensed matter physics, paleomagnetism, neuroscience and living systems biology, and industrial vector magnetometry. In this chapter, NV centers are explored for magnetic sensing in a number of contexts. In general, we introduce novel regimes for magnetic-field probes with NV ensembles. Specifically, NV centers are developed for sensitive magnetometers for applications where microwaves (MWs) are prohibitively invasive and operations need to be carried out under zero ambient magnetic field. The primary goal of our discussion is to improve the utility of these NV center-based magnetometers.
High spatial resolution quantum sensing of near-surface nitrogen vacancy (NV) centers in diamond has enabled detection of magnetic, electrical, and thermal signals at the nanoscale. At depths of just a few nanometers, NV centers serve as localized quantum probes for external spins or low-dimensional materials, but their proximity to the surface also enhances decoherence caused by fluctuating nuclear spins. While advances in surface engineering have stabilized the charge state of NV centers at depths of tens of nanometers, achieving both ultra-shallow implantation (0.5-2 nm) and long-term spin coherence remains a central challenge. In this work, we show using first-principles modeling that, by exploiting the interaction of surface-induced strain and weak dc magnetic fields, the spin coherence times of 1-nm-deep NV centers can be greatly improved near the spin-phonon-confined regime at room temperature in 12C-rich diamonds. We also demonstrate that this protocol benefits ~ 10-nm-deep NV centers in natural diamond, enabling vector magnetometry at the nanoscale. Shallow NV centers in diamond are advantageous for quantum sensing but suffer from surface magnetic noise. Using first-principles simulations supported by experiments, the authors show that a combination of small magnetic fields and surface strain can significantly enhance spin coherence of 1 nm-deep NV centers.
Nitrogen-vacancy (NV) color centers in diamond are excellent quantum sensors possessing high sensitivity and nano-scale spatial resolution. Their integration in photonic structures is often desired, since it leads to an increased photon emission and also allows the realization of solid-state quantum technology architectures. Here, we report the fabrication of diamond nano-pillars with diameters up to 1000 nm by electron beam lithography and inductively coupled plasma reactive ion etching in nitrogen-rich diamonds (type Ib) with [100] and [111] crystal orientations. The NV centers were created by keV-He ion bombardment and subsequent annealing, and we estimate an average number of NVs per pillar to be 4300 ± 300 and 520 ± 120 for the [100] and [111] samples, respectively. Lifetime measurements of the NVs’ excited state showed two time constants with average values of τ1 ≈ 2 ns and τ2 ≈ 8 ns, which are shorter as compared to a single color center in a bulk crystal (τ ≈ 10 ns). This is probably due to a coupling between the NVs as well as due to interaction with bombardment-induced defects and substitutional nitrogen (P1 centers). Optically detected magnetic resonance measurements revealed a contrast of about 5% and average coherence and relaxation times of T2 [100] = 420 ± 40 ns, T2 [111] = 560 ± 50 ns, and T1 [100] = 162 ± 11 μs, T1 [111] = 174 ± 24 μs. These pillars could find an application for scanning probe magnetic field imaging.
The recent decade has witnessed exciting developments in quantum science and technology. Quantum sensing is a rapidly growing branch, which exploits the fragility of quantum systems to detect small external signals. The extreme control at the single-atom level and the remarkably long coherence time of engineered quantum systems enable unprecedented sensitivity and precision, beating the performance of classical techniques. The nitrogen-vacancy (NV) center in diamond is one of the most promising quantum sensors. Its unique advantages have attracted considerable attention, including a long spin coherence time throughout a broad temperature range, nanoscale resolution limited by the sensor-sample distance, convenient optical control of its spin states and remarkably versatile sensing capabilities. Its properties are well studied under a bias magnetic field oriented along its quantization axis. However, its sensing capabilities in the presence of an off-axis magnetic field are much less explored. My research aims to unlock the full potential of NV quantum sensor by developing new sensing modalities under a magnetic field acting perpendicular to the NV axis, and furthermore, integrating them into a scanning probe microscope. In this dissertation, I will report our progress toward building a scanning NV multimodal quantum imaging platform, which will open up exciting opportunities in measuring nanoscale phenomena. The first chapter provides an introduction to the background of quantum sensing with NV centers, followed by a discussion on its basic properties and established sensing techniques. The second and third chapters are dedicated to two experiments performed under a perpendicular magnetic field where traditional NV magnetometry based on the Zeeman effect fails. In the second chapter, I will introduce a new sensing strategy that uses the entanglement between the electron and nuclear spins to restore the magnetic field sensitivity under this unfavored condition. This allows us to sense small changes in the magnetic field angle relative to the NV axis, and to detect anisotropic magnetic noise in the local environment. In the third chapter, I will present our latest development of scanning NV electrometry, where a single NV at the apex of a diamond scanning probe images external alternating (AC) and direct (DC) electric fields with sub-100 nm resolution. In the last chapter, I will discuss our efforts on four experiments that were left unfinished. I will present the results we have achieved, analyze the challenges that we faced and propose potential solutions to overcome them.
Among the possible defects that can occur in diamonds, one that draws attention is the nitrogen-vacancy (NV) center.Studied since the early 90s, in recent years, they became one of the most promising platforms for field applications of quantum technology at room temperature, especially for quantum sensing.They are sensitive to electric and magnetic fields, temperature, and strain, making these nanosensors a versatile platform for many applications.The NV center's spin state is easy to read and manipulate by optical means, and, most interestingly, it works well at room temperature, which facilitates its use.The great challenge to implement quantum protocols and quantum algorithms is the coherence time of the quantum states.The NV center stands out for having relatively high coherence times at room temperature.This dissertation presents measurements to characterize the electron spin coherence of NV centers in an ultrapure sample of diamond designed for quantum sensing applications.These measurements combine optical e magnetic resonance techniques.For that, a method was implemented using a conventional CCD camera and a clever imaging protocol, making it possible to perform various pulsed microwave experiments on the electron spin, such as Rabi oscillations and Hahn spin-echo, which were used for determining the characteristic relaxation times (T 1 and T 2 ).Results show that this system provides at least two readily accessible qubits that can be used in quantum protocols even at room temperature.
NV- center has been paid attention as a quantum sensor for highly sensitive detection of magnetic field, electric field, temperature and strain, etc.. Electron beam irradiation followed by subsequent thermal annealing is known as the effective procedures to create NV- center in diamond. The electron irradiation generates vacancies in diamond and the annealing enables vacancies to diffuse in the lattice. Then diffused vacancies are captured by nitrogen atoms, and as a result, NV centers are created. In addition, substitutional nitrogen atom at a lattice site (P1 center) also acts as a donor for NV center, the charge state of NV centers changes from neutral (NV0) to NV-. Creation high concentration of ensemble NV- centers is needed to achieve high sensitively sensing. The magnetic sensitivity is proportional to the reciprocal of the number of NV centers and T2 (spin coherence time), i.e., high concentration NV- centers with long T2 increase the sensitivity. P1 center has an important role for being a component of NV- centers and acting as donor to the NV center. But it also plays a role as decoherence source (decrease in magnetic field sensitivity). Therefore, it is important to create high concentration of NV- centers considering the amount of P1 centers. In current study, we investigate irradiation fluence dependence of the creation behavior of NV centers in type-Ib diamonds by using electron spin resonance (ESR) and photo-luminescence (PL) to understand the creation mechanism of NV- center. The values of T2 are also evaluated by Hahn-echo measurement, since it is one of the key parameters for highly sensitive magnetometry. Then, we discuss the creation mechanism of NV centers based on concentrations of defects.