Generally, a superconducting nanowire single-photon detector (SNSPD) is composed of wires with a typical width of ∼ 100 nm . Recent studies have found that superconducting strips with a micrometer-scale width can also detect single photons. Compared with the SNSPD covering the same area, the superconducting microstrip single-photon detector (SMSPD) has smaller kinetic inductance, higher working current, and lower requirements in fabrication accuracy, providing potential applications in the development of ultralarge active area detectors. However, the study of SMSPD is still in its infancy, and the realization of its high-performance and practical use remains an open question. This study demonstrates a NbN SMSPD with a nearly saturated system detection efficiency (SDE) of ∼ 92.2 % at a dark count rate of ∼ 200 cps , a polarization sensitivity of ∼ 1.03 , and a minimum timing jitter of ∼ 48 ps at the telecom wavelength of 1550 nm when coupled with a single-mode fiber and operated at 0.84 K. Furthermore, the detector’s SDE is over 70% when operated at a 2.1 K closed-cycle cryocooler.
Generally, a superconducting nanowire single-photon detector (SNSPD) is composed of wires with a typical width of ∼ 100 nm . Recent studies have found that superconducting strips with a micrometer-scale width can also detect single photons. Compared with the SNSPD covering the same area, the superconducting microstrip single-photon detector (SMSPD) has smaller kinetic inductance, higher working current, and lower requirements in fabrication accuracy, providing potential applications in the development of ultralarge active area detectors. However, the study of SMSPD is still in its infancy, and the realization of its high-performance and practical use remains an open question. This study demonstrates a NbN SMSPD with a nearly saturated system detection efficiency (SDE) of ∼ 92.2 % at a dark count rate of ∼ 200 cps , a polarization sensitivity of ∼ 1.03 , and a minimum timing jitter of ∼ 48 ps at the telecom wavelength of 1550 nm when coupled with a single-mode fiber and operated at 0.84 K. Furthermore, the detector’s SDE is over 70% when operated at a 2.1 K closed-cycle cryocooler.
Superconducting microstrips single-photon detectors (SMSPDs) are a novel type of single-photon sensor based on superconducting thin films patterned into micrometer-scale strip widths. Compared with superconducting nanowire single-photon detectors (SNSPDs), SMSPDs not only substantially lower the fabrication dependence on high-precision electron-beam lithography, but also exhibit lower kinetic inductance, higher bias current, and weaker polarization sensitivity. These advantages pave a new route toward superconducting single-photon detection systems with large active areas and low dark-count rates. Because of their performance, SMSPDs exhibit tremendous application potential in cutting-edge fields such as quantum communication, LiDAR, dark-matter searches, and high-energy particle detection. Accordingly, this paper provides a systematic review of recent advances in SMSPD research, covering the underlying physical mechanisms, material systems, geometrical design, readout circuitry, and application domains. Firstly, this review elaborates on the photon response mechanism of SMSPDs and clarifies its correlation with vortex dynamics. Secondly, this review categorizes the superconducting materials used for SMSPD fabrication and analyzes the influences of characteristic thin-film parameters on device performance. Furthermore, this work concludes the evolution and optimization strategies of geometrical design and readout circuit schemes for SMSPDs, and presents the current application status. Finally, we offer perspectives on its future development trajectory. This review provides a foundation in physical mechanisms and design guidance for the development of large active area SMSPDs with high efficiency and low dark counts.
Superconducting Single-Photon Detectors (SSPD) invented two decades ago have evolved to a mature technology and have become devices of choice in the advanced applications of quantum optics, such as quantum cryptography and optical quantum computing. In these applications SSPDs are coupled to single-mode fibers and feature almost unity detection efficiency, negligible dark counts, picosecond timing jitter and MHz photon count rate. Meanwhile, there are great many applications requiring coupling to multi-mode fibers or free space. `Classical’ SSPDs with 100-nm-wide superconducting strip and covering area of about 100 µm2 are not suitable for further scaling due to degradation of performance and low fabrication yield. Recently we have demonstrated single-photon counting in micron-wide superconducting bridges and strips. Here we present our approach to the realization of practical photon-counting detectors of large enough area to be efficiently coupled to multi-mode fibers or free space. The detector is either a meander or a spiral of 1-µm-wide strip covering an area of 50x50 µm2. Being operated at 1.7K temperature it demonstrates the saturated detection efficiency (i.e. limited by the absorption in the detector) up to 1550 nm wavelength, about 10 ns dead time and timing jitter in range 50-100 ps.
Ever since superconducting nanowire single-photon detectors (SNSPDs or SSPDs) were demonstrated, they have attracted a considerable attention due to the detectors’ promising performance that includes high detection efficiency (DE), low dark count rate (DCR), broadband sensitivity, and low timing jitter. The system detection efficiency (SDE) has been improved to be over 90% with a wavelength of 1550 nm in a fiber-coupled system by embedding the SNSPD in optical cavities. However, the implementation of optical cavity usually reduces the bandwidth of SNSPDs. As a result, there are some recent works on increasing the bandwidth of SNSPD. Furthermore, the size of the active area of meandered nanowires has to be compatible with the core size of an optical fiber such that good optical coupling can be achieved; this setup requires a long nanowire with a large kinetic inductance, thus resulting in a small counting rate and a large timing jitter, particularly for multi-mode fiber-coupled devices. Nevertheless, a particularly impressive waveguide-coupled SNSPD has been developed in recent years. By placing an SNSPD atop an optical waveguide that has been fabricated on various substrate materials, photons propagating in the waveguide have been found to be evanescently absorbed by nanowires that are only a few tens of microns long. The on-chip DE of this device has been estimated to be over 90%, thus indicating that it has both high absorptance and high intrinsic DE. If the waveguide and the nanowire are correctly dimensioned, the absorptance of this device can reach over 90% for a wavelength range of more than 700 nm. Furthermore, the length of the nanowire is shorter than that of the fiber-coupled SNSPD, thus leading to a higher count rate and lower timing jitter (~18 ps). However, unsatisfactory coupling losses between the optical fiber and the waveguide in such devices can decrease its SDE (~10%), thus limiting its applicability to quantum photonic integrated circuits (QPIC). Recently, we proposed a type of SNSPD that was coupled with microfibers (MFs), and simulations for this SNSPD indicated that its absorption would be as high as 90%. Microfibers and nanofibers, tapered adiabatically from standard fibers, with diameters close to or smaller than the wavelength of the guided light were demonstrated to have low transmittance losses by Tong et al. in 2003. MFs have been shown to have many interesting properties, such as strong evanescent fields, tight optical confinement, wideband abilities, and small masses; these properties are appealing for applications such as optical sensing and coupling. MFs also provide seamless connections with high transmittance from standard fibers; therefore, MF-coupled SNSPDs can achieve both high SDEs and wideband compatibility. We proposed and demonstrated the MF-coupled SNSPDs successfully. The simulation results indicate that with optimal device structure, the optical absorption with efficiency < 90% can be realized over a wavelength range of 350 nm to 2150 nm. The fabricated MF-coupled SNSPD, shows unparalleled broadband system detection efficiencies (SDEs) of more than 50% from 630 nm to 1500 nm. The SDEs reach 66% at 785 nm and 45% at 1550 nm. These results pave the way for ultra-broadband weak light detection with quantum-limit sensitivity.
Satellite-ground quantum communication requires single-photon detectors of 850-nm wavelength with both high detection efficiency and large sensitive area. We developed superconducting nanowire single-photon detectors (SNSPDs) on one-dimensional photonic crystals, which acted as optical cavities to enhance the optical absorption, with a sensitive-area diameter of 50 μm. The fabricated multimode fiber coupled NbN SNSPDs exhibited a maximum system detection efficiency (DE) of up to 82% and a DE of 78% at a dark count rate of 100 Hz at 850-nm wavelength as well as a system jitter of 105 ps.
The effective and convenient detection of single photons via advanced detectors with a large active area is becoming significant for quantum and classical applications. This work demonstrates the fabrication of a superconducting microstrip single-photon detector (SMSPD) with a millimeter-scale active area via the use of ultraviolet (UV) photolithography. The performances of NbN SMSPDs with different active areas and strip widths are characterized. SMSPDs fabricated by UV photolithography and electron beam lithography with small active areas are also compared from the aspects of the switching current density and line edge roughness. Furthermore, an SMSPD with an active area of 1 mm × 1 mm is obtained via UV photolithography, and during operation at 0.85 K, it exhibits near-saturated internal detection efficiency at wavelengths up to 800 nm. At a wavelength of 1550 nm, the detector exhibits a system detection efficiency of ∼5% (7%) and a timing jitter of 102 (144) ps, when illuminated with a light spot of ∼18 (600) µm in diameter, respectively.
Superconducting nanowire single-photon detectors (SNSPDs) play a pivotal role in infrared single-photon-detection applications owing to their free-running mode, near-unity detection efficiency, and excellent time resolution. However, conventional niobium nitride- (NbN) SNSPDs often have a trade-off between optimal detection efficiency and time resolution. We herein demonstrate NbN SNSPDs in the combination of high efficiency and time resolution by using the helium-ion-irradiated film of 10 nm and a homemade cryogenic amplifier to improve the signal-to-noise ratio. The proposed 18-μm-diameter device operated at 850 mK shows a saturated system detection efficiency of ∼90.5% at 1550 nm wavelength with a dark count rate below 50 counts per second (cps), and minimum system timing jitter of ∼14.7 ps. Meanwhile, the recovery time is 21.2 ns owing to its lower kinetic inductance. The time-of-flight light detection and ranging with this device was further carried out indoors, which demonstrates a submillimeter (<0.5 mm) depth resolution, as well as good depth and intensity reconstruction of a low-signature object even under the dwell time of 0.5 ms. It indicates that our device has a great advantage and potential in high-time-resolution and weak-signal-detection applications, such as real-time imaging, fluorescence lifetime detection, and remote laser sensing.