Coherent Manipulation with Resonant Excitation and Single Emitter Creation of Nitrogen Vacancy Centers in 4H Silicon Carbide
Zhao Mu, Soroush Abbasi Zargaleh, Hans Jürgen von Bardeleben, Johannes E. Fröch, Milad Nonahal, Hongbing Cai, Xinge Yang, Jianqun Yang, Xingji Li, Igor Aharonovich, Weibo Gao
Silicon carbide (SiC) has become a key player in the realization of scalable quantum technologies due to its ability to host optically addressable spin qubits and wafer-size samples. Here, we have demonstrated optically detected magnetic resonance (ODMR) with resonant excitation and clearly identified the ground state energy levels of the NV centers in 4H-SiC. Coherent manipulation of NV centers in SiC has been achieved with Rabi and Ramsey oscillations. Finally, we show the successful generation and characterization of single nitrogen vacancy (NV) center in SiC employing ion implantation. Our results highligh the key role of NV centers in SiC as a potential candidate for quantum information processing.
Silicon carbide (SiC) has become a key player in the realization of scalable quantum technologies due to its ability to host optically addressable spin qubits and wafer-size samples. Here, we have demonstrated optically detected magnetic resonance (ODMR) with resonant excitation and clearly identified the ground state energy levels of the NV centers in 4H-SiC. Coherent manipulation of NV centers in SiC has been achieved with Rabi and Ramsey oscillations. Finally, we show the successful generation and characterization of single nitrogen vacancy (NV) center in SiC employing ion implantation. Our results highligh the key role of NV centers in SiC as a potential candidate for quantum information processing.
Robust single spin color centers in solid state systems with telecom wavelength emission are vital to quantum photonics and quantum networks. The nitrogen vacancy (NV) centers in silicon carbide (SiC) have become promising platforms for those applications. However, little is known about the detailed optical properties of the NV centers. In this paper, we investigate the photophysics of the single NV centers in 4H-SiC. The results demonstrate that the NV centers comprise three energy-level electronic structures. Particularly, for c -axis NV centers, both the excitation and the emission polarization degrees are larger than 90%. Photon purity and photostability of the single NV centers are maintained at an elevated temperature up to 400 K. These experiments constitute an important step toward using the NV centers in SiC with respect to quantum photonics.
Divacancy defects in silicon carbide have long-lived electronic spin states and sharp optical transitions. Because of the various polytypes of SiC, hundreds of unique divacancies exist, many with spin properties comparable to the nitrogen-vacancy center in diamond. If ensembles of such spins can be all-optically manipulated, they make compelling candidate systems for quantum-enhanced memory, communication, and sensing applications. We report here direct all-optical addressing of basal plane-oriented divacancy spins in 4H-SiC. By means of magneto-spectroscopy, we fully identify the spin triplet structure of both the ground and the excited state, and use this for tuning of transition dipole moments between particular spin levels. We also identify a role for relaxation via intersystem crossing. Building on these results, we demonstrate coherent population trapping -a key effect for quantum state transfer between spins and photons- for divacancy sub-ensembles along particular crystal axes. These results, combined with the flexibility of SiC polytypes and device processing, put SiC at the forefront of quantum information science in the solid state.
Silicon carbide (SiC) is a promising platform for scalable quantum technologies owing to its well-established, wafer-scale industrial processing. SiC also hosts a variety of optically active color centres including the nitrogen vacancy defect that has a spin-triplet ground state. However, strong phonon coupling in the infrared range limits photon extraction from these defects. Here, we use nanophotonic structures, specifically micro-pillar and micro-disk resonators, to enhance optical collection and spin-readout. The micro-pillar geometry yields a 4-fold increase in photon collection, accompanied by a 2.4-fold reduction in spectral noise in optically detected magnetic resonance measurements. Consequently, the magnetic field sensitivity is improved by 24%. The large mode volume of the micro-disk supports resonances spanning 1150-1250 nm, enabling broadband coupling to nitrogen vacancy emission lines. Our results demonstrate that fabrication of scalable photonic structures efficiently improves performance of silicon carbide color centers for integrated quantum light generation and sensing.
Solid-state color centers with manipulatable spin qubits and telecom-ranged fluorescence are ideal platforms for quantum communications and distributed quantum computations. In this work, we coherently control the nitrogen-vacancy (NV) center spins in silicon carbide at room temperature, in which telecom-wavelength emission is detected. We increase the NV concentration sixfold through optimization of implantation conditions. Hence, coherent control of NV center spins is achieved at room temperature, and the coherence time T_{2} can be reached to around 17.1 μs. Furthermore, an investigation of fluorescence properties of single NV centers shows that they are room-temperature photostable single-photon sources at telecom range. Taking advantage of technologically mature materials, the experiment demonstrates that the NV centers in silicon carbide are promising platforms for large-scale integrated quantum photonics and long-distance quantum networks.
The V2 silicon vacancy defect in 4H-SiC has emerged as a promising system for quantum technologies due to its favorable optical and spin properties and the advantages of the SiC host. However, the readout contrast - an important benchmark for quantum sensing - of V2 ensembles for optically-detected magnetic resonance (ODMR) is relatively low, usually <1% at room temperature. To overcome this challenge, we resonantly excite the V2 ensembles at cryogenic temperatures and compare the results with the off-resonant case. We report a maximum ODMR contrast of 50% with only 2 μW of resonant laser power, almost 100 times improvement over off-resonant excitation. We attribute this high readout contrast to a subset of V2 centers that have one spin-selective optical transition resonant with the laser. The ODMR contrast decreases with temperature, approaching the non-resonant contrast by 60 K, likely due to broadening of the optical transition linewidths. We achieve a maximum sensitivity of 100 nT/Hz with a resonant laser power of 300 μW, while 100 times more non-resonant excitation power is needed to achieve comparable sensitivity.
The identification of a microscopic configuration of point defects acting as quantum bits is a key step in the advance of quantum information processing and sensing. Among the numerous candidates, silicon-vacancy related centers in silicon carbide (SiC) have shown remarkable properties owing to their particular spin-3/2 ground and excited states. Although, these centers were observed decades ago, two competing models, the isolated negatively charged silicon vacancy and the complex of negatively charged silicon vacancy and neutral carbon vacancy [Phys. Rev. Lett. 115, 247602 (2015)], are still argued as an origin. By means of high-precision first-principles calculations and high-resolution electron spin resonance measurements, we here unambiguously identify the Si-vacancy related qubits in hexagonal SiC as isolated negatively charged silicon vacancies. Moreover, we identify the Si-vacancy qubit configurations that provide room-temperature optical readout.