An experimental study of saturable absorption and excited-state absorption (ESA) in several inorganic saturable absorbers, Cr/sup 4+/:YAG, Cr/sup 4+/:GGG, and Cr/sup 4+/:YSGG, is presented. We provide the theoretical background of absorption characteristics in saturable absorbers that exhibit ESA, with some new results: approximate analytical solutions are proposed for the optical transmission in the case of a slow absorber, and for various light intensity conditions of spatially or temporally Gaussian beams in fast and slow absorbers. Experimentally, partial bleaching of the first excited state itself could be observed in Cr/sup 4+/:YAG at /spl lambda/=1064 nm, yielding the higher excited-state lifetime as /spl tau/*=(0.55/spl plusmn/0.1) ns. The regular transmission bleaching curve was measured in Cr/sup 4+/:GGG, for the first time in this material, yielding /spl sigma//sub ga/=(58/spl plusmn/5)/spl times/10/sup -1/ cm/sup 2/, and /spl sigma/e/sub s/=(13/spl plusmn/2)/spl times/10/sup -19/ cm/sup 2/ at /spl lambda/=1064 nm, ESA spectra were measured for the three materials between /spl sim/700 and 900 nm. All three exhibit crossing between saturable absorption at longer wavelengths and inverse saturable absorption at shorter wavelengths.
The refractive index of most ion-doped materials increases with the excited state population. This effect was studied in many laser materials, particularly those doped with Cr3+ and rare earth ions, using several techniques, such as interferometry, wave mixing, and Z-scans. This refractive index variation is athermal (has an electronic origin) and is associated with the difference in the polarizabilites of the Cr3+ ion in its excited and ground states, Δαp. The Cr3+ optical transitions in the visible domain are electric-dipole forbidden, and they have low oscillator strengths. Therefore, the major contribution to Δαp has been assigned to allowed transitions to charge transfer bands (CTBs) in the UV with strengths ∼3 orders of magnitude higher. Although this CTB model qualitatively explains the main observations, it was never quantitatively tested. In order to further investigate the physical origin of Δαp in Cr3+-doped crystals, excited state absorption (ESA) and Z-scan measurements were thus performed in Cr:Al2O3 (ruby) and Cr:GSGG. Cr:GSGG was selected because of the proximity of its E2 and T24 emitting levels, and thus the possibility to explore the role of the spin selection rule in the ESA spectra and the resulting variations in polarizability by comparing low and room temperature data, which were never reported before. On the other hand, Cr:Al2O3 (ruby) was selected because it is the only crystal for which it is possible to obtain CTB absorption data from both ground and excited states, and thus for which it is possible to check the CTB model more accurately. Thanks to these more accurate and more complete data, we came to the first conclusion that the spin selection rule does not play any significant role in the variation of the polarizability with the E2–T24 energy mismatch. We also discovered that using the CTB model in the case of ruby would lead to a negative Δαp value, which is contrary to all refractive index variation (including Z-scan) measurements.