This thesis investigates the theoretical foundations, material properties, and experimental realization of quantum sensors based on the Nitrogen-Vacancy (NV) centers in diamond, a solid-state system that combines quantum coherence with room-temperature operability. The first chapter introduces the principles of quantum sensing, outlining the fundamental definitions, operating protocols, and physical processes underlying the quantum measurement paradigm. Emphasis is placed on the quantum sensing Hamiltonian and the distinction between various classes of quantum sensors. The second chapter focuses on diamond as a host material and on the NV center as a quantum defect. The electronic structure, optical transitions, and spin properties of the NV center are analyzed in detail. Several techniques of NV-based magnetometry are presented, including continuouswave and pulsed optically detected magnetic resonance (ODMR). The discussion also addresses coherence times (T1, T2, and T∗2 ) and methods of diamond synthesis together with NV-center generation through irradiation and annealing. Chapter three develops the physical theory describing the NV center. The Hamiltonian formalism includes spin-spin, hyperfine, and quadrupolar interactions, as well as couplings to external magnetic fields. The chapter further introduces the Bloch sphere representation, magnetic resonance phenomena, and models of lightmatter interaction, ranging from the semiclassical to the fully quantum Rabi framework. A seven-level rate-equation model is proposed to capture the spin dynamics and optical cycling processes of the NV center. The fourth chapter reports the experimental results. After describing materials and methods, several ODMR-based vector magnetometry experiments are presented, highlighting different spectral regimes and the dependence of resonance features on the external magnetic field geometry. Additional studies demonstrate temperature sensing and microwave-free magnetometry techniques for mapping magnetic field distributions. Sensitivity analysis and calibration procedures are also discussed.
This thesis investigates the theoretical foundations, material properties, and experimental realization of quantum sensors based on the Nitrogen-Vacancy (NV) centers in diamond, a solid-state system that combines quantum coherence with room-temperature operability. The first chapter introduces the principles of quantum sensing, outlining the fundamental definitions, operating protocols, and physical processes underlying the quantum measurement paradigm. Emphasis is placed on the quantum sensing Hamiltonian and the distinction between various classes of quantum sensors. The second chapter focuses on diamond as a host material and on the NV center as a quantum defect. The electronic structure, optical transitions, and spin properties of the NV center are analyzed in detail. Several techniques of NV-based magnetometry are presented, including continuouswave and pulsed optically detected magnetic resonance (ODMR). The discussion also addresses coherence times (T1, T2, and T∗2 ) and methods of diamond synthesis together with NV-center generation through irradiation and annealing. Chapter three develops the physical theory describing the NV center. The Hamiltonian formalism includes spin-spin, hyperfine, and quadrupolar interactions, as well as couplings to external magnetic fields. The chapter further introduces the Bloch sphere representation, magnetic resonance phenomena, and models of lightmatter interaction, ranging from the semiclassical to the fully quantum Rabi framework. A seven-level rate-equation model is proposed to capture the spin dynamics and optical cycling processes of the NV center. The fourth chapter reports the experimental results. After describing materials and methods, several ODMR-based vector magnetometry experiments are presented, highlighting different spectral regimes and the dependence of resonance features on the external magnetic field geometry. Additional studies demonstrate temperature sensing and microwave-free magnetometry techniques for mapping magnetic field distributions. Sensitivity analysis and calibration procedures are also discussed.
In modern-day quantum metrology, quantum sensors are widely employed to detect weak magnetic fields or nanoscale signals. Quantum devices, exploiting quantum coherence, are inevitably connected to physical constants and can achieve accuracy, repeatability, and precision approaching fundamental limits. As a result, these sensors have shown utility in a wide range of research domains spanning both science and technology. A rapidly emerging quantum sensing platform employs atomic-scale defects in crystals. In particular, magnetometry using nitrogen-vacancy (NV) color centers in diamond has garnered increasing interest. NV systems possess a combination of remarkable properties, optical addressability, long coherence times, and biocompatibility. Sensors based on NV centers excel in spatial resolution and magnetic sensitivity. These diamond-based sensors promise comparable combination of high spatial resolution and magnetic sensitivity without cryogenic operation. The above properties of NV magnetometers promise increasingly integrated quantum measurement technology, as a result, they have been extensively developed with various protocols and find use in numerous applications spanning materials characterization, nuclear magnetic resonance (NMR), condensed matter physics, paleomagnetism, neuroscience and living systems biology, and industrial vector magnetometry. In this chapter, NV centers are explored for magnetic sensing in a number of contexts. In general, we introduce novel regimes for magnetic-field probes with NV ensembles. Specifically, NV centers are developed for sensitive magnetometers for applications where microwaves (MWs) are prohibitively invasive and operations need to be carried out under zero ambient magnetic field. The primary goal of our discussion is to improve the utility of these NV center-based magnetometers.
Quantum sensors encompass a diverse class of devices that exploit quantum coherence to detect weak or nanoscale signals. As their behavior is tied to physical constants, quantum sensors can achieve accuracy, repeatability, and precision approaching fundamental limits [1, 2]. As a result, these sensors have shown utility in a wide range of applications in both science and engineering leading to innovations. Among many solid-state spin systems, nitrogen-vacancy (NV) centers in diamonds have attracted considerable attention as a leading platform in many fields of quantum technologies, from quantum sensing to information processing and communication applications. They have superior physical properties, and their quantum coherence is preserved even at room temperature. The energy levels of NV centers are sensitive to magnetic fields, electric fields, strain, and temperature, and the spatial resolution is scalable from nanometers to millimeters. Therefore, diamond quantum sensors are distinctive sensors with multimodality and span scalable application fields. To realize an ideal quantum sensor for applications, the technical challenges in the sensor materials and the quantum control techniques, such as coherent microwave spin manipulation, effective optical spin-state initialization, and readout, have been developed. This chapter briefly explains the sensing principle using NV centers and then introduces sensor systems for biomedical applications, and monitoring of batteries for electric vehicles and internal power devices.
The fluorescence of the nitrogen-vacancy (NV) centre in artificial diamond has been widely studied for applications such as quantum communication protocols, quantum computation, fluorescence-based biolabelling, and optical sensing. Optical sensing by itself encompasses a wide range of possible applications: from magnetic and electric field sensing to temperature sensing and enabling, for example, the detection of paramagnetic ions and the identification of molecules by nuclear magnetic resonance. Compared to many other systems capable of optical sensing, the NV centre works at room temperature, and its spin-dependent fluorescence emission is the key property to achieve a high sensitivity to the surrounding environment. Additionally, the NV centre emission is highly photostable, has a relatively short lifetime (~ 12ns) and spans a broad wavelength range, from the red to the near-infrared region of the electromagnetic spectrum (600 - 800nm). While the common denominator of all mentioned applications is the NV centre, the properties of the artificial diamond surrounding the NV centre have a significant impact on its sensing performance. At present, the processing of artificial diamond has not been fully optimised, and research and development towards the realisation of the `best¿ diamond sample for optical sensing is far from over. Specifically, the role of other defects in diamond and their effects on the photo-physical properties of the NV centres are not entirely understood. In this thesis, I will discuss the potential benefits of a novel processing technique to create ensembles of NV centres, and the importance that surrounding nitrogen defects has on the achievable magnetic field sensitivity. Additionally, I will show both theoretical and experimental investigations of the NV centres photo-physical processes, with focus on magnetic field sensing. I will initially explore a protocol for microwave-free magnetometry. This protocol predicts a theoretical magnetic field sensitivity <10µT/√Hz in the range 0.3 - 30mT and I will demonstrate it experimentally with a maximum sensitivity of 3.6mT/Hz. Following, I will focus on exploring techniques to increase the magnetic field sensitivity by improving the material properties of the diamond samples. I will demonstrate that the simultaneous electron irradiation and annealing improves the creation efficiency of an ensemble of NV centres by up to 117%. Finally, I will investigate how substitutional nitrogen defects in the surrounding lattice affects the charge state of the NV centre, its emission intensity, its lifetime and its magnetic field sensitivity. I will study a sample characterised by multiple regions across its volume, with nitrogen concentration changing between 10ppm and 100ppm in each region. There si an optimal region with ~ 40ppm of substitutional nitrogen which demonstrates the highest fluorescence emission, mainly from the negatively-charged NV centre, and the highest magnetic field sensitivity of 1.6 ± 0.2µT/√Hz. However, both the regions with lower and higher substitutional nitrogen concentration than the optimal region show lower emission intensity and worse magnetic field sensitivity. Following is a summary of the content in each chapter: Chapter 1 will present an introduction to the diamond material and the classification of artificial diamond samples. It will introduce the NV centre, its fluorescence properties and the process to create NV centres in diamond. The chapter will also introduce the concepts around optical magnetometry and the working principle that allows the NV centre to sense magnetic fields as well as other external quantities, such as temperature or pressure. Finally, it will include a brief overview of the defects that are found in artificial diamond or are created during the sample processing. Chapter 2 will describe the working principle of the instruments utilised in this work. I will list the details of each instrument and describe the methods used for the analysis of the data. Chapter 3 will introduce the background of modelling the fluorescence emission from NV centres. I will discuss the implementation of a computational model based on the Lindblad master equation to simulate the photo-physical dynamics of the NV centre. I will demonstrate the successful simulation of the saturation emission, fluorescence lifetime and optically detected magnetic resonance using the theoretical model. Finally, I will explore the theoretically predicted sensitivity of microwave-free magnetometry, based on the NV centre emission intensity change under an external magnetic field. Chapter 4 will demonstrate experimentally the microwave-free magnetometry technique. In relation to the study of microwave-free magnetometry, this chapter will explore an unexpected increase in emission intensity at high magnetic fields > 100mT. Combining the experimental observations and the theoretical simulation developed in the previous chapter, I will identify and discuss a phenomenological decrease in the NV centre transition rate from the triplet state to the singlet state. The chapter will conclude comparing the experimental and theoretical sensitivities associated with the microwave-free magnetometry technique. Chapter 5 will show the characterisation of a diamond sample at each step of the process to create NV centres. I will study the electron irradiation followed by separate annealing on a high-pressure high-temperature diamond sample. I will then characterise the sample employing visible and infrared absorption spectroscopy, as well as measure the fluorescence spectra and lifetime of the defects identified at each step. Chapter 6 will examine an alternative method to create NV centres in diamond. I will compare diamond samples irradiated and annealed separately with samples simultaneously irradiated and annealed (referred to as 'annealing in situ'). To compare the two processes, I will estimate the concentration of nitrogen defects and NV centres and calculate their N-to-NV conversion efficiency. Chapter 7 will discuss the effects of substitutional nitrogen on the properties of the NV centres in diamond. For this discussion, I will use a single-crystal diamond that shows the presence of 4 growth sectors. Each growth sector is characterised by a different nitrogen concentration, as I will demonstrate at the beginning of the chapter. I will focus on 4 main properties affected by the concentration of nitrogen in the different sectors: the balance between the charge states of the NV centre, the overall fluorescence intensity from each sector, the fluorescence lifetime and its relation to non-radiative processes, and the magnetic field sensitivity obtained with the optically detected magnetic resonance technique. Chapter 8 will gather the results and conclusions of the entire body of work. It will also discuss future avenues of research in the topic of diamond processing and characterisations, to improve the existing optical sensing applications.
Among the possible defects that can occur in diamonds, one that draws attention is the nitrogen-vacancy (NV) center.Studied since the early 90s, in recent years, they became one of the most promising platforms for field applications of quantum technology at room temperature, especially for quantum sensing.They are sensitive to electric and magnetic fields, temperature, and strain, making these nanosensors a versatile platform for many applications.The NV center's spin state is easy to read and manipulate by optical means, and, most interestingly, it works well at room temperature, which facilitates its use.The great challenge to implement quantum protocols and quantum algorithms is the coherence time of the quantum states.The NV center stands out for having relatively high coherence times at room temperature.This dissertation presents measurements to characterize the electron spin coherence of NV centers in an ultrapure sample of diamond designed for quantum sensing applications.These measurements combine optical e magnetic resonance techniques.For that, a method was implemented using a conventional CCD camera and a clever imaging protocol, making it possible to perform various pulsed microwave experiments on the electron spin, such as Rabi oscillations and Hahn spin-echo, which were used for determining the characteristic relaxation times (T 1 and T 2 ).Results show that this system provides at least two readily accessible qubits that can be used in quantum protocols even at room temperature.
Quantum sensing using nitrogen-vacancy (NV) centers in diamond has emerged as a powerful platform for detecting ultra-low magnetic fields under ambient conditions. Owing to their long spin coherence times, optical addressability, and compatibility with aqueous environments, it has found widespread applications in biosensing and bio-imaging. This review presents the fundamental principles and recent advances in NV-based quantum magnetometry for biosensing applications, with a particular focus on measurements in aqueous medium and at cellular and molecular length scales. We discuss the underlying spin physics of NV centers and highlight two primary detection modalities: optically detected magnetic resonance (ODMR) and T1 relaxometry-based sensing and how these approaches aids in the detection of both static magnetic fields and dynamic magnetic noise arising from biological processes. The review explores key application areas, including nanoscale nuclear magnetic resonance (NMR), monitoring of neural activity, detection of abnormal or rogue cells using NV-based platforms etc. In addition, strategies for enhancing sensitivity, such as surface functionalization of nanodiamonds, femtosecond (fs) laser-written photonic structures, and integration with microfluidic and lab-on-chip systems have also been discussed in depth. We also address the critical challenges, including surface-induced decoherence, charge-state instability, and signal-to-noise limitations in biofluids associated with NV-based biosensing applications. Finally, we outline future prospects, highlighting how NV-based magnetic biosensing provides a promising pathway for translating quantum sensing technologies into practical biomedical applications.
The recent decade has witnessed exciting developments in quantum science and technology. Quantum sensing is a rapidly growing branch, which exploits the fragility of quantum systems to detect small external signals. The extreme control at the single-atom level and the remarkably long coherence time of engineered quantum systems enable unprecedented sensitivity and precision, beating the performance of classical techniques. The nitrogen-vacancy (NV) center in diamond is one of the most promising quantum sensors. Its unique advantages have attracted considerable attention, including a long spin coherence time throughout a broad temperature range, nanoscale resolution limited by the sensor-sample distance, convenient optical control of its spin states and remarkably versatile sensing capabilities. Its properties are well studied under a bias magnetic field oriented along its quantization axis. However, its sensing capabilities in the presence of an off-axis magnetic field are much less explored. My research aims to unlock the full potential of NV quantum sensor by developing new sensing modalities under a magnetic field acting perpendicular to the NV axis, and furthermore, integrating them into a scanning probe microscope. In this dissertation, I will report our progress toward building a scanning NV multimodal quantum imaging platform, which will open up exciting opportunities in measuring nanoscale phenomena. The first chapter provides an introduction to the background of quantum sensing with NV centers, followed by a discussion on its basic properties and established sensing techniques. The second and third chapters are dedicated to two experiments performed under a perpendicular magnetic field where traditional NV magnetometry based on the Zeeman effect fails. In the second chapter, I will introduce a new sensing strategy that uses the entanglement between the electron and nuclear spins to restore the magnetic field sensitivity under this unfavored condition. This allows us to sense small changes in the magnetic field angle relative to the NV axis, and to detect anisotropic magnetic noise in the local environment. In the third chapter, I will present our latest development of scanning NV electrometry, where a single NV at the apex of a diamond scanning probe images external alternating (AC) and direct (DC) electric fields with sub-100 nm resolution. In the last chapter, I will discuss our efforts on four experiments that were left unfinished. I will present the results we have achieved, analyze the challenges that we faced and propose potential solutions to overcome them.