The role of the dopant in the electronic structure of erbium-doped TiO2 for quantum emitters
Jessica B. Martins, Gregory D. Grant, D. Haskel, George E. Sterbinsky, Ignas Masiulionis, Kathryn E. Sautter, Evguenia Karapetrova, Supratik Guha, J. W. Freeland
Erbium-doped TiO2 materials are promising candidates for advancing quantum technologies, necessitating a thorough understanding of their electronic and crystal structures to tailor their properties and enhance coherence times. This study explored epitaxial erbium-doped rutile TiO2 films deposited on r-sapphire substrates using molecular beam epitaxy. Photoluminescence excitation spectroscopy demonstrated decreasing photoluminescence lifetimes with erbium doping, indicating limited optical coherence times. Lattice distortions associated with Er3+ were probed by x-ray absorption spectroscopy, indicating that erbium primarily occupies Ti4+ sites and influences oxygen vacancies. Significant lattice distortions in the higher-order shells and apparent full coordination around erbium suggest that additional defects are likely prevalent in these regions. These findings indicate that defects contribute to limited coherence times by introducing alternative decay pathways, leading to shorter photoluminescence lifetimes.
Erbium-doped TiO2 materials are promising candidates for advancing quantum technologies, necessitating a thorough understanding of their electronic and crystal structures to tailor their properties and enhance coherence times. This study explored epitaxial erbium-doped rutile TiO2 films deposited on r-sapphire substrates using molecular beam epitaxy. Photoluminescence excitation spectroscopy demonstrated decreasing photoluminescence lifetimes with erbium doping, indicating limited optical coherence times. Lattice distortions associated with Er3+ were probed by x-ray absorption spectroscopy, indicating that erbium primarily occupies Ti4+ sites and influences oxygen vacancies. Significant lattice distortions in the higher-order shells and apparent full coordination around erbium suggest that additional defects are likely prevalent in these regions. These findings indicate that defects contribute to limited coherence times by introducing alternative decay pathways, leading to shorter photoluminescence lifetimes.
Erbium-doped \ch{TiO2} materials are promising candidates for advancing quantum technologies, necessitating a thorough understanding of their electronic and crystal structures to tailor their properties and enhance coherence times. This study explored epitaxial erbium-doped rutile \ch{TiO2} films deposited on r-sapphire substrates using molecular beam epitaxy. Photoluminescence excitation spectroscopy demonstrated decreasing fluorescence lifetimes with erbium doping, indicating limited coherence times. Lattice distortions associated with \ch{Er^{3+}} were probed by X-ray absorption spectroscopy, indicating that erbium primarily occupies \ch{Ti^{4+}} sites and influences oxygen vacancies. Significant lattice distortions in the higher-order shells and full coordination around erbium suggest that additional defects are likely prevalent in these regions. These findings indicate that defects contribute to limited coherence times by introducing alternative decay pathways, leading to shorter fluorescence lifetimes.
Rare-earth ion doped oxide thin films integrated on silicon substrates provide a route toward scalable, chip-scale platforms for quantum coherent devices. Erbium-doped TiO2 is an attractive candidate: the Er3+ optical transition is compatible with C-band optical fiber communications, while TiO2 is an insulating dielectric compatible with silicon process technology. Through structural and optical studies of Er-doped TiO2 thin films grown via molecular beam deposition on silicon, SrTiO3, and sapphire substrates, we have explored the impact of polycrystallinity and microstructure on the optical properties of the Er emission. Comparing polycrystalline TiO2(rutile)/Si with single-crystalline TiO2(rutile)/r-sapphire and polycrystalline TiO2(anatase)/Si with single-crystalline TiO2(anatase)/SrTiO3, we observe that the inhomogeneous linewidth (Γinh) of the most prominent peak in the Er spectrum (the Y1–Z1 transition, 1520 and 1533 nm in rutile and anatase TiO2) is significantly narrower in the polycrystalline case. This implies a relative insensitivity to extended structural defects and grain boundaries in such films (as opposed to, e.g., point defects). We show that the growth of an undoped, underlying TiO2 buffer on Si can reduce Γinh by a factor of 4–5. Expectedly, Γinh also reduces with decreasing Er concentrations: we observe a ∼2 order of magnitude reduction from ∼1000 ppm Er to ∼10 ppm Er. Γinh then gets limited to a residual value of ∼5 GHz that is insensitive to further reduction in the Er concentration. Based upon the above results, we argue that the optical properties in these thin films are limited by the presence of high “grown-in” point defect concentrations.
Rare-earth ion dopants in solid-state hosts are ideal candidates for quantum communication technologies, such as quantum memories, due to the intrinsic spin–photon interface of the rare-earth ion combined with the integration methods available in the solid state. Erbium-doped cerium oxide (Er:CeO2) is a particularly promising host material platform for such a quantum memory, as it combines the telecom-wavelength (∼1.5μm) 4f–4f transition of erbium, a predicted long electron spin coherence time when embedded in CeO2, and a small lattice mismatch with silicon. In this work, we report on the epitaxial growth of Er:CeO2 thin films on silicon using molecular beam epitaxy, with controlled erbium concentration between 2 and 130 parts per million (ppm). We carry out a detailed microstructural study to verify the CeO2 host structure and characterize the spin and optical properties of the embedded Er3+ ions as a function of doping density. In as-grown Er:CeO2 in the 2–3 ppm regime, we identify an EPR linewidth of 245(1) MHz, an optical inhomogeneous linewidth of 9.5(2) GHz, an optical excited state lifetime of 3.5(1) ms, and a spectral diffusion-limited homogeneous linewidth as narrow as 4.8(3) MHz. We test the annealing of Er:CeO2 films up to 900 °C, which yields narrowing of the inhomogeneous linewidth by 20% and extension of the excited state lifetime by 40%.
Er 3 + color centers are promising candidates for quantum science and technology due to their long electron and nuclear spin coherence times, as well as their desirable emission wavelength. By selecting host materials with suitable, controllable properties, we introduce new parameters that can be used to tailor the Er3+ emission spectrum. PbTiO3 is a well-studied ferroelectric material with known methods of engineering different domain configurations through epitaxial strain. By distorting the structure of Er3+-doped PbTiO3 thin films, we can manipulate the crystal fields around the Er3+ dopant. This is resolved through changes in the Er3+ resonant fluorescence spectra, tying the optical properties of the defect directly to the domain configurations of the ferroelectic matrix. Additionally, we are able to resolve a second set of peaks for films with in-plane ferroelectric polarization. We hypothesize these results to be due to either the Er3+ substituting different sites of the PbTiO3 crystal, differences in charges between the Er3+ dopant and the original substituent ion, or selection rules. Systematically studying the relationship between the Er3+ emission and the epitaxial strain of the ferroelectric matrix lays the pathway for future optical studies of spin manipulation by altering ferroelectric order parameters.
Rare-earth ions (REIs) doped into solid-state crystal hosts offer an attractive platform for realizing quantum interconnects that can function as quantum memories and quantum repeaters. The 4f valence electrons of REIs are shielded by 5s and 5p electrons and undergo highly coherent transitions even when embedded in host crystals. In particular, Er3+ has an optical transition in the telecom band that is suitable for low-loss communication. Recently, REIs in thin film systems have gained interest due to potential advantages in providing a flexible host crystal environment, enabling scalable on-chip integration with other quantum devices. Here, we investigate the structural and optical properties of Er-doped anatase TiO2 thin films on LaAlO3 (001) substrates. By choosing a system with minimal lattice mismatch and adjusting Er-dopant concentration, we achieve optical inhomogeneous linewidths of 5 GHz at 4.5 K. We show that 9 nm-thick buffer and capping layers can reduce the linewidth by more than 40%, suggesting a pathway to further narrowing linewidths in this system. We also identify that Er3+ ions mainly incorporate into substitutional Ti4+ sites with non-polar D2d symmetry, which makes Er dopants insensitive to the first order to local electric fields from impurities and is desirable for coherence properties of Er3+ spins.
Atomic layer deposited (ALD) Y 2 O 3 thin films have been thoroughly investigated for optical or electronic applications. The coherent spectroscopy of lanthanide ions doped into this material has also recently attracted increasing interest in the field of quantum technologies for which they are considered promising candidates in quantum memories or as spin–photon interfaces. However, these most demanding applications require a deep control over the local positioning of the ions and their close environment in the crystalline matrix. This study focuses on the structural as well as optical properties of Eu 3+ and Er 3+ dopants in Y 2 O 3 using photoluminescence (PL), luminescence decay times, and inhomogeneous line width (Γ inh ) measurements within this particular context. While as-grown ALD films do not provide an ideal host for the emitters, we demonstrate that by optimizing the deposition conditions and using appropriate annealing post treatments narrow inhomogeneous lines can be obtained for the 7 F 0 ↔ 5 D 0 transition of Eu 3+ even for nanoscale films. Furthermore, about 1.5 ms lifetime has been measured for the infrared telecom transition of Er in ultrathin films (<10 nm), which is an order of magnitude higher than in nanoparticles of the same size. These results validate optimized rare-earth-doped ALD Y 2 O 3 films as a suitable platform for photonics applications where few-nanometer-thick films with well-localized emitters are mandatory. This approach provides the first building blocks toward the development of more complex devices for quantum sensing or hybrid structures coupled with other systems such as two-dimensional materials.