Ultrathin Eu- and Er-Doped Y2O3 Films with Optimized Optical Properties for Quantum Technologies
Marion Scarafagio, Alexandre Tallaire, Klaas‐Jan Tielrooij, Daniel Cano, André Grishin, Marie‐Hélène Chavanne, Frank H. L. Koppens, Armelle Ringuedé, M. Cassir, Diana Serrano, Philippe Goldner, Alban Ferrier
Atomic layer deposited (ALD) Y 2 O 3 thin films have been thoroughly investigated for optical or electronic applications. The coherent spectroscopy of lanthanide ions doped into this material has also recently attracted increasing interest in the field of quantum technologies for which they are considered promising candidates in quantum memories or as spin–photon interfaces. However, these most demanding applications require a deep control over the local positioning of the ions and their close environment in the crystalline matrix. This study focuses on the structural as well as optical properties of Eu 3+ and Er 3+ dopants in Y 2 O 3 using photoluminescence (PL), luminescence decay times, and inhomogeneous line width (Γ inh ) measurements within this particular context. While as-grown ALD films do not provide an ideal host for the emitters, we demonstrate that by optimizing the deposition conditions and using appropriate annealing post treatments narrow inhomogeneous lines can be obtained for the 7 F 0 ↔ 5 D 0 transition of Eu 3+ even for nanoscale films. Furthermore, about 1.5 ms lifetime has been measured for the infrared telecom transition of Er in ultrathin films (<10 nm), which is an order of magnitude higher than in nanoparticles of the same size. These results validate optimized rare-earth-doped ALD Y 2 O 3 films as a suitable platform for photonics applications where few-nanometer-thick films with well-localized emitters are mandatory. This approach provides the first building blocks toward the development of more complex devices for quantum sensing or hybrid structures coupled with other systems such as two-dimensional materials.
Atomic layer deposited (ALD) Y 2 O 3 thin films have been thoroughly investigated for optical or electronic applications. The coherent spectroscopy of lanthanide ions doped into this material has also recently attracted increasing interest in the field of quantum technologies for which they are considered promising candidates in quantum memories or as spin–photon interfaces. However, these most demanding applications require a deep control over the local positioning of the ions and their close environment in the crystalline matrix. This study focuses on the structural as well as optical properties of Eu 3+ and Er 3+ dopants in Y 2 O 3 using photoluminescence (PL), luminescence decay times, and inhomogeneous line width (Γ inh ) measurements within this particular context. While as-grown ALD films do not provide an ideal host for the emitters, we demonstrate that by optimizing the deposition conditions and using appropriate annealing post treatments narrow inhomogeneous lines can be obtained for the 7 F 0 ↔ 5 D 0 transition of Eu 3+ even for nanoscale films. Furthermore, about 1.5 ms lifetime has been measured for the infrared telecom transition of Er in ultrathin films (<10 nm), which is an order of magnitude higher than in nanoparticles of the same size. These results validate optimized rare-earth-doped ALD Y 2 O 3 films as a suitable platform for photonics applications where few-nanometer-thick films with well-localized emitters are mandatory. This approach provides the first building blocks toward the development of more complex devices for quantum sensing or hybrid structures coupled with other systems such as two-dimensional materials.
The use of rare earth ions (REIs)—typically embedded as atomic defects in solids—has emerged as a promising strategy for practical quantum memories. In particular, the Er ion has garnered significant attention due to its telecom C-band optical transition, which makes it a suitable candidate for integration into existing optical fiber networks without the need for photon wavelength conversion. However, successful scalability of such a quantum memory platform would benefit greatly from employing a host material that is fully compatible with silicon and modern CMOS fabrication processes. In this study, we present the synthesis of Er-doped TiO2 thin films directly on standard silicon or silicon-on-insulator (SOI) substrates using atomic layer deposition (ALD). Our thin film exhibits favorable emitter properties at cryogenic temperatures (T = 3.5 K), including a narrow inhomogeneous linewidth and optical lifetime approaching that of bulk values. Additionally, the ALD process provides ample opportunities for device fabrication and integration with other components, further enhancing its potential for practical applications. Overall, our findings suggest that Er-doped TiO2 thin films synthesized via ALD represent a promising approach for developing practical quantum memories that can be seamlessly integrated with silicon photonics. This work lays a foundation for the development of quantum technologies with potential applications in communication, computing, and cryptography.
The control of rare-earth ion doping profiles is a key challenge for several photonic applications and quantum technologies that require spatially localized emitters. In this work, we propose to use atomic layer deposition (ALD) followed by an annealing post-treatment to localize europium emitters close to the surface of a Y 2 O 3 film or a Y 2 SiO 5 single crystal by exploiting in-diffusion. Indeed, ALD is a conformal method that can provide in-depth nanometer-scale positioning accuracy on a large scale. However, the post-thermal annealing required to achieve higher crystalline quality and activate diffusion needs to be precisely controlled to maximize our ability to localize ions. In this paper, we evaluate europium ion diffusion in an ALD-grown Eu 2 O 3 /Y 2 O 3 /Si stack using Rutherford backscattering spectroscopy (RBS) and time-of-flight secondary ion mass spectrometry (TOF-SIMS). We then extend this approach to investigate diffusion from a Eu 2 O 3 ALD film into a single-crystalline substrate of Y 2 SiO 5 (YSO), a technologically relevant material system for quantum applications. We determine the Eu 3+ diffusion coefficients in both cases and show that diffusion starts at 950 °C in the polycrystalline Y 2 O 3 ALD submicron film, whereas it becomes significant only above 1200 °C in single-crystal YSO. Finally, spectral hole burning of such in-diffused emitters revealed homogeneous lines as narrow as 2 MHz. This study indicates that appropriate annealing of ALD-grown rare-earth oxide films can be harnessed to create localized dopants that preserve their outstanding optical properties, a prerequisite for their integration into photonic and quantum devices.
Rare-earth ions (REIs) have incomplete 4f shells and possess narrow optical intra-4f transitions due to shielding from electrons in the 5s and 5p orbitals, making them good candidates for solid-state optical quantum memory. The emission of Er3+ in the telecom C-band (1530 nm–1565 nm) makes it especially attractive for this application. In order to build practical, scalable devices, the REI needs to be embedded in a non-interacting host material, preferably one that can be integrated with silicon. In this paper, we show that Er3+ can be isovalently incorporated into epitaxial Y2O3 thin films on Si (111). We report on the synthesis of epitaxial, single-crystalline Er:Y2O3 on Si with a narrow inhomogeneous linewidth in the photoluminescence (PL) spectra, 5.1 GHz (<100 mK), and an optical excited state lifetime of 8.1 ms. The choice of Y2O3 was driven by its low nuclear spin and small lattice mismatch with Si. Using PL and electron paramagnetic resonance, we show that Er3+ substitutes for Y in the crystal lattice. The role of interfacial SiOx, diffusion of silicon into the film, and the effect of buffer layers on the inhomogeneous PL linewidth are examined. We also find that the linewidth decreased monotonically with film thickness but surprisingly exhibits no correlation with the film crystalline quality, as measured by the x-ray rocking curve scans, suggesting other factors at play that limit the inhomogeneous broadening in Y2O3 films.
Rare-earth ion dopants in solid-state hosts are ideal candidates for quantum communication technologies, such as quantum memories, due to the intrinsic spin–photon interface of the rare-earth ion combined with the integration methods available in the solid state. Erbium-doped cerium oxide (Er:CeO2) is a particularly promising host material platform for such a quantum memory, as it combines the telecom-wavelength (∼1.5μm) 4f–4f transition of erbium, a predicted long electron spin coherence time when embedded in CeO2, and a small lattice mismatch with silicon. In this work, we report on the epitaxial growth of Er:CeO2 thin films on silicon using molecular beam epitaxy, with controlled erbium concentration between 2 and 130 parts per million (ppm). We carry out a detailed microstructural study to verify the CeO2 host structure and characterize the spin and optical properties of the embedded Er3+ ions as a function of doping density. In as-grown Er:CeO2 in the 2–3 ppm regime, we identify an EPR linewidth of 245(1) MHz, an optical inhomogeneous linewidth of 9.5(2) GHz, an optical excited state lifetime of 3.5(1) ms, and a spectral diffusion-limited homogeneous linewidth as narrow as 4.8(3) MHz. We test the annealing of Er:CeO2 films up to 900 °C, which yields narrowing of the inhomogeneous linewidth by 20% and extension of the excited state lifetime by 40%.
Rare earth ions hosted in solids are good candidates for quantum technologies due to their chemical stability and optical and spin transitions exhibiting long coherence lifetimes. While bulk oxide crystals are usually the preferred host material, the development of a scalable silicon-compatible thin film platform would be desirable. In this paper, we report on the growth of Y2(1−x)Eu2xO3 thin films on silicon in the full range of Eu3+ concentration by direct liquid injection chemical vapor deposition (CVD). Our sub-micrometer polycrystalline films with a strong-(111) texture were grown for all compositions into the bixbyite cubic phase. The variation of growth rates with temperature and flow indicated that deposition occurred through a mass-transport controlled regime. Optical assessment of the Eu-doped thin films showed inhomogeneous linewidths as narrow as 50 GHz and fluorescence lifetimes of 1 ms for the lowest concentrations. Finally, a spectral hole was successfully burned in a 200 nm-thin film with a 2% Eu doping leading to a homogeneous linewidth of 11 MHz. These values are still below those reported for bulk single crystals indicating that additional decoherence mechanisms exist in such nanometric films, which might be alleviated by further improvement of the crystalline quality. Nevertheless, these results pave the way to the use of CVD-grown Eu:Y2O3 thin films as a platform for integrated quantum devices.
Rare-earth ions (REIs) doped into solid-state crystal hosts offer an attractive platform for realizing quantum interconnects that can function as quantum memories and quantum repeaters. The 4f valence electrons of REIs are shielded by 5s and 5p electrons and undergo highly coherent transitions even when embedded in host crystals. In particular, Er3+ has an optical transition in the telecom band that is suitable for low-loss communication. Recently, REIs in thin film systems have gained interest due to potential advantages in providing a flexible host crystal environment, enabling scalable on-chip integration with other quantum devices. Here, we investigate the structural and optical properties of Er-doped anatase TiO2 thin films on LaAlO3 (001) substrates. By choosing a system with minimal lattice mismatch and adjusting Er-dopant concentration, we achieve optical inhomogeneous linewidths of 5 GHz at 4.5 K. We show that 9 nm-thick buffer and capping layers can reduce the linewidth by more than 40%, suggesting a pathway to further narrowing linewidths in this system. We also identify that Er3+ ions mainly incorporate into substitutional Ti4+ sites with non-polar D2d symmetry, which makes Er dopants insensitive to the first order to local electric fields from impurities and is desirable for coherence properties of Er3+ spins.