Understanding the loss mechanisms in materials is crucial to improving coherence in superconducting quantum circuits. The authors present a technique based on multimode superconducting resonators that distinguishes and quantifies all loss channels in relevant materials. Applying this technique reveals that both chemical etching and diamond turning reduce surface losses in high-purity aluminum, while coating diamond-turned surfaces with thin-film aluminum significantly improves joint quality. This method can be used to design on-chip superconducting devices to characterize microwave losses, as well as to quantify the effects of fabrication processes.
Understanding the loss mechanisms in materials is crucial to improving coherence in superconducting quantum circuits. The authors present a technique based on multimode superconducting resonators that distinguishes and quantifies all loss channels in relevant materials. Applying this technique reveals that both chemical etching and diamond turning reduce surface losses in high-purity aluminum, while coating diamond-turned surfaces with thin-film aluminum significantly improves joint quality. This method can be used to design on-chip superconducting devices to characterize microwave losses, as well as to quantify the effects of fabrication processes.
Measuring the losses arising from different materials and interfaces is crucial to improving the coherence of superconducting quantum circuits. Although this has been of interest for a long time, current studies can either only provide bounds to those losses, or require several devices for a complete characterization. In this work, we introduce a method to measure the microwave losses of materials and interfaces with a single multi-mode superconducting resonator. We demonstrate a formalism for analyzing the loss sensitivity of multi-mode systems and discuss the design strategies of multi-mode resonators for material loss studies. We present two types of multi-mode superconducting resonators for the study of bulk superconductors: the forky whispering-gallery-mode resonator (FWGMR) and the ellipsoidal cavity. We use these resonators to measure the surface dielectric, conductor, and seam losses of high-purity (5N5) aluminum and aluminum alloy (6061), as well as how they are affected by chemical etching, diamond turning, and thin-film coating. We find that chemical etching and diamond turning reduce both the surface dielectric and conductive losses of high-purity aluminum, but provide no appreciable improvement to the seam. Coating the surfaces of diamond-turned aluminum alloys with e-beam evaporated or sputtered aluminum thin-films significantly reduces all three losses under study. In addition, we study the effect of chemical etching on the surface of high-purity aluminum using transmission electron microscopy (TEM) and find that the chemical etching process creates a thinner and more uniform oxide layer, consistent with the observed improvement in the surface dielectric loss.
The recent realization of millisecond-scale coherence with tantalum-on-silicon transmon qubits showed that depositing the Al/AlOx/Al Josephson junction in a high purity, ultrahigh vacuum environment was critical for achieving lifetime-limited coherence, motivating careful examination of the aluminum surface two-level system (TLS) bath. Here, we measure the microwave absorption arising from surface TLSs in superconducting aluminum resonators, following methodology developed for tantalum resonators. We vary film and surface properties and correlate microwave measurements with materials characterization. We find that the lifetimes of superconducting aluminum resonators are primarily limited by surface losses associated with TLSs in the 2.7 nm-thick native AlOx. Treatment with 49% HF removes surface AlOx completely; however, rapid oxide regrowth limits improvements in surface loss and long term device stability. Using these measurements we estimate that TLSs in aluminum interfaces contribute around 27% of the relaxation rate of state-of-the-art tantalum-on-silicon qubits that incorporate aluminum-based Josephson junctions.
Material losses in superconducting circuits fundamentally limit qubit coherence times and resonator quality factors. Most research efforts focus on mitigating losses at circuit interfaces, including metal--substrate, substrate--air, and metal--air interfaces. However, the correlation between TLS and non-TLS losses with the intrinsic properties of the superconducting metal and the dielectric edge smoothness is not well studied. In this work, we link the aluminum film grain size to non-TLS losses and the dielectric trimming profile and roughness to TLS loss; both loss mechanisms are subsequently mitigated. To reduce metal-related losses, we engineer the aluminum microstructure by heating during deposition, increasing grain size and reducing grain boundary density. Beyond mitigating metal losses, we introduce a two-step etching technique, Tropic etching, to suppress dielectric TLS loss by producing an ultra-smooth silicon surface with minimal defects and redeposition. These results lay out the fabrication pathway for aluminum resonators with lower loss, demonstrating two-orders-of-magnitude improvement in quality factor from 6×104 to 2.3×106. Since aluminum is the basis for most high-coherence Josephson junctions and dielectric edges are inherent to all common device geometries, the improvements in aluminum microstructure and edge profiling, presented here, can enhance the performance of superconducting quantum devices.
The performance of superconducting circuits for quantum computing is limited by materials losses. In particular, coherence times are typically bounded by two-level system (TLS) losses at single photon powers and millikelvin temperatures. The identification of low loss fabrication techniques, materials, and thin film dielectrics is critical to achieving scalable architectures for superconducting quantum computing. Superconducting microwave resonators provide a convenient qubit proxy for assessing performance and studying TLS loss and other mechanisms relevant to superconducting circuits such as non-equilibrium quasiparticles and magnetic flux vortices. In this review article, we provide an overview of considerations for designing accurate resonator experiments to characterize loss, including applicable types of losses, cryogenic setup, device design, and methods for extracting material and interface losses, summarizing techniques that have been evolving for over two decades. Results from measurements of a wide variety of materials and processes are also summarized. Finally, we present recommendations for the reporting of loss data from superconducting microwave resonators to facilitate materials comparisons across the field.
Scalable architectures characterized by quantum bits (qubits) with low error rates are essential to the development of a practical quantum computer. In the superconducting quantum computing implementation, understanding and minimizing material losses are crucial to the improvement of qubit performance. A new material that has recently received particular attention is indium, a low-temperature superconductor that can be used to bond pairs of chips containing standard aluminum-based qubit circuitry. In this work, we characterize microwave loss in indium and aluminum/indium thin films on silicon substrates by measuring superconducting coplanar waveguide resonators and estimating the main loss parameters at powers down to the sub-photon regime and at temperatures between 10 and 450 mK. We compare films deposited by thermal evaporation, sputtering, and molecular beam epitaxy. We study the effects of heating in a vacuum and ambient atmospheric pressure as well as the effects of pre-deposition wafer cleaning using hydrofluoric acid. The microwave measurements are supported by thin film metrology including secondary-ion mass spectrometry. For thermally evaporated and sputtered films, we find that two-level state are the dominant loss mechanism at low photon number and temperature, with a loss tangent due to native indium oxide of ∼5×10−5. The molecular beam epitaxial films show evidence of the formation of a substantial indium-silicon eutectic layer, which leads to a drastic degradation in resonator performance.
Many superconducting qubits are highly sensitive to dielectric loss, making the fabrication of coherent quantum circuits challenging. To elucidate this issue, we characterize the interfaces and surfaces of superconducting coplanar waveguide resonators and study the associated microwave loss. We show that contamination induced by traditional qubit lift-off processing is particularly detrimental to quality factors without proper substrate cleaning, while roughness plays at most a small role. Aggressive surface treatment is shown to damage the crystalline substrate and degrade resonator quality. We also introduce methods to characterize and remove ultra-thin resist residue, providing a way to quantify and minimize remnant sources of loss on device surfaces.