Quantum technologies are expected to significantly change our world in the next decades and the possible applications are diverse – ranging from quantum computation and encryption to metrology with unprecedented sensitivity. This thesis focuses on quantum sensing and imaging based on single nitrogen-vacancy (NV) centres in diamond to measure magnetic fields. Its electronic spin qualifies this point defect as a highly sensitive quantum sensor and its atomic size offers nanoscale spatial resolution. The simple optical initialisation and readout, together with the relatively long coherence time at ambient conditions, make NV centres promising candidates for biological applications and in particular for nuclear magnetic resonance (NMR) on the nanoscale. Recording the spectral information on the nanoscale allows to determine the structure of single or just a few molecules. However, the current main problems and challenges include insufficient spectral resolution, artificial signals and overall poor performance. In this thesis new spectroscopic techniques which tackle these issues are presented. First, it is shown that by randomisation of control pulse phases spurious harmonic signals can be suppressed, which otherwise complicate spectrum interpretation and can lead to false signal identification. At the same time the effects of pulse imperfections are mitigated. Furthermore, a protocol allowing to measure with a coherence independent spectral resolution is presented. It is demonstrated that linewidths below 1mHz are possible, which is an improvement of more than seven orders of magnitude compared to traditional methods. Due to its simple implementation, the protocol is relevant for many applications. Initially developed to measure signals oscillating up to several megahertz, it is further shown that modifications allow to extend the frequency range into the gigahertz domain. Finally, quantum frequency discrimination with the task to differentiate between two frequency distributions using a quantum sensor is analysed. An optimised protocol is introduced and the influences of different readout strategies are discussed with respect to the probability to make an incorrect decision. These findings are useful for diagnostic tests in NMR.
Quantum technologies are expected to significantly change our world in the next decades and the possible applications are diverse – ranging from quantum computation and encryption to metrology with unprecedented sensitivity. This thesis focuses on quantum sensing and imaging based on single nitrogen-vacancy (NV) centres in diamond to measure magnetic fields. Its electronic spin qualifies this point defect as a highly sensitive quantum sensor and its atomic size offers nanoscale spatial resolution. The simple optical initialisation and readout, together with the relatively long coherence time at ambient conditions, make NV centres promising candidates for biological applications and in particular for nuclear magnetic resonance (NMR) on the nanoscale. Recording the spectral information on the nanoscale allows to determine the structure of single or just a few molecules. However, the current main problems and challenges include insufficient spectral resolution, artificial signals and overall poor performance. In this thesis new spectroscopic techniques which tackle these issues are presented. First, it is shown that by randomisation of control pulse phases spurious harmonic signals can be suppressed, which otherwise complicate spectrum interpretation and can lead to false signal identification. At the same time the effects of pulse imperfections are mitigated. Furthermore, a protocol allowing to measure with a coherence independent spectral resolution is presented. It is demonstrated that linewidths below 1mHz are possible, which is an improvement of more than seven orders of magnitude compared to traditional methods. Due to its simple implementation, the protocol is relevant for many applications. Initially developed to measure signals oscillating up to several megahertz, it is further shown that modifications allow to extend the frequency range into the gigahertz domain. Finally, quantum frequency discrimination with the task to differentiate between two frequency distributions using a quantum sensor is analysed. An optimised protocol is introduced and the influences of different readout strategies are discussed with respect to the probability to make an incorrect decision. These findings are useful for diagnostic tests in NMR.
In modern-day quantum metrology, quantum sensors are widely employed to detect weak magnetic fields or nanoscale signals. Quantum devices, exploiting quantum coherence, are inevitably connected to physical constants and can achieve accuracy, repeatability, and precision approaching fundamental limits. As a result, these sensors have shown utility in a wide range of research domains spanning both science and technology. A rapidly emerging quantum sensing platform employs atomic-scale defects in crystals. In particular, magnetometry using nitrogen-vacancy (NV) color centers in diamond has garnered increasing interest. NV systems possess a combination of remarkable properties, optical addressability, long coherence times, and biocompatibility. Sensors based on NV centers excel in spatial resolution and magnetic sensitivity. These diamond-based sensors promise comparable combination of high spatial resolution and magnetic sensitivity without cryogenic operation. The above properties of NV magnetometers promise increasingly integrated quantum measurement technology, as a result, they have been extensively developed with various protocols and find use in numerous applications spanning materials characterization, nuclear magnetic resonance (NMR), condensed matter physics, paleomagnetism, neuroscience and living systems biology, and industrial vector magnetometry. In this chapter, NV centers are explored for magnetic sensing in a number of contexts. In general, we introduce novel regimes for magnetic-field probes with NV ensembles. Specifically, NV centers are developed for sensitive magnetometers for applications where microwaves (MWs) are prohibitively invasive and operations need to be carried out under zero ambient magnetic field. The primary goal of our discussion is to improve the utility of these NV center-based magnetometers.
When the word diamond comes up, the majority of people thinks about engagement rings or gemstones. In fact, it is additionally, one of the most promising host materials for the implementation of advanced technology, exploiting the nature of quantum physics. Such quantum technologies have disruptive potential, ones the quantum effects can be applied in macroscopic, commercial products. The nitrogen-vacancy (NV) centre in diamond is a promising candidate to perform such tasks in the fields of quantum computation, quantum cryptography or metrology. Especially in the field of quantum sensing, the NV sensor impresses with nano-scale spatial resolution paired with high sensitivity. The electronic spin of the atomic-sized point defect can be initialised, manipulated and read-out at ambient conditions and coherence lifetimes are comparably long. Diamond magnetometers based on negatively charged NV centres have shown to be very attractive, and the sensitivity goes down to the single-atom level. In order to exploit such a high sensitivity level for sensing prospects, in this thesis, the NV centres are fabricated well confined in a certain distance to the diamond surface, since the detectable field usually decays with the third power of the distance between sensor and target. The surface depicts a fracture of the spin wise protecting diamond lattice and charge fluctuations affect the stability of NV centres, which are overcome by diamond surface termination. In order to improve the sensitivity further, the sensor density, measurement contrast and interaction time are increased. The nitrogen doping technique, which is applied during a plasma-enhanced chemical vapour deposition (PECVD) diamond growth process is used to fabricate NV centre ensembles aligned along one diamond crystal axis, thereby improving the measurement contrast by a factor up to four. The interaction time limiting spin bath is analysed using the sensor capabilities of the NVs, which leads to enhanced growth strategies and the fabrication of sensitivity optimised NV centre ensembles for magnetometry applications.
The recent decade has witnessed exciting developments in quantum science and technology. Quantum sensing is a rapidly growing branch, which exploits the fragility of quantum systems to detect small external signals. The extreme control at the single-atom level and the remarkably long coherence time of engineered quantum systems enable unprecedented sensitivity and precision, beating the performance of classical techniques. The nitrogen-vacancy (NV) center in diamond is one of the most promising quantum sensors. Its unique advantages have attracted considerable attention, including a long spin coherence time throughout a broad temperature range, nanoscale resolution limited by the sensor-sample distance, convenient optical control of its spin states and remarkably versatile sensing capabilities. Its properties are well studied under a bias magnetic field oriented along its quantization axis. However, its sensing capabilities in the presence of an off-axis magnetic field are much less explored. My research aims to unlock the full potential of NV quantum sensor by developing new sensing modalities under a magnetic field acting perpendicular to the NV axis, and furthermore, integrating them into a scanning probe microscope. In this dissertation, I will report our progress toward building a scanning NV multimodal quantum imaging platform, which will open up exciting opportunities in measuring nanoscale phenomena. The first chapter provides an introduction to the background of quantum sensing with NV centers, followed by a discussion on its basic properties and established sensing techniques. The second and third chapters are dedicated to two experiments performed under a perpendicular magnetic field where traditional NV magnetometry based on the Zeeman effect fails. In the second chapter, I will introduce a new sensing strategy that uses the entanglement between the electron and nuclear spins to restore the magnetic field sensitivity under this unfavored condition. This allows us to sense small changes in the magnetic field angle relative to the NV axis, and to detect anisotropic magnetic noise in the local environment. In the third chapter, I will present our latest development of scanning NV electrometry, where a single NV at the apex of a diamond scanning probe images external alternating (AC) and direct (DC) electric fields with sub-100 nm resolution. In the last chapter, I will discuss our efforts on four experiments that were left unfinished. I will present the results we have achieved, analyze the challenges that we faced and propose potential solutions to overcome them.
Synthetic diamond has recently emerged as a candidate material for a number of quantum applications, including quantum information processing and quantum sensing. In this talk, I will show how single nitrogen-vacancy (NV) color centers can be created near the diamond surface and used as nanoscale sensors of electric and magnetic fields. I will also demonstrate novel dynamical decoupling techniques allowing to improve the sensitivity of diamond quantum sensors and discuss applications of small-scale quantum registers for nanoscale NMR. Applications of NV centers for hyperpolarisation of nuclear spins and application of optical spin polarization in MRI will be presented.
Enhancing quantum sensing The quantum properties of the nitrogen vacancy (NV) defect in diamond can be used as an atomic compass needle that is sensitive to tiny variations in magnetic field. Schmitt et al. and Boss et al. successfully enhanced this sensitivity by several orders of magnitude (see the Perspective by Jordan). They applied a sequence of pulses to the NV center, the timing of which was set by and compared with a highly stable oscillator. This allowed them to measure the frequency of an oscillating magnetic field (megahertz bandwidth) with submillihertz resolution. Such enhanced precision measurement could be applied, for example, to improve nuclear magnetic resonance-based imaging protocols of single molecules. Science , this issue p. 832 , p. 837 ; see also p. 802
The fluorescence of the nitrogen-vacancy (NV) centre in artificial diamond has been widely studied for applications such as quantum communication protocols, quantum computation, fluorescence-based biolabelling, and optical sensing. Optical sensing by itself encompasses a wide range of possible applications: from magnetic and electric field sensing to temperature sensing and enabling, for example, the detection of paramagnetic ions and the identification of molecules by nuclear magnetic resonance. Compared to many other systems capable of optical sensing, the NV centre works at room temperature, and its spin-dependent fluorescence emission is the key property to achieve a high sensitivity to the surrounding environment. Additionally, the NV centre emission is highly photostable, has a relatively short lifetime (~ 12ns) and spans a broad wavelength range, from the red to the near-infrared region of the electromagnetic spectrum (600 - 800nm). While the common denominator of all mentioned applications is the NV centre, the properties of the artificial diamond surrounding the NV centre have a significant impact on its sensing performance. At present, the processing of artificial diamond has not been fully optimised, and research and development towards the realisation of the `best¿ diamond sample for optical sensing is far from over. Specifically, the role of other defects in diamond and their effects on the photo-physical properties of the NV centres are not entirely understood. In this thesis, I will discuss the potential benefits of a novel processing technique to create ensembles of NV centres, and the importance that surrounding nitrogen defects has on the achievable magnetic field sensitivity. Additionally, I will show both theoretical and experimental investigations of the NV centres photo-physical processes, with focus on magnetic field sensing. I will initially explore a protocol for microwave-free magnetometry. This protocol predicts a theoretical magnetic field sensitivity <10µT/√Hz in the range 0.3 - 30mT and I will demonstrate it experimentally with a maximum sensitivity of 3.6mT/Hz. Following, I will focus on exploring techniques to increase the magnetic field sensitivity by improving the material properties of the diamond samples. I will demonstrate that the simultaneous electron irradiation and annealing improves the creation efficiency of an ensemble of NV centres by up to 117%. Finally, I will investigate how substitutional nitrogen defects in the surrounding lattice affects the charge state of the NV centre, its emission intensity, its lifetime and its magnetic field sensitivity. I will study a sample characterised by multiple regions across its volume, with nitrogen concentration changing between 10ppm and 100ppm in each region. There si an optimal region with ~ 40ppm of substitutional nitrogen which demonstrates the highest fluorescence emission, mainly from the negatively-charged NV centre, and the highest magnetic field sensitivity of 1.6 ± 0.2µT/√Hz. However, both the regions with lower and higher substitutional nitrogen concentration than the optimal region show lower emission intensity and worse magnetic field sensitivity. Following is a summary of the content in each chapter: Chapter 1 will present an introduction to the diamond material and the classification of artificial diamond samples. It will introduce the NV centre, its fluorescence properties and the process to create NV centres in diamond. The chapter will also introduce the concepts around optical magnetometry and the working principle that allows the NV centre to sense magnetic fields as well as other external quantities, such as temperature or pressure. Finally, it will include a brief overview of the defects that are found in artificial diamond or are created during the sample processing. Chapter 2 will describe the working principle of the instruments utilised in this work. I will list the details of each instrument and describe the methods used for the analysis of the data. Chapter 3 will introduce the background of modelling the fluorescence emission from NV centres. I will discuss the implementation of a computational model based on the Lindblad master equation to simulate the photo-physical dynamics of the NV centre. I will demonstrate the successful simulation of the saturation emission, fluorescence lifetime and optically detected magnetic resonance using the theoretical model. Finally, I will explore the theoretically predicted sensitivity of microwave-free magnetometry, based on the NV centre emission intensity change under an external magnetic field. Chapter 4 will demonstrate experimentally the microwave-free magnetometry technique. In relation to the study of microwave-free magnetometry, this chapter will explore an unexpected increase in emission intensity at high magnetic fields > 100mT. Combining the experimental observations and the theoretical simulation developed in the previous chapter, I will identify and discuss a phenomenological decrease in the NV centre transition rate from the triplet state to the singlet state. The chapter will conclude comparing the experimental and theoretical sensitivities associated with the microwave-free magnetometry technique. Chapter 5 will show the characterisation of a diamond sample at each step of the process to create NV centres. I will study the electron irradiation followed by separate annealing on a high-pressure high-temperature diamond sample. I will then characterise the sample employing visible and infrared absorption spectroscopy, as well as measure the fluorescence spectra and lifetime of the defects identified at each step. Chapter 6 will examine an alternative method to create NV centres in diamond. I will compare diamond samples irradiated and annealed separately with samples simultaneously irradiated and annealed (referred to as 'annealing in situ'). To compare the two processes, I will estimate the concentration of nitrogen defects and NV centres and calculate their N-to-NV conversion efficiency. Chapter 7 will discuss the effects of substitutional nitrogen on the properties of the NV centres in diamond. For this discussion, I will use a single-crystal diamond that shows the presence of 4 growth sectors. Each growth sector is characterised by a different nitrogen concentration, as I will demonstrate at the beginning of the chapter. I will focus on 4 main properties affected by the concentration of nitrogen in the different sectors: the balance between the charge states of the NV centre, the overall fluorescence intensity from each sector, the fluorescence lifetime and its relation to non-radiative processes, and the magnetic field sensitivity obtained with the optically detected magnetic resonance technique. Chapter 8 will gather the results and conclusions of the entire body of work. It will also discuss future avenues of research in the topic of diamond processing and characterisations, to improve the existing optical sensing applications.