We report the results of high-energy (1.8 MeV) proton implantation in a type-Ib diamond.The focused ion beam was used to introduce vacancies in a 20 µm-deep layer with applied doses in the range of 10 13 to 10 16 ions/cm 2 .The sample was subsequently annealed in vacuum which resulted in migration of vacancies and their association with the nitrogen present in the diamond matrix.We studied properties of the formed nitrogen-vacancy centers with photoluminescence and optically detected magnetic resonance.The samples are aimed to be used in sensing applications, e.g., magnetometry and bio-magnetic imaging.
The negatively-charged nitrogen-vacancy (NV) center is the most studied optical center in diamond and is very important for applications in quantum information science. Many proposals for integrating NV centers in quantum and sensing applications rely on their tailored fabrication in ultra pure host material. In this study, we use ion implantation to controllably introduce nitrogen into high purity, low nitrogen chemical vapor deposition diamond samples. The properties of the resulting NV centers are studied as a function of implantation temperature, annealing temperature, and implantation fluence. We compare the implanted NV centers with native NV centers present deep in the bulk of the as-grown samples. The results for implanted NV centers are promising but indicate, at this stage, that the deep native NV centers possess overall superior optical properties. In particular, the implanted NV centers obtained after annealing at 2000 °C under a stabilizing pressure of 8 GPa showed an ensemble linewidth of 0.17 nm compared to 0.61 nm after annealing at 1000 °C. Over the same temperature range, the ensemble NV−/NV0 ratio increased by a factor of ∼5, although this was accompanied by an overall decrease in the NV count.
Precise control over the spatial distribution and charge state of nitrogen-vacancy (NV) centers in diamond is a key requirement for further advancing this platform in quantum sensing and photonic applications. Here, we investigate nitrogen ion implantation as a scalable method to engineer NV centers in bulk single-crystalline (SC) and a 5 μ m -thick polycrystalline (PC) diamond membrane. Nitrogen-doped regions (1–80 ppm) were fabricated using a 0.7 MeV ion beam and high-temperature annealing, with NV center formation verified by confocal fluorescence imaging and spectral analysis. In SC bulk diamond, we estimate the NV concentration from spectral analysis and model the fluorescence response as a function of implantation dose, capturing both the initial increase at low concentrations and a saturation behavior at higher doses due to quenching mechanisms. In contrast, PC diamond membranes show a weaker dependence at low implantation fluences, consistent with pre-existing nitrogen impurities, thus making a statistical model significantly more complex. The activation yield is found to be of order of 1%, which is lower than in N-rich diamond samples, as implanted N is predominantly interstitial. Photoluminescence spectroscopy indicates that NV 0 is the dominant charge state in both materials, with a laser-power-dependent redistribution between neutral and negative charge states. Optically detected magnetic resonance (ODMR) measurements in SC bulk diamond resolve the hyperfine structure and allow extraction of the dephasing time ( T 2 ∗ ), while in PC diamond membranes, where NV centers tend do form near the grain boundaries, the ODMR signals are observed but spectral resolution is currently limited by impurities, grain-dependent NV orientations, and photoluminescence background.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.
We studied the parameters to optimize the production of negatively charged nitrogen-vacancy color centers (NV${}^{\ensuremath{-}}$) in type-1b single crystal diamond using proton irradiation followed by thermal annealing under vacuum. Several samples were treated under different irradiation and annealing conditions and characterized by slow positron beam Doppler-broadening and photoluminescence (PL) spectroscopies. At high proton fluences another complex vacancy defect appears limiting the formation of NV${}^{\ensuremath{-}}$. Concentrations as high as $2.3\ifmmode\times\else\texttimes\fi{}{10}^{18}$ cm${}^{\ensuremath{-}3}$ of NV${}^{\ensuremath{-}}$ have been estimated from PL measurements. Furthermore, we inferred the trapping coefficient of positrons by NV${}^{\ensuremath{-}}$. This study brings insight into the production of a high concentration of NV${}^{\ensuremath{-}}$ in diamond, which is of utmost importance in ultrasensitive magnetometry and quantum hybrid systems applications.