The nanometer‐scale engineering of single nitrogen‐vacancy (NV) centres in diamond can be obtained by low‐energy (keV) nitrogen implantation with limited straggling. However, shallow NV centres (a few nanometres deep) generally have inferior overall properties than deeply implanted or deep native NV centres, due to the surface proximity. It has already been shown that the spin coherence time of shallow NVs is improved by overgrowth of a thin diamond layer. However the influence of the overgrowth on the survival, the optical properties and the charge state of the centres has not been studied in detail. In this article, we have overgrown three diamond samples (containing NV centres implanted at different depths) using different procedures. We show the successful overgrowth of a pattern of very shallow (2 nm) implanted NV centres using an optimised overgrowth process. Furthermore, the charge state of ensembles and single NV centres was found to be shifted from NV0 to NV− and stabilised in the negative charge state after overgrowth. The combination of low‐energy high‐resolution ion implantation and high‐purity chemical vapour deposition (CVD) overgrowth procedures opens the way towards the fabrication of scalable and efficient quantum devices based on single defects in diamond. Left: implanted pattern of very shallow NV centres (depth ∼2 nm) using a pierced AFM tip. Right: same pattern after CVD overgrowth of a 4 μm‐thick diamond layer.
Engineering shallow nitrogen-vacancy (NV) centers in diamond holds the key to unlocking new advances in nanoscale quantum sensing. We find that the creation of near-surface NVs through delta doping during diamond growth allows for tunable control over both NV depth confinement (with a twofold improvement relative to low-energy ion implantation) and NV density, ultimately resulting in highly-sensitive single defects and ensembles with coherence limited by NV-NV interactions. Additionally, we demonstrate the utility of our shallow delta-doped NVs by imaging magnetism in few-layer CrSBr, a two-dimensional magnet. We anticipate that the control afforded by near-surface delta doping will enable new developments in NV quantum sensing from nanoscale NMR to entanglement-enhanced metrology.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.
Negatively charged nitrogen-vacancy (NV
−) centers located a few nanometers below the diamond surface are key quantum defects for nanoscale sensing of external spins. However, the creation of shallow NV
− centers with high yield remains a materials challenge. Here, we demonstrate that high-angle ion implantation enhances the creation efficiency of shallow NV
− centers. By implanting
15N ions at angles exceeding 60
∘, we achieve high NV
− yields approaching 10% with effective NV
− depths below 10 nm. These yields are significantly higher than those typically reported for shallow NV
− creation. The enhanced NV
− yield is consistent with an increased vacancy-to-nitrogen ratio in the near-surface region, which is expected to promote NV formation during annealing. The created NV
− ensembles show coherence properties comparable to those of single shallow NV
− centers at similar depths, and allow detection of nuclear spins in van der Waals materials attached to the diamond surface. Our results establish geometric control of ion implantation as a simple and broadly applicable approach to engineer shallow vacancy-related quantum defects.
High spatial resolution quantum sensing of near-surface nitrogen vacancy (NV) centers in diamond has enabled detection of magnetic, electrical, and thermal signals at the nanoscale. At depths of just a few nanometers, NV centers serve as localized quantum probes for external spins or low-dimensional materials, but their proximity to the surface also enhances decoherence caused by fluctuating nuclear spins. While advances in surface engineering have stabilized the charge state of NV centers at depths of tens of nanometers, achieving both ultra-shallow implantation (0.5-2 nm) and long-term spin coherence remains a central challenge. In this work, we show using first-principles modeling that, by exploiting the interaction of surface-induced strain and weak dc magnetic fields, the spin coherence times of 1-nm-deep NV centers can be greatly improved near the spin-phonon-confined regime at room temperature in 12C-rich diamonds. We also demonstrate that this protocol benefits ~ 10-nm-deep NV centers in natural diamond, enabling vector magnetometry at the nanoscale. Shallow NV centers in diamond are advantageous for quantum sensing but suffer from surface magnetic noise. Using first-principles simulations supported by experiments, the authors show that a combination of small magnetic fields and surface strain can significantly enhance spin coherence of 1 nm-deep NV centers.
To improve the sensitivity of magnetic sensors using negatively charged nitrogen-vacancy (NV−) centers, it is essential to improve the quality of diamond crystals and precisely control the nitrogen concentration in the crystals. We have utilized high-pressure, high-temperature synthesis [1] and chemical vapor deposition [2] for the growth of nitrogen-doped diamond. The concentration of substitutional nitrogen in the neutral charge state [NS0] were evaluated by electron paramagnetic resonance (EPR) measurements. As shown in Fig. 1, [NS0] were precisely controlled by the weight ratio of nitrogen getter material in the metal solvent for the HPHT method (Fig. 1(a)) and by the carbon to nitrogen gas ratio for the CVD method (Fig. 1(b)). Then, the diamond crystals were irradiated with electron beams followed by vacuum annealing so that 10% of the nitrogen at the substitutional site became NV− centers, and the negatively charged NV− centers were successfully formed preferentially [3]. T2 of these diamond crystals was inversely proportional to the nitrogen concentration. The product of T2 and nitrogen concentration of the obtained HPHT diamond crystal is slightly higher than the maximum value reported so far [4], suggesting that the crystal is expected to have high magnetic sensitivity.