Journal of Experimental and Theoretical Physics Letters
Fourier Transform Limited Linewidth of Optical Transitions in Single SiV Centers in “Adamantane” Nanodiamonds
Alexey M. Romshin, Oleg S. Kudryavtsev, Евгений Алексеевич Екимов, Alexey Shkarin, Dominik Rattenbacher, Maxim V. Rakhlin, Alexey A. Toropov, Igor I. Vlasov
Silicon-vacancy (SiV) color centers in diamond offer a promising system for quantum information applications owing to their intense narrowband emission and optically detectable spin states. Here, the fluorescent properties of ensembles and single SiV centers in diamonds obtained by high-pressure high-temperature synthesis from adamantane (below referred to as adamantane diamonds) are investigated at liquid-helium temperatures. Ensembles of SiV centers (~10 3 ) are studied in large diamond crystals (1–2 µm in size). Despite the large number of excited centers, the fine structure of the zero-phonon line, corresponding to four allowed optical transitions between the ground- and excited-state doublets of the SiV center, can be observed in the fluorescence spectra of these crystals. The width of individual lines is in the range of 60–80 GHz, which is explained by their inhomogeneous broadening. Single SiV centers are studied in diamond crystallites with sizes of about 200 nm. The width of the narrowest transition lines observed in the fluorescence spectra of single SiV centers under resonant excitation is almost three orders of magnitude smaller than linewidths in the spectra of SiV ensembles and is as small as 94 MHz; i.e., these lines are so narrow that their width is determined by the lifetime of the upper state of the transition. Therefore, adamantane nanodiamond features the narrowest emission line width of a single SiV center at cryogenic temperatures among other types of SiV-con-taining nanodiamonds of similar sizes obtained by the high-pressure high-temperature and chemical vapor deposition techniques.
Silicon-vacancy (SiV) color centers in diamond offer a promising system for quantum information applications owing to their intense narrowband emission and optically detectable spin states. Here, the fluorescent properties of ensembles and single SiV centers in diamonds obtained by high-pressure high-temperature synthesis from adamantane (below referred to as adamantane diamonds) are investigated at liquid-helium temperatures. Ensembles of SiV centers (~10 3 ) are studied in large diamond crystals (1–2 µm in size). Despite the large number of excited centers, the fine structure of the zero-phonon line, corresponding to four allowed optical transitions between the ground- and excited-state doublets of the SiV center, can be observed in the fluorescence spectra of these crystals. The width of individual lines is in the range of 60–80 GHz, which is explained by their inhomogeneous broadening. Single SiV centers are studied in diamond crystallites with sizes of about 200 nm. The width of the narrowest transition lines observed in the fluorescence spectra of single SiV centers under resonant excitation is almost three orders of magnitude smaller than linewidths in the spectra of SiV ensembles and is as small as 94 MHz; i.e., these lines are so narrow that their width is determined by the lifetime of the upper state of the transition. Therefore, adamantane nanodiamond features the narrowest emission line width of a single SiV center at cryogenic temperatures among other types of SiV-con-taining nanodiamonds of similar sizes obtained by the high-pressure high-temperature and chemical vapor deposition techniques.
Color centers in diamond are versatile solid state atomic-like systems suitable for quantum technological applications. In particular, the negatively charged silicon vacancy center (SiV) exhibits a narrow photoluminescence (PL) line and lifetime-limited linewidth in a bulk at cryogenic temperature. We present a low-temperature study of chemical vapour deposition (CVD)-grown diamond nano-pyramids containing SiV centers. The PL spectra feature a bulk-like zero-phonon line with ensembles of SiV centers, with a linewidth below 10 GHz which demonstrates very low crystal strain for such a nano-object.
The silicon-vacancy (SiV) color center in diamond is a solid-state single photon emitter and spin quantum bit suited as a component in quantum devices. Here, we show that SiV centers in nanodiamonds exhibit a strongly inhomogeneous distribution with regard to the center wavelengths and linewidths of the zero-phonon-line (ZPL) emission at room temperature. We find that the SiV centers separate in two clusters: one group exhibits ZPLs with center wavelengths within a narrow range ≈730–742 nm and broad linewidths between 5 and 17 nm, whereas the second group comprises a very broad distribution of center wavelengths between 715 and 835 nm, but narrow linewidths from below 1 up to 4 nm. Supported by ab initio Kohn–Sham density functional theory calculations we show that the ZPL shifts of the first group are consistently explained by strain in the diamond lattice. Further, we suggest, that the second group showing the strongly inhomogeneous distribution of center wavelengths might be comprised of a new class of silicon-related defects. Whereas single photon emission is demonstrated for defect centers of both clusters, we show that emitters from different clusters show different spectroscopic features such as variations of the phonon sideband spectra and different blinking dynamics.
Abstract Silicon vacancy (SiV) centers in diamonds have attracted much attention because of their stability and narrow emission linewidth, and are promising for applications in quantum information technology. SiV-center-encapsulated nanodiamonds have also attracted much attention because of their potential to be coupled to various photonic devices. One efficient way to fabricate nanodiamonds that contain SiV centers is Si ion implantation into nanodiamonds. However, the evaluation of a single SiV center in a nanodiamond produced by this method at low temperatures has not been performed. In this study, we report on the optical properties of a single SiV center in a nanodiamond produced by ion implantation at cryogenic temperatures. The emission spectrum from a single SiV center ( g 2 ( 0 ) = 0.19 ) was observed with four distinct fine splittings of the zero-phonon line (ZPL) at 4 K. At an excitation power of 50 μ W, the full width at half maximum of the ZPL reached the spectrometer resolution limit (0.09 nm). The temperature dependence of the emission peak is consistent with that of the emission coming from an SiV center under high strain. The results obtained in this work suggest that nanodiamonds containing single SiV centers formed using this method will be an important building block for the realization of quantum information applications.
Diamonds and nanodiamonds (NDs) containing quantum color centers, such as nitrogen-vacancy (NV) centers, have been widely studied in recent years for their promising applications across various fields, including cryptography and telecommunications, medical sciences, and sensing. In the context of sensing, recent studies on color centers such as silicon-vacancy (SiV) and germanium-vacancy (GeV) centers have shown great potential for measuring physical quantities like magnetic fields, temperature, and strain. This is due to their intense zero-phonon line (ZPL) optical signal, which accounts for about 80% of their total luminescence and is characteristic of group-IV color centers (G4V) [1]. In our recent papers, we demonstrated that as-grown CVD NDs containing SiV and GeV centers, featuring luminescent ZPLs and excellent photostability at room temperature, can function effectively as nanosensors under high stress and pressure conditions (up to 180 GPa) [2, 3]. To advance our research, in this work we investigate the optical properties of SiV centers in as-grown NDs at cryogenic temperatures. For SiV centers, which have spin 1/2, the fine structure should become accessible through the Jahn-Teller effect, which lifts the degeneracy at cryogenic temperatures (< 20 K). However, experiments on our as-grown NDs reveal significant spectral broadening even at around 9 K, caused by lattice strain, which prevents access to the optically addressable electronic spin states of the SiV center. To overcome this limitation, we propose an original post-treatment involving high-pressure and high-temperature (HPHT) annealing using the Paris–Edinburgh press. This approach allows the gradual increase of temperature and pressure allows for control over the undesired diamond-to-graphite phase transition. HPHT annealing experiments were conducted at the PSICHE beamline of Synchrotron SOLEIL [4], where X-ray diffraction and tomography analyses enabled precise monitoring of P-T parameters and made it possible for the first time to access single fine-structure transitions of SiV centers in such NDs.References[1] C. Bradac, et al., Nat. Commun. 10, 1 (2019). [2] B. Vindolet, et al., Phys. Rev. B 106, 214109 (2022).[3] M. De Feudis, et al., Adv. Mater. Interfaces 7, 1901408 (2019).[4] L. Henry et al., J. Synchrotron Rad. 29 (2022).
Silicon-vacancy (SiV) centers in diamond are promising systems for quantum information applications due to their bright single-photon emission and optically accessible spin states. Furthermore, SiV centers in low-strain diamond are insensitive to perturbations of the dielectric environment; i.e., they show very weak spectral diffusion. This property renders ensembles of SiV centers interesting for sensing applications. We here report on photoluminescence excitation (PLE) spectroscopy on an SiV ensemble in a low strain, chemical vapor deposition-grown high-quality diamond layer, where we measure the fine structure with high resolution and obtain the line widths and splittings of the SiV centers. We investigate the temperature dependence of the width and position of the fine structure peaks. Our measurements reveal line widths of about 10 GHz as compared to a lifetime limited width on the order of 0.1 GHz. This difference arises from the inhomogeneous broadening of the transitions caused by residual strain. To overcome inhomogeneous broadening we use spectral hole burning spectroscopy, which enables us to measure a nearly lifetime limited homogeneous line width of 279 MHz. Furthermore, we demonstrate evidence of coherent interaction in the system by driving a $\mathrm{\ensuremath{\Lambda}}$ scheme. Additional measurements on single emitters created by ion implantation confirm the homogeneous line widths seen in the spectral hole burning experiments and relate the ground-state splitting to the decoherence rate.
Ultrasmall (about 10 nm), low-strain, artificially produced diamonds with an internal, active color center have substantial potential for quantum information processing and biomedical applications. Thus, it is of great importance to be able to artificially produce such diamonds. Here, we report on the high-pressure, high-temperature synthesis of such nanodiamonds about 10 nm in size and containing an optically active, single silicon-vacancy color center. Using special sample preparation technique, we were able to prepare samples containing single nanodiamonds on the surface. By correlating atomic-force microscope images and confocal optical images, we verified the presence of optically active color centers in single nanocrystals, and using second-order correlation measurements, we proved the single-photon emission statistics of these nanodiamonds. These color centers have nonblinking, spectrally narrow emission with narrow distribution of spectral width and positions of zero-phonon line, thus proving the high quality of the nanodiamonds produced.