Abstract The nitrogen-vacancy (NV) centre in diamond is a promising candidate for quantum computing applications and magnetic sensing applications, because it is an atomic-scale defect with stable coherence time (T2) and reliable accessibility at room temperature. We demonstrated a method for improving the NV spin properties (the full width half maximum (FWHM) value of the magnetic resonance spectrum and T2) through a near-field (NF) etching method under ambient conditions. The NF etching method, based on a He-Cd ultraviolet laser (325 nm), which is longer than the absorption edge of the oxygen molecule, enabled selective removal of defects on the nanodiamond surface. We observed a decrease in the FWHM value close to 15% and an increase in T2 close to 25%. Since our technique can be easily reproduced, a wide range of NV centre applications could be improved, especially magnetic sensing applications. Our results are especially attractive, because they have been obtained under ambient conditions and only require a light source with wavelength slightly above the O2 absorption edge.
Abstract The nitrogen-vacancy (NV) centre in diamond is a promising candidate for quantum computing applications and magnetic sensing applications, because it is an atomic-scale defect with stable coherence time (T2) and reliable accessibility at room temperature. We demonstrated a method for improving the NV spin properties (the full width half maximum (FWHM) value of the magnetic resonance spectrum and T2) through a near-field (NF) etching method under ambient conditions. The NF etching method, based on a He-Cd ultraviolet laser (325 nm), which is longer than the absorption edge of the oxygen molecule, enabled selective removal of defects on the nanodiamond surface. We observed a decrease in the FWHM value close to 15% and an increase in T2 close to 25%. Since our technique can be easily reproduced, a wide range of NV centre applications could be improved, especially magnetic sensing applications. Our results are especially attractive, because they have been obtained under ambient conditions and only require a light source with wavelength slightly above the O2 absorption edge.
The NV defect center in diamond forms a pseudo-atomic quantum system with discreet optically excitable transitions between ground and excited states in the gap between valence and conduction bands, making the NV center a deep-level defect center in diamond. For the negatively charged NV center (NV-), both the ground and excited states are spin triplets (S=1) and coupling between optical and spin states provides unique opportunities for optical detection of magnetic resonance (ODMR) and quantum metrology under ambient conditions. As an atomically sized point defect that is stable in single nanodiamonds as small as a few nanometers, the NV center enables spin based imaging of temperature, electric fields, magnetic fields and mechanical strain with nanoscale spatial resolution. Made of carbon, nanodiamonds are also ideal nanoparticles for use in biological systems, exhibiting extremely low cytotoxicity, no photo bleaching and exceptional contrast in transmission electron and light microscopy. With the ability to act as both a passive, non perturbing sensor (e.g. a diamagnetic material used for sensing magnetic fields) and a connection point for two way, direct coupling of far field optics to NV− spins and indirectly to the highly localized neighborhood of atoms, electronic states and phonon modes in the local vicinity, NV diamond provides a route to nanoscale field sensing and spin based optical microscopy. These sensors are also stable in nanodiamonds. For nanoparticles, the reduction in particle diameter dramatically enhances the proportion of the material that is surface exposed, enhancing any surface related properties. Nitrogen Vacancy centers in nanodiamonds provide another example of material properties that vary with particle size. In chapter 5, evidence that modulation of nanodiamonds fluorescent emissions by electrical perturbations in their surrouding environment allows transduction of local electrodynamics into a far field optical signal capable of mapping action potentials in cardiomyocytes in presented. The unifying theme for all of the work presented in this dissertation is to enable the use of magnetic resonance signals and interactions for imaging and sensing in previously inaccessible regimes. The specific focus is on methods and techniques to enable nanoscale physical sensing and functional imaging in live tissues, with the ultimate aim to lay the predicate for the combination of both without compromise.
Fluorescent nanodiamonds (NDs) are crystal defect-based light-emitting nanoparticles that can be applied to quantum information science and quantum sensing. Of particular interest are nitrogen vacancy (NV) centers that allow optical access to their coherently controllable electron spin systems, leading to spin-photon quantum devices and nanoscale sensing of various physical parameters. However, the NV spin coherence time (T2) in NDs has been limited to one or two orders of magnitude shorter than those in bulk diamonds owing to the complicated surface effect that decoheres the NV spin systems. Here, we study the relation between the surface properties and T2 of single NV centers in NDs by systematically analyzing the effect of surface oxidation. We apply aerobic and acidic oxidation methods with various heating temperatures and processing times and find that aerobic oxidation most effectively oxidizes the surface and extends T2 by a factor of 1.6 to the original NDs. The ND-size dependence of T2 clearly shows that the surface oxidation removes a constant decoherence contribution irrespective of the ND size and that a new surface derived decoherence source emerges when the ND size reduces below 50 nm. The present results provide quantitative information on the decoherence sources of NV spin systems of NDs and will enable a strategic surface modification for better spin manipulations of NV centers in the context of quantum information science and nanoscale quantum sensing.
The nitrogen-vacancy (NV) center in a nanodiamond (ND) crystal is a promising material for quantum information processing, sensing, and computing applications. It is one of the best candidate materials for quantum sensing and metrology expected to work at elevated temperatures and pressures conditions. We computationally show the effect of strain on the defect band edges and band gaps in the NV center diamond. A low energy Hamiltonian is developed for the ±1 spin manifold at the ground state. We show the quantum sensing device is a few orders of magnitude superior in sensing than the traditional optical sensing devices. We also discuss experimental results from the optically detected magnetic resonance (ODMR) and the spin relaxometry for the field sensing applications. The presentation concludes by providing a model for free spins detection of the rare earth ions.
When the word diamond comes up, the majority of people thinks about engagement rings or gemstones. In fact, it is additionally, one of the most promising host materials for the implementation of advanced technology, exploiting the nature of quantum physics. Such quantum technologies have disruptive potential, ones the quantum effects can be applied in macroscopic, commercial products. The nitrogen-vacancy (NV) centre in diamond is a promising candidate to perform such tasks in the fields of quantum computation, quantum cryptography or metrology. Especially in the field of quantum sensing, the NV sensor impresses with nano-scale spatial resolution paired with high sensitivity. The electronic spin of the atomic-sized point defect can be initialised, manipulated and read-out at ambient conditions and coherence lifetimes are comparably long. Diamond magnetometers based on negatively charged NV centres have shown to be very attractive, and the sensitivity goes down to the single-atom level. In order to exploit such a high sensitivity level for sensing prospects, in this thesis, the NV centres are fabricated well confined in a certain distance to the diamond surface, since the detectable field usually decays with the third power of the distance between sensor and target. The surface depicts a fracture of the spin wise protecting diamond lattice and charge fluctuations affect the stability of NV centres, which are overcome by diamond surface termination. In order to improve the sensitivity further, the sensor density, measurement contrast and interaction time are increased. The nitrogen doping technique, which is applied during a plasma-enhanced chemical vapour deposition (PECVD) diamond growth process is used to fabricate NV centre ensembles aligned along one diamond crystal axis, thereby improving the measurement contrast by a factor up to four. The interaction time limiting spin bath is analysed using the sensor capabilities of the NVs, which leads to enhanced growth strategies and the fabrication of sensitivity optimised NV centre ensembles for magnetometry applications.
Nitrogen Vacancy (NV) centers are point defects in diamond that allow magnetic field sensing based on Optically Detected Magnetic Resonance (ODMR). They are processed in ultrapure single-domain CVD grown diamond crystals and can be operated at room temperature. This results in solid-state sensors with a wide variety of applications. Ensemble of NV centers can be used to perform wide-field magnetic imaging with sensitivity in the nT range. Single NV centers can also be processed, which allows sensing at the atomic scale. This possibility, combined with its unique coherence properties, make NV center an ideal candidate for quantum sensing.
The fluorescence of the nitrogen-vacancy (NV) centre in artificial diamond has been widely studied for applications such as quantum communication protocols, quantum computation, fluorescence-based biolabelling, and optical sensing. Optical sensing by itself encompasses a wide range of possible applications: from magnetic and electric field sensing to temperature sensing and enabling, for example, the detection of paramagnetic ions and the identification of molecules by nuclear magnetic resonance. Compared to many other systems capable of optical sensing, the NV centre works at room temperature, and its spin-dependent fluorescence emission is the key property to achieve a high sensitivity to the surrounding environment. Additionally, the NV centre emission is highly photostable, has a relatively short lifetime (~ 12ns) and spans a broad wavelength range, from the red to the near-infrared region of the electromagnetic spectrum (600 - 800nm). While the common denominator of all mentioned applications is the NV centre, the properties of the artificial diamond surrounding the NV centre have a significant impact on its sensing performance. At present, the processing of artificial diamond has not been fully optimised, and research and development towards the realisation of the `best¿ diamond sample for optical sensing is far from over. Specifically, the role of other defects in diamond and their effects on the photo-physical properties of the NV centres are not entirely understood. In this thesis, I will discuss the potential benefits of a novel processing technique to create ensembles of NV centres, and the importance that surrounding nitrogen defects has on the achievable magnetic field sensitivity. Additionally, I will show both theoretical and experimental investigations of the NV centres photo-physical processes, with focus on magnetic field sensing. I will initially explore a protocol for microwave-free magnetometry. This protocol predicts a theoretical magnetic field sensitivity <10µT/√Hz in the range 0.3 - 30mT and I will demonstrate it experimentally with a maximum sensitivity of 3.6mT/Hz. Following, I will focus on exploring techniques to increase the magnetic field sensitivity by improving the material properties of the diamond samples. I will demonstrate that the simultaneous electron irradiation and annealing improves the creation efficiency of an ensemble of NV centres by up to 117%. Finally, I will investigate how substitutional nitrogen defects in the surrounding lattice affects the charge state of the NV centre, its emission intensity, its lifetime and its magnetic field sensitivity. I will study a sample characterised by multiple regions across its volume, with nitrogen concentration changing between 10ppm and 100ppm in each region. There si an optimal region with ~ 40ppm of substitutional nitrogen which demonstrates the highest fluorescence emission, mainly from the negatively-charged NV centre, and the highest magnetic field sensitivity of 1.6 ± 0.2µT/√Hz. However, both the regions with lower and higher substitutional nitrogen concentration than the optimal region show lower emission intensity and worse magnetic field sensitivity. Following is a summary of the content in each chapter: Chapter 1 will present an introduction to the diamond material and the classification of artificial diamond samples. It will introduce the NV centre, its fluorescence properties and the process to create NV centres in diamond. The chapter will also introduce the concepts around optical magnetometry and the working principle that allows the NV centre to sense magnetic fields as well as other external quantities, such as temperature or pressure. Finally, it will include a brief overview of the defects that are found in artificial diamond or are created during the sample processing. Chapter 2 will describe the working principle of the instruments utilised in this work. I will list the details of each instrument and describe the methods used for the analysis of the data. Chapter 3 will introduce the background of modelling the fluorescence emission from NV centres. I will discuss the implementation of a computational model based on the Lindblad master equation to simulate the photo-physical dynamics of the NV centre. I will demonstrate the successful simulation of the saturation emission, fluorescence lifetime and optically detected magnetic resonance using the theoretical model. Finally, I will explore the theoretically predicted sensitivity of microwave-free magnetometry, based on the NV centre emission intensity change under an external magnetic field. Chapter 4 will demonstrate experimentally the microwave-free magnetometry technique. In relation to the study of microwave-free magnetometry, this chapter will explore an unexpected increase in emission intensity at high magnetic fields > 100mT. Combining the experimental observations and the theoretical simulation developed in the previous chapter, I will identify and discuss a phenomenological decrease in the NV centre transition rate from the triplet state to the singlet state. The chapter will conclude comparing the experimental and theoretical sensitivities associated with the microwave-free magnetometry technique. Chapter 5 will show the characterisation of a diamond sample at each step of the process to create NV centres. I will study the electron irradiation followed by separate annealing on a high-pressure high-temperature diamond sample. I will then characterise the sample employing visible and infrared absorption spectroscopy, as well as measure the fluorescence spectra and lifetime of the defects identified at each step. Chapter 6 will examine an alternative method to create NV centres in diamond. I will compare diamond samples irradiated and annealed separately with samples simultaneously irradiated and annealed (referred to as 'annealing in situ'). To compare the two processes, I will estimate the concentration of nitrogen defects and NV centres and calculate their N-to-NV conversion efficiency. Chapter 7 will discuss the effects of substitutional nitrogen on the properties of the NV centres in diamond. For this discussion, I will use a single-crystal diamond that shows the presence of 4 growth sectors. Each growth sector is characterised by a different nitrogen concentration, as I will demonstrate at the beginning of the chapter. I will focus on 4 main properties affected by the concentration of nitrogen in the different sectors: the balance between the charge states of the NV centre, the overall fluorescence intensity from each sector, the fluorescence lifetime and its relation to non-radiative processes, and the magnetic field sensitivity obtained with the optically detected magnetic resonance technique. Chapter 8 will gather the results and conclusions of the entire body of work. It will also discuss future avenues of research in the topic of diamond processing and characterisations, to improve the existing optical sensing applications.