The sensitivity of present Nb diffusion-cooled hot-electron bolometer (HEB) mixers is not quantum limited, and can be improved by reducing the superconducting transition temperature TC. Lowering TC reduces thermal fluctuations, resulting in a decrease of the mixer noise temperature TM. However, lower TC mixers have reduced dynamic range and saturate more easily due to background noise. We present 30 GHz microwave measurements on a bilayer HEB system, Nb–Au, in which TC can be tuned with Au layer thickness to obtain the maximum sensitivity for a given noise background. These measurements are intended as a guide for the optimization of THz mixers. Using a Nb–Au mixer with TC=1.6 K, we obtain TM=50 K with 2 nW of local oscillator (LO) power. Good mixer performance is observed over a wide range of LO power and bias voltage and such a device should not exhibit saturation in a THz receiver.
We present microwave (30 GHz) measurements on aluminum superconducting hot-electron bolometer (HEB) mixers. Aluminum HEB mixers have a lower superconducting transition temperature than niobium and niobium nitride devices, and are predicted to have improved sensitivity and require less local oscillator power. The devices studied consist of a narrow superconducting aluminum microbridge with contacts comprised of thick aluminum, titanium, and gold. A perpendicular magnetic field is used to suppress superconductivity in the contacts. The device length is much shorter than the electron–phonon inelastic length [L≪(Dτe–ph)1/2] and thus the intermediate frequency (IF) bandwidth is set by the diffusion time of hot electrons from the microbridge into the contacts. We discuss limitations on the IF bandwidth in very short HEB mixers with fully normal contacts. Overall, the microwave heterodyne mixing results show good performance with a mixer noise temperature inferred from the conversion efficiency and output noise of TM⩾4 K, double side band (DSB). Measurements at 618 GHz yield a conversion efficiency approximately 10 dB lower than observed at 30 GHz. Output saturation by background radiation is postulated to contribute significantly to this difference. A similar decrease in conversion efficiency in the microwave mixing measurements is observed when broadband noise is added to the rf input signal. We discuss the tradeoff between increased sensitivity and the occurrence of saturation effects in low transition temperature HEBs.
In this article, we measure the double sideband (DSB) receiver noise temperature (
TrecDSB)of an NbN hot electron bolometer (HEB) mixer at three local oscillator frequencies of 1.6, 2.5, and 5.3 THz. The HEB has cleaned contact interfaces with a 200-nm-thick Au layer. The measured
TrecDSBvalues are 530 ± 11 K, 640 ± 18 K, and 2190 ±150 K at 1.6, 2.5, and 5.3 THz, respectively, using an air setup with total optical losses of 2.60 ± 0.04, 2.63 ± 0.16, and 4.70 ± 0.24 dB, respectively. We derived low mixer noise temperatures (
TmixerDSB)of 240 ± 6 K at 1.6 THz and 290 ± 13 K at 2.5 THz, achieving over 30% improvement compared to published NbN HEB mixers. This enhancement can reduce the integration time of a heterodyne instrument by roughly a factor of 2. At 5.3 THz,
TmixerDSBis 620 ± 55 K, showing limited improvement due to nonoptimized antenna geometry. These results also contribute to understanding the device physics of a wide HEB (4 μm) at high frequencies. The mixer was developed for the proposed Orbiting Astronomical Satellite for Investigating Stellar Systems and Single Aperture Large Telescope for Universe Studies (concept) missions.
To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.
Superconductive hot-electron bolometer (HEB) mixers have been built and tested in the frequency range from 1.1 THz to 2.5 THz. The mixer device is a 0.15 - 0.3 micrometer microbridge made from a 10 nm thick Nb film. This device employs diffusion as a cooling mechanism for hot electrons. The double sideband noise temperature was measured to be less than or equal to 3000 K at 2.5 THz and the mixer IF bandwidth is expected to be at least 10 GHz for a 0.1 micrometer long device. The local oscillator (LO) power dissipated in the HEB microbridge was 20 - 100 nW. Further improvement of the mixer characteristics can be potentially achieved by using Al microbridges. The advantages and parameters of such devices are evaluated. The HEB mixer is a primary candidate for ground based, airborne and spaceborne heterodyne instruments at THz frequencies. HEB receivers are planned for use on the NASA Stratospheric Observatory for Infrared Astronomy (SOFIA) and the ESA Far Infrared and Submillimeter Space Telescope (FIRST). The prospects of a submicron-size YBa2Cu3O7-(delta ) (YBCO) HEB are discussed. The expected LO power of 1 - 10 (mu) W and SSB noise temperature of approximately equals 2000 K may make this mixer attractive for various remote sensing applications.
Superconductive hot-electron bolometer (HEB) mixers have been built and tested in the frequency range 1.1-2.5 THz. The mixer device is a 0.15-03 /spl mu/m microbridge made from a 10 nm thick Nb film. This device employs diffusion as a cooling mechanism for hot electrons. The double sideband noise temperature was measured to be /spl les/3000 K at 2.5 THz and the mixer IF bandwidth is /spl ap/9-10 GHz for a 0.1 /spl mu/m long device. The local oscillator (LO) power dissipated in the HEB microbridge was 20-100 nW. Further improvement of the mixer characteristics can be potentially achieved by using Al microbridges. The advantages and parameters of such devices are evaluated The HEB mixer Is a primary candidate for ground based, airborne and spaceborne heterodyne instruments at THz frequencies. HEB receivers are planned for use on the NASA Stratospheric Observatory for Infrared Astronomy (SOFIA) and the ESA Far Infrared and Submillimeter Space Telescope (FIRST). The prospects of a submicron-size YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// (YBCO) HEB are also discussed. The expected LO power of 1-10 /spl mu/W and SSB noise temperature of /spl ap/2000 K may make this mixer attractive for various remote sensing applications.