We present microwave (30 GHz) measurements on aluminum superconducting hot-electron bolometer (HEB) mixers. Aluminum HEB mixers have a lower superconducting transition temperature than niobium and niobium nitride devices, and are predicted to have improved sensitivity and require less local oscillator power. The devices studied consist of a narrow superconducting aluminum microbridge with contacts comprised of thick aluminum, titanium, and gold. A perpendicular magnetic field is used to suppress superconductivity in the contacts. The device length is much shorter than the electron–phonon inelastic length [L≪(Dτe–ph)1/2] and thus the intermediate frequency (IF) bandwidth is set by the diffusion time of hot electrons from the microbridge into the contacts. We discuss limitations on the IF bandwidth in very short HEB mixers with fully normal contacts. Overall, the microwave heterodyne mixing results show good performance with a mixer noise temperature inferred from the conversion efficiency and output noise of TM⩾4 K, double side band (DSB). Measurements at 618 GHz yield a conversion efficiency approximately 10 dB lower than observed at 30 GHz. Output saturation by background radiation is postulated to contribute significantly to this difference. A similar decrease in conversion efficiency in the microwave mixing measurements is observed when broadband noise is added to the rf input signal. We discuss the tradeoff between increased sensitivity and the occurrence of saturation effects in low transition temperature HEBs.
We present microwave (30 GHz) measurements on aluminum superconducting hot-electron bolometer (HEB) mixers. Aluminum HEB mixers have a lower superconducting transition temperature than niobium and niobium nitride devices, and are predicted to have improved sensitivity and require less local oscillator power. The devices studied consist of a narrow superconducting aluminum microbridge with contacts comprised of thick aluminum, titanium, and gold. A perpendicular magnetic field is used to suppress superconductivity in the contacts. The device length is much shorter than the electron–phonon inelastic length [L≪(Dτe–ph)1/2] and thus the intermediate frequency (IF) bandwidth is set by the diffusion time of hot electrons from the microbridge into the contacts. We discuss limitations on the IF bandwidth in very short HEB mixers with fully normal contacts. Overall, the microwave heterodyne mixing results show good performance with a mixer noise temperature inferred from the conversion efficiency and output noise of TM⩾4 K, double side band (DSB). Measurements at 618 GHz yield a conversion efficiency approximately 10 dB lower than observed at 30 GHz. Output saturation by background radiation is postulated to contribute significantly to this difference. A similar decrease in conversion efficiency in the microwave mixing measurements is observed when broadband noise is added to the rf input signal. We discuss the tradeoff between increased sensitivity and the occurrence of saturation effects in low transition temperature HEBs.
We report on microwave measurements of superconducting aluminum hot-electron bolometers (Al HEBs). Diffusion-cooled Al HEB mixers are good candidates for space-borne applications in the Terahertz frequency range since they are predicted to have small local oscillator (LO) power requirements, intermediate frequency (IF) bandwidths /spl gsim/10 GHz, and a noise temperature lower than that of Nb and NbN HEB mixers. Mixer measurements were made at an LO frequency /spl sim/30 GHz, with an IF in the range 0.1 to 7.3 GHz. For T<0.8 K, a magnetic field H=0.1-0.3 T was applied to suppress the superconductivity in the contact pads, and partly in the bridge. For a 0.6 /spl mu/m long device, we measure an IF bandwidth of 4 GHz, a conversion efficiency /spl eta/=-8 dB, and a mixer noise temperature T/sub M//spl gsim/4 K, DSB (T/sub mixer/=T/sub output noise//2/spl eta/). These results are shown to be in quantitative agreement with simple theoretical predictions.
We report on microwave measurements of superconducting aluminum hot-electron bolometers (Al HEBs). Diffusion-cooled Al HEB mixers are ideal candidates for space-borne and terrestrial remote-sensing applications in the Terahertz frequency range since they are predicted to have small local oscillator (LO) power requirements, intermediate frequency (IF) bandwidths ! 10 GHz, and a noise temperature lower than that of Nb and NbN HEBs. Mixer measurements were made at an LO frequency ~30 GHz LO, with an IF in the range 0.1-7.3 GHz. For T < 0.8 K, a magnetic field H=0.1-0.3T was applied to suppress the superconductivity in the contact pads, and partly in the bridge. For a 0.6 μm long Al HEB, we measure an IF bandwidth of 4 GHz, a conversion efficiency η = -8dB, and a mixer noise temperature Tm ! 4K, DSB (Tmixer=Toutput noise/2η). These results are shown to be in quantitative agreement with simple theoretical predictions.
We report a systematic, comprehensive set of measurements on the dynamics and noise processes in diffusion and phonon-cooled superconducting hot-electron bolometer mixers which will serve as ultralow noise detectors in THz heterodyne receivers. The conversion efficiency and output noise of devices of varying lengths were measured with radio frequency between 8 and 40 GHz. The devices studied consist of 100-Å-thin film Nb bridges connected to thick (1000 Å), high conductivity normal metal (Au) leads. The lengths of the devices studied range from 0.08 to 3 μm. For devices longer than the electron–phonon interaction length Le–ph≡Dτe–ph, with D the diffusion constant and τe–ph−1 the electron–phonon interaction rate, the hot electrons are cooled dominantly by the electron–phonon interaction, which in Nb is too slow for practical applications. If the device length is less than πLe–ph(≈1 μm at 4.2 K), then out diffusion of heat into the high conductivity leads dominates the cooling process. In this limit, the intermediate frequency (IF) bandwidth is found to vary as L−2, with L the bridge length, as expected for diffusion cooling. The shortest device has an IF bandwidth greater than 6 GHz, the largest reported for a low-Tc superconducting bolometric mixer. The dominant component of the output noise decreases with frequency in the same manner as the conversion efficiency, consistent with a model based on thermal fluctuations. The noise bandwidth is larger than the gain bandwidth, and the mixer noise is low, ranging from 100 to 530 K (double sideband). The crossover from phonon dominated to diffusion dominated behavior is also demonstrated using noise thermometry measurements in the normal state. Scalar measurements of the device differential impedance in the intermediate state agree with a theoretical model which takes into account the thermal and electrical dynamics. We also present detailed comparisons with theoretical predictions of the output noise and conversion efficiency.
The sensitivity of present Nb diffusion-cooled hot-electron bolometer (HEB) mixers is not quantum limited, and can be improved by reducing the superconducting transition temperature TC. Lowering TC reduces thermal fluctuations, resulting in a decrease of the mixer noise temperature TM. However, lower TC mixers have reduced dynamic range and saturate more easily due to background noise. We present 30 GHz microwave measurements on a bilayer HEB system, Nb–Au, in which TC can be tuned with Au layer thickness to obtain the maximum sensitivity for a given noise background. These measurements are intended as a guide for the optimization of THz mixers. Using a Nb–Au mixer with TC=1.6 K, we obtain TM=50 K with 2 nW of local oscillator (LO) power. Good mixer performance is observed over a wide range of LO power and bias voltage and such a device should not exhibit saturation in a THz receiver.
A reduction in the mixer noise is expected when using superconductors with a lower transition temperature (Tc) since the thermal noise components of the mixer noise should scale with Tc. Also, the local oscillator (LO) power required for a diffusion-cooled device should decrease as Tc when Tbath<<Tc. We previously studied mixing in aluminum based hot-electron bolometers (HEBs) at microwave frequencies (~30 GHz), and observed a significant improvement in noise performance, and a reduction in LO power as predicted. However, the bias voltage range over which good mixer performance was observed was ~ 5-10 μV. These devices are thus susceptible to saturation effects, in particular output saturation. In the present work, we have investigated Nb HEBs whose Tc is lowered by applying a magnetic field. The goal is to study a case intermediate between Nb and Al, and hopefully to find properties that will allow use in practical receivers. A 15 kOe perpendicular magnetic field was applied to a Nb HEB (L=0.16 μm, W=0.08 μm, RN=90Ω) to reduce Tc from 5.2 K to 2.4 K. The mixer noise, as inferred from the output noise and the conversion efficiency, decreased from 390 K, DSB to 171 K, DSB. The LO power required for near optimum mixer conversion efficiency (ηmixer = 9 dB in this device) was 8nW in zero field, and ~ 2 nW when Tc was reduced to 2.4K. Tbath=0.22K. The conversion bandwidth was previously measured to be 2.4 GHz and the same bandwidth was observed in the presence of a magnetic field. By lowering Tc, the voltage range over which good mixing was observed also decreased. However, even with Tc reduced to 2.4 K, the conversion efficiency dropped by 3dB from its maximum value only when the bias voltage was changed by ~ 90 μV. Saturation effects should thus be much less of a concern in these devices than in Al HEBs. In situations where the application of a large magnetic field is not feasible, we suggest using Ta based HEBs. Ta HEBs should have Tc ~ 3-3.5K and material properties very similar to Nb.
A reduction in the mixer noise is expected when using superconductors with a lower transition temperature (T(sub c)) since the thermal noise components of the mixer noise should scale with T(sub c). Also, the local oscillator (LO) power required for a diffusion-cooled device should decrease as T(sub c) when T(sub bath) << T(sub c). We previously studied mixing in aluminum based hot-electron bolometers (HEBs) at microwave frequencies (approximately 30 GHz), and observed a significant improvement in noise performance, and a reduction in LO power as predicted. However, the bias voltage range over which good mixer performance was observed was approximately 5 - 10 microV. These devices are thus susceptible to saturation effects, in particular output saturation. In the present work, we have investigated Nb HEBs whose T(sub c) is lowered by applying a magnetic field. The goal is to study a case intermediate between Nb and Al, and hopefully to find properties that will allow use in practical receivers. A 15 kOe perpendicular magnetic field was applied to a Nb HEB (L = 0.16 micrometers, W = 0.08 micrometers, R(sub N) = 90 ohms) to reduce T(sub c) from 5.2 K to 2.4 K. The mixer noise, as inferred from the output noise and the conversion efficiency, decreased from 390 K, DSB to 171 K, DSB. The LO power required for near optimum mixer conversion efficiency (eta(sub mixer) = -9 dB in this device) was 8 nW in zero field, and approximately 2 nW when T(sub c) was reduced to 2.4 K. T(sub bath) = 0.22 K. The conversion bandwidth was previously measured to be 2.4 GHz and the same bandwidth was observed in the presence of a magnetic field. By lowering T(sub c), the voltage range over which good mixing was observed also decreased. However, even with T(sub c) reduced to 2.4 K, the conversion efficiency dropped by 3 dB from its maximum value only when the bias voltage was changed by approximately 90 microV. Saturation effects should thus be much less of a concern in these devices than in Al HEBS. In situations where the application of a large magnetic field is not feasible, we suggest using Ta based HEBS. Ta HEBs should have T(sub c) = 3 - 3.5 K and material properties very similar to Nb.