Prop erties of Terahertz Superconducting Hot Electron Bolometer Mixers

J. Chen, Biao Jin, Weizong Xu, Peiheng Wu, Weiwei Zhang, Ling Jiang

Published Jan 1, 2008• 3 citations

Abstract

A quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixer has been fabricated and measured in the terahertz (THz) frequency range of 0.5~2.52 THz. A receiver noise temperature of 2000 K at 2.52 THz has been obtained for the mixer without corrections. Also, the effect of a Parylene C anti-reflection (AR) coating on the silicon (Si) lens has been studied.

Related papers

Low Noise Receivers Using Niobium Nitride Hot Electron Bolometer Mixers from 0.76 to 3.1 THz

J. Chen, Min Liang, Lin Kang +5 more

Low noise receivers using quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured in the terahertz (THz) frequency range for THz applications in astronomy and cosmology. The NbN HEB mixers consist of a planar complementary antenna and several nanometer (nm) thick NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. A double sideband (DSB) receiver noise temperature of 664 K at 0.76 THz, 920 K at 1.6 THz, 1630 K at 2.5 THz and 1710 K at 3.1 THz has been obtained without corrections and no anti-reflection (AR) coating on the surface of the lens.

Jan 1, 20091 citation

Low Noise Receivers at 1.6 THz and 2.5 THz Based on Niobium Nitride Hot Electron Bolometer Mixers

Jianhui Chen, Min Liang, Lin Kang +7 more

Low noise receivers based on superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured in the terahertz (THz) frequency range for applications in astronomy and cosmology. The NbN HEB mixer consists of a planar antenna and an NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. Double sideband (DSB) receiver noise temperatures of 920 K at 1.6 THz and 1630 K at 2.5 THz have been obtained at 4.2 K without corrections. Effects of Parylene C AR coating on the lens have been studied; with such a coating a lowest DSB receiver noise temperature of 1135 K at 2.5 THz has been obtained at 4.2 K.

IEEE Transactions on Applied SuperconductivityMay 27, 200916 citations

Superconducting NbN hot electron bolometer mixer at terahertz

Biaobing Jin, Jianhui Chen, Min Liang +3 more

Superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers at terahertz (THz) have been designed, fabricated and measured for applications in astronomy and cosmology. The NbN HEB mixer consists of a planar antenna and an NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. Double sideband (DSB) receiver noise temperatures of 698 K at 0.65 THz, 904 K at 1.6 THz, 1026 K at 2.5 THz and 1386 K at 3.1 THz have been obtained at 4.2 K without corrections and using changeable input local oscillation (LO) power to eliminate the affects of direct detection and instability of the LO power. The excess quantum noise factor beta of about 4 has been estimated using a quantum noise model.

International Conference on Infrared, Millimeter, and Terahertz Waves (IRMMW-THz)Sep 1, 20090 citations

Fabrication of 3 THz Quasi-Optical NbN Hot Electron Bolometer Mixers

Akira KAWAKAMI, Yoshihisa Irimajiri, Shukichi Tanaka +2 more

Hot electron bolometer mixers (HEBM) are expected to be used as low-noise heterodyne mixers in the terahertz frequency range. We are developing quasi-optical HEBMs for applications such as atmospheric remote sensing and radio astronomy in the terahertz frequency range. Therefore, we developed a fabrication method using niobium nitride (NbN) ultrathin films deposited on a silicone (Si) substrate for terahertz applications. First, a magnesium oxide buffer layer 50 nm thick was deposited on a Si substrate at approximately 525 °C. After deposition of this layer, NbN ultrathin films were deposited at ambient temperature. Using the buffer layers, we found the transition temperature of the 3.5-nm-thick NbN thin films to be approximately 10 K. The same method was applied to fabricate NbN-HEBMs on a Si substrate. The fabricated quasi-optical mixers were designed to operate at 3.1 THz. The receiver noise temperature was found to be approximately 1930 K (DSB) at 3.1 THz.

TEION KOGAKU (Journal of Cryogenics and Superconductivity Society of Japan)Jan 1, 20140 citations

Low Noise Receivers Based on Superconducting Niobium Nitride Hot Electron Bolometer Mixers from 0.65 to 3.1 Terahertz

Min Liang, Jian Chen, Lin Kang +3 more

Low noise terahertz (THz) receivers based on superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured for applications in astronomy and cosmology. The NbN HEB mixer consists of a planar antenna and an NbN bridge connecting across the antenna's inner terminals on a high-resistivity Si substrate. To eliminate the influence of direct detection and instability of the local oscillation (LO) power, a wire grid has been used to change the input LO power for compensating the shift of bias current during Y-factor measurement. The double sideband (DSB) receiver noise temperatures at 4.2K without corrections have been measured from 0.65 to 3.1THz. The excess quantum noise factor β of about 4 has been obtained, which agrees well with the calculated value. Allan variance of the HEB has been characterized, and Allan time TA longer than 0.4s is obtained. We also estimated the temperature resolution of the HEB from the Allan variance and obtained the minimum temperature resolution of 1.1K using a Gunn oscillator with its multipliers at 0.65THz as an LO source.

IEICE Transactions on ElectronicsJan 1, 20107 citations

NbN Hot Electron Bolometric Mixers for a Quasi--Optical THz Receiver

M. Kroug

Experimental work on the development of a quasi-optical heterodyne receiver for the THz frequency range is reported. The mixing device is a superconducting hot electron bolometer (HEB) made from ultrathin, d = 3 - 5 nm, niobium nitride (NbN) films. Work described in this thesis comprises: The design of a prototype receiver using quasi-optical coupling. Device fabrication involving reactive magnetron sputtering of NbN films and lithographic definition of the antenna integrated mixer. An investigation of the receiver performance at frequencies between 0.6 THz and 2.5 THz. The best performance is obtained with HEB mixers made from NbN films with a thickness d = 3-3.5 nm and a critical temperature T c = 9 - 9.5 K. Double-side band receiver noise temperatures are 530 K at 0.6 THz, 650 K at 1.6 THz and 1100 K at 2.5 THz. Corrected for losses in the receiver input optics, these values amount to only 10 times the theoretical quantum limit. MgO as the substrate material has been shown to provide improved acoustic coupling between NbN film and the substrate compared to other materials such as Si or sapphire. A maximum IF gain bandwidth of 4.5 GHz has been measured under the same operating conditions which yield lowest noise temperature. The local oscilltor power requirement is ~250 nW absorbed in the bolometer. Quasi-optically coupled HEB mixers have become the device-of-choice for radio astronomical applications in the frequency regime at and above 1 THz.

Jan 1, 20014 citations