NbN Hot Electron Bolometric Mixers for a Quasi--Optical THz Receiver

M. Kroug

Published Jan 1, 2001• 4 citations
OpenAlex

Abstract

Experimental work on the development of a quasi-optical heterodyne receiver for the THz frequency range is reported. The mixing device is a superconducting hot electron bolometer (HEB) made from ultrathin, d = 3 - 5 nm, niobium nitride (NbN) films. Work described in this thesis comprises: The design of a prototype receiver using quasi-optical coupling. Device fabrication involving reactive magnetron sputtering of NbN films and lithographic definition of the antenna integrated mixer. An investigation of the receiver performance at frequencies between 0.6 THz and 2.5 THz. The best performance is obtained with HEB mixers made from NbN films with a thickness d = 3-3.5 nm and a critical temperature T c = 9 - 9.5 K. Double-side band receiver noise temperatures are 530 K at 0.6 THz, 650 K at 1.6 THz and 1100 K at 2.5 THz. Corrected for losses in the receiver input optics, these values amount to only 10 times the theoretical quantum limit. MgO as the substrate material has been shown to provide improved acoustic coupling between NbN film and the substrate compared to other materials such as Si or sapphire. A maximum IF gain bandwidth of 4.5 GHz has been measured under the same operating conditions which yield lowest noise temperature. The local oscilltor power requirement is ~250 nW absorbed in the bolometer. Quasi-optically coupled HEB mixers have become the device-of-choice for radio astronomical applications in the frequency regime at and above 1 THz.

Related papers

Fabrication of 3 THz Quasi-Optical NbN Hot Electron Bolometer Mixers

Akira KAWAKAMI, Yoshihisa Irimajiri, Shukichi Tanaka +2 more

Hot electron bolometer mixers (HEBM) are expected to be used as low-noise heterodyne mixers in the terahertz frequency range. We are developing quasi-optical HEBMs for applications such as atmospheric remote sensing and radio astronomy in the terahertz frequency range. Therefore, we developed a fabrication method using niobium nitride (NbN) ultrathin films deposited on a silicone (Si) substrate for terahertz applications. First, a magnesium oxide buffer layer 50 nm thick was deposited on a Si substrate at approximately 525 °C. After deposition of this layer, NbN ultrathin films were deposited at ambient temperature. Using the buffer layers, we found the transition temperature of the 3.5-nm-thick NbN thin films to be approximately 10 K. The same method was applied to fabricate NbN-HEBMs on a Si substrate. The fabricated quasi-optical mixers were designed to operate at 3.1 THz. The receiver noise temperature was found to be approximately 1930 K (DSB) at 3.1 THz.

TEION KOGAKU (Journal of Cryogenics and Superconductivity Society of Japan)•Jan 1, 2014•0 citations

Low Noise Receivers Using Niobium Nitride Hot Electron Bolometer Mixers from 0.76 to 3.1 THz

J. Chen, Min Liang, Lin Kang +5 more

Low noise receivers using quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured in the terahertz (THz) frequency range for THz applications in astronomy and cosmology. The NbN HEB mixers consist of a planar complementary antenna and several nanometer (nm) thick NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. A double sideband (DSB) receiver noise temperature of 664 K at 0.76 THz, 920 K at 1.6 THz, 1630 K at 2.5 THz and 1710 K at 3.1 THz has been obtained without corrections and no anti-reflection (AR) coating on the surface of the lens.

•Jan 1, 2009•1 citation

Heterodyne measurements of a NbN superconducting hot electron mixer at terahertz frequencies

Pavel A. Yagoubov, M. Kroug, H. Merkel +6 more

The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The best results of the DSB noise temperature at 1.5 GHz IF frequency obtained with one device are: 1300 K at 650 GHz, 4700 K at 2.5 THz and 10000 K at 3.12 THz. The measurements were performed at 4.5 K ambient temperature. The amount of local oscillator (LO) power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain measured at 650 GHz is -9 dB, the total conversion gain is -14 dB.

IEEE Transactions on Applied Superconductivity•Jun 1, 1999•6 citations

Performance of a quasi-optical NbN hot-electron bolometric mixer at terahertz frequencies

Yoshinori Uzawa, Shigehito Miki, Z Wang +4 more

The performance of a hot-electron bolometric (HEB) mixer based on NbN from 0.9 to 2.5 THz was investigated using a quasi-optical receiver configuration. An HEB mixer is an ultra-thin superconducting NbN strip located at the feed point of a thick normal conducting Au spiral antenna on a high-resistivity Si substrate. The active area of the mixer was 3 nm thick, 0.4 μm long and 4 μm wide. The quasi-optics consisted of an MgO hyperhemisphere with anti-reflection caps made of Kapton-JP polyimide film and an offset parabola to reduce input losses. The frequency dependence of the double-sideband receiver noise temperature was investigated at several frequencies by using a backward wave oscillator or an optically pumped far-infrared laser as the local oscillator. Results demonstrated low-noise and wide-band characteristics, below 1 K GHz −1 over the measured frequency range. At 917 GHz, the measured receiver noise temperature was 550 K across a 500 MHz intermediate-frequency bandwidth centred at 1.5 GHz, which is slightly better than that of other HEB mixers at around this frequency. This paper was presented at the 8th International Superconductive Electronics Conference, Osaka, Japan, 19–22 June 2001.

Superconductor Science and Technology•Dec 19, 2001•5 citations

Performance of NbN phonon-cooled hot-electron bolometric mixer at Terahertz frequencies

Pavel A. Yagoubov, M. Kroug, H. Merkel +6 more

The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The results of the DSB noire temperature are: 1300 K at 650 GHz, 4700 K at 2.5 TBz and 10000 K at 3.12 THz. The RF bandwidth of the receiver is at least 2.5 THz. The amount of LO power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain is measured to be -9 dB, the total conversion gain -14 dB.

IEEE International Conference on Terahertz Electronics (THz)•Nov 27, 2002•1 citation

Noise performance of quasioptical ultrathin NbN hot-electron bolometer mixer at 2.5 and 3.8 THz

Sergey V. Antipov, Yu.B. Vachtornin, S. N. Maslennikov +5 more

To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.

International Kharkiv Symposium on Physics and Engineering of Microwaves, Millimeter and Submillimeter Waves•Oct 26, 2004•0 citations
Experimental work on the development of a quasi-optical heterodyne receiver for the THz frequency range is reported. The mixing device is a superconducting hot electron bolometer (HEB) made from ultrathin, d = 3 - 5 nm, niobium nitride (NbN) films. Work described in this thesis comprises: The design of a prototype receiver using quasi-optical coupling. Device fabrication involving reactive magnetron sputtering of NbN films and lithographic definition of the antenna integrated mixer. An investigation of the receiver performance at frequencies between 0.6 THz and 2.5 THz. The best performance is obtained with HEB mixers made from NbN films with a thickness d = 3-3.5 nm and a critical temperature T c = 9 - 9.5 K. Double-side band receiver noise temperatures are 530 K at 0.6 THz, 650 K at 1.6 THz and 1100 K at 2.5 THz. Corrected for losses in the receiver input optics, these values amount to only 10 times the theoretical quantum limit. MgO as the substrate material has been shown to provide improved acoustic coupling between NbN film and the substrate compared to other materials such as Si or sapphire. A maximum IF gain bandwidth of 4.5 GHz has been measured under the same operating conditions which yield lowest noise temperature. The local oscilltor power requirement is ~250 nW absorbed in the bolometer. Quasi-optically coupled HEB mixers have become the device-of-choice for radio astronomical applications in the frequency regime at and above 1 THz.
Hot electron bolometer mixers (HEBM) are expected to be used as low-noise heterodyne mixers in the terahertz frequency range. We are developing quasi-optical HEBMs for applications such as atmospheric remote sensing and radio astronomy in the terahertz frequency range. Therefore, we developed a fabrication method using niobium nitride (NbN) ultrathin films deposited on a silicone (Si) substrate for terahertz applications. First, a magnesium oxide buffer layer 50 nm thick was deposited on a Si substrate at approximately 525 °C. After deposition of this layer, NbN ultrathin films were deposited at ambient temperature. Using the buffer layers, we found the transition temperature of the 3.5-nm-thick NbN thin films to be approximately 10 K. The same method was applied to fabricate NbN-HEBMs on a Si substrate. The fabricated quasi-optical mixers were designed to operate at 3.1 THz. The receiver noise temperature was found to be approximately 1930 K (DSB) at 3.1 THz.
Low noise receivers using quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured in the terahertz (THz) frequency range for THz applications in astronomy and cosmology. The NbN HEB mixers consist of a planar complementary antenna and several nanometer (nm) thick NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. A double sideband (DSB) receiver noise temperature of 664 K at 0.76 THz, 920 K at 1.6 THz, 1630 K at 2.5 THz and 1710 K at 3.1 THz has been obtained without corrections and no anti-reflection (AR) coating on the surface of the lens.
The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The best results of the DSB noise temperature at 1.5 GHz IF frequency obtained with one device are: 1300 K at 650 GHz, 4700 K at 2.5 THz and 10000 K at 3.12 THz. The measurements were performed at 4.5 K ambient temperature. The amount of local oscillator (LO) power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain measured at 650 GHz is -9 dB, the total conversion gain is -14 dB.
The performance of a hot-electron bolometric (HEB) mixer based on NbN from 0.9 to 2.5 THz was investigated using a quasi-optical receiver configuration. An HEB mixer is an ultra-thin superconducting NbN strip located at the feed point of a thick normal conducting Au spiral antenna on a high-resistivity Si substrate. The active area of the mixer was 3 nm thick, 0.4 μm long and 4 μm wide. The quasi-optics consisted of an MgO hyperhemisphere with anti-reflection caps made of Kapton-JP polyimide film and an offset parabola to reduce input losses. The frequency dependence of the double-sideband receiver noise temperature was investigated at several frequencies by using a backward wave oscillator or an optically pumped far-infrared laser as the local oscillator. Results demonstrated low-noise and wide-band characteristics, below 1 K GHz −1 over the measured frequency range. At 917 GHz, the measured receiver noise temperature was 550 K across a 500 MHz intermediate-frequency bandwidth centred at 1.5 GHz, which is slightly better than that of other HEB mixers at around this frequency. This paper was presented at the 8th International Superconductive Electronics Conference, Osaka, Japan, 19–22 June 2001.
The performance of a NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixer is investigated in the 0.65-3.12 THz frequency range. The device is made from a 3 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The in-plane dimensions of the bolometer strip are 0.2/spl times/2 /spl mu/m. The results of the DSB noire temperature are: 1300 K at 650 GHz, 4700 K at 2.5 TBz and 10000 K at 3.12 THz. The RF bandwidth of the receiver is at least 2.5 THz. The amount of LO power absorbed in the bolometer is about 100 nW. The mixer is linear to within 1 dB compression up to the signal level 10 dB below that of the LO. The intrinsic single sideband conversion gain is measured to be -9 dB, the total conversion gain -14 dB.
To put space-based and airborne heterodyne instruments into operation at frequencies above 1 THz the superconducting NbN hot-electron bolometer (HEB) will be incorporated into heterodyne receiver as a mixer. At frequencies above 1.3 THz the sensitivity of the NbN HEB mixers outperform the one of the Schottky diodes and SIS-mixers, and the receiver noise temperature of the NbN HEB mixers increase with frequency. In this paper we present the results of the noise temperature measurements within one batch of NbN HEB mixers based on 3.5 mn thick superconducting NbN film grown on Si substrate with MgO buffer layer at the LO frequencies 2.5 THz and 3.8 THz.