IEEE Transactions on Applied Superconductivity

Performance of all-NbN quasi-optical SIS mixers for the terahertz band

Yoshinori Uzawa, Akira Kawakami, Shigehito Miki, Zhen Wang

Published Mar 1, 2001• 21 citations

Abstract

We have designed, fabricated, and tested terahertz superconductor-insulator-superconductor (SIS) mixers having a self-compensated NbN/AlN/NbN tunnel junction and an epitaxially grown NbN/MgO/NbN microstripline. The junction as a distributed element was 0.8-/spl mu/m wide and 2.4-/spl mu/m long, and its current density was 50 kA/cm/sup 2/. The microstripline consisted of a 200-nm-thick NbN ground plane, a 180-nm-thick MgO insulator, and a 350-nm-thick NbN wiring layer. An investigation of the mixer in our receiver configuration showed flat noise characteristics from 870 to 960 GHz. The lowest receiver noise temperature of about 550 K was obtained at 909 GHz, including a 9-/spl mu/m-thick Mylar beam splitter loss and other optical losses. These characteristics suggest that SIS mixers with self-compensated NbN/AlN/NbN junctions and NbN/MgO/NbN microstriplines are appropriate for used in wideband and low-noise operations at terahertz frequencies.

DOI: 10.1109/77.919315

Related papers

Terahertz NbN/AlN/NbN mixers with Al/SiO/NbN microstrip tuning circuits

Yoshinori Uzawa, Zhen Wang, Akira Kawakami

We have developed a low-noise quasioptical NbN/AlN/NbN superconductor-insulator-superconductor (SIS) mixer that operates at terahertz frequencies. The mixer uses a MgO hyperhemispherical lens with an antireflection cap, a single-crystal NbN log-periodic antenna, and two-junction tuning circuits which employ Al/SiO/NbN microstriplines. The NbN/AlN/NbN junction size was about 0.9 μm in diameter, and the current density was about 45 kA/cm2. The frequency dependence of the receiver noise temperature was investigated by using an optically pumped far-infrared laser and a backward-wave oscillator as a local oscillator at several frequencies from 670 to 1082 GHz. The experimental results showed that the center frequency was around 800 GHz, and the receiver noise temperature measured by the standard Y-factor method was 457 K (DSB) at 783 GHz including a 9-μm-thick Mylar beam splitter loss and other optical losses at the physical bath temperature of 4.2 K. This is the first SIS mixer based on NbN with low-noise performance (12hν/kB) above the gap frequency of Nb.

Applied Physics LettersAug 3, 199844 citations

Quasi-optical NbN/AlN/NbN mixers in submillimeter wave band

Yoshinori Uzawa, Z. Wang, Akira Kawakami

We have designed, fabricated and evaluated a quasi-optical SIS receiver with NbN/AlN/NbN tunnel junctions in the submillimeter-wave region. The receiver consists of a planar self-complementary log-periodic antenna and MgO hyperhemispherical lens with an anti-reflection cap for RF optics, NbN SIS junctions and a radial short stub tuner to resonate out its capacitance for RF matching. The prepared NbN SIS junction has a current density of 20 kA/cm/sup 2/ and is about 1 /spl mu/m in diameter, supplying a small /spl omega/C/sub J/R/sub N/ product (/spl omega/C/sub J/R/sub N/=3 at 300 GHz). From 297 to 356 GHz the average double sideband (DSB) receiver noise temperature measured by using the standard Y-factor method was about 200 K. The lowest receiver noise temperature, 167 K (DSB), was obtained at around 303 GHz. These results suggest that our NbN SIS junctions can be used for terahertz mixer elements instead of Nb SIS junctions.

IEEE Transactions on Applied SuperconductivityJun 1, 199714 citations

A submillimetre-wave SIS mixer using NbN/MgO/NbN trilayers grown epitaxially on an MgO substrate

Yoshinori Uzawa, Akira Kawakami, Atsushi SAITO +2 more

We have designed, fabricated and tested a quasi-optical superconductor–insulator–superconductor (SIS) mixer employing distributed NbN/MgO/NbN tunnel junctions and NbN/MgO/NbN microstriplines at submillimetre-wave frequencies. These trilayers were fabricated by dc- and rf-magnetron sputtering on an MgO substrate at ambient temperature so that the NbN and MgO films were grown epitaxially. Our SIS mixer consists of an MgO hyperhemispherical lens with an antireflection cap and a self-complementary log-periodic antenna made of a single-crystal NbN film, on which the distributed SIS junctions and the two-section impedance transformers were mirror-symmetrically placed at the feed point of the antenna. As designed, the junctions are 0.6 μm wide and 15.5 μm long, which is sufficient to absorb the incoming signal along this lossy transmission line, assuming a current density of 10 kA cm −2 . The mixer showed good I – V characteristics, with subgap-to-normal resistance ratios of about 13, although weak-link breaks were observed above the gap voltage. The minimum double side band receiver noise temperature was 334 K at 678 GHz, including the input noise of about 200 K as estimated by the standard technique. The noise temperature gradually rose to 672 K at 820 GHz. This behaviour may be caused by RF losses from the weak-link parts, due to the steps between the distributed junctions and the microstriplines being less than 1 μm wide.

Superconductor Science and TechnologyNov 21, 20026 citations

All-NbN Quasi-Optical SIS Mixers at Terahertz Frequencies

Yoshinori Uzawa, Then Wang, Akira Kawakami

We have theoretically and experimentally investigated submillimeter-wave receiver performances employing NbN/ALN/NbN tunnel junctions with high current density and high energy. gap. The receiver noise based on parameters for our typical NbN SIS junction were analyzed using Tucker's quantum theory of mixing, which showed that DSB receiver noise temperatures of below 3hv/K B can be achieved by using the NbN SIS junctions for frequencies up to 2 THz. An experimental receiver has been designed and tested for the 1 THz band. The mixer consists of a MgO hyperhemispherical lens with anti-reflection cap, a NbN twin-slot antenna, and NbN tuning circuits. The prepared NbN/A1N/NbN junction size was about 0.5 !mut), and the current density was about 30 kA/cm 2 (o)CJRN = 11 at 1 THz). Although the junctions showed good dc I-V characteristics with a small sub-gap leakage current, the receiver noise temperature measured by the standard Y-factor method was about 2700 K(DSB) at 761 GHz, which is much larger than the theoretical prediction. The relative high noise performance may be caused by the large RF losses in the tuning circuit of polycristalline NbN on the SiO.

Jan 1, 19971 citation

0.5-THz waveguide SIS mixers with NbN/AlN/NbN technology

Jing Li, Masanori Takeda, Zhen Wang +1 more

Heterodyne mixers based on superconducting SIS (superconductor-insulator-superconductor) tunnel junctions have been demonstrated to be the most sensitive coherent detectors at millimeter and submillimeter wavelengths. In fact, conventional superconducting SIS mixers with Nb/AlOx/Nb junction and Nb/SiO2/Nb tuning circuit have shown good performances with the noise temperature reaching as low as three times the quantum limit below 0.7THz, which is the gap frequency of Nb-based SIS junctions. However, due to the large loss in Nb thin-film superconducting microstrip lines, the noise performance of Nb SIS mixers deteriorates significantly above 0.7THz. With a gap frequency double that of Nb-based SIS junctions, NbN-based SIS junctions are of particular interest for the development of heterodyne mixers in the terahertz region. Considering the bandwidth and output power of local-oscillator (LO) signal sources are quite limited around 1THz, we firstly develop a waveguide NbN-based SIS mixer at 0.5THz. Three types of SIS junctions, i.e., long junction, parallel-connected tunnel junction (PCTJ) and distributed junction array (DJ) are investigated. They are all comprised of NbN-AlN-NbN tri-layer fabricated on an MgO substrate and have the same current density (Jc) of 10kA/cm2. In this paper, we describe their design, fabrication and preliminary experimental results.

Proceedings of SPIE, the International Society for Optical Engineering/Proceedings of SPIENov 29, 20073 citations

Design and analysis of an All-NbN SIS mixer using a tuning circuit with two half-wavelength distributed junctions

Yoshinori Uzawa, Mahoto Takeda, Akira Kawakami +1 more

We have designed an all-NbN superconductor-insulator-superconductor mixer with a broadband tuning circuit for the terahertz band, which enables the use of junctions with a lower current density. It uses the reactance compensation efficiently produced by two half-wavelength distributed junctions connected by a half-wavelength microstripline. Based on the design and simulated noise performance, a tuning circuit using NbN junctions with a current density of 25 kA/cm/sup 2/ should be able to cover the 780-950 GHz band with an SSB receiver noise temperature below 4hfk/sub B/.

IEEE Transactions on Applied SuperconductivityJun 1, 20037 citations