We report on the performance of a fiber-coupled superconducting nanowire single-photon detector (SNSPD) from 4 K down to the ultralow temperature of 16 mK for a 1550 nm wave length. The system detection efficiency (DE) increased with de creasing the temperature and reached the considerably high value of 15% with a dark count rate less than 100 cps below 1.5 K, even without an optical cavity structure. We also observed saturation of the system DE in its bias current dependency at 16 mK, which indicates that the device DE of our SNSPD nearly reached intrinsic DE despite the device having a large active area of 20 μm × 20 μm. The dark count was finite even at 16 mK and the black body radiation becomes its dominant origin in the low temperatures for fiber-coupled devices.
We report on the performance of a fiber-coupled superconducting nanowire single-photon detector (SNSPD) from 4 K down to the ultralow temperature of 16 mK for a 1550 nm wave length. The system detection efficiency (DE) increased with de creasing the temperature and reached the considerably high value of 15% with a dark count rate less than 100 cps below 1.5 K, even without an optical cavity structure. We also observed saturation of the system DE in its bias current dependency at 16 mK, which indicates that the device DE of our SNSPD nearly reached intrinsic DE despite the device having a large active area of 20 μm × 20 μm. The dark count was finite even at 16 mK and the black body radiation becomes its dominant origin in the low temperatures for fiber-coupled devices.
We present the performances of a superconducting nanowire single-photon detector (SNSPD) in an ultralow-temperature region from 16 mK to 4 K. The system detection efficiency of the SNSPD showed saturation in the bias-current and temperature dependences, and reached the considerably high value of 15% for 100 Hz dark count rate below 1.4 K at a wavelength of 1550 nm even without an optical cavity structure. We found that the dark count exists even at 16 mK and black body radiation becomes its dominant origin in the low temperatures for fiber-coupled devices.
The realization of an ultralow-dark-count rate (DCR) along with the conservation of high detection efficiency (DE) is critical for many applications using single photon detectors in quantum information technologies, material sciences, and biological sensing. For this purpose, a fiber-coupled superconducting nanowire single-photon detector (SNSPD) with a meander-type niobium nitride nanowire (width: 50 nm) is studied. Precise measurements of the bias current dependence of DE are carried out for a wide spectral range (from 500 to 1650 nm in steps of 50 nm) using a white light source and a laser line Bragg tunable band-pass filter. An ultralow DCR (0.0015 cps) and high DE (32%) are simultaneously achieved by the SNSPD at a wavelength of 500 nm.
Ever since superconducting nanowire single-photon detectors (SNSPDs or SSPDs) were demonstrated, they have attracted a considerable attention due to the detectors’ promising performance that includes high detection efficiency (DE), low dark count rate (DCR), broadband sensitivity, and low timing jitter. The system detection efficiency (SDE) has been improved to be over 90% with a wavelength of 1550 nm in a fiber-coupled system by embedding the SNSPD in optical cavities. However, the implementation of optical cavity usually reduces the bandwidth of SNSPDs. As a result, there are some recent works on increasing the bandwidth of SNSPD. Furthermore, the size of the active area of meandered nanowires has to be compatible with the core size of an optical fiber such that good optical coupling can be achieved; this setup requires a long nanowire with a large kinetic inductance, thus resulting in a small counting rate and a large timing jitter, particularly for multi-mode fiber-coupled devices. Nevertheless, a particularly impressive waveguide-coupled SNSPD has been developed in recent years. By placing an SNSPD atop an optical waveguide that has been fabricated on various substrate materials, photons propagating in the waveguide have been found to be evanescently absorbed by nanowires that are only a few tens of microns long. The on-chip DE of this device has been estimated to be over 90%, thus indicating that it has both high absorptance and high intrinsic DE. If the waveguide and the nanowire are correctly dimensioned, the absorptance of this device can reach over 90% for a wavelength range of more than 700 nm. Furthermore, the length of the nanowire is shorter than that of the fiber-coupled SNSPD, thus leading to a higher count rate and lower timing jitter (~18 ps). However, unsatisfactory coupling losses between the optical fiber and the waveguide in such devices can decrease its SDE (~10%), thus limiting its applicability to quantum photonic integrated circuits (QPIC). Recently, we proposed a type of SNSPD that was coupled with microfibers (MFs), and simulations for this SNSPD indicated that its absorption would be as high as 90%. Microfibers and nanofibers, tapered adiabatically from standard fibers, with diameters close to or smaller than the wavelength of the guided light were demonstrated to have low transmittance losses by Tong et al. in 2003. MFs have been shown to have many interesting properties, such as strong evanescent fields, tight optical confinement, wideband abilities, and small masses; these properties are appealing for applications such as optical sensing and coupling. MFs also provide seamless connections with high transmittance from standard fibers; therefore, MF-coupled SNSPDs can achieve both high SDEs and wideband compatibility. We proposed and demonstrated the MF-coupled SNSPDs successfully. The simulation results indicate that with optimal device structure, the optical absorption with efficiency < 90% can be realized over a wavelength range of 350 nm to 2150 nm. The fabricated MF-coupled SNSPD, shows unparalleled broadband system detection efficiencies (SDEs) of more than 50% from 630 nm to 1500 nm. The SDEs reach 66% at 785 nm and 45% at 1550 nm. These results pave the way for ultra-broadband weak light detection with quantum-limit sensitivity.
We report the fabrication of a superconducting nanowire single-photon detector (SSPD or SNSPD) with an ultralow dark count rate. By introducing optical band-pass filters at the input of the SSPD and cooling the filters at 3 K, the dark count rate is reduced to less than 1/100 at low bias. An SSPD with 0.1 cps dark count rate and 5.6% system detection efficiency at 1550 nm wavelength is obtained. We show that a quantum key distribution (QKD) over 300 km of fiber is possible based on a numerical calculation assuming a differential phase shift QKD protocol implemented with our SSPDs.
We demonstrate superconducting nanowire single photon detector (SNSPD) for the wavelength at around 2 μm. The linewidth of the NbN nanowire is squeezed to 56 nm to increase the intrinsic response efficiencies at longer wavelengths such as 2 μm. Serially connecting avalanche architecture is applied to increase the signal-to-noise ratio (SNR) of the response signal. Further, the optical cavity is optimized to improve the absorption of the device. A silica single-mode fiber is adopted to introduce photons to the SNSPD at a temperature of 2.25 K using a Gifford-McMahon cryocooler. The SNSPD exhibits detection efficiencies of 58%, 67%, and 63% at wavelengths of 1550, 1700, and 2000 nm, respectively, with dark count rate of ~12 kcps, which is reduced to 2 cps when the attached fiber pigtail is all placed inside the 40-K cryostat. The detection efficiency at 2000 nm is 2.5 times greater than that of the best previously developed detector with an efficiency of 25%. Our SNSPD is promising for practical applications in molecular science and earth meteorology.
Single photon detection advanced rapidly in the last decade. The superconducting nanowire single-photon detector (SNSPD) is an emerging technology, which offers low dark count rates, broadband sensitivity from visible to mid-infrared wavelengths and very high quantum efficiency. All these features are appealing for future emerging applications in remote gas sensing, quantum key distribution and quantum information processing. By enclosing the detector in an optical cavity, tuned to the operating wavelength, the total system detection of the SNSPD is improved. Based on the cavity design, the detector absorption is boosted at the desired experimental wavelength. Devices have been fabricated and tested, in this thesis, with enhanced detection efficiency at near-infrared, infrared and mid-infrared wavelengths. NbTiN detectors fabricated on Ta2O5 / SiO2 distributed Bragg reflectors (DBR) for front-side coupling exhibit a system detection efficiency of ≈ 90% at λ = 940 nm for the best device measured. SNSPDs were also fabricated in NbTiN on metallic mirrors for back-side coupling for 1550 and 2333 nm experimental wavelengths. The first design exhibited a system detection efficiency of ≈ 84.5%, at λ = 1550 nm for the best device measured. The second exhibited low system detection efficiency since the device suffered from unexpectedly high dark count rate mainly due to blackbody radiation at 2.2 K. However, it was possible to measure the timing jitter of this device at 350 mK indicating a FWHM of 84 ps. Another technique to improve the total system detection efficiency of the SNSPD, is by fabricating a hairpin-shaped nanowire atop a single mode waveguide. In this design, photons travel through the waveguide and via evanescent coupling are absorbed in the nanowire. These SNSPD devices have been designed to thread along single mode Si ridge waveguides using a hairpin-shaped nanowire structure, which offers enhanced coupling and absorption efficiency via evanescent coupling. These ultra-thin superconducting MoSi detectors are precisely patterned on top of a single mode Si waveguide (600 nm) with alignment error less than 40 nm. Low temperature electrical and nano-optical characterization was carried out using a two-stage pulse tube (PT) coldhead, using an additional 4He / 3He sorption pump, low vibration characterization of SNSPD devices at 350 mK was carried out. Characterised devices exhibit low dark count rate <5 counts per second and timing jitter of ≈ 83 ps full width half maximum (FWHM) at wavelength (λ) = 1550 nm and at critical current ≈ 30 µA.