Development of THz Waveguide NbTiN HEB Mixers

Ling Jiang, S. Shiba, K. Shimbo, Nami Sakai, T. Yamakura, M. Sugimura, P. G. Ananthasubramanian, Hiroyuki Maezawa, Yoshihisa Irimajiri, Satoshi Yamamoto

Published Jun 1, 2009• 16 citations

Publisher

Abstract

In this paper, we present the development of the waveguide niobium titanium nitride (NbTiN) superconducting hot electron bolometer (HEB) mixers, cryogenically cooled by a 4 K close-cycled refrigerator. The NbTiN thin film is formed on a crystalline quartz substrate by sputtering an NbTi target with the Ar and N2gas at room temperature. The HEB mixer element is fabricated by using the 12 nm NbTiN film, and is mounted on a waveguide block. Measurement of a Fourier transform spectrometer shows that the response of the mixer is centered near 810 GHz with a bandwidth of about 500 GHz. The uncorrected DSB receiver noise temperature is measured to be 500 K, and the noise bandwidth is to be 1.4 GHz at 810 GHz. The present result shows that a good noise performance can be obtained for the NbTiN HEB mixer even with a relatively thick film (12 nm) fabricated at the room temperature.

DOI: 10.1109/tasc.2009.2019071

Related papers

Development of 1.5 THz waveguide NbTiN superconducting hot electron bolometer mixers

Ling Jiang, Shoichi Shiba, Tatsuya Shiino +7 more

We present a characterization of a 1.5 THz waveguide niobium titanium nitride (NbTiN) superconducting hot electron bolometer (HEB) mixer which can be pumped by a commercial solid state tunable local oscillator (LO) source. The NbTiN HEB mixer is made from a 12 nm thick NbTiN thin film deposited on a quartz substrate at room temperature. A gold electrode is formed in situ on the NbTiN thin film without breaking vacuum to ensure good contact. The uncorrected DSB receiver noise temperature is measured to be 1700 K at 1.5 THz, whereas the mixer noise temperature is derived to be 1000 K after corrections for losses of the input optics and the intermediate frequency (IF) amplifier chain. The required LO power absorbed in the HEB mixer is evaluated to be 340 nW by using an isothermal technique. The IF gain bandwidth is supposed to be about 1.3 GHz or higher. The present results show that good performance can be obtained at 1.5 THz even with a relatively thick NbTiN film (12 nm), as in the case of 0.8 THz. In order to investigate the cooling mechanism of our HEB mixers, we have conducted performance measurements for a few HEB mixers with different microbridge sizes both at 1.5 and 0.8 THz. The noise performance of the NbTiN HEB mixers is found to depend on the length of the NbTiN microbridge. The shorter the microbridge is, the lower the receiver noise temperature is. This may imply a contribution of the diffusion cooling in addition to the phonon cooling.

Superconductor Science and TechnologyMar 19, 201020 citations

Development of 0.8 THz and 1.5 THz Waveguide NbTiN HEB Mixers

Ling Jiang, Shunsuke Shiba, K. Shimbo +5 more

I n this p aper, we p resent res ults on th e n oise performance o f the waveguide Niobium Titanium Nitride (NbTiN) superconducting hot electron bolometer (HEB) mixers, cryogenically cooled b y a 4- K clos e-cycled ref rigerator. The NbTiN superconducting HE B mixer is fabricated on a crystalline qua rtz su bstrate, and is mou nted in a w aveguide mixer bloc k for RF and LO c oupling. At 0. 81 THz , the uncorrected DSB rec eiver noise temperature is measured to be 500 K and the noise bandw idth is 1.4 GHz . The same mixer shows the DSB receiver noise temperature of 640 K at 0.65 THz. We also investigate the DC performance o f superconduct ing NbTiN HEB mixer designed for 1.5 THz. I. INTRODUCTION

Softwaretechnik-TrendsApr 1, 20083 citations

Low-noise 1.5 THz waveguide-type hot-electron bolometer mixers using relatively thick NbTiN superconducting film

Tatsuya Shiino, Ryuta Furuya, Tatsuya Soma +7 more

Abstract We have developed waveguide-type low-noise superconducting hot-electron bolometer (HEB) mixers for astronomical observations in the 1.3–1.5 THz region by using a relatively thick NbTiN superconducting film (10.8 nm). We have achieved a receiver noise temperature of 490 K (DSB: double side band) at 1.475 THz. This noise temperature corresponds to seven times the quantum noise. According to gain bandwidth measurements, the contribution of diffusion cooling is found to be responsible for such a good noise performance.

Japanese Journal of Applied PhysicsFeb 20, 20151 citation

Stability of a Quasi-Optical Superconducting NbTiN Hot-Electron Bolometer Mixer at 1.5 THz Frequency Band

Hiroyuki Maezawa, T. Yamakura, T. Shiino +10 more

We are developing quasi-optical superconducting hot-electron bolometer (HEB) mixer receivers for astronomical and atmospheric remote sensing applications. The microbridge of the HEB mixer was fabricated at room temperature from a 6.8-nm-thick niobium titanium nitride (NbTiN) film deposited on a 20-nm-thick aluminum nitride (AlN) buffer layer, using a helicon sputtering technique at a slow deposition rate. The mixer was cooled to 4.2 K using a closed-cycled mechanical 4 K pulse-tube cryocooler with a temperature fluctuation of$\pm$1.6 mK. The stability of a large-volume NbTiN HEB mixer was studied at 1.47 THz by changing local oscillator (LO) power with the mixer bias voltage fixed. The intermediate frequency (IF) signal measured at 1.5 GHz had a maximum peak at a certain mixer bias current. The receiver noise temperature was lowest at around the IF maximum peak. It was also found that the IF signal was most stable at around the IF maximum peak under conditions in which the instability of LO pumping level, induced by small mechanical vibrations of the cryostat, remained in the optical system.

IEEE Transactions on Applied SuperconductivityJan 24, 20116 citations

Fabrication and Noise Measurement of NbTiN Hot Electron Bolometer Heterodyne Mixers at THz Frequencies

P. Khosropanah, S. Bedorf, Serguei Cherednichenko +4 more

The paper reports the latest development and the measured results of NbTiN hot electron bolometer mixers at THz frequencies. The devices are based on 4-7 nm thin NbTiN films, which were deposited by reactive magnetron sputtering of NbTi target in an Ar/N2 atmosphere, on heated high-resistivity Si substrates over a 20 nm thick AlN buffer layer. The quality parameters of the film are transition temperature and normal-state resistivity, which were optimized by varying the sputtering parameters. The resistivity and the critical temperature of the films are about 400 μΩcm and 9 K, respectively. Bolometers (4 μm wide and 0.7 μm long), integrated with logarithmic spiral antennas are fabricated. Mixer noise performance is tested in a quasi-optical receiver in 1.5-4 GHz IF band. The DSB receiver noise temperature of 700 K, 1100 K and 3000 K is obtained at 0.7, 1.6 and 2.6 THz LO frequencies, respectively.

Apr 1, 20035 citations

Low Noise Receivers Using Niobium Nitride Hot Electron Bolometer Mixers from 0.76 to 3.1 THz

J. Chen, Min Liang, Lin Kang +5 more

Low noise receivers using quasi-optical superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured in the terahertz (THz) frequency range for THz applications in astronomy and cosmology. The NbN HEB mixers consist of a planar complementary antenna and several nanometer (nm) thick NbN bridge connecting across the antenna's inner terminals on high-resistivity Si substrates. A double sideband (DSB) receiver noise temperature of 664 K at 0.76 THz, 920 K at 1.6 THz, 1630 K at 2.5 THz and 1710 K at 3.1 THz has been obtained without corrections and no anti-reflection (AR) coating on the surface of the lens.

Jan 1, 20091 citation