Millimeter and submillimeter wave responses of YBa/sub 2/Cu/sub 3/O/sub 7/ step-edge Josephson junctions

Hisashi Shimakage, Yoshinori Uzawa, Z. Wang, Akira Kawakami, Wataru Chujo, Bokuji Komiyama

Published Jun 1, 1995• 13 citations

Abstract

We have fabricated YBCO step-edge Josephson junctions and measured the responses to millimeter and submillimeter irradiation. In the substrate milling process for the purpose of fabricating the step, the step angle was controlled using a Nb metal mask. At a step angle of 20 degrees, we obtained Josephson junctions, the characteristics of which are consistent with the RSJ model. We estimated the capacitance to be 4.4 fF using the RSJ model, but such a value for an 8 /spl mu/m wide and 300 nm thick junction seems too small. When the junctions were irradiated by 300 GHz radiation, Shapiro steps up to the 4th were observed. The junctions were used as mixers in the 100 GHz band, and as harmonic mixers in the 100 GHz LO and 700 GHz RF bands. Beat signals were observed in both cases. We also estimated the quasi-optical conversion losses of the step-edge junctions as mixers.>

DOI: 10.1109/77.403173

Related papers

Millimeter and submillimeter wave responses of YBa2Cu307 step-edge Josephson junctions

Hisashi Shimakage, Yoshinori Uzawa, Z. Wang +3 more

We have fabricated YBCO step-edge Josephson junctions and measured the responses to the millimeter and submillimeter irradiation. In the substrate milling process for the purpose of fabricat- ing the step, the step angle was controlled using a Nb metal mask. At a step angle of 20 degrees, we obtained Josephson junctions, the characteristics of which are consistent with the RSJ model. We estimated the ca- pacitance to be 4.4 fF using the RSJ model, but such a value for an 8 pm wide and 300 nm thick junction seems too small. When the junctions were irradiated by 300 GHz, Shapiro steps up to the 4th were ob- served. The junctions were used as mixers in the 100 GHz band, and as harmonic mixers in the 100 GHz LO and 700 GHz RF bands. Beat signals were observed in both cases. We also estimated the quasi-optical con- version losses of the stepedge junctions as mixers.

Jan 1, 19950 citations

High T/sub c/ superconducting step-edge junctions and their properties in millimeter-wave band

Yijun Feng, L. Kang, X. B. Wang +8 more

Superconducting step-edge junctions were fabricated on step-edges in (100) LaAlO/sub 3/ substrates by sputter-deposited epitaxial YBaCuO and TlBaCaCuO thin films. The substrate steps were patterned by ion beam etching using metal film as a mask. The transport properties of the junctions were characterized by four-probe electrical measurements. The critical current-normal resistance product (I/sub c/R/sub N/) was larger than 0.2 mV (77 K) for most of the junctions. Clear Shapiro steps were observed in the current-voltage characteristics of the junctions with 36 GHz or 95 GHz millimeter-wave irradiation. The high frequency properties of these high T/sub c/ Josephson junctions showed that they were quite suitable for the Josephson harmonic mixer used in the digital phase locked millimeter and sub-millimeter wave sources.>

IEEE Transactions on Applied SuperconductivityJun 1, 19951 citation

Detection of the Josephson self-radiation from YBCO step-edge junctions in millimeter-wave

K. Lee, Ienari Iguchi

We have investigated both DC and AC Josephson effects of the YBa/sub 2/Cu/sub 3/O/sub y/ (YBCO) thin film step-edge junctions; single step-edge junction on LaAlO/sub 3/ substrate with the step angle about 50-60/spl deg/ and biepitaxial double step-edge junction made on MgO substrate with a CeO/sub 2/ seed layer. The Josephson self-radiation was directly detected using the total power radiometer receiver systems with receiving frequencies of K band (21-23 GHz) and millimeter-wave (46-48 GHz and 71-73 GHz) range, respectively. For single step-edge junctions, the Josephson self-radiation peaks exhibited at the voltages corresponding to the basic Josephson voltage-frequency relation. The maximum first-harmonic self-radiation power at receiving frequency f/sub REC/=72 GHz and Josephson linewidth were P(I)=2.0/spl times/10/sup -3/W and /spl Delta/f=3.62 GHz at 4.2 K, respectively. For microwave irradiation, the harmonic Shapiro steps and additional half integer steps with their quasi-periodic variation satisfying the Josephson equation V=(n/m)(hf/2e) were clearly observed. For double step-edge junctions, we also observed the steps corresponding to the two junction boundaries on the two steep steps. These behaviors described with different current-phase relations corresponding to the crystal orientation relationship between the two junction boundaries.>

IEEE Transactions on Applied SuperconductivityJun 1, 19952 citations

MIXING EXPERIMENTS AT W-BAND USING HIGH-TC JOSEPHSON JUNCTIONS

Oliver Harnack, Marian Darula, S. Beuven +1 more

We report on the mixing properties of high-T, superconductor (HTS) Josephson junctions. Direct radiation and heterodyne mixing experiments in the frequency range 78 GHz-119 GHz have been performed using YBa 2Cu30 7_ x (YBCO) step-edge junctions (SEJ) and bicrystal junctions (BO) on LaA10 3 and MgO substrates. Under external radiation our junctions showed harmonic phase synchronization (Shapiro steps) up to 1.88 THz. Junctions with current voltage characteristics (PVC) dose to predictions of the resistively shunted junction model (RSJ) were mounted into a heterodyne mixing setup. Under the radiation of two monochromatic signals we obtained conversion efficiencies around -14 dB in the 11 GHz intermediate frequency (IF) band. In the fundamental mixing regime we observed response at IF at working temperatures up to 72K. We demonstrated the operation of HTS Josephson junctions in the self-mixing mode. The experimental results are in good agreement with simulations using the RSJ model.

Jan 1, 19970 citations

Mixing and detection in YBaCuO step-edge Josephson junction arrays up to 670 GHz

Janusz Konopka, I. Wolff, S. Beuven +1 more

Submillimeter wave detectors and mixers based on YBa/sub 2/Cu/sub 3/O/sub 7/ (YBCO) step-edge Josephson junctions incorporated into planar antennas were designed and tested up to 670 GHz at temperatures from 12 to 65 K. A quasi-optic coupling system with a LaAlO/sub 3/ lens was used. In some samples the noise intrinsic in the detection process does not follow the Johnson noise law but has a minimum, which for a given sample may occur in the temperature range between 35 to 50 K. Harmonic mixing recorded at 670 GHz proves that the system equilibrium is established in a time shorter than 500 fs.>

IEEE Transactions on Applied SuperconductivityJun 1, 19956 citations

Near-millimeter-wave response of high T c ramp-type Josephson junctions

R. Gupta, Qing Hu, D. Terpstra +2 more

We have studied the response of a YBCO/PBCO/YBCO ramp-type junction to coherent radiation at 176 and 270 GHz. The I-V characteristic of the junction closely resembles the prediction of the RSJ model. The IcRn product of the junction is 0.25 mV at 5 K. The millimeter-wave radiation is coupled to the junction via a quasioptical structure that focuses the radiation onto the junction through a yttrium-stabilized ZrO2 substrate. At 176 GHz, we have observed as many as six Shapiro steps at the maximum power level of our Gunn oscillator-pumped frequency doubler. Shapiro steps are still clearly seen up to 65 K. The amplitudes of the zeroth, first, and second Shapiro steps, as functions of the square root of the radiation power, agree remarkably well with a Bessel function fit, indicating the junction is voltage-biased at the radiation frequency (rf). At 270 GHz, due to a combination of the heavy rf loss in the ZrO2 substrate and the lack of radiation power, we have observed only the first Shapiro step.

Applied Physics LettersJun 21, 199310 citations