The Journal of Chemical Physics

Potassium spin polarization lifetime for a 30-carbon chain siloxane film

Amber M. Hibberd, Susanna L. Bergman, Yu Lin Zhong, Steven L. Bernasek

Published Nov 2, 2012• 10 citations
Publisher

Abstract

The siloxane film derived from the 30-carbon chain triacontyltrichlorosilane (TCTS) is studied as an anti-relaxation coating for atomic vapor cells. The longitudinal spin relaxation lifetime of optically pumped potassium atoms in the presence of TCTS is measured and the average number of non-relaxing atom-wall collisions, or bounces, enabled by the coated surface is determined. X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) of TCTS were performed to investigate changes in chemical states and surface morphology of TCTS arising from K atom deposition on the film surface. TCTS was found to give approximately 530 bounces. Following lifetime measurements, K2p signals were clearly observed in XPS spectra. AFM images display non-preferential K deposition on the TCTS surface, however additional AFM studies with a TCTS surface exposed to Rb atoms show deposition occurs along surface defects. In agreement, Rb is found to preferentially deposit along the step edges of an 18-carbon chain monolayer film derived from 1-Octadecene. Finally, AFM indicates a much smoother surface for a tetracontane coating relative to TCTS. The importance of siloxane surface morphology versus film thickness with respect to coating performance is discussed.

DOI
10.1063/1.4761934

Related papers

Effects of organic film morphology on the formation of Rb clusters on surface coatings in alkali metal vapor cells

David M. Rampulla, Nuri Oncel, Esta Abelev +3 more

Surface relaxation rates differ for spin-polarized alkali atoms interacting with monolayer or bilayer octadecyltrichlorosilane (OTS) coatings. The morphology and composition of Rb vapor-exposed films of OTS have been studied with atomic force microscopy (AFM) and x-ray photoelectron spectroscopy (XPS). On OTS monolayers, numerous small (<500 nm wide) Rb containing islands nucleate at the boundaries of the ∼1–2 μm wide organic domains. On OTS bilayers, singular large (∼3 μm wide) Rb containing islands were found. Alkali island formation mediated by surface structure could affect the antirelaxation behavior of organic coatings used in atomic magnetometer cells.

Applied Physics Letters•Jan 26, 2009•26 citations

Relaxation of Cs atomic polarization at surface coatings characterized by X-ray photoelectron spectroscopy

Kotaro Kushida, Toshihiro Niwano, Takemasa Moriya +4 more

Abstract Paraffin coatings on glass slides were investigated through both X-ray photoelectron spectroscopy (XPS) and spin relaxation measurement for cesium (Cs) vapor. The components of the glass substrate, such as silicon and oxygen, existed in the XPS spectra of the coated slides, indicating the imperfection of the prepared paraffin coatings. The substrate was not observed after the annealing of the coatings in Cs vapor, which is known as a “ripening” process for spin relaxation measurement. We found a general trend that effective anti-spin relaxation performance requires high paraffin and low Cs coverage on the surface. We also examined a type of diamond-like carbon film, anticipating the effect of anti-spin relaxation; our attempts have failed to date.

arXiv:1410.8321•Japanese Journal of Applied Physics•May 1, 2015•3 citations

Investigation of antirelaxation coatings for alkali-metal vapor cells using surface science techniques

Scott J. Seltzer, David J. Michalak, Marcus H. Donaldson +17 more

Many technologies based on cells containing alkali-metal atomic vapor benefit from the use of antirelaxation surface coatings in order to preserve atomic spin polarization. In particular, paraffin has been used for this purpose for several decades and has been demonstrated to allow an atom to experience up to 10 000 collisions with the walls of its container without depolarizing, but the details of its operation remain poorly understood. We apply modern surface and bulk techniques to the study of paraffin coatings in order to characterize the properties that enable the effective preservation of alkali spin polarization. These methods include Fourier transform infrared spectroscopy, differential scanning calorimetry, atomic force microscopy, near-edge x-ray absorption fine structure spectroscopy, and x-ray photoelectron spectroscopy. We also compare the light-induced atomic desorption yields of several different paraffin materials. Experimental results include the determination that crystallinity of the coating material is unnecessary, and the detection of C[Double Bond]C double bonds present within a particular class of effective paraffin coatings. Further study should lead to the development of more robust paraffin antirelaxation coatings, as well as the design and synthesis of new classes of coating materials.

arXiv:1002.4417•The Journal of Chemical Physics•Oct 11, 2010•63 citations

A comprehensive study of the effects of different factors on anti-relaxation properties of octadecyltrichlorosilane-coated rubidium vapor cells

Haotian Chi, Heng Yuan, Zhongyu Cai +4 more

Abstract Anti-relaxation coatings play an important role in enhancing the polarization lifetime of polarized alkali-metal atoms. In this study, octadecyltrichlorosilane (OTS) was coated in spherical rubidium vapor cells fabricated using borosilicate glass with two stems as anti-relaxation coatings. An orthogonal experiment method was employed to obtain the optimal conditions. The results showed that OTS concentration is the dominant factor in the number of bounces, followed by the soaking time and molar ratio/(H2O:OTS). The optimal parameters were 6 mM of OTS, 6:1 of molar ratio/(H2O:OTS), and 80 min of soaking time. The number of bounces can be up to 200. Atomic force microscope images showed that the number and coverage ratio of clusters on the anti-relaxation coating fabricated by the optimized parameters are significantly less than the number and coverage ratio of clusters formed by other conditions. This means that the clusters in the coatings significantly affect the anti-relaxation performance. In addition, five OTS-coated cells were fabricated by A3B3C5 combination. However, the variability from cell to cell using the exact same preparation procedure can be up to 43.6%. The variability may be caused by the different aging times of the OTS solution. Because only one beaker of OTS solution was prepared, the OTS solution was pumped into the cells in sequence, not at the same time.

Journal of Physics D Applied Physics•Oct 12, 2021•12 citations

Effect of Preparation Processes on Structural Thermal Stability and Collision Energy Dissipation of Common Antirelaxation Coatings on Quartz Substrates

Xinxin He, Xiaoya Liu, Jun Tang +5 more

Paraffin and octadecyltrichlorosilane (OTS) coatings can alleviate collisions between alkali-metal atoms and cell walls and then prolong the atomic spin-polarization lifetime. The surface structure and collision effects of these antirelaxation coatings, as well as the methods to avoid antirelaxation invalidity, have been the focus of researchers. This study investigated the thermolability of coating surface structure and the collision interactions between alkali metal atoms and coatings, considering the influence of various coating preparation factors, where this collision interaction is indirectly analyzed by measuring the collision energy dissipation between an atomic force microscopy (AFM) probe and the atoms on the coating surface. We found that appropriate evaporation time, carbochain length, and postannealing process can enhance the thermostability of the paraffin coating and eliminate its morphological defects. Furthermore, the OTS/water concentration, the soaking time, and the type of solvent have different levels of influence on the cluster formation and the thermostability of the OTS coatings. Moreover, the antirelaxation performance of coatings has been shown to be characterized by counting the energy dissipated when the AFM probe collides with the antirelaxation coating, replacing the conventional light-atom interaction- based method for measuring the relaxation characteristics, but requiring specific coating preparation factors to be maintained.

Langmuir•Aug 31, 2023•3 citations

Method for characterizing self-assembled monolayers as antirelaxation wall coatings for alkali vapor cells

Youngwoo Yi, H. G. Robinson, Svenja A. Knappe +5 more

We describe a method for characterizing self-assembled monolayers (SAMs) in terms of their performance as antirelaxation wall coatings for alkali atom vapor cells. A combination of initial surface analysis and subsequent laser spectroscopy is used to provide insight into the quality of the coating, as well as its performance under the exposure to alkalis as it occurs, for example, when used in applications such as atomic magnetometers or clocks. Fused silica plates coated with octadecyltrichlorosilane SAMs were used to make cubic R87b gas cells. The surface was characterized by x-ray diffraction, contact angle measurements, and atomic force microscopy. Measurements of hyperfine resonance linewidths and frequency shifts show that the rubidium vapor atoms collide up to 40 times with the walls of the cells before their coherence relaxes and their adsorption energy is around 0.065 eV. Chemical analysis of the cell indicates some weak reactions between the coating and the rubidium atoms.

Journal of Applied Physics•Jul 15, 2008•75 citations
The siloxane film derived from the 30-carbon chain triacontyltrichlorosilane (TCTS) is studied as an anti-relaxation coating for atomic vapor cells. The longitudinal spin relaxation lifetime of optically pumped potassium atoms in the presence of TCTS is measured and the average number of non-relaxing atom-wall collisions, or bounces, enabled by the coated surface is determined. X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) of TCTS were performed to investigate changes in chemical states and surface morphology of TCTS arising from K atom deposition on the film surface. TCTS was found to give approximately 530 bounces. Following lifetime measurements, K2p signals were clearly observed in XPS spectra. AFM images display non-preferential K deposition on the TCTS surface, however additional AFM studies with a TCTS surface exposed to Rb atoms show deposition occurs along surface defects. In agreement, Rb is found to preferentially deposit along the step edges of an 18-carbon chain monolayer film derived from 1-Octadecene. Finally, AFM indicates a much smoother surface for a tetracontane coating relative to TCTS. The importance of siloxane surface morphology versus film thickness with respect to coating performance is discussed.
Surface relaxation rates differ for spin-polarized alkali atoms interacting with monolayer or bilayer octadecyltrichlorosilane (OTS) coatings. The morphology and composition of Rb vapor-exposed films of OTS have been studied with atomic force microscopy (AFM) and x-ray photoelectron spectroscopy (XPS). On OTS monolayers, numerous small (<500 nm wide) Rb containing islands nucleate at the boundaries of the ∼1–2 μm wide organic domains. On OTS bilayers, singular large (∼3 μm wide) Rb containing islands were found. Alkali island formation mediated by surface structure could affect the antirelaxation behavior of organic coatings used in atomic magnetometer cells.
Abstract Paraffin coatings on glass slides were investigated through both X-ray photoelectron spectroscopy (XPS) and spin relaxation measurement for cesium (Cs) vapor. The components of the glass substrate, such as silicon and oxygen, existed in the XPS spectra of the coated slides, indicating the imperfection of the prepared paraffin coatings. The substrate was not observed after the annealing of the coatings in Cs vapor, which is known as a “ripening” process for spin relaxation measurement. We found a general trend that effective anti-spin relaxation performance requires high paraffin and low Cs coverage on the surface. We also examined a type of diamond-like carbon film, anticipating the effect of anti-spin relaxation; our attempts have failed to date.
Many technologies based on cells containing alkali-metal atomic vapor benefit from the use of antirelaxation surface coatings in order to preserve atomic spin polarization. In particular, paraffin has been used for this purpose for several decades and has been demonstrated to allow an atom to experience up to 10 000 collisions with the walls of its container without depolarizing, but the details of its operation remain poorly understood. We apply modern surface and bulk techniques to the study of paraffin coatings in order to characterize the properties that enable the effective preservation of alkali spin polarization. These methods include Fourier transform infrared spectroscopy, differential scanning calorimetry, atomic force microscopy, near-edge x-ray absorption fine structure spectroscopy, and x-ray photoelectron spectroscopy. We also compare the light-induced atomic desorption yields of several different paraffin materials. Experimental results include the determination that crystallinity of the coating material is unnecessary, and the detection of C[Double Bond]C double bonds present within a particular class of effective paraffin coatings. Further study should lead to the development of more robust paraffin antirelaxation coatings, as well as the design and synthesis of new classes of coating materials.
Abstract Anti-relaxation coatings play an important role in enhancing the polarization lifetime of polarized alkali-metal atoms. In this study, octadecyltrichlorosilane (OTS) was coated in spherical rubidium vapor cells fabricated using borosilicate glass with two stems as anti-relaxation coatings. An orthogonal experiment method was employed to obtain the optimal conditions. The results showed that OTS concentration is the dominant factor in the number of bounces, followed by the soaking time and molar ratio/(H2O:OTS). The optimal parameters were 6 mM of OTS, 6:1 of molar ratio/(H2O:OTS), and 80 min of soaking time. The number of bounces can be up to 200. Atomic force microscope images showed that the number and coverage ratio of clusters on the anti-relaxation coating fabricated by the optimized parameters are significantly less than the number and coverage ratio of clusters formed by other conditions. This means that the clusters in the coatings significantly affect the anti-relaxation performance. In addition, five OTS-coated cells were fabricated by A3B3C5 combination. However, the variability from cell to cell using the exact same preparation procedure can be up to 43.6%. The variability may be caused by the different aging times of the OTS solution. Because only one beaker of OTS solution was prepared, the OTS solution was pumped into the cells in sequence, not at the same time.
Paraffin and octadecyltrichlorosilane (OTS) coatings can alleviate collisions between alkali-metal atoms and cell walls and then prolong the atomic spin-polarization lifetime. The surface structure and collision effects of these antirelaxation coatings, as well as the methods to avoid antirelaxation invalidity, have been the focus of researchers. This study investigated the thermolability of coating surface structure and the collision interactions between alkali metal atoms and coatings, considering the influence of various coating preparation factors, where this collision interaction is indirectly analyzed by measuring the collision energy dissipation between an atomic force microscopy (AFM) probe and the atoms on the coating surface. We found that appropriate evaporation time, carbochain length, and postannealing process can enhance the thermostability of the paraffin coating and eliminate its morphological defects. Furthermore, the OTS/water concentration, the soaking time, and the type of solvent have different levels of influence on the cluster formation and the thermostability of the OTS coatings. Moreover, the antirelaxation performance of coatings has been shown to be characterized by counting the energy dissipated when the AFM probe collides with the antirelaxation coating, replacing the conventional light-atom interaction- based method for measuring the relaxation characteristics, but requiring specific coating preparation factors to be maintained.
We describe a method for characterizing self-assembled monolayers (SAMs) in terms of their performance as antirelaxation wall coatings for alkali atom vapor cells. A combination of initial surface analysis and subsequent laser spectroscopy is used to provide insight into the quality of the coating, as well as its performance under the exposure to alkalis as it occurs, for example, when used in applications such as atomic magnetometers or clocks. Fused silica plates coated with octadecyltrichlorosilane SAMs were used to make cubic R87b gas cells. The surface was characterized by x-ray diffraction, contact angle measurements, and atomic force microscopy. Measurements of hyperfine resonance linewidths and frequency shifts show that the rubidium vapor atoms collide up to 40 times with the walls of the cells before their coherence relaxes and their adsorption energy is around 0.065 eV. Chemical analysis of the cell indicates some weak reactions between the coating and the rubidium atoms.