We measured the optical transitions due to the internal energy levels of an exciton and biexciton in a CuCl single crystal using pump-probe spectroscopy. The transient absorption bands due to the transitions from the
1s to
2p and from the
1s to
3p exciton states were observed at 3 K, which is consistent with their reported energies. Simultaneously, the transient absorption peak due to the biexciton was observed, which corresponds to a transition from the lowest state (composed of two
1s excitons) to higher states (composed of
1s and
2p excitons). The value of the observed biexciton peak energy was reasonable considering the hydrogen molecule orbitals and the electron-to-hole effective mass ratio. In addition, the transient absorption peaks were broadened at 77 K, because of the increase in the homogeneous width of the
2p exciton state. The transient absorption spectrum was almost completely determined by this width. Our findings are of importance with regard to the optical phenomena in the infrared region related to the quantum coherence of excitons and biexcitons in semiconductors.
Abstract We investigated the influence of excitation processes of a biexciton on the generation of superfluorescence, which is pulsed radiation from coherently coupled two-level systems, from biexcitons in CuCl quantum dots. Two excitation processes of biexcitons were examined: resonant two-photon excitation of biexcitons, and resonant one-photon excitation of excitons. The excitation density dependence of the time-resolved photoluminescence was measured. The results showed that for one-photon excitation, a stronger peak intensity, longer delay time and wider pulse width were observed compared to resonant two-photon excitation. The high density of the excited dots in the one-photon excitation process results in the strong pulse, while an initial population of excitons results in a suppression of coherent coupling.