This thesis investigates how the coherence time of the 3H4 – 1D2 transition of praseodymium doped into a YSO crystal is affected by an externally applied magnetic field. Such crystals, kept at or below helium temperature, are con-sidered for use as hardware in a future quantum computer, and the coherence time is one important factor affecting the error rate of gate operations in this computer. If the coherence time could be increased by magnetic fields, it could increase the fidelity of gate operations, bringing it closer to values where quan-tum computing becomes viable. The measurements were made using two-pulse photon echoes, and the measured coherence times were determined to approximately 60 µs, which corresponds to a homogeneous linewidth of 5 kHz. The coherence times showed no clear magnetic field dependence and were substantially shorter that previously reported. It could not be determined whether this was the result of unforeseen processes destroying the coherence or due to an experimental artifact.
This thesis investigates how the coherence time of the 3H4 – 1D2 transition of praseodymium doped into a YSO crystal is affected by an externally applied magnetic field. Such crystals, kept at or below helium temperature, are con-sidered for use as hardware in a future quantum computer, and the coherence time is one important factor affecting the error rate of gate operations in this computer. If the coherence time could be increased by magnetic fields, it could increase the fidelity of gate operations, bringing it closer to values where quan-tum computing becomes viable. The measurements were made using two-pulse photon echoes, and the measured coherence times were determined to approximately 60 µs, which corresponds to a homogeneous linewidth of 5 kHz. The coherence times showed no clear magnetic field dependence and were substantially shorter that previously reported. It could not be determined whether this was the result of unforeseen processes destroying the coherence or due to an experimental artifact.
The optical spectroscopy and dynamics of three materials; Eu^3+:Y2SiO5, Pr^3+:Y2SiO5, and Tm^3+:Y2SiO5 that are of interest for application in persistent spectral holeburning optical memory and signal processing devices were investigated using linear and nonlinear spectroscopic techniques.Two-pulse photon echoes have been used to measure the homogeneous linewidths.The effects of instantaneous spectral diffusion were systematically studied to allow accurate determination of the optical resonance widths, and external magnetic fields were applied to characterize the effects of fluctuating nuclear spins of the host lattice on dephasing of the dopant ion.The 7F0 → 5D0 transition of 0.1% Eu^3+ in the two crystallographic sites of Y2SiO5 was studied using photon echoes.Using this material, we succeeded in measuring the narrowest optical resonance in a solid by shielding the crystal from stray electromagnetic fields and using sufficiently low laser power to minimize contributions from instantaneous diffusion.The homogeneous linewidths measured in a magnetic field of 100 G are 122 Hz (site 1) and 167 Hz (site 2).These widths are dominated by population decay, but up to 20 Hz is attributed to 89Y spin fluctuations which have been reduced by the applied magnetic field.Similar studies were performed to determine the contributions to the homogeneous linewidth of the 3H4(1) → 1D2(1) transition for both sites of 0.02% Pr^3+ in Y2SiO5.Linewidths of 2.1 kHz (site 1) and 0.85 kHz (site 2) were obtained with an applied magnetic field of 77 G.A significant contribution of 89Y nuclear spin fluctuations to the zero-field homogeneous linewidth was found.Optically detected nuclear magnetic resonance measurements determined the hyperfine structure of the 3H4 ground state for each site, and photon echo nuclear double resonance was used to determine the hyperfine levels of the lowest component of the 1D2 manifold. 3) 2.1? Ec,2S
This thesis presents a spectroscopic study of Pr3+ ions in a novel passive waveguide architecture. To make this structure, the high refractive glass TeO2 was selected as the thin film and it was deposited on a Pr3+:Y2SiO5 crystal. In this waveguide, the 3H4 to 1D2 transition of Pr3+ ions were probed by the optical evanescent field extending into the substrate. The main concern in assessing the suitability of this material for quantum information applications was ensuring that the coherence properties of rare-earth ions, making them suitable for quantum information purposes, are preserved in this architecture. After which, to make low loss devices with these waveguides, efficient coupling techniques had to be developed. To prove that the coherence properties of the rare-earth ion doped crystal were preserved, the critical parameters of inhomogeneous linewidth, the absorption of the ions, the coherence time and spin lifetimes of the Pr3+ ions were studied. The inhomogeneous linewidth of evanescent coupled ions was about 10.0 GHz, which was consistent with the linewidth of bulk samples with the same Pr3+ doping concentration (Hedges, 2011). The absorption due to the evanescent coupling was 9.38 dB, approximately 90% of what was expected with respect to the bulk crystal with the same doping concentration. Therefore, despite using the evanescent field, the absorption is high enough for quantum memory applications. An optical coherence time of about 121 microseconds was measured, which corresponded to a homogeneous linewidth of about 2.6 kHz. This is very close to bulk sample measurements of 111 microseconds, with the same temperature and doping concentration (R. W. Equall, 1995). The spin state lifetime observed was about 9.8 s, which is also very close to the bulk sample measurement of 8.67 s (Mieth, 2016). Initial Stark shifting experiments were performed to determine whether the active ions in the substrate of the passive waveguides could be electrically controlled by applying a small voltage to electrodes on the thin film. In these experiments with a voltage change of 100 mV, the measured holewidth broadening was increasing about 0.55 MHz, which was similar to the calculated values of 0.45 MHz. The Stark coefficient for site 1 was 51.6 kHzcm/V along the D2 axis of the crystal (site 1 will be explained in Section 4.3). (F.R. Graf, 1997). Prism coupling and grating coupling were used to couple light to the ions in the substrate. Prism coupling is an easy and quick method to couple light into a waveguide and observe the properties of the system. However, grating coupling is much more practical when moving towards building a device using this method. The measurements described above indicated that the properties of ions interacting with the evanescent tail of the waveguide mode were consistent with those of bulk ions. This investigation also showed that depositing a glass thin film on a rare-earth ion doped crystal was not affecting the good coherence properties of the substrate. These results establish the foundation for large, integrated, controllable and high performance rare earth ion quantum waveguide systems.
This master's thesis investigates the ground state hyperfine levels coherence time in Pr3+:Y2Si05• This property is important for the future development of quantum computers based on this or similar crystals.A suitable method to measure the coherence time at liquid helium temperature for two hyperfine levels in the 4 H3 level of Pr3+ was developed and the coherence time has also been determined approximately to 540 J.l-S.Examensarbetet undersoker koherenstiden for tva hyperfin nivaer i grundtillstandet for Pr3+:Y2Si05 .Detta ar en egenskap som ar viktig for en framtida kvantdator baserad pa denna eller liknande kristaller.En metod att mata koherenstiden vid flytande helium temperatur for tva av hyperfinnivaerna i grundtillstandet for Pr3+ har utvecklats och koherenstiden har med denna metod matts upp till 540 J.l-S.
In this Letter, we present a method for increasing the coherence time of praseodymium hyperfine ground state transitions in Pr(3+):Y(2)SiO5 by the application of a specific external magnetic field. The magnitude and angle of the external field is applied such that the Zeeman splitting of a hyperfine transition is at a critical point in three dimensions, making the first order Zeeman shift vanishingly small for the transition. This reduces the influence of the magnetic interactions between the praseodymium ions and the spins in the host lattice on the transition frequency. Using this method a phase memory time of 82 ms was observed, a value 2 orders of magnitude greater than previously reported. It is shown that the residual dephasing is amenable to quantum error correction.
This thesis investigates the coherence properties of the hyperfine transitions of the 151Eu3+ ions in Eu3+:Y2SiO5 and evaluates the potential of developing quantum memories using these transitions. Quantum memories for light with long storage times are required for quantum commu- nication applications. For these memories to be useful they need to have storage times long compared to the transmission times across the communication network. For a global optical communication network this requires storage time longer than 100 ms. Rare-earth doped crystals have been identified as a suitable storage material. The storage time of these systems is limited by the coherence time of the hyperfine transitions of the optically active rare-earth ions. In previous work it had been demonstrated that coherence times as long as 1.4 seconds could be achieved for hyperfine transitions in Pr3+:Y2SiO5 by ap- plying a particular magnetic field such that the first order Zeeman shift of the transition nulled. This technique is known as zero first-order Zeeman (ZEFOZ). Due to the relatively large second order Zeeman efficient of the transitions in Pr3+:Y2SiO5, an extension of the coherence time, significantly beyond the 1.4 second mark using ZEFOZ, is not expected. However, it has been predicted that coherence times more than two orders of magnitude longer could be achieved in Eu3+:Y2SiO5 due to the smaller second order Zeeman shifts associated with the relevant hyperfine transitions. The dominant decoherence mechanism for the hyperfine transitions in diluted Eu3+:Y2SiO5 is the magnetic field perturbations caused by the random spin reconfigu- ration of the Y3+ ions in the host. By applying the ZEFOZ technique, previously used in Pr3+:Y2SiO5, the sensitivity of the transition’s frequency to environmental magnetic field perturbations was significantly reduced. Further, this strong ZEFOZ magnetic field was also shown to induce a frozen core around the Eu3+ ion, which resulted in a signifi- cant suppression of the reconfiguration of the nearby Y3+ spins. The combined effect of the reduced sensitivity and frozen core effect allowed a decoherence rate of 8 × 10−5 s−1 over 100 milliseconds to be demonstrated. The observed decoherence rate is at least an order of magnitude lower than that of any other system suitable for an optical quantum memory. Furthermore, by employing dynamic decoherence control, a coherence time of 370 ± 60 minutes was achieved. This 6 hour coherence time observed here opens up the possibility of distributing quantum entanglement via the physical transport of memories as an alternative to optical communications. It was found that even at the critical point alignment the observed coherence times showed that the Y3+ spin flips remain the dominant decoherence mechanism. To aid in the development of future strategies to further extend the coherence time beyond 6 hours, a study of the Y3+ spin dynamics in the frozen core was conducted. Four of the Y3+ sites were resolved and a complete mapping of all frozen-core Y3+ sites was limited by the inhomogeneity of the applied magnetic field. The Rabi frequency, the coherence time and lifetime as well as the interaction strength with the Eu3+ ion of one of these Y3+ ions were measured. The observed lifetime of the Y3+ ion is 27 s, which is four orders of magnitude longer than the low field value. With the technique developed, a detailed understanding of the frozen-core dynamics is possible, which would allow an extension of the hyperfine coherence time of the Eu3+ ion towards the lifetime limit. In summary, this thesis provides a detailed characterisation of the decoherence mecha- nisms of the hyperfine transitions in Eu3+:Y2SiO5. The potential of using rare-earth doped crystals for the long-term storage of quantum information with applications to long-range quantum communications is identified. The demonstrated long coherence time of the quantum transitions for information storage allows a new way of entanglement distribu- tion: entanglement is transported by physically transporting the memory crystal rather than the light. This approach opens a new regime for both quantum communication and fundamental tests of quantum mechanics.
Optical coherence and spin population dynamics in 171Yb3+:Y2SiO5 single crystals
171Yb3+-doped Y2SiO5 crystals are a promising platform for optical quantum memories in long-distance quantum communications. The relevance of this material lies in 171Yb long optical and spin coherence times, along with a large hyperfine splitting, enabling long quantum storage over large bandwidths. Mechanisms affecting the optical decoherence are however not precisely known, especially since low-temperature measurements have so far focused on the 2 to 4 K range. In this work, we performed two- and three-pulse photon echoes and spectral hole burning to determine optical homogeneous linewidths in two 171 Yb:YSO crystals doped at 2 and 10 ppm. Experiments were performed in the 40 mK to 18 K temperature range, leading to linewidths between 320 Hz, among the narrowest reported for rare-earth ions, and several MHz. Our results show that above 6 K the homogeneous linewidth is mainly due to an elastic two-phonon process which results in a slow broadening with temperature, the homogeneous linewidth reaching only 25 kHz at 10 K. At lower temperatures, interactions with 89Yb nuclear spin-flips, paramagnetic defects or impurities, and also Yb-Yb interactions for the higher concentrated crystal, are likely the main limiting factor to the homogeneous linewidth. In particular, we conclude that the direct effect of spin and optical excited state lifetime is a minor contribution to optical decoherence in the whole temperature range studied. Our results indicate possible paths and regimes for further decreasing the homogeneous linewidths or maintaining narrow lines at higher 171Yb concentration.