This thesis presents a spectroscopic study of Pr3+ ions in a novel passive waveguide architecture. To make this structure, the high refractive glass TeO2 was selected as the thin film and it was deposited on a Pr3+:Y2SiO5 crystal. In this waveguide, the 3H4 to 1D2 transition of Pr3+ ions were probed by the optical evanescent field extending into the substrate. The main concern in assessing the suitability of this material for quantum information applications was ensuring that the coherence properties of rare-earth ions, making them suitable for quantum information purposes, are preserved in this architecture. After which, to make low loss devices with these waveguides, efficient coupling techniques had to be developed. To prove that the coherence properties of the rare-earth ion doped crystal were preserved, the critical parameters of inhomogeneous linewidth, the absorption of the ions, the coherence time and spin lifetimes of the Pr3+ ions were studied. The inhomogeneous linewidth of evanescent coupled ions was about 10.0 GHz, which was consistent with the linewidth of bulk samples with the same Pr3+ doping concentration (Hedges, 2011). The absorption due to the evanescent coupling was 9.38 dB, approximately 90% of what was expected with respect to the bulk crystal with the same doping concentration. Therefore, despite using the evanescent field, the absorption is high enough for quantum memory applications. An optical coherence time of about 121 microseconds was measured, which corresponded to a homogeneous linewidth of about 2.6 kHz. This is very close to bulk sample measurements of 111 microseconds, with the same temperature and doping concentration (R. W. Equall, 1995). The spin state lifetime observed was about 9.8 s, which is also very close to the bulk sample measurement of 8.67 s (Mieth, 2016). Initial Stark shifting experiments were performed to determine whether the active ions in the substrate of the passive waveguides could be electrically controlled by applying a small voltage to electrodes on the thin film. In these experiments with a voltage change of 100 mV, the measured holewidth broadening was increasing about 0.55 MHz, which was similar to the calculated values of 0.45 MHz. The Stark coefficient for site 1 was 51.6 kHzcm/V along the D2 axis of the crystal (site 1 will be explained in Section 4.3). (F.R. Graf, 1997). Prism coupling and grating coupling were used to couple light to the ions in the substrate. Prism coupling is an easy and quick method to couple light into a waveguide and observe the properties of the system. However, grating coupling is much more practical when moving towards building a device using this method. The measurements described above indicated that the properties of ions interacting with the evanescent tail of the waveguide mode were consistent with those of bulk ions. This investigation also showed that depositing a glass thin film on a rare-earth ion doped crystal was not affecting the good coherence properties of the substrate. These results establish the foundation for large, integrated, controllable and high performance rare earth ion quantum waveguide systems.
This thesis presents a spectroscopic study of Pr3+ ions in a novel passive waveguide architecture. To make this structure, the high refractive glass TeO2 was selected as the thin film and it was deposited on a Pr3+:Y2SiO5 crystal. In this waveguide, the 3H4 to 1D2 transition of Pr3+ ions were probed by the optical evanescent field extending into the substrate. The main concern in assessing the suitability of this material for quantum information applications was ensuring that the coherence properties of rare-earth ions, making them suitable for quantum information purposes, are preserved in this architecture. After which, to make low loss devices with these waveguides, efficient coupling techniques had to be developed. To prove that the coherence properties of the rare-earth ion doped crystal were preserved, the critical parameters of inhomogeneous linewidth, the absorption of the ions, the coherence time and spin lifetimes of the Pr3+ ions were studied. The inhomogeneous linewidth of evanescent coupled ions was about 10.0 GHz, which was consistent with the linewidth of bulk samples with the same Pr3+ doping concentration (Hedges, 2011). The absorption due to the evanescent coupling was 9.38 dB, approximately 90% of what was expected with respect to the bulk crystal with the same doping concentration. Therefore, despite using the evanescent field, the absorption is high enough for quantum memory applications. An optical coherence time of about 121 microseconds was measured, which corresponded to a homogeneous linewidth of about 2.6 kHz. This is very close to bulk sample measurements of 111 microseconds, with the same temperature and doping concentration (R. W. Equall, 1995). The spin state lifetime observed was about 9.8 s, which is also very close to the bulk sample measurement of 8.67 s (Mieth, 2016). Initial Stark shifting experiments were performed to determine whether the active ions in the substrate of the passive waveguides could be electrically controlled by applying a small voltage to electrodes on the thin film. In these experiments with a voltage change of 100 mV, the measured holewidth broadening was increasing about 0.55 MHz, which was similar to the calculated values of 0.45 MHz. The Stark coefficient for site 1 was 51.6 kHzcm/V along the D2 axis of the crystal (site 1 will be explained in Section 4.3). (F.R. Graf, 1997). Prism coupling and grating coupling were used to couple light to the ions in the substrate. Prism coupling is an easy and quick method to couple light into a waveguide and observe the properties of the system. However, grating coupling is much more practical when moving towards building a device using this method. The measurements described above indicated that the properties of ions interacting with the evanescent tail of the waveguide mode were consistent with those of bulk ions. This investigation also showed that depositing a glass thin film on a rare-earth ion doped crystal was not affecting the good coherence properties of the substrate. These results establish the foundation for large, integrated, controllable and high performance rare earth ion quantum waveguide systems.
We report the measurement of the inhomogeneous linewidth, homogeneous linewidth, and spin-state lifetime of Pr3+ ions in a novel waveguide architecture. The TeO2 slab waveguide deposited on a bulk ${\mathrm{Pr}}^{3+}\ensuremath{\mathbin:}{\mathrm{Y}}_{2}{\mathrm{SiO}}_{5}$ crystal allows the ${^{3}\mathrm{H}}_{4}{\ensuremath{\leftrightarrow}}^{1}{\mathrm{D}}_{2}$ transition of Pr3+ ions to be probed by the optical evanescent field that extends into the substrate. The 2-GHz inhomogeneous linewidth, the optical coherence time of $70\ifmmode\pm\else\textpm\fi{}5\text{ }\text{ }\ensuremath{\mu}\mathrm{s}$, and the spin-state lifetime of $9.8\ifmmode\pm\else\textpm\fi{}0.3\text{ }\text{ }\mathrm{s}$ indicate that the properties of ions interacting with the waveguide mode are consistent with those of bulk ions. This result establishes the foundation for large, integrated, and high performance rare-earth-ion quantum systems based on a waveguide platform.
When doped into solid state transparent crystals, rare-earth ions can have optically excited states with milliseconds coherence time and up to six hours coherence time for hyperfine levels after being cooled down to liquid helium temperature. This long coherence property makes them unique as solid state material and attractive for quantum information applications.The rare-earth ions have narrow homogeneous linewidths on the order of ~ kHz. When doped into a crystal, the lattice structure is slightly distorted due to the size mismatch between the dopant and the host ions, resulting in slight differences in the local crystal fields at the dopant sites. Therefore, the resonance frequencies of the rare-earth ions are shifted relatively, resulting in an inhomogeneously broadened absorption profile, typically on the order of a few GHz. This provides the possibility of addressing each group of ions individually and engineering the absorption profile for different purposes by optical pumping using a narrow linewidth laser, and makes rare-earth-ion-doped crystals suitable for ensemble based quantum memories.Quantum memories are vital components for developing longdistance quantum communication. Part of this thesis project focused on making quantum memories with high efficiency and long storage time, especially using materials with low optical depth. To achieve this goal, a low finesse, unsymmetrical cavity was employed and experiments were carried out at (or close to) the impedance matched condition. Atomic frequency comb (AFC) protocol proposed for such an inhomogeneously broadened system was used to store coherent light for a certain time. 56% overall efficiency was achieved, and the main limiting factor for reaching even higher efficiency was the inefficient coupling between incoming light and the cavity mode. Other possible loss mechanisms were analyzed as well.Long-time, on-demand, quantum memory experiments were conducted with the help of two efficient radio-frequency rephasing pulses. Storage time was extended from microseconds to milliseconds after compensating (most of) the residual earth magnetic field in the lab. The opportunities and challenges of combing the cavity assistant quantum memory and the long time, on demand quantum memory were analyzed and possible solutions were proposed. Another part of the thesis project involves slow light-based applications in rare-earth-ion-doped crystals. The strong slow light effect at the presence a spectral hole is due to the fact that the light interacts with the absorbing ions outside the spectral hole off-resonantly, and most of the light energy is stored inside the ions as a polarization. For example, with a group velocity of 300 km/s, 99.9% of the pulse energy is stored in the ions when the pulse propagates inside the crystal. The slower the light propagates, the more energy is stored inside the medium. Based on this, a frequency shifter that is capable of shifting the light frequency of ± 4 MHz was demonstrated, and frequency shift up to GHz was proposed. Group velocity control by a factor of 20 and pulse compression in time by a factor of 2 were also demonstrated. The frequency shift and group velocity of the light are solely controlled by the external electric field, which makes them ideal for weak light situation. The unique property of such a frequency shifter and group velocity controller is that they could be made to accept light from an arbitrary incoming angle and polarization, for example, scattered light.
Rare-earth ion ensembles doped in single crystals are a promising materials system with widespread applications in optical signal processing, lasing, and quantum information processing. Incorporating rare-earth ions into integrated photonic devices could enable compact lasers and modulators, as well as on-chip optical quantum memories for classical and quantum optical applications. To this end, a thin film single crystalline wafer structure that is compatible with planar fabrication of integrated photonic devices would be highly desirable. However, incorporating rare-earth ions into a thin film form-factor while preserving their optical properties has proven challenging. We demonstrate an integrated photonic platform for rare-earth ions doped in a single crystalline thin film lithium niobate on insulator. The thin film is composed of lithium niobate doped with Tm 3+ . The ions in the thin film exhibit optical lifetimes identical to those measured in bulk crystals. We show narrow spectral holes in a thin film waveguide that require up to 2 orders of magnitude lower power to generate than previously reported bulk waveguides. Our results pave the way for scalable on-chip lasers, optical signal processing devices, and integrated optical quantum memories.
In the last decade, the solid-state rare-earth-ion system has demonstrated increasing appeal for quantum computation. Despite this progress, two hardware limitations prevent a scalable implementation. These current limitations are the inability to miniaturise and the inability to perform single-ion qubit readout. This thesis addresses both these limitations and demonstrates that neither poses a fundamental restriction on increasing the scale of rare-earth-ion quantum computers. The challenge in miniaturising rare-earth-ion quantum hardware arises from the increases in homogeneous and inhomogeneous broadening that accompany micron-scale architectures. The success of miniaturised architectures, such as waveguides, depends on the properties of bulk ions being preserved within microns of the crystal surface. In addition, bulk ion properties must also be preserved in regions of high residual stress resultant from waveguide fabrication. The inhomogeneous and homogeneous properties of near-surface ions and ions in highly stressed environments in Pr3+:Y2SiO5 were studied via white light interferometry combined with micron resolution fluorescence microscopy. It was found that the bulk ion properties could be preserved both near the surface and in highly stressed regions close to micron-scale surface damage. The observation of excess inhomogeneous and homogeneous broadening was found to be consistent with the damage present at the crystal surface. The main outcome of the study was a set of waveguide fabrication guidelines to ensure that the appealing properties of bulk crystals can be maintained in a miniaturised architecture. The current inability to perform single-ion qubit readout is a consequence of the difficulty in isolating a single ion and lack of cyclicity in rare-earth-ion materials. Two techniques are proposed to form a solution: Stark activation and Zeeman enhanced cyclicity. When combined, these techniques offer direct readout for single-ion frequency-based quantum computing. Stark activation is designed to isolate a single rare-earth ion in a macroscopic crystal. The proposal is based on defining the condition for resonant excitation through a spatially varying electric field. A proof-of-principle experiment successfully created a 10 um absorption region within a millimetre thick crystal. In addition, the signal-to-noise ratio of the technique was characterised in experiments probing Pr3+:Y2SiO5 at the single-ion level. Future improvements to the apparatus should allow the nanometre spatial resolution and the noise level to be reduced to allow single-ion optical detection. High cyclicity is essential for high-fidelity optical readout of a single-ion qubit. Zeeman enhanced cyclicity achieves this by manipulating the hyperfine structure of the resonant crystal field levels to induce strong hyperfine selection rules. The technique is shown to be applicable to even the lowest symmetry sites. The simulated level of cyclicity in Pr3+:Y2SiO5 was greater than 99.99% by applying a 10 T field. The investigation of scalability in the rare-earth-ion system marks a movement away from the traditional ensemble-based methods in macroscopic crystals. This study required an understanding of these materials at a single-ion level and the development of high spatial resolution spectroscopic techniques. These advances extend the ability to engineer rare-earth-ion systems for applications including, but not limited to, quantum computing.
This thesis describes experiments aimed at developing a key component in applications such as quantum networks and long-distance quantum communication systems: quantum memories. Quantum memories for light using photon-echo and coherent rephrasing techniques have been developed. The work is carried out on rare-earth-ion-doped inorganic crystals. Several properties are associated with these crystals such as long coherence times and long-lived ground state sublevels that are particularly interesting in connection applications in the area of quantum information science. It is demonstrated the preparation of optical inhomogeneous absorption profiles such that the light only interacts with a specific transition at a selected frequency. Narrow absorbing structures with widths of <100 kHz have been prepared with no absorption in the surrounding spectral interval. Most of the experiments were carried out using Pr3+:Y2SiO5. However, in our search for suitable a Λ-system in the material under consideration, we also performed spectral hole-burning spectroscopy in Nd:Y2SiVO4. As part of the search for host materials for Pr, Pr:La2(WO4)3 crystal was characterized using a variety of methods, such as, hole burning and photon-echoes. Electromagnetically induced transparency was also observed in this crystal. The most important criteria for evaluating quantum memory performance and the most important physical requirements are discussed. After investigating the standard photon echo techniques and controlled reversible inhomogeneous broadening (CRIB) for quantum state storage, we considered an efficient multimode quantum memory protocol; the atomic frequency comb (AFC) protocol. Combs with peaks of widths 100-300 kHz and an optical depth of~ 10 were created by optical pumping inside an emptied region of the inhomogeneous profile of Pr3+:Y2SiO5, allowing us to improve the efficiency of light storage. Light storage combining a photon-echo technique based on an AFC and spin-wave storage have been demonstrated, and an experimental AFC scheme for the storage of weak coherent light pulses in Pr3+:Y2SiO5 is presented. Finally, we have investigated superradiance and slow light effects. Both these effects occur in the high optical depth regime and can influence the memory performance. Under certain conditions superradiance results in the immediate re-emission of the stored light in a single burst of coherent radiation, and inside spectrally structured materials, slow light effects may result when storage is performed.
Rare-earth-ion doped crystals are an interesting system for quantum computing investigations due to their long optical and hyperfine coherence times. In particular, the ground-state coherence times can be longer than one second, which makes them perfect for long-term storage of quantum states. They also have the advantage of being a solid-state system. At present, many of the fundamental requirements for quantum computing have been demonstrated using rare-earth-ions; however, quantum state readout has yet to be achieved. The strong-coupling regime is of great importance in cavity quantum electrodynamics, as in this regime interactions between single atoms and single photons can be realized. Strong coupling thereby provides a method of enabling qubit-qubit interactions. It is desirable to achieve this regime with rare-earth-ion doped resonators, as it would enable on-demand readout of quantum states, a necessity for quantum computing, and provide the scalability required for implementation of quantum networks. This thesis describes the work that has gone into investigating the suitability of rare-earth-ion doped whispering-gallery mode resonators for quantum computing applications. A theoretical analysis of the strong-coupling regime is performed, followed by experiments investigating the properties of ions in resonators, and of new rare-earth-ion materials. A final set of experiments studies a new quantum memory protocol for use with rare-earth-ions. A theoretical investigation is undertaken to determine whether the strong-coupling regime will be attainable with rare-earth-ion doped whispering-gallery mode resonators. Emphasis is given to determining which rare-earth-ion materials will have the best properties when used as resonators. Specific applications of the strong-coupling regime are examined for this system; in particular, whether it will be possible to demonstrate the reversible transfer of quantum states, and detection of single dopants. Experiments are performed, measuring the properties of millimetre-sized Pr3+:Y2SiO5 resonators. Direct measurements of cavity quantum electrodynamics parameters are made using photon echoes, giving good agreement with theoretical predictions. Interactions between the atom and cavity are observed and a theoretical model is presented to describe these effects. Thus, a more realistic picture is obtained of the experimental requirements for achieving the strong-coupling regime. The properties of different rare-earth-ion doped materials are measured and analysed to determine their suitability for quantum computing applications. The spin Hamiltonian parameters of Pr3+:YAG are measured using Raman heterodyne spectroscopy, and then used to find the optical transitions with zero first-order Zeeman shift, as this should allow the coherence time to be extended to a point where this system is useful for resonator applications. Hyperfine transitions with zero first-order Zeeman shift are also calculated for Er3+:Y2SiO5, with the aim of enabling long-term storage in a telecommunication-wavelength memory. The thesis concludes with an experimental investigation into a new quantum memory technique that does not require spectral hole burning. The hybrid photon echo rephasing protocol uses strong optical pulses to perform rephasing, thus utilizing the advantageous properties of the two-pulse photon echo. Furthermore, the use of external broadening fields removes the usual problem of noise from amplified spontaneous emission. The properties of this memory are examined using a Pr3+:Y2SiO5 crystal.