Homogeneous Linewidth and Relaxation Time Measurements on Rare-Earth-Ion-Doped Crystals

Thomas Schmidt, P. J. van der Zaag, B. C. Schokker +1 more

Rare-earth ions doped in glasses or crystals have extremely narrow homogeneous optical linewidths at low temperature and are, therefore, excellent probes for studying small spectral splittings [1]. They are further potential candidates for data storage applications.

G. Zumofen, F.R Graf, Alois Renn +1 more

Graf, Felix R.

Solids containing rare earth (RE) ions have attracted spectroscopists' attention since the beginning of this century.In the last 30 years, their extremely narrow spectral features in combination with the use of non linear spectroscopy have served to sensitively measure ion-solid interactions and to progressively observe narrower homogeneous linewidths.The potential for using RE ion doped crystals as optical storage materials and processors has lately been a driving force in their investigations, Here, the ratio of inhomogeneous to homogeneous linewidth is regarded as an adequate measure of storage density and can become as big as 10 7 at cryogenic temperatures.Therefore, the analysis of line broadening is of fundamental as well as applied interest.This work is concerned with the investigation of interactions of RE ions with their environment.By means of a laser with a kilohertz resolution and non-linear spectroscopy, spectral dynamics as a function of intrinsic, external electric field, or light-pulse induced perturbations are analyzed on different time scales.In the first part, the theoretical background for the spectroscopy of RE ion doped crystals is outlined.The energy levels are presented and it is shown that due to their electronic properties RE ions have spectrally narrow electronic transitions, sometimes in the sub-kHz regime.The investigations of these narrow spectral features on the seconds to minutes time scale require very stable tunable laser sources.At present, such devices are not commercially available.In the second part, the performance of ahorne built laser system is characterized using persistent spectral holes, The results show that frequency selective materials can be used as powerful tools for the high resolution Vlll Abstract spectral analysis of laser sources.Complementary to that, they give a measure for the long term evolution of the spectral holes for the particular hole burning substance.In the third part, the effect of an external electric field on RE ion doped crystals is investigated.It is shown that for these systems the electric field induced frequency shifts are fully reversible.A general theory of Stark splittings of RE doped crystals is introduced and two methods are presented which allow for the determination of the magnitude and orientation of the electric dipole moment differences with sub-degree accuracy.Finally in the last part, spectral line broadening mechanisms of RE ion doped crystals are discussed and investigated by means of two-pulse photon echoes.Through variation of the experimental parameters, a discrimination between the different contributions is partly achieved and characteristic properties for different dephasing mechanisms are presented.In combination with the measurements from the third part, quantitative predictions of the electric dipole-dipole induced broadening are carried out, which are compared to the experimental results,

Diana Serrano, Senthil Kumar Kuppusamy, Benoı̂t Heinrich +4 more

Sara Marzban

This thesis presents a spectroscopic study of Pr3+ ions in a novel passive waveguide architecture. To make this structure, the high refractive glass TeO2 was selected as the thin film and it was deposited on a Pr3+:Y2SiO5 crystal. In this waveguide, the 3H4 to 1D2 transition of Pr3+ ions were probed by the optical evanescent field extending into the substrate. The main concern in assessing the suitability of this material for quantum information applications was ensuring that the coherence properties of rare-earth ions, making them suitable for quantum information purposes, are preserved in this architecture. After which, to make low loss devices with these waveguides, efficient coupling techniques had to be developed. To prove that the coherence properties of the rare-earth ion doped crystal were preserved, the critical parameters of inhomogeneous linewidth, the absorption of the ions, the coherence time and spin lifetimes of the Pr3+ ions were studied. The inhomogeneous linewidth of evanescent coupled ions was about 10.0 GHz, which was consistent with the linewidth of bulk samples with the same Pr3+ doping concentration (Hedges, 2011). The absorption due to the evanescent coupling was 9.38 dB, approximately 90% of what was expected with respect to the bulk crystal with the same doping concentration. Therefore, despite using the evanescent field, the absorption is high enough for quantum memory applications. An optical coherence time of about 121 microseconds was measured, which corresponded to a homogeneous linewidth of about 2.6 kHz. This is very close to bulk sample measurements of 111 microseconds, with the same temperature and doping concentration (R. W. Equall, 1995). The spin state lifetime observed was about 9.8 s, which is also very close to the bulk sample measurement of 8.67 s (Mieth, 2016). Initial Stark shifting experiments were performed to determine whether the active ions in the substrate of the passive waveguides could be electrically controlled by applying a small voltage to electrodes on the thin film. In these experiments with a voltage change of 100 mV, the measured holewidth broadening was increasing about 0.55 MHz, which was similar to the calculated values of 0.45 MHz. The Stark coefficient for site 1 was 51.6 kHzcm/V along the D2 axis of the crystal (site 1 will be explained in Section 4.3). (F.R. Graf, 1997). Prism coupling and grating coupling were used to couple light to the ions in the substrate. Prism coupling is an easy and quick method to couple light into a waveguide and observe the properties of the system. However, grating coupling is much more practical when moving towards building a device using this method. The measurements described above indicated that the properties of ions interacting with the evanescent tail of the waveguide mode were consistent with those of bulk ions. This investigation also showed that depositing a glass thin film on a rare-earth ion doped crystal was not affecting the good coherence properties of the substrate. These results establish the foundation for large, integrated, controllable and high performance rare earth ion quantum waveguide systems.

Bess Fang, Nicolas Galland, Nemanja Lučić +6 more