Characterization of Hydroxyls in Surface Oxide of Superconducting Tantalum and Their Mitigation in Quantum Circuits
Ekta Bhatia, Nicholas Pieniazek, Aleksandra Barbara Biedron, Sandra B. Schujman, Hunter Frost, Zhihao Xiao, Jakub Nalaskowski, Kevin Musick, Thomas Murray, Satyavolu Papa Rao
Recently, tantalum (Ta) has gained attention in superconducting quantum circuits due to the longer coherence times achieved when replacing niobium (Nb) in capacitor pads. Previous literature shows that surface oxides that form upon ambient exposure on superconducting metals such as Ta, Al, and Nb host two-level system (TLS) defects, which are a leading source of microwave loss and decoherence. While the surface oxides of Nb and Al have been extensively studied, Ta oxides remain less well understood. Using secondary ion mass spectrometry of alpha-Ta films deposited at 300 mm wafer scale, we show for the first time that hydroxyls accumulate in the Ta suboxide region above the underlying Ta. Angle-resolved X-ray photoelectron spectroscopy shows that the surface region is dominated by Ta2O5, with sub-stoichiometric TaOx present in between the Ta2O5 and underlying Ta. The thickness of the tantalum oxide is confirmed by transmission electron microscopy. We demonstrate that [OH] incorporation can be suppressed by replacing the native oxide with an oxide formed during chemical mechanical planarization of alpha-Ta films. Our findings support the hypothesis that TLS defects are non-uniform within the oxide thickness and suggest hydroxyls as a probable molecular origin of these loss channels. Furthermore, we show the feasibility of plasma nitridization as a method to decrease hydroxyl loading on alpha-Ta surfaces. The modulation of hydroxyl content through surface engineering of alpha-Ta can enable the fabrication of more robust, high-coherence superconducting quantum circuits by addressing a potential TLS source.
Recently, tantalum (Ta) has gained attention in superconducting quantum circuits due to the longer coherence times achieved when replacing niobium (Nb) in capacitor pads. Previous literature shows that surface oxides that form upon ambient exposure on superconducting metals such as Ta, Al, and Nb host two-level system (TLS) defects, which are a leading source of microwave loss and decoherence. While the surface oxides of Nb and Al have been extensively studied, Ta oxides remain less well understood. Using secondary ion mass spectrometry of alpha-Ta films deposited at 300 mm wafer scale, we show for the first time that hydroxyls accumulate in the Ta suboxide region above the underlying Ta. Angle-resolved X-ray photoelectron spectroscopy shows that the surface region is dominated by Ta2O5, with sub-stoichiometric TaOx present in between the Ta2O5 and underlying Ta. The thickness of the tantalum oxide is confirmed by transmission electron microscopy. We demonstrate that [OH] incorporation can be suppressed by replacing the native oxide with an oxide formed during chemical mechanical planarization of alpha-Ta films. Our findings support the hypothesis that TLS defects are non-uniform within the oxide thickness and suggest hydroxyls as a probable molecular origin of these loss channels. Furthermore, we show the feasibility of plasma nitridization as a method to decrease hydroxyl loading on alpha-Ta surfaces. The modulation of hydroxyl content through surface engineering of alpha-Ta can enable the fabrication of more robust, high-coherence superconducting quantum circuits by addressing a potential TLS source.
High Resolution Image Download MS PowerPoint Slide Improving the qubit’s lifetime (T 1 ) is crucial for fault-tolerant quantum computing. Recent advancements have shown that replacing niobium (Nb) with tantalum (Ta) as the base metal significantly increases T 1, likely due to a less lossy native surface oxide. However, understanding the formation mechanism and nature of both surface oxides is still limited. Using aberration-corrected transmission electron microscopy and electron energy loss spectroscopy, we found that Ta surface oxide has fewer suboxides than Nb oxide. We observed an abrupt oxidation state transition from Ta 2 O 5 to Ta, as opposed to the gradual shift from Nb 2 O 5, NbO 2, and NbO to Nb, consistent with thermodynamic modeling. Additionally, amorphous Ta 2 O 5 exhibits a closer-to-crystalline bonding nature than Nb 2 O 5, potentially hindering H atomic diffusion toward the oxide/metal interface. Finally, we propose a loss mechanism arising from the transition between two states within the distorted octahedron in an amorphous structure, potentially causing two-level system loss. Our findings offer a deeper understanding of the differences between native amorphous Ta and Nb oxides, providing valuable insights for advancing superconducting qubits through surface oxide engineering.
Superconducting qubits are among the most advanced platforms for quantum information, offering potential scalability and compatibility with standard device fabrication techniques [1-5]. Among the materials investigated for superconducting qubits, Tantalum (Ta) has emerged as a compelling candidate due to its self-terminating stoichiometric surface oxide and chemical resistance to harsh post-fabrication processes. Efforts to mitigate surface loss by treating the surface oxides and utilizing high-resistivity silicon substrates have led to Ta-based qubits with lifetime and coherence times exceeding 1 ms [3]. Guided by these successes in reducing dielectric loss in Ta-based devices, we are interested in exploring material engineering approaches that enhance the superconducting gap. Alloying Ta with another element to enhance the superconducting performance expands the range of viable material candidates available to tackle different loss channels in superconducting circuits [1]. Recently, we explore superconducting gap engineering in Ta-based devices as a powerful strategy for expanding the range of suitable host materials. By alloying 20 at.% hafnium (Hf) into Ta thin films, we achieve a superconducting transition temperature (Tc) of 6.09 K as observed in direct current (DC) transport measurements, reflecting an increase in the superconducting gap. Here we demonstrate an approach for controlling varying deposition conditions to control film orientation and transport properties of Ta and Ta-Hf alloy thin films. We investigate the microstructure and composition distribution of the thin films by using high-resolution scanning transmission electron microscopy (STEM) with super-X EDS system (no serious beam damage issue [6-8]). Our structural analysis using TEM diffraction and STEM verifies the BCC structure across all the films (Figure 1), and direct current (DC) transport measurements reveal a 40% enhancement in Tc relative to undoped Ta (Tc=4.3 K). We monitored oxide growth over an 18-day period following film deposition to better understand how Hf incorporation influences surface oxides. In both Ta and Hf spectra, the fraction of fully oxidized (Ta2O5 and HfO2) states gradually increased during the 18-day exposure, indicating progressive surface oxidation. To estimate the surface oxide thickness, we use cross-sectional TEM/EDS mapping (Figure 1c). The analysis reveals that the oxide thickness for the 1 ks Ta-Hf alloy film is approximately 3 nm in thickness, comparable to the 3 nm oxide observed on native Ta [2]. For the 2 ks Ta-Hf film, the oxide thickness increases slightly to about 4 nm (Figure 1). The measured surface loss tangent of the Ta-Hf alloy remains comparable to that of native Ta. This result suggests that the surface oxide of the Ta-Hf alloy, which contains a measurable fraction of HfOx, does not introduce additional dielectric loss. By engineering the alloy composition and film deposition, this study achieves both improved superconducting properties and compatibility with fabrication processes. These findings show that material doping and alloying can strategically expand the suite of viable materials for superconducting quantum devices. This approach provides a pathway for tailoring material properties to support the next generation of quantum technologies and offers broad relevance to researchers in materials science, quantum information, and device engineering [9]. STEM images on cross sections of 1 ks (a) and 2 ks (b) Ta-Hf thin films, both films were sputtered at 750 ◦C. (c) Cross-sectional EDS elemental mapping on Ta-Hf. Cross-sectional EDS mapping Ta (blue) and Hf (orange) confirmed a uniform Ta-Hf alloy with the Ta to Hf atomic ratios for the bulk to be (83% : 17%). The oxygen (red) map reveals a surface oxide layer with the estimated surface oxide thickness of around 4 nm. The 1 ks Ta-Hf film exhibits an oxide thickness of approximately 3 nm, similar to that of native Ta. The EDS resolution limit is 0.5 atomic percent.
Fabrication and Structural Analysis of Trilayers for Tantalum Josephson Junctions with Ta2O5 Barriers
Tantalum (Ta) has emerged as a promising low-loss material, enabling record coherence times in superconducting qubits. This enhanced performance is largely attributed to its stable native oxide, which may host fewer two-level system (TLS) defects, which are the key contributors to decoherence in superconducting circuits. Nevertheless, aluminum oxide remains the predominant choice for Josephson junction (JJ) barriers in most qubit architectures. Here, we investigate techniques for forming high-quality oxide layers on α-phase tantalum films to develop tantalum-oxide JJ barriers. We explore thermal oxidation in a tube furnace, rapid thermal annealing, and plasma oxidation of both room-temperature and heated Ta films, characterize the resulting structures using X-ray techniques and electron microscopy, and propose a mechanistic picture of the oxidation pathways. We find that plasma oxidation provides the smoothest Ta2O5 layers, is compatible with in situ Ta deposition, and offers thickness control through the annealing temperature, advantageous for JJ fabrication. Lastly, we evaluate methods for growing Ta/TaOx/Ta trilayers. All trilayers showed c-axis-oriented columnar growth of the bottom Ta layer, with sapphire substrates producing larger, better-aligned grains yet higher dislocation densities than silicon. Nucleation of c-axis-oriented α-Ta on tantalum-oxide required an Nb seed layer, as direct Ta deposition yielded amorphous Ta. These results demonstrate the feasibility of α-Ta/Nb/TaOx/α-Ta stacks for JJs with clean interfaces.
Tantalum films incorporated into superconducting circuits have exhibited low surface losses, resulting in long-lived qubit states. The remaining loss pathways originate in microscopic defects that manifest as two level systems (TLSs) at low temperatures. These defects limit performance, so careful attention to tantalum film structures is critical for optimal use in quantum devices. In this work, we investigate the growth of tantalum using magnetron sputtering on sapphire, Si, and photoresist substrates. In the case of sapphire, we present procedures for the growth of fully-oriented films with α-Ta [1 1 1]//Al2O3 [0 0 0 1] and α-Ta [1 −1 0]//Al2O3 [1 0 −1 0] orientational relationships and having residual resistivity ratio (RRR) ∼ 60 for 220 nm thick films. On Si, we find a complex grain texturing with Ta [1 1 0] normal to the substrate and RRR ∼ 30. We further demonstrate airbridge fabrication using Nb to nucleate α-Ta on photoresist surfaces. For the films on sapphire, resonators show TLS-limited quality factors of 1.3 ± 0.3 × 106 at 10 mK (for a waveguide gap and conductor width of 3 and 6 μm, respectively). Structural characterization using scanning electron microscopy, x-ray diffraction, low temperature transport, secondary ion mass spectrometry, and transmission electron microscopy reveal the dependence of residual impurities and screw dislocation density on processing conditions. The results provide practical insights into the fabrication of advanced superconducting devices including qubit arrays and guide future works on crystallographically deterministic qubit fabrication.
Over the past decades, superconducting qubits have emerged as one of the leading hardware platforms for realizing a quantum processor. Consequently, researchers have made significant effort to understand the loss channels that limit the coherence times of superconducting qubits. A major source of loss has been attributed to two level systems that are present at the material interfaces. It is recently shown that replacing the metal in the capacitor of a transmon with tantalum yields record relaxation and coherence times for superconducting qubits, motivating a detailed study of the tantalum surface. In this work, the chemical profile of the surface of tantalum films grown on c-plane sapphire using variable energy X-ray photoelectron spectroscopy (VEXPS) is studied. The different oxidation states of tantalum that are present in the native oxide resulting from exposure to air are identified, and their distribution through the depth of the film is measured. Furthermore, it is shown how the volume and depth distribution of these tantalum oxidation states can be altered by various chemical treatments. Correlating these measurements with detailed measurements of quantum devices may elucidate the underlying microscopic sources of loss.
We demonstrate a substantial reduction in two-level system loss in tantalum coplanar waveguide resonators fabricated on high-resistivity silicon substrates through the use of an ultrathin titanium sacrificial layer. A 0.2nm titanium film, deposited atop pre-sputtered α-tantalum, acts as a solid-state oxygen getter that chemically modifies the native Ta oxide at the metal-air interface. After device fabrication, the titanium layer is removed using buffered oxide etchant, leaving behind a chemically reduced Ta oxide surface. Subsequent high-vacuum annealing further suppresses two-level system loss. Resonators treated with this process exhibit internal quality factors Qi exceeding an average of 1.5 million in the single-photon regime across ten devices, over three times higher than otherwise identical devices lacking the titanium layer. These results highlight the critical role of interfacial oxide chemistry in superconducting loss and reinforce atomic-scale surface engineering as an effective approach to improving coherence in tantalum-based quantum circuits. The method is compatible with existing fabrication workflows applicable to tantalum films, offering a practical route to further extending T1 lifetimes in superconducting qubits.