Ensembles of nitrogen-vacancy (NV) centers in diamond are versatile quantum sensors with broad applications in the physical and life sciences. The concentration of neutral substitutional nitrogen ( [ N s 0 ]) strongly influences NV electronic spin coherence times, sensitivity, and optimal sensing strategies. Diamonds with [ N s 0 ] ∼ 1–10 ppm are a focus of recent material engineering efforts, with higher concentrations being favorable for continuous-wave optically detected magnetic resonance (CW-ODMR) and lower concentrations expected to benefit pulsed magnetometry techniques through extended NV spin coherence times and improved sensing duty cycles. In this work, we synthesize and characterize low- [ N s 0 ] ( ∼ 0.8 ppm), NV-enriched diamond material, engineered through low-strain chemical vapor deposition (CVD) growth on high-quality substrates, 12 C isotopic purification, and controlled electron irradiation and annealing. Our results demonstrate good strain homogeneity in diamonds grown on CVD substrates and spin-bath-limited NV dephasing times. By measuring NV spin and charge properties across a wide range of optical NV excitation intensity, we provide direct comparisons of photon-shot-noise-limited magnetic field sensitivity between the current low- [ N s 0 ] and previously studied higher- [ N s 0 ] ( ∼ 14 ppm) NV-diamond sensors. We show that low- [ N s 0 ] diamond can outperform higher- [ N s 0 ] diamond at moderate and low optical NV excitation intensity. Our results provide practical benchmarks and guidance for selecting NV-diamond sensors tailored to specific experimental constraints and sensing requirements.
Ensembles of nitrogen-vacancy (NV) centers in diamond are versatile quantum sensors with broad applications in the physical and life sciences. The concentration of neutral substitutional nitrogen ( [ N s 0 ]) strongly influences NV electronic spin coherence times, sensitivity, and optimal sensing strategies. Diamonds with [ N s 0 ] ∼ 1–10 ppm are a focus of recent material engineering efforts, with higher concentrations being favorable for continuous-wave optically detected magnetic resonance (CW-ODMR) and lower concentrations expected to benefit pulsed magnetometry techniques through extended NV spin coherence times and improved sensing duty cycles. In this work, we synthesize and characterize low- [ N s 0 ] ( ∼ 0.8 ppm), NV-enriched diamond material, engineered through low-strain chemical vapor deposition (CVD) growth on high-quality substrates, 12 C isotopic purification, and controlled electron irradiation and annealing. Our results demonstrate good strain homogeneity in diamonds grown on CVD substrates and spin-bath-limited NV dephasing times. By measuring NV spin and charge properties across a wide range of optical NV excitation intensity, we provide direct comparisons of photon-shot-noise-limited magnetic field sensitivity between the current low- [ N s 0 ] and previously studied higher- [ N s 0 ] ( ∼ 14 ppm) NV-diamond sensors. We show that low- [ N s 0 ] diamond can outperform higher- [ N s 0 ] diamond at moderate and low optical NV excitation intensity. Our results provide practical benchmarks and guidance for selecting NV-diamond sensors tailored to specific experimental constraints and sensing requirements.
Abstract The nitrogen-vacancy (NV) center in diamond is a promising quantum system for magnetometry applications exhibiting optical readout of minute energy shifts in its spin sub-levels. Key material requirements for NV ensembles are a high NV − concentration, a long spin coherence time and a stable charge state. However, these are interdependent and can be difficult to optimize during diamond growth and subsequent NV creation. In this work, we systematically investigate the NV center formation and properties in bulk chemical vapor deposition (CVD) diamond. The nitrogen flow during growth is varied by over four orders of magnitude, resulting in a broad range of single substitutional nitrogen concentrations of 0.2–20 parts per million. For a fixed nitrogen concentration, we optimize electron-irradiation fluences with two different accelerated electron energies, and we study defect formation via optical characterizations. We discuss a general approach to determine the optimal irradiation conditions, for which an enhanced NV concentration and an optimum of NV charge states can both be satisfied. We achieve spin–spin coherence times T 2 ranging from 45.5 to 549 μ s for CVD diamonds containing 168 to 1 parts per billion NV − centers, respectively. This study shows a pathway to engineer properties of NV-doped CVD diamonds for improved sensitivity.
Because of their high sensitivity, quantum materials are extremely promising for new technologies. The main challenge lies in maintaining a sufficiently quantum coherence times for quantum computation or quantum sensing systems. NV centers in diamond which are point defects consisting of a substitutional nitrogen atom neighboring an atomic vacancy, where an electron pair can reside in a triplet state – are ideal candidates for the development of industrial-scale quantum systems. These spin states exhibit ms-long coherence times at room temperature and can be manipulated optically, hence opening interesting perspectives for sending magnetic fields with high sensitivity1.At HiQuTe Diamond, we take up the challenge of mastering the entire nitrogen-doped diamond production chain synthesized by Microwave Plasma-Assisted Chemical Vapor Deposition (MPACVD). We aim at creating affordable diamonds specially engineered to achieve long coherence times with high NV density and high doping uniformity. This quest require to overcome the impact of several external factors that contribute to electron spin decoherence. First, the chemical composition of the diamond, specifically the types and concentrations of impurities within the diamond matrix (such as substitutional nitrogen NS, NV centres, mono-vacancies and clusters, hydrogen, etc.), as well as their electrical charge states (NS⁰, NS⁺, NV⁰, NV⁻) should be carefully controlled. Thanks to extensive scientific research conducted over the past decade, combined with our own R&D efforts, we are now able to quantify these parameters using experimental techniques compatible with industrial applications (Raman and UV-Vis spectroscopy) and compare our results with key performance indicators2. Second, we study the relationship between coherence (T2*) and strain inhomogeneities in our diamond layers, which we analyse using birefringence measurements. Our findings demonstrate our capability to produce CVD diamond layers with reduced strain and extended defect and confirm that strain could be a critical limiting factor for T2*.In this poster, I will review the efforts carried out at HiQuTe Diamond to develop specific material that is well suited for quantum sensing applications.References1.Barry, J. F., Schloss, J. M., Bauch, E., Turner, M. J., Hart, C. A., Pham, L. M., & Walsworth, R. L. (2020). Sensitivity optimization for NV-diamond magnetometry. Reviews of Modern Physics, 92(1), 015004.2.Langer, J. (2022). Quantum-grade diamond for cavity-based solutions. Fraunhofer Verlag.
Abstract Ensembles of nitrogen-vacancy (NV) centres in diamond are a leading platform for practical quantum sensors. Reproducible and scalable fabrication of NV-ensembles with desired properties is crucial, as is an understanding of how those properties influence performance. This work addresses these issues by characterising nitrogen-doped diamond produced by the chemical vapour deposition (CVD) method across a range of synthesis conditions. This is shown to produce material with widely differing absorption characteristics, which is linked to the level of defects other than substitutional nitrogen (NS) and NV. In such material, the achievable concentration of NV− ([NV−]) is found to be influenced by the as-grown properties. At the 10–20 ppm level for [NS], the production of CVD-grown material with strain levels sufficient not to limit achievable device sensitivity is demonstrated and a favourable product of [NV−] and T 2 * is obtained. Additionally, reproducible properties over a batch of 23 samples from a single synthesis run are achieved, which appears promising for the scalability efforts underway in this area of research.
To improve the sensitivity of magnetic sensors using negatively charged nitrogen-vacancy (NV−) centers, it is essential to improve the quality of diamond crystals and precisely control the nitrogen concentration in the crystals. We have utilized high-pressure, high-temperature synthesis [1] and chemical vapor deposition [2] for the growth of nitrogen-doped diamond. The concentration of substitutional nitrogen in the neutral charge state [NS0] were evaluated by electron paramagnetic resonance (EPR) measurements. As shown in Fig. 1, [NS0] were precisely controlled by the weight ratio of nitrogen getter material in the metal solvent for the HPHT method (Fig. 1(a)) and by the carbon to nitrogen gas ratio for the CVD method (Fig. 1(b)). Then, the diamond crystals were irradiated with electron beams followed by vacuum annealing so that 10% of the nitrogen at the substitutional site became NV− centers, and the negatively charged NV− centers were successfully formed preferentially [3]. T2 of these diamond crystals was inversely proportional to the nitrogen concentration. The product of T2 and nitrogen concentration of the obtained HPHT diamond crystal is slightly higher than the maximum value reported so far [4], suggesting that the crystal is expected to have high magnetic sensitivity.
The negatively charged nitrogen−vacancy (NV − ) center ensembles in diamonds offer enormous potential for developing integrated sensors with an improved signal-to-noise ratio (SNR) and high sensitivity. However, the preparation and treatment of diamond samples with suitable NV − concentrations and dephasing time have remained challenging. This work provided insight into the NV − center formation mechanism and reconstruction via a comprehensive analysis of the concentration and dephasing time of a set of diamond samples treated by various parameters. By varying the electron irradiation dose and subsequent annealing duration, the conversion rate of nitrogen to NV − is up to 18.45%, and the corresponding maximum NV − concentration is 3.69 ppm. The dephasing time for all samples varies around 300 ns. The nitrogen-related NV − center ensemble dephasing rate per unit density is 146.4 (ppm·ms) −1 , indicating that the treatment did not substantially alter the paramagnetic spin environment around the NV − center. This study not only offers support to exquisite sensitivities of NV-based sensors but also provides valuable experience for the preparation of unique properties of synthetic diamonds.
This thesis investigates the theoretical foundations, material properties, and experimental realization of quantum sensors based on the Nitrogen-Vacancy (NV) centers in diamond, a solid-state system that combines quantum coherence with room-temperature operability. The first chapter introduces the principles of quantum sensing, outlining the fundamental definitions, operating protocols, and physical processes underlying the quantum measurement paradigm. Emphasis is placed on the quantum sensing Hamiltonian and the distinction between various classes of quantum sensors. The second chapter focuses on diamond as a host material and on the NV center as a quantum defect. The electronic structure, optical transitions, and spin properties of the NV center are analyzed in detail. Several techniques of NV-based magnetometry are presented, including continuouswave and pulsed optically detected magnetic resonance (ODMR). The discussion also addresses coherence times (T1, T2, and T∗2 ) and methods of diamond synthesis together with NV-center generation through irradiation and annealing. Chapter three develops the physical theory describing the NV center. The Hamiltonian formalism includes spin-spin, hyperfine, and quadrupolar interactions, as well as couplings to external magnetic fields. The chapter further introduces the Bloch sphere representation, magnetic resonance phenomena, and models of lightmatter interaction, ranging from the semiclassical to the fully quantum Rabi framework. A seven-level rate-equation model is proposed to capture the spin dynamics and optical cycling processes of the NV center. The fourth chapter reports the experimental results. After describing materials and methods, several ODMR-based vector magnetometry experiments are presented, highlighting different spectral regimes and the dependence of resonance features on the external magnetic field geometry. Additional studies demonstrate temperature sensing and microwave-free magnetometry techniques for mapping magnetic field distributions. Sensitivity analysis and calibration procedures are also discussed.