Nitrogen-vacancy (NV) centers in diamonds have been an epicenter of research for diverse applications in quantum technologies. It is therefore imperative that their fabrication techniques are well understood and characterized for the technological scalability of these applications. A comparative study of the optical and spin properties of NVs created by ion implantation and chemical vapor deposition delta-doping is thus presented, combined with an investigation on the impact of annealing in vacuum at different temperatures. In addition, nanopillars are fabricated by electron beam lithography and reactive ion etching for enhanced photon collection efficiency. An extensive combination of characterization techniques is employed. Notably, the smallest nanopillars present fluorescence enhancements of factor around 50, compared to the unstructured regions. Annealing is also demonstrated to increase the optical contrast between the NVs' electronic states, the coherence and relaxation times both in bulk as in pillars. Regarding the NV preparation technique, the delta-doping is shown to create NVs with less lattice defects and strain compared to implantation. • Comparative study of optical and spin properties of implanted and δ-doped CVD NVs • Impact of structuring with nanopillars and annealing on the NV properties • Fluorescence enhancement factors of above 30 in 100–150 nm diameter pillars • 3-Fold increase in ODMR contrast of all samples after annealing • Increase of coherence and relaxation times after annealing
The negatively-charged nitrogen-vacancy (NV) center is the most studied optical center in diamond and is very important for applications in quantum information science. Many proposals for integrating NV centers in quantum and sensing applications rely on their tailored fabrication in ultra pure host material. In this study, we use ion implantation to controllably introduce nitrogen into high purity, low nitrogen chemical vapor deposition diamond samples. The properties of the resulting NV centers are studied as a function of implantation temperature, annealing temperature, and implantation fluence. We compare the implanted NV centers with native NV centers present deep in the bulk of the as-grown samples. The results for implanted NV centers are promising but indicate, at this stage, that the deep native NV centers possess overall superior optical properties. In particular, the implanted NV centers obtained after annealing at 2000 °C under a stabilizing pressure of 8 GPa showed an ensemble linewidth of 0.17 nm compared to 0.61 nm after annealing at 1000 °C. Over the same temperature range, the ensemble NV−/NV0 ratio increased by a factor of ∼5, although this was accompanied by an overall decrease in the NV count.
Nitrogen-vacancy (NV) color centers in diamond are excellent quantum sensors possessing high sensitivity and nano-scale spatial resolution. Their integration in photonic structures is often desired, since it leads to an increased photon emission and also allows the realization of solid-state quantum technology architectures. Here, we report the fabrication of diamond nano-pillars with diameters up to 1000 nm by electron beam lithography and inductively coupled plasma reactive ion etching in nitrogen-rich diamonds (type Ib) with [100] and [111] crystal orientations. The NV centers were created by keV-He ion bombardment and subsequent annealing, and we estimate an average number of NVs per pillar to be 4300 ± 300 and 520 ± 120 for the [100] and [111] samples, respectively. Lifetime measurements of the NVs’ excited state showed two time constants with average values of τ1 ≈ 2 ns and τ2 ≈ 8 ns, which are shorter as compared to a single color center in a bulk crystal (τ ≈ 10 ns). This is probably due to a coupling between the NVs as well as due to interaction with bombardment-induced defects and substitutional nitrogen (P1 centers). Optically detected magnetic resonance measurements revealed a contrast of about 5% and average coherence and relaxation times of T2 [100] = 420 ± 40 ns, T2 [111] = 560 ± 50 ns, and T1 [100] = 162 ± 11 μs, T1 [111] = 174 ± 24 μs. These pillars could find an application for scanning probe magnetic field imaging.
We present the increase in the nitrogen vacancy center concentration in nitrogen delta-doped layers by almost one order of magnitude. To achieve this, we employ a low-pressure, high-temperature annealing step at 1750 °C in vacuum. We demonstrate an enhancement of the photoluminescence intensity of NV centers compared to annealing steps at lower temperatures of 1200 °C. To achieve this, we fabricate nitrogen-doped thin films with a thickness of 50 nm via chemical vapor deposition. We show that the nitrogen is mainly incorporated in a 6 nm thin film at the layer interface. We link the strong enhancement of the NV concentration to a possible decomposition of NVH centers and the mobility of various species at elevated temperatures, including vacancies and nitrogen in these two-dimensional structures. Additionally, after the high temperature annealing, we observe a Hahn-echo spin coherence time of 7.9 μ s, which is in line with literature data on achievable coherence time in highly nitrogen-doped layers. Our results could pave the way for the precise fabrication of improved diamond elements, e.g., used in magnetic field sensors and offer an alternative route to implantation techniques.
The Nitrogen-Vacancy (NV) color center is a defect of diamond which behaves as an artificial atom hosted in a solid-state matrix. Due to its electron spin properties which can be read-out and manipulated as an elementary quantum system, the NV center has found a wide panel of applications as a qubit for quantum information and as a magnetic field sensor. However these applications require to control the properties of the NV centers and their localization. This doctoral thesis investigates methods allowing us to tailor the properties of NV centers by combining techniques for the implantation of nitrogen atoms and the plasma-assisted (CVD) synthesis of diamond.The manuscript is divided into six chapters. The first chapter summarizes the properties of the NV center which will set our objectives for the NV engineering. The second chapter will describe how arrays of NV centers can be created using Focused Ion Beam implantation. The results open a wide range of applications for the targeted creation of NV centers in diamond structures such as photonic crystals and tips. However the low kinetic energy which is required for achieving implantation within a spot of 10-nm diameter leads to shallow defects which properties are strongly affected by the sample surface. The third chapter investigates how the overgrowth of a diamond layer over implanted NV centers can remove the detrimental influence of the surface. The fourth and fifth chapters describe effective methods for NV center fabrication through the control of the CVD growth conditions of the hosting crystal. Thin layers with high NV doping can be grown and almost perfect control of the orientation of the NV axis can be achieved. With the goal to optimize the spin coherence properties, the sixth chapter investigates how the electron spin of the NV center can be protected from decoherence effects induced by magnetic noise due to the unpolarized spins in the diamond lattice.
Silicon has turned from a niche laboratory-scale material into the backbone of modern electronics. Diamond functionalized with color centers could follow a similar path and grow from proof-of-concepts experiments to application-oriented quantum technologies. Quantum sensing, communication, and information processing with color centers has been proven to work in scientific experiments and enhanced sensitivities as well as novel functionalities have been reported. While the first generation of diamond quantum devices relied on color centers formed uncontrolled in natural diamond with a high statistical variation in composition and crystallinity, the situation has changed nowadays. With the emergence of high purity monocrystals and the option for isotopic purification of the carbon matrix, technological progress in materials science on the atomic-scale enabled tailoring the spin properties in diamond. But, since many color centers typically require vacancies to combine with impurities in the carbon lattice via diffusion, the generation of color centers underlies a statistical process providing only little control on the center's final position in the crystal lattice. The negatively charged nitrogen-vacancy (NV
−) center is the most studied optically active defect in diamond and exhibits remarkable spin properties and sensing capabilities, even on the nanoscale and at room temperature. The spin properties of NV
− centers close to the surface (1\,nm - 30\,nm) have been thoroughly studied and the deeper the spins are located in diamond the less decoherence from surface defects is observed. Creating NV
− centers at the surface by nitrogen ion implantation and burying them beneath a thin diamond layer via chemical vapor deposition (CVD) of diamond is reported to enhance the coherence times significantly. By separating the color center generation from controlling the resulting depth by an additional diamond layer, narrow depth profiles can be achieved by reducing the ion energy during implantation. Although the coherence properties improve, many of the implanted NV
− center are reported to vanish in the hydrogen-rich plasma of growth CVD chambers. The mechanism responsible for the instability of NV
− centers towards the plasma remains unclear, though. One hypothesis is the formation of nitrogen-vacancy-hydrogen centers from diffusing hydrogen and implanted NV
− centers but is has not been proven, yet. Here, we demonstrate the fabrication of depth confined NV
− centers by combining low energy (1\,keV - 5\,keV) ion implantation and CVD overgrowth. By increasing the thickness of the overgrown layer (6\,nm - 100\,nm) the influence of surface noise is shown to decrease leading to bulk-like coherence properties of up to $450\,\upmu$s (Hahn-echo) and
T2∗ dephasing times around $20\,\upmu$s. Monitoring the NV
− density as a function of the overgrowth time, we analyze the kinetics of the passivation in case of implanting ion doses of 10
11 15N
+/cm
2 and 10
12 15N
+/cm
2. The passivation turns out to occur faster for lower doses offering insights into sub-surface hydrogen diffusion in diamond. Analyzing the spin bath before and after overgrowth reveals a drastic reduction in paramagnetic spins after the CVD process but no NVH
− is found around the surviving NV
− centers. Checking the chemical composition in overgrown implantation sites with secondary-ion-mass-specrometry (SIMS), however, confirms significant amounts of hydrogen in the
15N-implanted layers. Since the concentration found for hydrogen exceeds the one for nitrogen by far, we suggest that diffusing hydrogen interacts also with vacancies forming probably mostly diamagnetic defects. In the last part of this dissertation, NV
− centers are generated with sub-nanometer precision below a thin
13C-enriched layer for quantum simulation. For fabricating the spin architecture starting from a
12C base layer, we overgrow implanted nitrogen with a
13C layer and bury the spins beneath a 30\,nm-thick
12C capping layer. By measuring the coupling strength between the electron and nuclear spins, we deduce a NV
− placement accuracy reaching below one nanometer with respect to the
13C-layer. Regarding the spin properties of the electron spins, no reduction in
T2 is observed despite of the proximity to the dense
13C-bath. As a consequence, the overgrowth of NV
− centers is demonstrated as a bottom-up approach to produce buried spin architectures with sharp isotopic transitions and efficient
13C-NV
− coupling. Together with the potential for bulk-like coherence properties the synergy of implantation and overgrowth is a powerful tool to fabricate reproducible quantum systems with tailored properties and high depth confinement.