Impact of Helium Ion Implantation Dose and Annealing on Dense Near-Surface Layers of NV Centers

Andris Bērziņš, Hugo Grube, Einārs Sprūģis, Guntars Vaivars, Ilja Fescenko

Published Jun 29, 2022• 11 citations

Abstract

The implantation of diamonds with helium ions has become a common method to create hundreds-nanometers-thick near-surface layers of NV centers for high-sensitivity sensing and imaging applications; however, optimal implantation dose and annealing temperature are still a matter of discussion. In this study, we irradiated HPHT diamonds with an initial nitrogen concentration of 100 ppm using different implantation doses of helium ions to create 200-nm thick NV layers. We compare a previously considered optimal implantation dose of ∼1012 He+/cm2 to double and triple doses by measuring fluorescence intensity, contrast, and linewidth of magnetic resonances, as well as longitudinal and transversal relaxation times T1 and T2. From these direct measurements, we also estimate concentrations of P1 and NV centers. In addition, we compare the three diamond samples that underwent three consequent annealing steps to quantify the impact of processing at 1100 °C, which follows initial annealing at 800 °C. By tripling the implantation dose, we have increased the magnetic sensitivity of our sensors by 28±5%. By projecting our results to higher implantation doses, we demonstrate that it is possible to achieve a further improvement of up to 70%. At the same time, additional annealing steps at 1100 °C improve the sensitivity only by 6.6 ± 2.7%.

DOI: 10.3390/nano12132234

Related papers

Doping optimization of charge state stability for shallow nitrogen-vacancy center ensembles in HPHT diamonds

Qin Wu, Die Fang, Yu Ma +9 more

Since nitrogen-vacancy (NV) centers in diamond have emerged as crucial quantum sensors in physics and biology, the massive preparation of high-quality and high-concentration shallow NV center samples has become urgent and demanding. As NV centers approach the surface and their concentration increases, charge state instability can degrade coherence and introduce additional noise. This problem is further complicated in high-pressure and high-temperature (HPHT) diamonds due to the presence of unclear impurities and inhomogeneous strain. Through optically detected magnetic resonance testing on various implanted samples, we analyzed the spin and charge state properties of shallow NV center ensembles. Our results reveal that the doping dose significantly influences the quantity of NV−, charge, and charge stability. Our findings indicate that over-implanting nitrogen as electron donors before starting graphitization helps stabilize the charge environment of the shallow NV center ensembles. By controlling the nitrogen ion implantation dose, we optimized charge state stability under photoionization and prepared high-quality NV center ensemble samples in HPHT diamonds at the optimal implantation dose range of 2×1013–8×1013 ions/cm2. This method, which relies solely on nitrogen ion implantation and annealing on HPHT diamond, significantly reduces the cost of sensor samples, greatly benefiting the promotion of quantum sensing.

Applied Physics LettersJun 16, 20251 citation

Nitrogen ion implantation for controlled nitrogen-vacancy center creation in single- and polycrystalline diamond

Zeeshan Rashid, Nemanja Markešević, S. Lagomarsino +11 more

Precise control over the spatial distribution and charge state of nitrogen-vacancy (NV) centers in diamond is a key requirement for further advancing this platform in quantum sensing and photonic applications. Here, we investigate nitrogen ion implantation as a scalable method to engineer NV centers in bulk single-crystalline (SC) and a 5 μ m -thick polycrystalline (PC) diamond membrane. Nitrogen-doped regions (1–80 ppm) were fabricated using a 0.7 MeV ion beam and high-temperature annealing, with NV center formation verified by confocal fluorescence imaging and spectral analysis. In SC bulk diamond, we estimate the NV concentration from spectral analysis and model the fluorescence response as a function of implantation dose, capturing both the initial increase at low concentrations and a saturation behavior at higher doses due to quenching mechanisms. In contrast, PC diamond membranes show a weaker dependence at low implantation fluences, consistent with pre-existing nitrogen impurities, thus making a statistical model significantly more complex. The activation yield is found to be of order of 1%, which is lower than in N-rich diamond samples, as implanted N is predominantly interstitial. Photoluminescence spectroscopy indicates that NV 0 is the dominant charge state in both materials, with a laser-power-dependent redistribution between neutral and negative charge states. Optically detected magnetic resonance (ODMR) measurements in SC bulk diamond resolve the hyperfine structure and allow extraction of the dephasing time ( T 2 ∗ ), while in PC diamond membranes, where NV centers tend do form near the grain boundaries, the ODMR signals are observed but spectral resolution is currently limited by impurities, grain-dependent NV orientations, and photoluminescence background.

Diamond nitrogen-vacancy centers created by scanning focused helium ion beam and annealing

Zhihong Huang, W.-D. Li, Charles Santori +7 more

We demonstrate a method to create nitrogen-vacancy (NV) centers in diamond using focused helium ion microscopy. Near-surface NV centers can be created with spatial resolution below 0.6 μm. We studied the density, creation efficiency, and spectral linewidths at optical and microwave frequencies for NV centers produced using various helium ion implantation doses. The optical linewidths are narrower than those of similar nitrogen-vacancy centers produced using nitrogen ion implantation.

Applied Physics LettersAug 19, 201369 citations

Hot ion implantation to create dense NV center ensembles in diamond

Midrel Wilfried Ngandeu Ngambou, Pauline Perrin, Ionuț Gabriel Balașa +9 more

Creating dense and shallow nitrogen-vacancy (NV) ensembles with good spin properties is a prerequisite for developing diamond-based quantum sensors exhibiting better performance. Ion implantation is a key enabling tool for precisely controlling spatial localization and density of NV color centers in diamond. However, it suffers from a low creation yield, while higher ion fluences significantly damage the crystal lattice. In this work, we realize N2+ ion implantation in the 30–40 keV range at high temperatures. At 800 °C, NV's ensemble photoluminescence emission is three to four times higher than room temperature implanted films, while narrow electron spin resonance linewidths of 1.5 MHz, comparable to well-established implantation techniques, are obtained. In addition, we found that ion fluences above 2 × 1014 ions/cm2 can be used without graphitization of the diamond film, in contrast to room temperature implantation. This study opens promising perspectives in optimizing diamond films with implanted NV ensembles that could be integrated into quantum sensing devices.

Applied Physics LettersMar 25, 202415 citations

Highly nitrogen-vacancy doped diamond nanostructures fabricated by ion implantation and optimum annealing

Hisashi Sumikura, Kazuyuki Hirama, Katsuhiko Nishiguchi +2 more

Nitrogen-vacancy (NV) centers in diamond photonic nanostructures have attracted much attention as efficient single photon emitters and quantum bits. These quantum optical devices mostly require single or low-density NV centers doped in thin diamond membranes. In contrast, this study focuses on diamond photonic nanostructures with a high concentration of NV centers to achieve a diamond color center laser with a sufficient gain available as a visible light source and a sensitive magnetic-field sensor. We employ high-dose helium ion implantation to type-Ib diamond substrates and thermal annealing, which enables us to obtain uniform thin diamond membranes containing a dense ensemble of NV centers. Luminescence spectroscopy reveals the kinetics of NV centers at high temperature from which we find an optimum annealing temperature maximizing the NV center emission while suppressing the transformation from NV to H3 centers. Furthermore, fine photonic nanowires are also successfully fabricated in the air-suspended diamond membrane, and they exhibit intense photoluminescence from the NV centers with a concentration as high as 7 × 1016 cm−3 (0.4 ppm). These results suggest a route to the fabrication of diamond photonic nanostructures containing a dense ensemble of NV centers, which can be a key material for developing diamond-based light emitting and magnetic-field sensing devices.

APL MaterialsMar 1, 202032 citations

Creation of NV- center in type-Ib diamonds by high temperature post-annealing

Ishii Shuya, Saiki Seiichi, Onoda Shinobu +3 more

Negatively charged nitrogen-vacancy (NV-) center in diamond has been paid attention as a highly sensitive detector for magnetic field. The magnetic sensitivity is proportional to the reciprocal of √(NT_2 ), where N is the number of NV centers and T2 is the spin coherence time. To improve the sensitivity, high concentration of NV- centers and extended coherence time are necessary. It is generally known that electron beam irradiation into type-Ib diamond which include high initial concentration of isolated substitutional nitrogen (P1 center) is a useful method to create high concentration of NV- centers. The electron beam irradiation generates vacancies in diamond and the subsequently annealing enables vacancies to diffuse in the lattice. Then diffused vacancies are captured by nitrogen atoms, as a result, NV centers are created. The post annealing has been performed at 1000°C or higher temperature for the purpose of improving the spin properties of NV- centers. In current study, we focused on post-annealing at high temperature to improve magnetic sensitivity of quantum sensing. We investigated annealing temperature and time dependence of the creation behavior of NV centers in type-Ib diamonds to understand appropriate annealing process for enhancing sensitivity of NV- center.

Nov 16, 20230 citations