Microwave loss in niobium metallic structures used for superconducting quantum circuits is limited by a native surface oxide layer formed over a timescale of minutes when exposed to an ambient environment. In this work, we show that nitrogen plasma treatment forms a niobium nitride layer at the metal–air interface, which prevents such oxidation. X-ray photoelectron spectroscopy confirms the doping of nitrogen more than 5 nm into the surface and a suppressed oxygen presence. This passivation remains stable after aging for 15 days in an ambient environment. Cryogenic microwave characterization shows an average filling-factor-adjusted two-level-system loss tangent FδTLS of (2.9±0.5)·10−7 for resonators with a 3 μm center strip and (1.0±0.3)·10−7 for a 20 μm center strip, exceeding the performance of unpassivated samples by a factor of four.
Microwave loss in niobium metallic structures used for superconducting quantum circuits is limited by a native surface oxide layer formed over a timescale of minutes when exposed to an ambient environment. In this work, we show that nitrogen plasma treatment forms a niobium nitride layer at the metal–air interface, which prevents such oxidation. X-ray photoelectron spectroscopy confirms the doping of nitrogen more than 5 nm into the surface and a suppressed oxygen presence. This passivation remains stable after aging for 15 days in an ambient environment. Cryogenic microwave characterization shows an average filling-factor-adjusted two-level-system loss tangent FδTLS of (2.9±0.5)·10−7 for resonators with a 3 μm center strip and (1.0±0.3)·10−7 for a 20 μm center strip, exceeding the performance of unpassivated samples by a factor of four.
Superconducting coplanar waveguide (CPW) microwave resonators in quantum circuits are the best components for reading and changing the state of artificial atoms because of their excellent coupling to quantum systems. This coupling forms the basis of the developing circuit quantum electrodynamic architecture. In quantum processors, oscillators are used to store and transmit quantum information using microwave-frequency wave packets. However, the presence of amorphous thin-film defects is deleterious and can result in an irrevocable loss of coherent information with uncontrolled degrees of freedom. Although there has been extensive research into techniques to reduce the coherent loss of such devices, the precise structure of amorphous dielectric layers on surfaces and interfaces and their associated loss mechanism are being actively studied. In particular, planar superconducting resonators are very sensitive to defects on their surfaces, such as two-level systems in oxidized metals and nonequilibrium quasiparticles, making these devices suitable probes for the different loss mechanisms. In this work, we present the design, fabrication, and characterization of Nb CPW resonators with different surface treatments with self-assembled monolayers (SAMs), which mitigate the growth of oxides in superconducting circuits. We demonstrate SAM-passivated resonators having internal quality factors of greater than 10 6 at a single-photon excitation power (measured at 100 mK), which were probed using scanning electron microscopy, X-ray photoelectron spectroscopy, and transmission electron microscopy to demonstrate the efficiency of our surface treatment. Finally, we compared the improvements in the experimental quality factors to those obtained by numerical simulation.
Superconducting coplanar waveguide resonators are essential components in quantum processors, where their internal quality factor (Qi) constrains qubit coherence and readout fidelity. In niobium devices, microwave losses at millikelvin temperatures are strongly influenced by two-level systems (TLS) associated with the complex NbOx surface oxide. To mitigate these losses, we investigate a surface-engineering approach in which Nb films are capped in situ with a thin tantalum layer to suppress Nb2O5 formation and replace the native NbOx interface with a Ta-based oxide.
We fabricate Nb/Ta bilayer and reference Nb resonators on high-resistivity silicon using identical DC sputtering and wet etching conditions, and characterize their performance at millikelvin temperatures. Fresh Ta-encapsulated devices exhibit internal quality factors up to 2.4 x 10^6 in the near-single-photon regime, with power dependence consistent with reduced TLS-related loss at the metal-air interface. A control Nb device fabricated under the same process shows comparatively lower Q_TLS, consistent with the beneficial effect of the Ta capping layer. Furthermore, ageing tests performed on Nb/Ta resonators after six months reveal a moderate reduction in Q_TLS relative to their initial values, yet the performance remains superior to newly fabricated Nb-only devices. These results suggest that thin Ta encapsulation enhances interface quality and contributes to improved temporal stability while remaining compatible with Nb-based fabrication workflows.
Native oxide formation (NbOx) at the niobium (Nb) metal–air interface is a source of microwave loss and performance variability in superconducting resonators. We introduce vapor-phase hexamethyldisilazane (HMDS) as a dry surface passivation treatment compatible with standard nanofabrication workflows. In five independent fabrication runs, HMDS-passivated resonators consistently demonstrate improved internal quality factor (Qi) and narrower performance distribution relative to paired unpassivated controls. The Qi improvement occurs across the full microwave power range, suggesting NbOx suppression as a contributing mechanism. Statistical depth profile analysis of Nb oxidation state by electron energy loss spectroscopy corroborates this mechanism, revealing smaller chemical shifts and shallower oxidation depth in passivated specimens relative to the control. Furthermore, re-measurement after 60 days of ambient storage shows that HMDS-passivated resonators retain their Qi, indicating their ambient stability. These results establish vapor-phase HMDS as a surface passivation strategy with strong potential for superconducting quantum devices.
Resonators and qubits with a niobium (Nb) base metal layer achieve some of the highest coherence times in superconducting quantum devices. The performance of such devices is often limited by loss associated with two-level systems, which are found primarily at material surfaces and interfaces. The metal-air (MA) interface is a major contributor to device loss. In this work, we develop a fast-sealing microwave cavity that enables devices to be placed under vacuum within five minutes of oxide removal, thereby significantly reducing the MA interface loss compared to common device processing and packaging approaches. Using coplanar stripline resonators, we demonstrate that devices sealed in such a cavity exhibit internal quality factors exceeding one million at single-photon power. After re-exposure to air, the devices show downward resonance frequency shifts and quality factor degradations, quantitatively consistent with a model of Nb oxide regrowth. The fast-sealing microwave cavity provides a practical and consistent method to mitigate MA interface loss and sustain high coherence in Nb devices, and establishes a controlled platform for studying metal oxide regrowth kinetics and dielectric properties, the understanding of which is critical to achieving high coherence in superconducting quantum devices.
Materials imperfections in Nb -based superconducting quantum circuits—in particular, two-level-system (TLS) defects—are a major source of decoherence, ultimately limiting the performance of quantum computation and sensing. Thus, identifying and understanding the microscopic origin of possible TLS defects in these devices will help develop strategies that eliminate them, which are key to superconducting qubit performance improvement. In this paper, we demonstrate an order-of-magnitude reduction in two-level system losses in three-dimensional superconducting radio frequency (SRF) niobium resonators by a 10-h high vacuum (HV) heat treatment at 650 °C, even after exposure to air and high-pressure rinsing (HPR). X-ray photoelectron spectroscopy (XPS) and high-resolution scanning transmission electron microscopy (STEM) reveal an alteration of the native oxide composition regrown after air exposure and HPR and the creation of nanoscale crystalline oxide regions, which correlates with the measured tenfold quality factor enhancement at low fields of the 1.3 GHz niobium resonator. Tunneling spectroscopy measurements show a pronounced proximity effect that further confirms the presence of metallic layers on the niobium surface.
To improve the performance of state-of-the-art superconducting quantum devices, microwave loss due to defects at amorphous interfacial layers must be reduced, via proper surface treatment. The authors study niobium resonators after removing native oxides by HF etching, which reduces losses about tenfold and yields a quality factor of $7\ifmmode\times\else\texttimes\fi{}{10}^{6}$ in the single-photon limit. Losses reappear as oxides form upon exposure to air; Nb2O5 is the only surface oxide that grows significantly in the first week. These findings are of interest for a panoply of devices, inluding superconducting qubits, quantum-limited amplifiers, microwave kinetic-inductance detectors, and single-photon detectors.