Spectral features of Pb-related color centers in diamond – a systematic photoluminescence characterization

Sviatoslav Ditalia Tchernij, Emilio Corte, Tobias Lühmann, P. Traina, Sébastien Pezzagna, Ivo Pietro Degiovanni, G. Provatas, Ekaterina V. Moreva, Jan Meijer, P. Olivero, Marco Genovese, J. Forneris

Published May 20, 2021• 13 citations
arXivHTMLPDF

Abstract

Abstract We report on the systematic characterization of the optical properties of diamond color centers based on Pb impurities. An ensemble photoluminescence analysis of their spectral emission was performed at different excitation wavelengths in the 405–520 nm range and at different temperatures in the 4–300 K range. The series of observed spectral features consist of different emission lines associated with Pb-related defects. Finally, a room-temperature investigation of single-photon emitters under 490.5 nm laser excitation is reported, revealing different spectral signatures with respect to those already reported under 514 nm excitation. This work represents a substantial progress with respect to previous studies on Pb-related color centers, both in the attribution of an articulated series of spectral features and in the understanding of the formation process of this type of defect, thus clarifying the potential of this system for high-impact applications in quantum technologies.

DOI
10.1088/1367-2630/ac038a

Related papers

Single-Photon Emitters in Lead-Implanted Single-Crystal Diamond

Sviatoslav Ditalia Tchernij, Tobias Lühmann, Tobias Herzig +14 more

Abstract We report on the creation and characterization of Pb-related color centers in diamond upon ion implantation and subsequent thermal annealing. Their optical emission in the photoluminescence (PL) regime consists of an articulated spectrum with intense emission peaks at 552.1 and 556.8 nm, accompanied by a set of additional lines in the 535–700 nm range. The attribution of the PL emission to stable Pb-based defects is corroborated by the correlation of its intensity with the implantation fluence of Pb ions. PL measurements performed as a function of sample temperature (in the 143–300 K range) and under different excitation wavelengths (i.e., 532, 514, 405 nm) suggest that the complex spectral features observed in Pb-implanted diamond might be related to a variety of different defects and/or charge states. The emission of the 552.1 and 556.8 nm lines is reported at the single-photon emitter level, demonstrating that they originate from the same individual defect. This work follows from previous reports on optically active centers in diamond based on group-IV impurities, such as Si, Ge, and Sn. In perspective, a comprehensive study of this set of defect complexes could bring significant insight on the common features involved in their formation and opto-physical properties, thus offering a basis for the development of a new generation of quantum-optical devices.

arXiv:1806.01608•ACS Photonics•Nov 12, 2018•101 citations

Photo-physical properties of He-related color centers in diamond

G. Prestopino, Marco Marinelli, Enrico Milani +10 more

Diamond is a promising platform for the development of technological applications in quantum optics and photonics. The quest for color centers with optimal photo-physical properties has led in recent years to the search for novel impurity-related defects in this material. Here, we report on a systematic investigation of the photo-physical properties of two He-related (HR) emission lines at 535.2 nm and 559.7 nm (as measured at a temperature of 25 K) created in three different diamond substrates upon implantation with 1.3 MeV He+ ions and subsequent annealing. The spectral features of the HR centers were studied in an “optical grade” diamond substrate as a function of several physical parameters, namely, the measurement temperature, the excitation wavelength, and the intensity of external electric fields. The emission lifetimes of the 535.2 nm and 559.7 nm lines were also measured by means of time-gated photoluminescence measurements. The Stark shifting of the HR centers under the application of an external electrical field was observed in a CVD diamond film equipped with buried graphitic electrodes, suggesting the lack of inversion symmetry in the defects' structure. Furthermore, the photoluminescence mapping under 405 nm excitation of a “detector grade” diamond sample implanted at a He+ ion fluence of 1 × 1010 cm−2 enabled us to identify the spectral features of both the HR emission lines from the same localized optical spots. The reported results provide an insight into the structure of He-related defects in diamond and their possible utilization in practical applications.

arXiv:1708.08616•Applied Physics Letters•Sep 11, 2017•18 citations

Single-Photon-Emitting Optical Centers in Diamond Fabricated upon Sn Implantation

Sviatoslav Ditalia Tchernij, T. Herzig, J. Forneris +11 more

The fabrication of luminescent defects in single-crystal diamond upon Sn implantation and annealing is reported. The relevant spectral features of the optical centers (emission peaks at 593.5, 620.3, 630.7, and 646.7 nm) are attributed to Sn-related defects through the correlation of their photoluminescence (PL) intensity with the implantation fluence. Single Sn-related defects were identified and characterized through the acquisition of their second-order autocorrelation emission functions, by means of Hanbury-Brown and Twiss interferometry. The investigation of their single-photon emission regime as a function of excitation laser power revealed that Sn-related defects are based on three-level systems with a 6 ns radiative decay lifetime. In a fraction of the studied centers, the observation of a blinking PL emission is indicative of the existence of a dark state. Furthermore, absorption dependence on the polarization of the excitation radiation with ∼45% contrast was measured. This work shed light on the existence of a new optical center associated with a group-IV impurity in diamond, with similar photophysical properties to the already well-known Si–V and Ge–V emitters, thus, providing results of interest from both the fundamental and applicative points of view.

arXiv:1708.01467•ACS Photonics•Sep 25, 2017•130 citations

Production of Multiple Diamond-Based Single-Photon Sources

Stefania Castelletto, Andrew Mark Edmonds, T. Gaebel +1 more

Fluorescent emitters in diamond are considered to be a valuable resource for fields such as quantum communication, quantum photonics, and biological imaging. In this paper, we report a wide range of narrow bandwidth ( ~ 1.5 nm) spectral emission lines arising from different color centers at room temperature. The defects were created by chemical vapor deposition of thin diamond films grown on silica substrates seeded with nanoparticles of diamond and nickel. These fluorescent lines also possess single or few centers photon statistics. We correlate the zero-phonon lines, observed using confocal microscopy, with previously identified nickel-related centers which have been observed in high-pressure high-temperature diamond, with a Si/Ni complex and silicon vacancy defects. We compare our findings with recent results demonstrating single-photon emission in diamond associated with nickel-related centers to clarify and summarize previous studies concerning this specific dopant. The great variety of emission lines observed in the synthesized material, mainly associated with nickel-related centers, could be an important resource for applications relying on the presence of several emitters of single photons in the same sample. Moreover, the possibility of mass production of these centers in nanodiamonds in colloidal suspension may provide an important resource for biomarking and microscopy.

IEEE Journal of Selected Topics in Quantum Electronics•Aug 29, 2012•22 citations

Lead-Related Quantum Emitters in Diamond

Matthew E. Trusheim, Noel Wan, Girish Malladi +4 more

We investigate the optical properties of quantum emitters formed in diamond after the implantation of Pb and subsequent high-temperature annealing. We find narrow-band emission in two spectral ranges, indicating multiple classes of Pb-related color centers.

Conference on Lasers and Electro-Optics•Jan 1, 2018•5 citations

680-890nm spectral range of nickel-nitrogen and nickel-silicon complex single centres in diamond

Stefania Castelletto, Andrew Mark Edmonds

Fluorescent emitters in nanodiamonds are considered to be a valuable resource for emerging fields such as quantum communication, quantum photonics and biological imaging. In this paper we report a wide range of narrow bandwidth spectral emission lines arising from different color centers at room temperature. We associate the zero phonon lines, observed using confocal microscopy, with previously identified nickel-related centers in high pressure high temperature diamond, with a Si/Ni complex and silicon vacancy defects. In particular we show the first observation of a 850 nm emission in diamond with single photon signature, indicating the potential for diamond to harbor infrared single-photon sources. Index Terms diamond defects, single-photon emission, confocal microscopy.

Proceedings of SPIE, the International Society for Optical Engineering/Proceedings of SPIE•Oct 15, 2012•10 citations
Abstract We report on the systematic characterization of the optical properties of diamond color centers based on Pb impurities. An ensemble photoluminescence analysis of their spectral emission was performed at different excitation wavelengths in the 405–520 nm range and at different temperatures in the 4–300 K range. The series of observed spectral features consist of different emission lines associated with Pb-related defects. Finally, a room-temperature investigation of single-photon emitters under 490.5 nm laser excitation is reported, revealing different spectral signatures with respect to those already reported under 514 nm excitation. This work represents a substantial progress with respect to previous studies on Pb-related color centers, both in the attribution of an articulated series of spectral features and in the understanding of the formation process of this type of defect, thus clarifying the potential of this system for high-impact applications in quantum technologies.
Abstract We report on the creation and characterization of Pb-related color centers in diamond upon ion implantation and subsequent thermal annealing. Their optical emission in the photoluminescence (PL) regime consists of an articulated spectrum with intense emission peaks at 552.1 and 556.8 nm, accompanied by a set of additional lines in the 535–700 nm range. The attribution of the PL emission to stable Pb-based defects is corroborated by the correlation of its intensity with the implantation fluence of Pb ions. PL measurements performed as a function of sample temperature (in the 143–300 K range) and under different excitation wavelengths (i.e., 532, 514, 405 nm) suggest that the complex spectral features observed in Pb-implanted diamond might be related to a variety of different defects and/or charge states. The emission of the 552.1 and 556.8 nm lines is reported at the single-photon emitter level, demonstrating that they originate from the same individual defect. This work follows from previous reports on optically active centers in diamond based on group-IV impurities, such as Si, Ge, and Sn. In perspective, a comprehensive study of this set of defect complexes could bring significant insight on the common features involved in their formation and opto-physical properties, thus offering a basis for the development of a new generation of quantum-optical devices.
Diamond is a promising platform for the development of technological applications in quantum optics and photonics. The quest for color centers with optimal photo-physical properties has led in recent years to the search for novel impurity-related defects in this material. Here, we report on a systematic investigation of the photo-physical properties of two He-related (HR) emission lines at 535.2 nm and 559.7 nm (as measured at a temperature of 25 K) created in three different diamond substrates upon implantation with 1.3 MeV He+ ions and subsequent annealing. The spectral features of the HR centers were studied in an “optical grade” diamond substrate as a function of several physical parameters, namely, the measurement temperature, the excitation wavelength, and the intensity of external electric fields. The emission lifetimes of the 535.2 nm and 559.7 nm lines were also measured by means of time-gated photoluminescence measurements. The Stark shifting of the HR centers under the application of an external electrical field was observed in a CVD diamond film equipped with buried graphitic electrodes, suggesting the lack of inversion symmetry in the defects' structure. Furthermore, the photoluminescence mapping under 405 nm excitation of a “detector grade” diamond sample implanted at a He+ ion fluence of 1 × 1010 cm−2 enabled us to identify the spectral features of both the HR emission lines from the same localized optical spots. The reported results provide an insight into the structure of He-related defects in diamond and their possible utilization in practical applications.
The fabrication of luminescent defects in single-crystal diamond upon Sn implantation and annealing is reported. The relevant spectral features of the optical centers (emission peaks at 593.5, 620.3, 630.7, and 646.7 nm) are attributed to Sn-related defects through the correlation of their photoluminescence (PL) intensity with the implantation fluence. Single Sn-related defects were identified and characterized through the acquisition of their second-order autocorrelation emission functions, by means of Hanbury-Brown and Twiss interferometry. The investigation of their single-photon emission regime as a function of excitation laser power revealed that Sn-related defects are based on three-level systems with a 6 ns radiative decay lifetime. In a fraction of the studied centers, the observation of a blinking PL emission is indicative of the existence of a dark state. Furthermore, absorption dependence on the polarization of the excitation radiation with ∼45% contrast was measured. This work shed light on the existence of a new optical center associated with a group-IV impurity in diamond, with similar photophysical properties to the already well-known Si–V and Ge–V emitters, thus, providing results of interest from both the fundamental and applicative points of view.
Fluorescent emitters in diamond are considered to be a valuable resource for fields such as quantum communication, quantum photonics, and biological imaging. In this paper, we report a wide range of narrow bandwidth ( ~ 1.5 nm) spectral emission lines arising from different color centers at room temperature. The defects were created by chemical vapor deposition of thin diamond films grown on silica substrates seeded with nanoparticles of diamond and nickel. These fluorescent lines also possess single or few centers photon statistics. We correlate the zero-phonon lines, observed using confocal microscopy, with previously identified nickel-related centers which have been observed in high-pressure high-temperature diamond, with a Si/Ni complex and silicon vacancy defects. We compare our findings with recent results demonstrating single-photon emission in diamond associated with nickel-related centers to clarify and summarize previous studies concerning this specific dopant. The great variety of emission lines observed in the synthesized material, mainly associated with nickel-related centers, could be an important resource for applications relying on the presence of several emitters of single photons in the same sample. Moreover, the possibility of mass production of these centers in nanodiamonds in colloidal suspension may provide an important resource for biomarking and microscopy.
Fluorescent emitters in nanodiamonds are considered to be a valuable resource for emerging fields such as quantum communication, quantum photonics and biological imaging. In this paper we report a wide range of narrow bandwidth spectral emission lines arising from different color centers at room temperature. We associate the zero phonon lines, observed using confocal microscopy, with previously identified nickel-related centers in high pressure high temperature diamond, with a Si/Ni complex and silicon vacancy defects. In particular we show the first observation of a 850 nm emission in diamond with single photon signature, indicating the potential for diamond to harbor infrared single-photon sources. Index Terms diamond defects, single-photon emission, confocal microscopy.